Effect of electric pulse treatment on solidification structure of an A1-15%Si alloy

The effect of electric pulse modifying on the solidification structure of an Al-15%Si alloy was investigated. The result shows that the primary silicon disappears sometimes and the eutectic phase is refined after the treatrnent of EP （electric pulse） though there are different modalities in different treating durations. DSC （differential scanning calorimetry） analysis indicates that the super-cooling texture decreases and the freezing range narrows evidently after the electric pulse treatment.     

保温条件下过共晶Al-Si合金半固态浆料的组织演变

研究了保温时间和保温温度对电磁搅拌ZL117合金半固态浆料稳定性的影响.试验结果表明：半固态浆料中初生Si的颗粒直径随着保温时间的延长而逐渐增大,但在前15 min内增长速度比较缓慢,15 min后增长较快;随着保温温度的升高而缓慢增大;初生Si的形状系数随着保温时间的延长而变得越来越大,但也在前15 min内变化较为缓慢,15 min后变大速度突然加快;初生Si的形状系数在620 ℃下保温时最小,在610～620 ℃之间随着保温温度的升高而缓慢变小;在620～650 ℃之间随着保温温度的升高而逐渐增加.     

过共晶铝硅自生梯度复合材料的组织与性能

用电磁分离工艺成功制备了初生Si相体积分数、材料显微硬度和耐磨性沿径向呈梯度分布的棒状复合材料 ,讨论了梯度层的形成过程。微观组织观察和力学性能测试结果表明 :在近外壁区域形成了体积分数高达16 %的细小初生Si相偏聚区 ,此区硬度高 ,耐磨性好 ,中心区为细小和均匀的共晶组织 ,两部分之间为颗粒体积分数渐变的过渡区 ,可使耐磨层与基体的结合强度得到保证     

层流等离子体射流铝合金表面熔覆SiCp/Al-Si涂层的磨损过程

采用层流等离子体炬作为加热热源，在ZL104铝硅合金表面制备镍包SiCp／Al-Si复合熔覆层。磨损过程中，该熔覆层中的SiCp颗粒微凸体对磨轮的切削产生的切屑，在熔覆层表面形成机械混合层(MML)，此机械混合层硬度较高，耐磨性好，使熔覆层在磨损过程中经历了较长距离的磨损孕育阶段，从而改变了铝合金的磨损过程，延缓了中等磨损向严重磨损的转变。     

Modification mechanism of cerium on the Al-18Si alloy

The effect of the rare earth cerium （Ce） on the hypereutectic Al-Si alloy under different casting states have been studied by optical microscope and quantitative image analysis. It is found that the size and the quantity of primary silicon in castings decrease with the increase of added Ce in the melt. Meanwhile primary silicon changes from branched shape to fine facetted shape. Although the modification on eutectic silicon in castings also improves with the increase of added Ce in the melt, the effect of modification on eutectic silicon away from primary silicon is more obvious than that on eutectic silicon close to primary silicon. The modification mechanism was analyzed in detail by means of scanning electron microscope equipped with energy dispersive analysis of X-ray and thermodynamics analysis, which included the analysis on the change in standard Gibbs energy of reaction and reaction equilibrium.     

含共晶碳化物Fe－Cr－Mn合金在高温含硫气氛中的腐蚀研究

对含碳量为０．５０－２．６３％的Ｆｃ－Ｃｒ－Ｍｎ合金在８００℃下含硫混合气氛中进行腐蚀试验．用Ｘ射线物相分析法分析了腐蚀产物种类及其相对含量，现实测定了元素在腐蚀产物中的分布及试样亚表层共晶碳化物的腐蚀行为。结果表明：试验合金比高Ｎｉ耐热钢具有高的抗腐蚀性；合金的腐蚀行为受硫化及氧化腐蚀双重制约，因而使合金的腐蚀增重呈现峰值，随气氛氧化性增强，峰值向低碳方向移动；共晶碳化物具有比金属基体略好的抗腐蚀性。     

Al4C3的形成及对Gr-Al-Si复合材料的作用

Al4C3的生成会影响Gr-Al-Si复合材料的界面反应，然而研究证明在原料中少量的Al4C3存在，有利于提高石墨分布的均匀性，又不影响该材料的高温抗拉强度等综合性能。Al4C3的形成温度以550～600℃为宜，Al4C3的含量可用X射线定量分析来确定。     

耐磨锰钢中共晶体的球化

对Ｃａ变质处理的奥氏体－贝氏体耐磨锰钢进行了热力学二维点阵错配度计算，采用ＴＥＭ和ＳＥＭ观察及电子探针分析，发现ＣａＳ可以作为共晶体（奥氏体－渗碳体）的异质核心而使共晶体球化．     

亚共晶铝硅合金锶变质处理的孕育和衰退

通过考察A356合金变质后在静置和重熔过程中细化效果的变化,分析研究了亚共晶铝硅合金变质处理的孕育和衰退,以及合金锭预变质对变质效果的影响.结果表明,变质衰退表现为Sr含量低于某一临界值,有效期取决于初始Sr含量、熔化工艺及精炼方法等;变质处理孕育期的直接成因是中间合金释放Sr元素并与Si晶胚达到吸附平衡需要一定的时间;采用预变质合金锭,能够消除变质处理孕育期,稳定变质效果.     

微量元素对钛硅共晶合金压缩性能的改善

研究了钇、铍、钐、硼、钕等微量元素对Ti-8.5%Si(质量分数)共晶合金微观组织和室温压缩性能的影响。试验表明,添加适量钇、铍、钐、硼、钕等元素,均可有效提高Ti-8.5%Si合金的室温压缩强度和塑性,并细化其微观组织。其中,硼对Ti-8.5%Si合金室温压缩塑性的改善最为显著。分析认为,硼很可能以异质形核质点的形式,提高合金的形核率,从而细化合金的微观组织,改善合金的室温塑性。