Electric and mechanical performances of Bi0.5Sb1.5Te3 prepared by spark plasma sintering

Thermoelectric (TE) materials are a kind of functional materials which can be used to convert directly heat energy to electricity or reversely.The thermoelectric effects hold great potential for application in power generation and refrigeration.Bi2Te3 and its alloys are well known as best TE materials currently available near room temperature.This paper studies respectively the effects of spark plasma sintering (SPS) on electric performance of Bi0.5Sb1.5Te3 thermoelectric materials that are prepared through vacuum melting and ball milling.Through X-ray Diffraction and cold field emission scanning electric microscope s4800, the phase constituent and microstructure of the TE materials samples were analyzed.Electric conductivity and power factor can be improved with the rise of Spark Plasma Sintering temperature (from 300 to 500 ℃) and pressure(from 30 to 60 MPa), and the density and mechanical strength of Bi0.5Sb1.5Te3 thermoelectric material increase, too.     

高铁三水铝石型铝土矿的烧结特性

以Al2O3含量为26.35%,总Fe含量为31.22%,铝硅比为3.17的某高铁三水铝石型铝土矿为原料,研究了碱度、焦粉用量、混合料水分等对烧结矿质量指标的影响。结果表明:烧结矿碱度增加时,其转鼓强度和成品率下降,烧结矿自粉化程度加重;焦粉用量增加时,烧结矿转鼓强度和成品率提高;当混合料水分为9.0%、焦粉用量为8.0%、烧结矿碱度为4时,烧结矿转鼓强度为69.1%,成品率为81.2%,垂直烧结速度为30 mm/min,利用系数为1.2 t/(h.m2);烧结矿碱度为4时,样品存放2天粉化率为5%,烧结矿平均粒度由22.2 mm减小到21.9 mm,延长存放时间,烧结矿自粉化率增大,平均粒度显著减小。该烧结矿的冶金性能能基本满足高炉冶炼的要求。     

复合助剂对低温常压烧结AIN性能的影响

研究了Y2O3,LiO2,CaO烧结助剂对AlN陶瓷常压烧结致密度和性能的影响。结果发现,同时添加Y2O3,LiO2,CaO作为助剂,在1600℃低温烧结就能获得具有高致密度、较小的晶粒尺寸(1μm~4μm)、较高的抗弯强度(331MPa)、断裂韧性(3.8MPa·m1/2)及导热率(118W·m-1·K-1)的AlN陶瓷。     

稀土Y对纳米粉90W-Ni-Fe合金性能和微观结构的影响

采用SEM和金相仪器对添加不同Y量的纳米粉90W-7Ni-3Fe合金试样断口进行形貌观察和W晶粒测试：并对烧结态试样的相对密度、抗拉强度、延伸率等性能进行测定与分析。结果表明：当Y量在0．2％～0．6％（质量百分数，下同）时，试样相对密度为99.2％～99．6％，抗拉强度为1000MPa-1100MPa，延伸率为16％-19．5％：添加0．4％Y后，W晶粒从原来的20μm～25μm减小到12μm，W晶粒形状由不加稀土时的球形变为近球形或多边形。添加0．4％Y后，在界面上形成了W13．07Ni2.96Fe1.52Y23．65Ox（摩尔数比）的中间相，其阻止了W原子在粘结相中的扩散，阻止了W晶粒长大，细化了W晶粒，提高了合金的性能。     

高浓度熟料溶出的工艺研究

优化烧结法生产 ,提高产量、节约能耗是氧化铝生产急需解决的问题之一。实现高浓度溶出可以提高精液浓度 ,减少湿法系统物料流量 ,达到提高产能、增加产量、降低成品成本的目的。本文通过对国内外高浓度熟料溶出发展情况和烧结法影响高浓度溶出的因素进行分析研究 ,提出了提高熟料A/S的必要性 ;指出了适合我国条件的熟料A/S大小和生料配方 ;分析了温度和αk 对溶出和分离的影响机理和规律 ;提出了适合高浓度溶出的溶出条件和浓度大小。对生产有一定的指导意义。     

