Main influence factors on desulfurization of coal by sulfolobas 总被引:1,自引:0,他引:1
1 INTRODUCTIONHighsulfurcoalwhichletsoutpoisonousandharm fulgassuchassulfurdioxideintheprocessofcoalcom bustion ,isamainfactortoform greatareaacidrainandoccupiesonethirdreservesoftotalcoalinChina .Manhaspaidmuchattentiontoseriousenvironmentpollutionmadebysulfurincoalandsearchedforaspeed ,low costandeffectivetechnologyofdesulfurizationwhichhasbecomeasignificantenvironmentprotectiontasknowadays[1] .Coaldesulfurizationcanbesortedintofore burning ,aflame burningandafter burningbyburningproce… 相似文献
2.
从超富集植物Berkheya coddii中回收镍 总被引:1,自引:0,他引:1
提出了超富集植物的"焚烧→湿法提取与净化→电化学沉积/化学沉淀法→金属/化工产品"工艺.以镍的超富集植物Berkheya coddii为例,对该收扶物进行焚烧处理后,对焚烧产物进行氨法浸出,对浸出液进行一定处理后直接进行电积镍,最终得到高纯镍板(99.999%),该工艺既实现了对超富集植物收获物的去毒化处理,又实现了收获物中有价金属的回收.对于浸出实验,优化实验条件分别为:浸出温度60℃,氯化铵及氨水的摩尔比(n(NH4Cl):n(NH3))0.6,液固LL(L/S)5:1,浸出时间2 h;对于镍电积实验,优化实验条件为:p(Ni2+)浓度23 g/L,极距3.5 cm;电流密度200A/m2,温度40℃. 相似文献
3.
4.
目前我国大型冶炼企业产生的污酸均被当做一种高浓度重金属废水来处理,不仅需要高额的废水处理费用,而且还会产生大量的废水处理渣。结合污酸及氧化锌烟灰的主要成份,采用循环浸出工艺,利用污酸对氧化锌烟灰进行浸出,浸出完全后,综合回收浸出液中的Cu、Zn、As。实验研究了终点pH、浸出温度、浸出时间对污酸一次浸出和二次循环浸出的影响,以及双氧水加入量、温度、时间对一次除As的影响和硫化钠加入量、温度、时间对二次除As的影响。实验表明:最佳一次浸出条件为终点pH值为1.5、反应温度为85 ℃、反应时间为5 h;最佳二次循环浸出条件为终点pH值为4、反应温度为85 ℃;最佳一次除As条件为每毫升二次循环浸出液添加0.067 mL双氧水、反应温度为40 ℃、反应时间为1.5 h;最佳二次除As条件为每毫升一次除As后液添加0.02 g硫化钠、反应温度为35 ℃、反应时间为2 h。污酸综合利用后, 原来的高浓度重金属废水变成了中性废水,其中的重金属(As、Cu、Zn)质量浓度分别降至3.26、2.63和50.63 mg·L?1,稍加处理即可达到污水综合排放标准。此工艺既综合回收了污酸和氧化锌烟灰中的有价成份,又集中处理了有害元素As,消减了危险废物的产生量,达到了节能减排的目的。 相似文献
5.
6.
7.
Leaching of heavy metals from Sedum alfredii Hance biomass was studied with ammonia-ammonium chloride solution as leaching agent. The research was carried out in two phases: 1) a leaching study to determine the zinc extraction efficiency of this leaching agent, and 2) a thermodynamic analysis to identify the likely reactions and stable Zn(II) species formed in the leaching systems. Taguchi orthogonal experiment, with four variable parameters, leaching temperature, molar ratio of NH4Cl to NH3, leaching time and solid-to-liquid(L/S) ratio, and each at three levels, was used to optimize the experiment parameters by the analysis of variances. The results indicate that leaching temperature has the most dominant effect on metal extraction performance, followed by molar ratio of NH4Cl to NH3, solid-to-liquid ratio and leaching time. The optimum condition was obtained as follows: temperature of 60°C, molecular ratio of NH4Cl to NH3 of 0.6, leaching time of 2 h and solid-to-liquid ratio of 5:1. The total zinc leaching efficiency under optimum conditions reaches 97.95%. The thermodynamic study indicates that the dominant species produced by the leaching process should be the soluble Zn(NH3)42+. 相似文献
8.
9.
研究了脆硫锑铅矿精矿与铅碱性精炼废渣同时浸出制取三氧化二锑的工艺流程,得出了浸出、还原、水解、中和等过程的最优工艺条件。该工艺的技术特点是:在浸出过程中,铅碱性精炼锑酸钠渣与脆硫锑铅矿精矿互作氧化剂和还原剂。实验结果表明:浸出过程中Sb浸出率为94.56%,Pb入渣率为97.43%,很地实现了Sb与Pb的分离;浸出液经还原后,冲衡水解率达99.55%;经碱液中和,得到的三氧化二锑颜色呈白色,且其化学成分平均含量中,Sh2O3为97.69%,As为0.0055%,Pb为0.0034%,As和Pb含量低,在用等离子体法制取超细氧化锑时可作为原料。该工艺具有综合利用程度高、环境污染小、易于实现工业化生产等优点,对于铅碱性精炼废渣的资源化利用,消除因其堆存赞成的 环境污染,具有十分重要的意义。 相似文献
10.
在扩大试验基础上,以软锰矿、锌烟灰和铁屑为原料,进行了500t/a锰锌铁共沉淀粉湿法制备工艺工业试验。结果表明,Fe,Mn和zn总回收率分别为97.33%,97.16%和98.66%;Fe,Mn和zn的总直收率分别为83.58%,88.18%和85.57%。共沉淀粉的质量较高,配比非常接近理论值,杂质元素含量低。按单槽共沉粉中的金属质量推算,每槽可产铁氧体粉料(∑MexOy)0.548t,每年铁氧体粉料产量为493t,基本达到设计能力。工业试验中以共沉淀粉制成的铁氧体样环的磁性能,除个别高温高频功耗,其余均达到日本TDK公司PC30产品质量指标。 相似文献