The 8% (mass fraction) yttrium-partially-stabilized zirconia (8YSZ) ceramic was fabricated via liquid phase sintering at 1
200–1 400 °C by adding different mass ratios of CuO-16.7%TiO2 (molar fraction) as sintering aid. Relative density, microstructure, Vickers hardness and bending strength as a function
of sintering temperature and additive content were investigated. The experiment results show that liquid phase sintering at
low temperature can be realized through adding CuO-16.7% TiO2 to 8YSZ. The Vickers hardness and bending strength of samples with sintering aid are generally much higher than those of
samples without sintering aid for all sintering temperatures, and increase with the increase of sintering temperature. When
the addition content of CuO-16.7% TiO2 is beyond 0.5%, the relative density, Vickers hardness and bending strength decrease with the increase of the mass ratio
of sintering aid. Low additions of sintering aid are beneficial to aiding densification; high additions of sintering aid are
detrimental to the sintered properties mainly due to greater amounts of pores generated by the volatilization of oxygen with
the eutectic reaction between copper oxide and titanium dioxide. It is found that the fine grain size and high relative density
are two main reasons of the high bending strength and Vickers hardness of the materials. 相似文献
2.
首先分析了旋耕机单位体积功耗数学模型,根据数学模型的特点,提出用广义最小二乘法确定目标函数和用最速下降法优化运动参数,为旋耕机总体参数的优化设计提供了可靠的计算模型。 相似文献
3.
4.
利用超音速火焰喷涂方法制备出NiCr/ Cr3C2 和NiCr/ Cr3C2-BaF2 ·CaF2 两种涂层,?炝肆街滞坎愕淖橹?测定了两种涂层在650 ℃和800 ℃下的摩擦磨损性能,进而分析了BaF2 ·CaF2 共晶相对涂层的润滑减摩作用,讨论了两种涂层的适用范围。结果表明,NiCr/ Cr3C2-BaF2 ·CaF2 涂层在800 ℃展现出优异的耐磨自润滑效果,摩擦系数最低,仅为0. 2644,磨损率也较小,为5. 88×10-6 mm3 / (N·m);而NiCr/ Cr3C2 涂层在650℃的磨损率更小,仅为3. 66×10-6 mm3 / ( N·m)。两种涂层在不同温度下表现出不同的摩擦磨损机制:NiCr/Cr3C2 涂层在650 ℃和800 ℃均表现为典型的粘着磨损,但在650 ℃时有疲劳迹象,在800 ℃时则发生严重塑性变形;NiCr/ Cr3C2-BaF2·CaF2 涂层在650 ℃以磨粒磨损为主,在800 ℃时,由于氟化物润滑膜的作用,仅发生轻微的粘着剥落。 相似文献
5.
采用X射线衍射(XRD)、扫描电子显微镜(SEM)、维氏硬度计、电子万能材料试验机研究MoSi_2-Si_3N_(4(p))/SiC_(w)复合材料的结构、形貌、硬度、断裂韧性,并对SiC晶须和Si_3N_4颗粒复合强韧化MoSi_2的机理进行了探讨.结果表明,SiC晶须和Si_3N_4颗粒对MoSi_2具有协同强韧化作用,MoSi_2-20%Si_3N_(4(p))-20%SiC_(w)(体积分数,下同)复合材料的抗弯强度达427 MPa,室温断裂韧性达到10.4 MPa·m~(1/2),均高于单一强韧化剂的强韧化效果.MoSi_2-20%Si_3N_(4(p))-20%SiC_(w)复合材料的强化机理为细晶强化和弥散强化;韧化机制为细晶韧化、裂纹偏转与分支和微桥接韧化. 相似文献
6.
7.
通过分析生产调度理论研究的现状和存在的问题,提出了敏捷制造(AM)环境下具有可变性特征制造系统的智能自适应调度方法,阐述了智能自适应调度方法研究的基本思路,旨在为AM环境下生产调度提供一种有效的方法。 相似文献
8.
溶胶-凝胶法制备的ZnO:Al薄膜的微观结构及光学、电学性能 总被引:1,自引:0,他引:1
采用溶胶-凝胶法制备了ZnO:Al(AZO)透明导电薄膜.通过X射线衍射(XRD)、紫外-可见分光光度计 (UV-Vis)、扫描电镜(SEM)和电阻测量装置,考察了Al掺杂量、退火温度及镀膜层数等工艺参数对薄膜的微观结构和光电性能的影响.结果表明,退火温度越高,多晶AZO薄膜的(001)晶面择优取向生长的趋势越强,并且随退火温度升高,薄膜的晶粒尺寸增大,透光率增加.薄膜晶体结构为纯ZnO的六角纤锌矿结构.在掺杂浓度1%(摩尔分数)、退火温度500℃及镀膜层数10的条件下,得到了电阻率为3.2×10-3Ω·cm、可见光区的平均透射率超过90%的AZO薄膜. 相似文献
9.
公路隧道射流风机与竖(斜)井排出式组合通风排烟设计及控制方案研究 总被引:1,自引:0,他引:1
针对公路隧道射流风机与竖(斜)井排出式组合通风排烟方式建立系统设计理论计算模型,分析不同工况下的通风排烟控制方案要求及影响因素,并进行实例分析,以便为该组合通风排烟方式的系统及通风排烟控制方案设计提供参考. 相似文献
10.
以碳纤维增强环氧树脂作为基体材料, 设计并制备了一种轻质、环保的隔热涂层。为解决基体材料与涂层之间热膨胀系数差别大导致易于开裂的问题, 同时实现具有高反射率和低热导率的目标, 通过添加聚氨酯、TiO2、SiO2、Al2O3等填料制备连接层、阻隔层、反射层等三个不同功能层形成复合隔热涂层。通过优化涂层脱落时间、反射率、热导率等, 得到连接层、阻隔层、反射层最优厚度分别为80、120和90 μm。优化后的隔热涂层具有优异性能: 涂层的反射率高达0.95, 导热系数为0.048 W·m -1·K -1, 隔热温差为20.1 ℃; 耐热冲击性能良好, 190 ℃的最大失重率为3.7%, 并在随后保持稳定; 在160 ℃连续保温4 h后表面变黄, 但无明显脱落现象, 同时, 纳米填料颗粒保持原状态。 相似文献