ZrB2-SiC基超高温陶瓷（UHTCs）的反应烧结及SHS粉体制备

用普通反应热压方法（RHP）和反应放电等离子体方法（R-SPS）原位反应制备了ZrB2-SiC，ZrB2-SiC—ZrC，ZrB2-SiC-ZrN，以及ZrB2-SiC-AIN4种复合材料。从密度，物相以及显微结构等方面比较了两种烧结方式之间的差别，对于升温速度较慢的普通热压方法，反应分步进行，显微结构不均匀；对于升温速度快的放电等离子体烧结，原料间的自蔓延反应被点着，反应速度快，显微结构均匀。同时以红外灯的热量为点火源，引发了Zr，Si及B4C间在空气气氛下的自蔓延反应，制备了较纯及粒径约为1μm的活性粉体。     

Effect of sintering process on microstructure and magnetic properties of high frequency power ferrite

An oxide ceramic process was adopted to prepare high frequency manganese-zinc (MnZn) power ferrite. In combination with the microstructure analysis of material, the influences of sintering process on initial permeability (μi) and high frequency loss in unit volume (Pcv) of MnZn power ferrite were investigated. The results show that in order to obtain fine microstructure and high frequency properties, the preferable sintering temperature and atmosphere are 1230 ℃ and oxygen partial pressure ( PO2) of 4%, respectively.     

Study on sintering process and characteristic of nanosized soft magnetic MnZn ferrite powders

The effect of sintering process (especially the sintering temperature) on the magnetic property and microstructure of sintered sample of nanosized soft magnetic MnZn ferrite powder was investigated. The sintered sample of MnZn ferrite was prepared by both traditional pressing and cool isostatic pressing on MnZn ferrite nanoparticals. The sintering process of which was segmented. Thedensity, microstructure and phase composition of sintered sample were analyzed by Archimedes'law, scanning electron microscopy (SEM) and X-ray diffraction (XRD). The grain growth and densification in sintering process of MnZn ferrite were investigated. The magnetic property was measured by vibrating sample magnetometer (VSM) and Nim2000 magnetic material testing system. The results show that the better sintering temperature is 850 ℃, at which the better magnetic property and microstructure of sintered compact were obtained.     

纳米陶瓷的热压烧结及超塑成形(英文)

纳米陶瓷具有优良的室温和高温力学性能 ,如较高的抗弯强度、断裂韧性、耐磨性等 ,使其在切削刀具、轴承、高温发动机部件等诸多方面都有广泛的应用。利用纳米陶瓷的超塑性进行成形加工是实现复杂形状零件近净成形的重要手段。本文采用化学沉淀法制备了平均粒径 10nm ,且无硬团聚的 3Y TZP (3%摩尔氧化钇稳定的四方相氧化锆多晶体 )粉体 ,研究了不同密度素坯的热压烧结行为。 3Y TZP毛坯的超塑性拉深试验表明在 14 5 0℃压头速率为 0 2mm·min-1时可以实现半球形件的成形 ,其成形高度达到 5 7mm ;Al2 O3 ZrO2 纳米复相陶瓷的正挤压试验表明 ,这种典型的晶间 /晶内型纳米陶瓷在很高的温度下可以 0 . 5mm·min-1的压头速率进行挤压成形 ,在某种程度上可以满足工业成形的需求 ;Si3 N4 Si2 N2 O复合陶瓷通过烧结锻造可以成形陶瓷齿轮 ,其烧结温度为 16 0 0℃ ,超塑性锻造温度为 15 5 0℃。     

中频炉酸性炉衬使用寿命的探讨

通过对炉衬材料的选择,作用机理及影响石英砂炉衬材料寿命的相关因素的阐述,说明了SD-T-A石英砂干振料可提高中频炉酸性炉衬使用寿命的原因.