Electrochemical C-V Characteristics and Photoluminescence of a-C∶N Films

Amorphous carbon (a-C) films and amorphous carbon films incorporating with the nitrogen (a-C∶N) were deposited on silicon substrates in a radio-frequency driven plasma enhanced chemical vapour deposition system, while the surface electrical properties of films were investigated by electrochemical capacitance-voltage measurements. It was examined the effect of the interface defects on the properties and deduced that the conducting type of a-C∶N films was n-type. Subsequently, a comparative studies of a-C and a-C∶N films were performed by photoluminescence spectra depending on the temperature. With the decrease of the temperature, the main band with peak energy of 2.48 eV in the a-C∶N films was more intense compared with the other three bands caused by amorphous C in the a-C films.     

铸铁热分析用试样新型激冷剂的实验研究

从冷却曲线上相变段倾角最小原则出发，研究了新型激冷剂的配比与热分析法检测铸铁成分精度的关系，实验结果表明，能使相变段倾角最小的成分配比，也能提高对铸铁成分的热分析和检测精度。     

钻井过程中硫化氢的处理工艺

目的：防止钻井过程中出现的硫化氢对人身安全和钻具造成危害。方法：分析氢脆破坏机理和处理硫化氢的化学原理。结果：提出了处理硫化氢的关键技术，并结合塔中162井的实钻经验，总结出了钻井过程中对硫化氢的几点认识。结论：提高泥浆pH值、加入除硫剂及提高泥浆密度等措施是钻井过程中处理硫化氢的关键技术，从而有利于富含硫化氢的灰岩、白云岩等裂缝性油气藏的钻井生产。     

Graphite formation on Ni film by chemical vapor deposition

Thin film formation of graphite by chemical vapor deposition using 2-methyl-1,2′-naphthyl ketone as a starting material was carried out on Ni film substrates. On Ni films directly deposited on quartz glass, the graphite films were obtained when the Ni film thickness was above 1 000 Å and above 5 000 Å at 700 °C and 1 000 °C, respectively. Depositions on thinner Ni film substrates comprise amorphous carbon (a-C) or graphite tubes which was owing to the thermal coagulation of the Ni film into droplets. On the other hand, graphite film was obtained on the Ni film with thickness 10 Å when a-C was inserted between the Ni film and the quartz glass. The coagulation of the Ni film is considered to be avoided by inserting a-C layer.     

Characterization and modification of fillers for paints and coatings

This paper highlights the possibility of inverse gas chromatography for the surface characterization of common fillers (CaCO₃, talc, SiO₂,) for paints and coatings. Divided solids are described, on the one hand, by the dispersive component of their surface energy and, on the other, by a specific parameter indicating their acid-base interaction potential. The role of the surface morphology at a molecular level is also examined. It is demonstrated that steric effects play an important role in the adsorption of probes on lamellar solids like talc. The consequences of surface treatments as well as examples of practical applications are also reported.     

Hybrid gas-to-particle conversion and chemical vapor deposition for the production of porous alumina films

Porous alumina films can be found in a wide variety of materials, including filters, thermal insulation components, dielectrics, biomedical and catalyst supports, coatings and adsorbents. Production methods for these films are as equally diverse as their applications. In this work, a hybrid process based upon chemical vapor deposition and gas-to-particle conversion is presented as an alternative technique for producing porous alumina films, with the main advantages of solvent-free, low substrate-temperature operation. In this process, nanoparticles were produced in the vapor phase by reaction of aluminum acetylacetonate in the presence of oxygen. Downstream of this reaction zone, these nanoparticles were collected via thermophoresis onto a cooled substrate, forming a porous film. Some deposited films were subjected to post-processing in the form of annealing in air. Fourier-transform infrared spectra and X-ray energy-dispersive spectroscopy analysis confirmed the production of alumina at processing temperatures above 973 K. X-Ray diffraction revealed that the films were amorphous. Film thickness, ranging from 30 to 250 μm, and the average deposition rate were determined from scanning electron microscopy results. From transmission electron microscopy, the average primary particle size was determined to be approximately 18 nm and the formation of nanoparticle aggregates was evident. Annealing of the films at temperatures ranging from 523 to 1173 K in the presence of air did not have an effect on particle size. The specific surface area of the powder composing the films ranged from 10 to 185 m² g⁻¹, as determined from nitrogen gas adsorption by the Brunauer–Emmett–Teller method.     

A novel technique to prepare LiNbO3 at low temperature

Fresh niobium hydroxide was first precipitated from NbF₅ solution using an aqueous ammonium hydroxide under basic conditions. Then a simple procedure of mixing lithium and niobium hydroxides together and heating at a low temperature (400 °C) produced pure ultrafine single phase LiNbO₃ (LN). In the literature, this is the lowest temperature so far reported on the formation of LN. The phase content and lattice parameters are determined by X-ray diffraction (XRD). The average particle size and morphology were studied by transmission electron microscopy (TEM).     

Formation of mushroom-like ZnO microcrystals through a solution calcination process

Mushroom-like ZnO microcrystals have been prepared via a solution calcination route, using Zn(NO₃)₂ as Zn source in the absence of any surfactants, templates or catalysts. This is the first example to prepare mushroom-like crystals as semiconductors, which are expected to show particular physical properties. The ZnO products were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy and photoluminescence (PL) spectrum measurements. A suitable concentration of Zn(NO₃)₂ solution was important for the growth of the mushroom-like products. The reported synthetic procedure is straightforward and inexpensive, and thus can be readily adopted to produce large quantities of mushroom-like ZnO microcrystals.     

Corrosion Condition Evaluation at Muddy Creek Bridge

Corrosion rates were measured at the exposed spots of rebars near three corners of Muddy Creek Bridge located in northern West Virginia using a 3LP device. Also, chloride contents of the concrete samples taken from the vicinity of the spots were analyzed using a wet chemical method that had been developed in this study. The average corrosion rate over the three spots was 4.66 mA/m2, which is in the range of corrosion damage possible in 10–15 years. The average chloride content of the concrete over the three spots was 703 parts per million (ppm), which is well above the threshold limit value of 260 ppm. Although the corrosion rate measurement method using a 3LP device is by manual operation, it is found to be reliable and effective, and, thus, recommended for future studies of this kind of research. The wet chemical method developed in this study is found to be effective.