低温烘烤型双组分水性聚氨酯涂料

采用溶液聚合法，合成了丙烯酸五元共聚物；将该共聚物中的羧基中和后制成丙烯酸多元醇分散体，将其作为B组分与一种低黏度的多异氰酸酯固化剂(A组分)组成双组分水性聚氨酯涂料。研究发现：引发剂含量、羟基含量、中和度以及A、B两组分混合搅拌方式都对双组分涂膜的性能产生重要影响。当引发剂含量为1％，羟基含量为2．7％，中和度为100％，A、B组分采用机械搅拌混合时所得的涂膜综合性能最好。水性涂料的适用期达到8h，超过相应的溶剂型涂料。     

Synthesis and properties of UV-curable hyperbranched polyurethane and its application in the negative-type photoresist

UV-curable hyperbranched polyurethane(UV-HBPU) containing carboxyl groups was synthesized from isophorone diisocyanate(IPDI), diethanolamine(DEOA), polyethylene glycol(PEG-400), hydroxyethyl acrylate(HEA), and 2,2-bis(hydroxymethyl) propionic acid(DMPA). The UV-HBPU was used as a negative-type photoresist for a printed circuit board(PCB). Fourier-transform infrared spectroscopy(FTIR) and proton nuclear magnetic resonance(1HNMR) spectroscopy of UV-HBPUs indicated that the synthesis was successful. Differential scanning calorimetry(DSC) and thermogravimetric analysis(TGA) showed that the thermal stability of the UV-HBPUs decreased as the HEA content increased. The polymer exhibited excellent photoresist properties, and the resolution of circuits based on this negative-type photoresist reached 10 μm.     

PDMS/氨基硅氧烷复合改性水性聚氨酯的制备与性能研究

以聚二甲基硅氧烷(PDMS)、聚碳酸酯二元醇(PCD)、异佛尔酮二异氰酸酯(IPDI)、二羟甲基丙酸(DMPA)和γ-氨丙基三乙氧基硅烷(KH550)为原料通过丙酮法合成PDMS/氨基硅氧烷复合改性水性聚氨酯。采用傅里叶红外光谱仪、纳米粒度仪、电子万能试验机、紫外可见分光光度计对预聚体、复合乳液以及复合膜的结构和性能进行了分析。研究结果表明,相较于未改性水性聚氨酯膜,当PDMS含量为8%(wt,质量分数,下同),KH550含量为5%时,复合改性水性聚氨酯膜的杨氏模量、拉伸强度和耐水性能得到显著提高。     

论Photoshop cs5抠图的方法

Photoshop是当前最主流的图像处置软件之一,它的功用完善,运用方便.本文主要介绍Photoshop cs5中枢图的方法.枢图即是把图像中的某一局部从原图像中"剥离"的进程.Photoshop cs5有很多方法可以把要枢取的对象和背景分开,笔者在实践操作中总结了几种方法,可以方便不同状况运用.     

pH响应性共聚微球的制备及其粒径控制

由聚甲基丙烯酸(PMAA)大分子单体参与的分散共聚反应,制得PMAA接枝聚苯乙烯(PSt-g-PMAA)共聚微球.通过扫描电子显微镜、Zeta电位及粒径分析仪对微球粒径与形态进行了表征;同时探讨了多种聚合反应务件(介质的极性、PMAA大分子单体的浓度和反应温度)对共聚微球粒径的影响,发现通过改变反应条件可有效地将微球的直径控制在340～1200nm的范围内;并发现微球在分散状态下对pH的变化有明显的响应性,该类共聚微球可望在药物负载和蛋白质吸附分离等方面得到应用.     

超支化聚硫醚改性环氧丙烯酸酯光固化涂料的制备及性能研究

目的 研究超支化聚硫醚的结构对环氧丙烯酸酯复合光固化涂层性能的影响.方法 利用存在明显反应速率差异的巯基-点击化学反应,首先以三羟甲基丙烷三(3-巯基丙酸)酯(TMPMP)和甲基丙烯酸缩水甘油酯(GMA)为原料,一锅法合成端巯基超支化聚硫醚(HBP-SH);然后以四氢呋喃丙烯酸酯(THFA)为改性单体,按HBP-SH与...     

