Aldol condensation of campholenic aldehyde and MEK over activated hydrotalcites

In this paper, activated Mg-Al hydrotalcites were used as catalysts in the aldol condensation of campholenic aldehyde and methyl ethyl ketone (MEK). These materials represent an attractive alternative to less environmentally friendly liquid bases in a number of base-catalyzed reactions involved in the pharmaceutical and fragrance industries. The presence of basic hydroxyl groups in the interlayer space leads to very active materials. However, the relation between the activity of reconstructed hydrotalcites and the rehydration procedure is still not well understood. Different rehydration protocols in combination with extensive characterization studies were performed, including XRD, SEM, IR spectroscopy and TPD of CH₃CN and CH₃NO₂. The materials were tested as catalysts in the aldol condensation of campholenic aldehyde and MEK, and relationships between the catalytic performance of the activated hydrotalcites and the rehydration procedure were derived. Several factors may influence the activity and selectivity of this reaction, such as the reaction temperature, the molar ratio of the reactants and the degree of rehydration of the hydrotalcite-like catalysts. The selectivity towards the formation of the desired branched isomer increases when performing the reaction at low temperatures.     

一类含查尔酮结构的光敏性二胺的合成研究

以醛、酮为原料经羟醛缩合反应合成了具有一类含查尔酮结构的光敏性二胺:1-(3-氨基苯基)-3-(4-氨基苯基)-2-丙烯-1-酮与对-二(间氨基肉桂酰)苯.通过优化实验得到最佳的合成工艺为:醛、酮在温度为0℃下,以乙醇为溶剂,氢氧化钠为催化剂,进行羟醛缩合反应3h.收率可达到86%,经液相色谱分析其纯度分别为99.92%,99.91%,紫外可见最大吸收波长分别为349nm、361nm.所得方法操作简便,收率较高,原料易得.并用元素分析、核磁共振、红外光谱等手段对产物的结构进行了表征.     

Organic–silicate hybrid catalysts based on various defined structures for Knoevenagel condensation

Two types of organic–inorganic hybrid base catalysts are prepared. Organic-functionalized molecular sieves (OFMSs), particularly “amine-immobilized porous silicates”, are designed based on common idea to immobilize catalytic active sites on silicate surface. Silicate–organic composite materials (SOCMs), such as “ordered porous silicate–quaternary ammonium composite materials”, are the precursors of ordered porous silicates obtained during the synthesis. Both the OFMS and the SOCM are used as the catalysts for Knoevenagel condensation. Among the OFMSs, there is clear tendency that the use of molecular sieve with larger pore volume and/or surface area gives the product in higher yield. Aminopropylsilyl (AP)-functionalized mesoporous silicates such as AP-MCM-41 gives the product in high yield under mild conditions. No loss of activity is observed after repeated use for three times. The SOCMs are also active for the same reaction. The precursors of the mesoporous silicates are more active than those of microporous silicates. This material can be repeatedly used without significant loss of activity. High activity is not due to the leached species. The active sites of the SOCM catalysts are considered to be SiO⁻ moieties located on the pore-mouth. Activity of the SOCM increases when the reaction is carried out without solvent, whereas decrease in activity of the OFMS is observed in the solvent-free system.     

聚乳酸的直接合成研究(Ⅱ)

研究了以乳酸单体为原料的直接熔融缩聚的工艺条件,包括工艺路线、原料含水率、催化剂种类、温度及余压对合成的影响。结果表明:采用适当的工艺能通过熔融缩聚法制备出高分子质量的聚乳酸,且具有良好的生物降解性能。     

3-取代苯基-5-羟基-5-三氟甲基异噁唑啉的合成

3 取代苯基 5 羟基 5 三氟甲基异口恶唑啉是合成具有异口恶唑结构的原卟啉原氧化酶抑制剂类除草剂的重要中间体。通过以下途径制得4个具有不同取代基的异口恶唑啉中间体:首先,在回流状态,n(甲醇钠)∶n(取代苯乙酮)=2∶1的甲醇钠存在下,取代苯乙酮与三氟乙酸乙酯缩合得到取代苯基 4,4,4 三氟 1,3 丁二酮;后者可在室温下,于二氯甲烷溶剂中,用氯化硫酰氯化,在侧链上引入氯原子;最后,以乙酸作溶剂,回流下,具有不同取代基的苯基 1,3 丁二酮与盐酸羟胺闭环得到产物。反应总收率大于95%。产品结构经质谱、核磁共振氢谱、碳谱确认正确。     

磁性漆酚缩甲醛微球的制备与表征

在共沉淀法合成磁流体的基础上,用悬浮缩聚法制备了磁性漆酚缩甲醛微球,并用X射线粉末衍射、透射电镜和热重分析等对微球进行结构表征。实验结果表明,Fe3O4磁流体的粒径为纳米量级,纳米Fe3O4粒子能够提高复合物的热性能。该微球粒径约1mm,是核壳结构,具有良好的耐溶剂性和耐热性。     

树脂固体酸催化剂用于合成尿囊素研究

对三阳离子交换树脂在乙醛酸与尿素缩合反应中的催化活性进行了研究。实验得到其最佳反应条件为：尿素与乙醛酸摩尔比4：1，反应温度70℃，反应时问8h。在此条件下，尿囊素产率达到69．6％。实验结果还表明，阳离子交换树脂催化剂优于HZSM-5分子筛催化性能。     

Aldol condensation of butanal over alkali metal zeolites

Alkali metal zeolites and metal oxides were used for the aldol condensation of n-butanal to 2-ethyl-2-hexenal. The order of activity at 150 °C and 1 atm. was: CsNaY > NaY > LiNaY > MgO >Al₂O₃. Selectivity to 2-ethyl-2-hexenal was 100% for both pure and mixed isomer feed. Infrared spectroscopic studies showed that stable catalysts were produced by propene pretreatments which blocked Lewis acid sites. Adsorption of ammonia and carbon dioxide on CsNaY during aldol condensation of n-butanal causes a decrease in rate. This result, along with the order of activity, suggests that the presence of both acid and basic sites produce higher activity than strongly basic MgO.Work performed at San Jose State University.     

富氮生物质热解气的分级冷凝特性研究

采用固定床热解反应系统对稻壳负载尿素进行了热解耦合分级冷凝的研究，实验采用三级冷凝的方法，对比了热解温度(400、500、600℃)和冷凝温度(30、60、90℃)对产物分布和富集的影响，研究了生物质富氮热解和分级冷凝的机理。结果表明：富氮热解促进了Maillard反应产生含氮杂环物；分级冷凝富集规律明显，一级生物油富集了高露点的酚类，二级生物油富集了低露点的含氮杂环物；提高热解温度可以增加二级生物油中含氮杂环物的含量和降低二级生物油水分含量，热解温度为500℃时，液体产物产率和酚类产物产率最大；提高冷凝温度能增强各级油组分的富集效果，并降低一级生物油水分含量，一级冷凝温度为90℃时，水分几乎完全富集在第二级中，且一级生物油酚类产物含量最高。     

高粘度二甲基二苯基室温硫化硅橡胶制备

探讨了水解缩聚、环体开环共聚两种合成方法制备高粘度二甲基二苯基室温硫化硅橡胶的可行性，讨论了工艺过程对产品性能的影响因素。