Formation and wear mechanism of nickel titanium intermetallics during heat treatment of nickel coating on Ti-6Al-4V substrate

In the present work, inter-diffusion of nickel and titanium and formation of Ni-Ti intermetallic compounds on Ti-6Al-4V substrate have been studied. Initially, nickel was electrodeposited on the alloy using a modified Watts bath solution at a current density of 2 A dm^?2 for 1?h. The coated specimens were then heat treated for different durations at 750, 800 and 850 °C under argon atmosphere. The effects of temperature and time on the characteristics, hardness and wear resistance of intermetallic phases were investigated. The results showed that a multilayer structure was formed after heat treatment, an outer layer of residual nickel, an area of intermetallic layers with different compositions followed by a solid solution of Ni-Ti. It was also observed that an increase in time or temperature at first led to the formation of thicker intermetallic layers; however, after passing a critical point, the intermetallic layers seem to dissolve into the substrate. Furthermore, the wear rates of the diffusion treated samples were four times lower compared to Ti-6Al-4V alloy when sliding against AISI 52100 hardened steel.     

Influence of SiC content on the oxidation of carbon fibre reinforced ZrB2/SiC composites at 1500 and 1650 °C in air

The microstructure and the oxidation resistance in air of continuous carbon fibre reinforced ZrB₂–SiC ceramic composites were investigated. SiC content was varied between 5–20?vol.%, while maintaining fibre content at ～40?vol.%. Short term oxidation tests in air were carried out at 1500 and 1650?°C in a bottom-up loading furnace. The thickness, composition and microstructure of the resulting oxide scale were analysed by SEM-EDS and X-Ray diffraction. The results show that contents above 15?vol.% SiC ensure the formation of a homogeneous protective borosilicate glass that covers the entire sample and minimizes fibre burnout. The scale thickness is ～90?μm for the sample containing 5?vol.% SiC and decreases with increasing SiC content.     

Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

Studying the effect of organo-modified nanoclay loading on the thermal stability,flame retardant,anti-corrosive and mechanical properties of polyurethane nanocomposite for surface coating

Clay polyurethane nanocomposite (CPN) coating films were fabricated by uniformly dispersing nanoclay, organically modified with 25–30 wt.% octadecylamine in varying concentrations up to 5 wt.%, in a commercial two component, glossy, acrylic aliphatic polyurethane using ultrasonication. Organo-modified nanoclay was characterized by X-ray diffraction (XRD). The dispersion of the nanoclay into the matrix was investigated by scanning electron microscopy (SEM). CPN coating films were characterized by thermogravimetric analysis (TGA), and flame retardant, corrosion resistance and mechanical properties were also investigated. The XRD measurement indicated that, the organo-modified nanoclay particles were mainly constituted of montmorillonite with traces of quartz and calcite also found to be present. The SEM analysis showed that the nanoclay layers were dispersed and intercalated into the polyurethane coating. Thermogravimetric analysis showed that incorporating 5 wt.% organo-nanoclay into polyurethane considerably enhanced the thermal stability and increased the char residue to 14.11 wt.% relative to 4.58 for the sample without organo-nanoclay (blank polyurethane). The limiting oxygen index (LOI) test revealed that incorporation of organo-nanoclay led to a further increase in LOI values, which indicate an improvement in flame retardancy properties. The corrosion resistance also improved and this improvement increases with increase nanoclay wt.%. The mechanical resistance measurements demonstrated that the gloss of the CPN coating films slightly decreased, although hardness, adhesion and impact resistance of the CPN coating films improved with the incorporation of the organo-nanoclay.     

YSZ/MoS2 self-lubricating coating fabricated by thermal spraying and hydrothermal reaction

Thermal sprayed ceramic coatings have extensively been used in components to protect them against friction and wear. However, the poor lubricating ability severely limits their application. Herein, yttria-stabilized zirconia (YSZ)/MoS₂ composite coatings were successfully fabricated on steel substrate with the combination of thermal spraying technology and hydrothermal reaction. Results show that the synthetic MoS₂ powders are composed of numbers of ultra-thin sheets (about 7 ~ 8?nm), and the sheet has obvious lamellar structure. After vacuum impregnation and hydrothermal reaction, numbers of MoS₂ powders, look like flowers, generate inside the plasma sprayed YSZ coating. Moreover, the growing point of the MoS₂ flower is the intrinsic micro-pores of YSZ coating. The friction and wear tests under high vacuum environment indicate that the composite coating has an extremely long lifetime (>?100,000 cycles) and possesses a low friction coefficient less than 0.1, which is lower by about 0.15 times than that of YSZ coating. Meanwhile, the composite shows an extremely low wear rate (2.30?×?10^?7 mm³ N^?1 m^?1) and causes slight wear damage to the counterpart. The excellent lubricant and wear-resistant ability are attributed to the formation of MoS₂ transfer films and the ultra-smooth of the worn surfaces of hybrid coatings.     

Effect of in-situ formation of columnar mullite and pore structure refinement on high temperature properties of corundum casatbles

The effects of in-situ synthesis columnar mullite and pore structure on the hot modulus of rupture (HMOR), thermal shock resistance and corrosion resistance of corundum castables have been investigated in this paper. When 2% nano silica was added, the pore diameters of castables could be decreased to 15 nm (at 110 °C), 1 μm (1100 °C) and 6 μm (1500 °C), respectively. The corresponding reducing magnitude of pore size is 98.5%, 83.3% and 33.3%. The HMOR of castables fired at 1500 °C increased by 110% to 3.64 MPa. Furthermore, after three thermal shock cycles, the residual strength ratio of castables increased from 5.2% to 15.3%. A large amount of cross-distributed columnar mullite was formed between nano silica and α-Al₂O₃ by the two-dimensional nucleation mechanism, which remarkably enhanced the high temperature properties. The penetration index reduced from 30.86% to 19.88%, suggesting that smaller pore size and higher viscosity had a great influence to the penetration process.     

Effect of grinding-induced cyclic heating on the hardened layer generation in the plunge grinding of a cylindrical component

This paper discusses the effects of the grinding-induced cyclic heating on the properties of the hardened layer in a plunge cylindrical grinding process on the high strength steel EN26. It was found that a multi-pass grinding brings about a uniform and continuous hardened layer along the circumference of the cylindrical workpiece. An increase of the number of grinding passes, leads to a thicker layer of hardening, a larger compressive residual stress and a deeper plastic deformation zone. Within the plastic deformation zone, the martensitic grains are refined by the thermo-mechanical loading, giving rise to a hardness of 12.5% higher than that from a conventional martensitic transformation. The coupled effects of heat accumulation and wheel wear in the multi-pass grinding are the main causes for the thickening of the hardened layer. A too small infeed per workpiece revolution would result in insufficient grinding heat, and in turn, bring about an undesirable tempered hardened layer and a reduction of its hardness.     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.