Preparation and characterization of carboxylterminated poly (butadiene-co-acrylonitrile) -epoxy resin prepolymers for fusion-bonded-epoxy powder coating

Liquid carboxyl-terminated poly(butadiene-co-acrylonitrile)(CTBN)-epoxy resin(EP) prepolymers were prepared with different contents of CTBN.The chemical reactions between EP and CTBN were characterized by Fourier ransform infrared(FTIR) spectroscopy and gel permeation chromatography(GPC).The scanning electron micrograph(SEM) and dynamic mechanical analysis(DMA) of curing films showed phase separation,and the rubber particles were finely dispersed in the epoxy matrix.Mechanical properties analysis of curing films showed that impact strength and elongation at break increased significantly upon the addition of CTBN,indicating good toughness of the modified epoxy resins.Thermogravimetric analysis(TGA) showed that the incorporation of CTBN had little effect on the thermal stability of EP.Fusion-bonded-epoxy(FBE) powder coatings modified with CTBN-EP prepolymers were prepared.The experimental results demonstrate the ability of CTBN-EP prepolymers,toughening technology to dramatically enhance the flexibility and impact resistance of FBE coatings without compromising other key properties such as corrosion protection.     

改进的盲签名电子现金方案

针对在线电子现金系统现有的重复攻击和用户信息泄露等不安全因素,设计了一种通过可信第三方加入序列号的RSA盲签名方案,并对方案的安全性及效率性进行了分析,该方案具有防重复攻击、防抵赖攻击、防重复支取、不可跟踪性等一系列安全性更高的特点,另外避免时间戳的加入,无需对电子现金信息进行跟踪、存储,只需存储所对应的序列号,大大提高了空间效率。     

光固化复合电泳涂层材料的制备及其传感性能

目的 研究电泳沉积条件及光交联对氧化石墨烯与胶束共沉积制备的生物传感涂层形貌、性能的影响。方法 首先通过光敏单体甲基丙烯酸羟乙酯（HEMA）改性生物大分子γ-聚谷氨酸制备可光交联的大分子γ-PGA-HEMA。然后,将光敏大分子与辣根过氧化酶（HRP）在溶液中静电自组装制备功能性纳米粒子溶液,利用纳米粒度分析仪、透射电子显微镜（TEM）对纳米粒子的粒径和形貌进行表征。随后,诱导复合纳米组装体与前驱体氧化石墨烯（GO）共组装制备多组分复合沉积液。最后,在上述复合沉积液的基础上进行电化学还原GO,控制不同沉积条件,通过电泳沉积法在玻碳电极表面制备具有特异性识别功能的生物传感涂层,利用扫描电子显微镜（SEM）、电化学工作站等研究了电泳沉积条件及光交联对涂层形貌及性能的影响。结果 当沉积电压为1.5 V,沉积时间为120 s,GO质量浓度为0.1 mg/mL时,电泳沉积制备的涂层表面光滑,具有较好的致密性和均一性。光交联后,涂层的致密性和稳定性进一步提高,此时该涂层对过氧化氢（H2O2）具有良好的电流响应。结论 电泳沉积复合共组装胶束制备光交联涂层过程中,沉积时间、沉积电压、GO含量均存在最优值,最优值下制备的涂层结构完整,致密性最好。光交联可进一步提高涂层的稳定性,生物传感性能最好。     

基于聚苯胺的光固化防腐蚀涂层

利用十二烷基苯磺酸 (DBSA) 对本征态的聚苯胺 (PANI) 进行掺杂,将不同含量的掺杂后的聚苯胺分别加入到光固化树脂聚氨酯丙烯酸酯 (6071) 中,制备了一种低VOC排放的光固化聚苯胺防腐蚀涂层。通过实时红外以及漆膜性能的测试选择了合适的光引发剂,通过电化学阻抗谱、盐雾实验以及极化曲线对涂层的防腐蚀性能进行了测试。结果表明,加入0.4%DBSA-PANI的光固化涂层具有最佳的防腐蚀性能。