TiN/SiNx submicronic multilayer coatings obtained by chemical vapor deposition in a fluidized bed reactor at atmospheric pressure (AP/FBR-CVD)

TiN/SiN_x multilayer coatings were deposited on stainless steel by Chemical Vapor Deposition in a Fluidized Bed Reactor at Atmospheric Pressure (AP/FBR-CVD) by reaction of TiCl₄ and SiCl₄ with NH₃ at 850 °C. Due to the immiscibility of crystalline TiN and amorphous SiN_x, interdiffusion between layers is avoided even at the high working temperature. The thickness of the individual layer was in the nanometer range. Coatings were characterized by means of SEM, TEM, GD-OES, SIMS, XRD and nanoindentation. A mechanism for the growth rate and diffusion of Ti and Si into the steel is discussed.     

Wear resistance of ceramic coating on AZ91 magnesium alloy by micro-arc oxidation

The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation （MAO） was characterized. The results show that the ceramic coating （3.4-23 μm in thickness）on the surface ofAZ91 alloy was attained under different micro-arc oxidation treatment conditions, which consist mainly of MgO, Mg2SiO4 and MgSiO3 phases. Nano-hardness in a cross-sectional specimen was determined by nano-indentation experiment. The MAO coatings exhibit higher hardness than the substrate. Dry sliding wear tests for the MAO coatings and AZ91 alloy were also carded out using an oscillating friction and wear tester in a ball-on-disc contact configuration. The wear resistance of the MAO coatings is improved respectively under different treatment time as a result of different structures of ceramic coatings formed on AZ91 alloy.     

小波分析在火箭发动机包覆质量检测中的应用

将小波分析方法应用到固体火箭发动机包覆层胶接质量检测中，利用小波分析的多分辨率特征，对超声检测信号的小波系数进行特征提取，从而获得包覆层胶接状态的灰度图像，图像效果很好，而且与试件情况基本吻合。     

Influence of expandable graphite on fire resistance and water resistance of flame-retardant coatings

Expandable graphite (EG) coating and ammonium polyphosphate-pentaerythritol-melamine (APP-PER-MEL) coating were prepared. Thermal degradation and char formation of the coatings were investigated by differential thermal analysis (DTA), thermogravimetry (TG), X-ray diffraction (XRD), scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The results have shown that the anti-oxidation and fire-resistant properties of expandable graphite coating containing EG with size of 74 μm are better than those of APP-PER-MEL coating. The static immersion test was applied to study water resistance of the coatings, and the fire protection test and mechanical test were used to analyse heat insulation and mechanical properties of coatings before and after water immersion. The fire-resistant and mechanical properties of APP-PER-MEL coating were severely damaged by water immersion, whereas EG coating containing 8.5% EG with size of 74 μm could retain the good fire resistance even after 500 h water immersion.     

Ambient temperature cured TiB_2 cathode coating for aluminum electrolysis

1　INTRODUCTIONAluminumindustryhasbeendevelopingrapidlyinChinainrecentyears ,soderbergcellshavebeenre placedwithmodernprebakecellsinmanyaluminumsmelters,theaveragecelllifehowever ,forprebakecellsinourcountrywasonlyabout130 0d ,muchlowerthantheaveragecelllife ,i.e .above 2 5 0 0d ,forthecellsindevelopedcountries .TiB2 cathodecoating (TCC)couldbeoneofthesolutionstoreducegreatlytheopportunitytotheearlyfailureofcellsandextendthecelllifeofprebakecell[14 ] .Theconceptoftitaniumdiboride (TiB2 …     

Na2SiO3—KOH—（NaPO3）6溶液中Ti6Al4V微弧氧化陶瓷膜研究

用非平衡交流微弧氧化法于Na2SiO3-KOH-(NaPO3)6溶液中在Ti6Al4V表面形成氧化物陶瓷膜。分别用扫描电镜、电子探针及X射线衍射研究了陶瓷膜的组织形貌、元素分布和相组成。相对致密均匀的膜层主要由TiO2(钙钛矿相及金红石相)及非晶相组成。厚约20μm的膜可分为3层：过渡层、致密层与疏松层。电解液所含元素Si，P进入到膜层中，表明电解液组元急烈参与微弧氧化反应，这为通过选择电解液来设计膜层的相组成进而对膜层进一步改性提供途径。     

激光熔覆TiC增强FeAl金属间化合物基复合材料涂层磨损性研究

利用激光熔覆技术在1Cr18Ni9Ti奥氏体不锈钢表面制得了以TiC为增强相、以FeAl 金属间化合物为基体的耐磨复合材料涂层，研究了激光熔覆。FiC／FeAl复合材料涂层在干滑动磨损条件下的耐磨性能及磨损机制。结果表明：随着载荷和滑动速率的增加，TiC／FeAl金属间化合物基复合材料涂层的磨损速率增加，其磨损机制随着载荷的增加逐渐由磨料磨损向粘着磨损转变；激光熔覆层中TiC体积分数的增加，一方面提高了涂层的磨料磨损抗力，另一方面降低了熔覆层表面与对磨材料之间的粘着倾向，提高了TiC／FeAl涂层的滑动磨损性能。激光熔覆TiC/FeAl金属间化合物基复合材料涂层具有优异的耐磨性能并随TiC体积分数的增加而提高。     

杭州湾跨海大桥钢管桩的涂层防护

杭州湾跨海大桥采用钢管桩沉桩基础。钢管桩的腐蚀问题采用涂层加阴极保护的防护体系,其中涂层部分采用单层/双层/三层重防腐环氧粉末喷涂防护方案解决。介绍了三种涂层结构及其用途。     

风力发电机塔架的涂装

按照设计要求制备用于风力发电机塔架的防腐蚀配套涂料,塔架的筒体内部涂层由环氧树脂聚酰胺富锌底漆和环氧树脂聚酰胺云母氧化铁中涂漆组成,筒体外部涂层由环氧树脂聚酰胺富锌底漆、环氧树脂聚酰胺云母氧化铁中涂漆和丙烯酸脂肪族聚氨酯面漆组成。该涂料体系的防腐涂层可常温固化,厚度达到275μm,防腐蚀寿命可达20年之久,其防腐效果、耐冲击性和耐候性良好。文章同时讨论了涂装工艺过程中易出现的问题及解决办法。     

水性聚氨酯材料配方设计技巧

介绍了优选法的0.618法和分数法,对其进行改进创新和原理证明,并应用于生产涂料配方设计中。