聚1-丁烯热塑性弹性体的老化与防护

以拉伸性能为主要检测指标，考察了聚1-丁烯[P(1-Bt)]热塑性弹性体的热氧老化、紫外光老化和耐酸碱老化性能，制备了P(1-Bt)和三元乙丙胶(EPDM)防水卷材试样并进行对比：结果表明：单独使用抗氧剂1010，其用量在0．1～0．2质量份时具有较好的防热氧效果；1010与DLTP配合使用效果更佳，最佳配比为m(1010)：n(DLTP)=1：3(1010为0．2份)。热氧防老剂与紫外光吸收剂并用明显优于热氧防老剂或紫外光吸收剂单用时的防紫外光效果；ZnO对热氧老化和紫外光老化也具有很好的防护作用。P(1-Bt)制备的防水卷材的耐紫外光老化性能接近EPDM防水卷材，耐酸碱性能优于后者。     

CPE/P(AA-AM-HMA)吸水膨胀弹性体的研究

采用机械共混将氯化聚乙烯(CPE)与自制的吸水树脂丙烯酸-丙烯酰胺-甲基丙烯酸羟乙酯共聚物[P(AA-AM-HMA)]共混，并且以合成的两亲聚合物为共混试样的增容剂实施增容，讨论了吸水树脂以及增容荆对共混试样的力学性能和溶胀性能的影响。结果表明简单共混时随吸水树脂量增大。共混试样的拉伸强度降低，其吸水率增大。CPE-g-PEG的加入改善了试样的力学性能，与氯化聚乙烯／丙烯酸-丙烯酰胺共聚物共混体系相比，CPE／丙烯酸-丙烯酰胺．羟甲基丙烯酸共聚物试样吸水慢．平衡吸水率较大，质量损失率较小，而且受盐的影响较小。     

废胶粉/聚丙烯热塑性弹性体的界面增容研究

采取多种相容剂和反应加工手段，设计轮胎胎面废胶粉（WRP）与聚丙烯（PP）体系的不同界面，旨在制备出性能优异的热塑性弹性体（TPE）。研究了纯WRP／纯PP、三元乙丙橡胶（EPDM）包覆WRP／纯PP、丁苯吡橡胶（BSPR）包覆WRP／接枝马来酸酐聚丙烯（MPP）／PP、特殊高分子相容剂（SMC）包覆WRP／纯PP、原位接枝胺基WRP／MPP／PP、动态接枝纯WRP／纯PP等六种体系制备的TPE的性能，WRP／树脂质量比为70／30。结果表明，采用后三种体系制备的TPE性能优良，已经接近天然橡胶／聚丙烯TPE的性能水准，但WRP必须用酚醛树脂进行改性。据此，提出强界面和合适的界面模量过渡是制备废胶粉／树脂热塑性弹性体的关键。TEM的相态研究表明：胶粉的分散粒径在几到十几个微米之间，较原始粒径有很大的细化。     

聚四甲撑醚二醇聚氨酯弹性体性能和应用

聚四甲撑醚二醇（PTMG）和异氰酸酯合成的聚氨酯是一类具有广泛开发前景的材料，可用以制成各种类型的泡沫，纤维，涂料，粘合剂，弹性体等产品，阐述了PTMG型聚氨酯弹性体的合成及其性能，特点和应用，PTMG型PU有热固型和热塑型两种，可用浇注、叶涂、注射、挤出等方法成型加工，且都具有优异的性能，如良好的耐低温性能、耐生物降解性、耐水性、高回弹性，以及优良的动力学性能，所有这些使其相对于其它低聚物多元醇合成的PU，具有广泛的优越性，现在PTMG型PU已应用于冶金、矿山、纺织、造船和造纸等工业，有报道说在运动和医学领域也已开始使用。     

新溶剂体系对SBS生产工艺的影响

讨论了一种新溶剂体系对热塑性弹性体SBS工业生产工艺条件的影响，并与原应用纯环己烷溶剂的生产工艺进行比较。工业试生产结果表明，对SBS生产中溶剂精制工艺过程，应用新溶剂体系时精制塔系的气相压力增大，塔温降低，聚合反应单体质量分数在l8．0％～20．0％时对聚合反应与凝聚工艺控制没有影响，可较显著地提高装置生产能力，降低产品生产成本，同时其凝固点较低，有利于提高SBS生产体系对季节与地域的适应能力。     

锂系溶聚装置产品发展分析

阐述了国内外以锂系化合物为催化剂的溶聚装置主要产品的现状、技术及需求情况，并对锂系产品进行了成长性分析。对其发展趋势进行了预测。     

Morphology of epoxy resin modified with silyl‐crosslinked urethane elastomer

Silyl‐crosslinked urethane elastomer modifying epoxy resin has drawn much interest. Here the triethoxysilyl‐terminated polycaprolactone elastomer (PCL‐TESi) modifying diglycidylether of bisphenol A epoxy resins (DGEBA) system was chosen, and then the effect of the type of curing agent on the phase structure of the studied epoxy resin system was investigated. The modified systems were obtained with different phase structures by varying the formulations of the curing agent. It was experimentally shown that with the addition of aminosilane (KBE‐9103), the crosslinked density was greatly increased. The cured system also showed from SEM and TEM analysis that addition of KBE‐9103 increased the compatibility between the PCL‐TESi and DGEBA, which made the ductility of the system decrease, but also indicated from TEM that addition of much KBE‐9103 made the reacted silicone particles coagulate each other. The state of phase separation from TEM in the cured system was theoretically explained. These would serve the deeper studies of the mechanism of silyl‐crosslinked urethane elastomer modifying epoxy resin in the future. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 611–619, 2005     

环氧胶粘剂增韧改性研究进展

概述了关于近些年环氧树脂以及环氧树脂胶粘剂增韧改性的研究进展情况,简单地介绍了以无机刚性填料(颗粒)增韧改性环氧胶粘剂的情况,比较详细地叙述了以橡胶弹性体和热塑性树脂增韧改性环氧胶粘剂的一些重要研究情况及相关的增韧机理,指出了国内外之间环氧胶粘剂发展的差距,同时提出了环氧胶粘剂将来的重点和发展趋势。     

透明性聚氨酯弹性体的合成

采用预聚体法以不同的聚合物多元醇、异氰酸酯与1,4-丁二醇合成了透明聚氨酯弹性体,分析了异氰酸酯种类、n(-NCO)/n(-OH)(R值)、聚合物多元醇种类及分子质量、熟化时间和温度等对聚氨酯弹性体透明性、力学性能的影响。结果表明,采用脂肪族的IPD I,R值取1.02,硬段质量分数36.9%,相对分子质量1 000~2000的聚四亚甲基二醇,熟化条件为130℃/3 h时合成的PU弹性体具有较好的透明性和力学性能。     

弹性条缝筛网用聚氨酯弹性体的研制

采用预聚法常压浇注制备煤矿用聚氨酯筛网，考察了聚醚多元醇、甲苯二异氰酸酯异构体种类、预聚体的NCO质量分数、扩链反应温度、后熟化温度及时间等条件对制筛网用的浇注型聚氨酯弹性体体系操作性能及物理性能的影响。实验表明，采用聚四氢呋喃二醇与聚氧化丙烯二醇的混合二醇(质量比为80：20)，制得的预聚体NCO质量分数控制在4．5％左右；再以MOCA和一种三官能度扩链剂的混合扩链剂进行扩链，制得的浇注型聚氨酯弹性体满足洗煤用筛网的性能要求。