The effects of yttrium and cerium on the compression properties of Ni_3Al-base alloys have beeninvestigated.The results reveal that the addition of about 0.1 wt% Y to Ni_3Al-B alloy is effective for improvingthe ductility at 1100℃.A ductility increase of about 100% is observed for this Y doped alloy.The yttrium re-fines grains of the alloy.An YNi_5 phase is found to be precipitated on the grain boundaries in the alloy con-taining 0.3 wt% Yor more.Adding about 0.1 wt% Ce to Ni_3Al-B-Cr-Zr alloy obviously improves the ductilityof the alloy at 1100℃.A ductility increase of about 50% is obtained for this alloy.The added cerium also pre-vents the formation of γ+γ' eutectic and refines it.The bulk phase of CeNi_4 appeares at the front of the eutecticin the alloys containing 0.1 wt% Ce or more. 相似文献
3.
4.
合金元素对Fe_3Al和FeAl合金力学性能的影响SCIEI 总被引:3,自引:0,他引:3
本文研究了Mo,Si,B和化学计量成分对Fe_3Al和FeAl合金室温和高温拉伸性能以及组织结构的影响,结果表明,三种合金元素都使两种铁铝化物得到明显强化,但Mo和Si使其严重变脆,硼使FeAl增加塑性,断口由沿晶型变为穿晶准解理型。富Al的Fe_3Al和富Fe的FeAl合金室温塑性较化学计量化合物有明显提高。Fe_3Al从400—550℃,FeAl从400—500℃出现反常温度关系,用组织结构方面的结果对此进行了讨论。 相似文献
5.
6.
长程有序金属间化合物FeAl和Fe_3Al合金的高温氧化行为 总被引:3,自引:0,他引:3
本文用等温氧化法研完了FeAl、FeAl+lat%B和FeAl+4at%Si以及Fe_3Al,Fe_3Al+4at%Si和Fe_3Al+4at%Mo合金的高温氧化行为。结果表明,FeAl及其合金在1000℃的氧化动力学服从抛物线规律。3种FeAl合金100h的氧化增重仅及1Cr18Ni9Ti不锈钢的三分之一。Si使氧化增重增加,B改善后期(约90h以后)的抗氧化性能。X-射线衍射分析表明,氧化膜均为单一的α-Al_2O_(30)Fe_3Al及其合金经540℃,100h氧化后,前者氧化增重类似于1Cr18N 相似文献
7.
本文研究了不同含量混合 RE 和 Ce 对 Ni_3Al-B 和 Ni_3Al-B-Cr-Zr 合金在1050℃,0.1MPa 下氧化行为的影响,以及混合 RE 对 Ni_3Al-B-Cr-Zr 合金不同温度下瞬时拉伸性能的影响。结果表明,合金中加入少量的稀土元素,促进 Al_2O_3形核,加速致密氧化膜形成,提高合金的抗氧化性。混合 RE 以固溶方式进入氧化膜,细化 NiO 和 Al_2O_3晶粒,增加塑性,不易剥落。少量 Ce 加入 Ni_3Al-B-Cr-Zr 合金,有利于形成细小密集“树根状”氧化物,使氧化膜紧密粘附在基体金属表面。加入0.1%RE 使Ni_3Al-B-Cr-Zr 合金低温抗张强度升高,对塑性影响不大,但对高温强度和塑性有害。 相似文献
8.
9.