Microstructure and mechanical behaviour of 3Y-TZP/Mo nanocomposites possessing a novel interpenetrated intragranular microstructure

Yttria stabilized tetragonal zirconia polycrystal (Y-TZP)/0-100 vol % molybdenum (Mo) composites were fabricated by hot-pressing a mixture of Y-TZP powder containing 3 mol % yttria (Y₂O₃) and a fine Mo powder in vacuum. This composite system possessed a novel microstructural feature composed of an interpenetrated intragranular nanostructure, in which either nanometer sized Mo particles or equivalent sized zirconia (ZrO₂) particles located within the ZrO₂ grains or Mo grains, respectively. The strength and toughness were both greatly enhanced with increasing Mo content for the 3Y-TZP/Mo composites thus breaking through the strength-toughness tradeoff relation in transformation toughened ZrO₂ and its composite materials. They exhibited a maximum strength of 2100 MPa and a toughness of 11.4 MPa·m^1/2 for the composite containing 70 vol % Mo. These simultaneous improvements in strength and toughness were determined to be the result of a decrease in flaw size associated with the interpenetrated intragranular nanostructure, and a stress shielding effect created in the crack tip by the elongated Mo polycrystals bridging the crack tip in addition to the stress induced phase transformation.     

Analysis of brushless three-phase synchronous generator without exciter

Recently, a demand for small-capacity generators has been increasing as electric sources in small ships and automobiles or as portable electric sources driven by engines. It is desired that the structure of small-capacity generators be simple and robust, and that the generators be highly reliable, easily maintained and controlled. This paper describes an analysis of the original brushless synchronous generator without exciter. The output voltage can be adjusted in the wide range by controlling the stator dc current. To analyze the characteristics of this generator, the finite element method is applied. It is found that the results of theoretical analysis agree well with the experimental results.     

Flashover voltage characteristics of contaminated station insulators under temporary ac overvoltages in the ac system connected with a frequency converter station

According to the recent analysis results of temporary ac overvoltage in the ac system connected with a frequency converter station, large-magnitude over-voltages were confirmed to occur under some special system conditions. Most of the station insulators currently used cannot withstand such overvoltages according to an evaluation based on the data obtained earlier. The necessity of tests to be done to evaluate such performance more accurately was recognized. Both power frequency and switching impulse overvoltage flashover tests were made on contaminated insulators by the method well simulating the natural wetting condition. Switching impulse flashover voltage with the waveshape having a long wavefront time of 2 ms can be well correlated with the flashover voltage characteristics of temporary ac overvoltage. Higher flashover voltage characteristics were obtained by a clean fog test method compared with those obtained by equivalent fog test method.     

IBM's Linux watch, the challenge of miniaturization

Nearly four years in development, the IBM Linux watch contains a complete computer system that runs Linux, displays X11 graphics, and has wireless connectivity. The system fits in a case that could pass as a slightly unusual analog timepiece with a somewhat odd shape and an extraordinarily brilliant face. The developers have created two versions of the watch, one with an organic light-emitting diode display and the other with a liquid crystal display. Still considered a research prototype, the watch already runs some personal information management applications, and it can communicate with PCs, PDAs, and other wireless-enabled devices, viewing condensed e-mail and directly receiving pager-like messages. Eventually, users will be able to access various Internet-based services, such as up-to-the-minute information about weather, traffic conditions, the stock market, and sports     

A 6-ns ECL 100 K I/O and 8-ns 3.3-V TTL I/O 4-Mb BiCMOS SRAM

The authors report a 4 M word×1 b/1 M word×4 b BiCMOS SRAM that can be metal mask programmed as either a 6-ns access time for an ECL 100 K I/O interface to an 8-ns access time for a 3.3-V TTL I/O interface. Die size is 18.87 mm×8.77 mm. Memory cell size is 5.8 μm×3.2 μm. In order to achieve such high-speed address access times the following technologies were developed: (1) a BiCMOS level converter that directly connects the ECL signal level to the CMOS level; (2) a high-speed BiCMOS circuit with low threshold voltage nMOSFETs; (3) a design method for determining the optimum number of decoder gate stages and the optimum size of gate transistors; (4) high-speed bipolar sensing circuits used at 3.3-V supply voltage; and (5) 0.55-μm BiCMOS process technology with a triple-well structure     

Silica removal from Mokai, New Zealand, geothermal brine by treatment with lime and a cationic precipitant

Preliminary experiments using two chemicals (CaO, a quicklime, and a cationic nitrogen-bearing precipitant, EC-004) to remove silica from geothermal brine were undertaken at the Mokai geothermal plant, New Zealand. The brine was mixed with the reagent (CaO or EC-004). The reaction was studied from the start of the experiment (NRT, 0 min, no retaining time) and after 15 min (15RT) at 90 °C. The concentration of silica in the brine was initially 954 mg/l, and decreased linearly with increasing reagent concentration. When CaO is added, the silica concentration at 15RT was 200 mg/l lower than at NRT and became almost zero on addition of 1.5 g/l. In contrast, when EC-004 is added, the total silica concentration nearly reaches the solubility of amorphous silica at 90 °C. In order to prevent silica scaling in Mokai brines cooled to 90 °C, the CaO and EC-004 added should be individually adjusted to 0.5 g/l and 80 mg/l, respectively.     

Deposition of carbon films by electrolysis of a water-ethylene glycol solution

An attempt was made to deposit carbon films by electrolysis of a water-ethylene glycol solution. Carbon plate and an n-type silicon substrate were dipped in the solution and a high d.c. potential was negatively applied on the silicon substrate. Some deposits were observed in the region between the boiling point curve and the line approximately 50 °C below and parallel to the boiling point, when electrolysis was carried out at 1 kV for 6 h. For higher potentials of 1.4–2.0 kV and longer electrolysis of 12 h, some samples showed a broad X-ray diffraction peak and Raman peaks, corresponding to graphitic carbon.     

Steady-state torque control system with secondary-current feedback for three-phase squirrel-cage induction motors

This paper presents a highly stable steady-state torque control system with a feedback of a secondary current signal. The torque control system is constructed with a feedback of the secondary current (I₂) signal using a quick response magnetic-field sensor constructed with an amorphous core multivibrator bridge, which can solve the secondary resistance change problem for temperature variation in the IM. Moreover, we added a state feedback to the system to improve the response speed for the unit step function of a torque order. The I₂ sensor method has advantages especially at a low-speed range, in which conventional method using an integrator shows control errors.