通过对耐热耐蚀合金Incoloy 80 0H的性能分析 ,指出它与普通奥氏体不锈钢相比具有较优的抗氧化性能、耐蚀性和高温蠕变强度。针对催化裂化装置同轴式沉降再生器内部所用Incoloy 80 0H焊件易出现裂纹的问题进行分析 ,认为在施焊过程中由于合金凝固时有低熔点金属或化合物的液态膜残留在晶界区 ,该合金具有高的焊接热裂纹敏感性 ,若焊材选择不当 ,焊丝填充不充分、缺少保护气等将导致晶间裂纹产生。提出了该合金采用TIG焊接防止热裂纹产生的措施。     

加氢裂化热高分油管线弯头开裂分析

对国产加氢裂化热高分油管线的弯头开裂原因进行了分析 ,对预防连多硫酸腐蚀提出了相应的防范措施 :选用碳含量 <0 .0 3 %并含有稳定化元素Ti、Nb的奥氏体不锈钢或双相钢 ;控制焊缝硬度不大于HB2 0 0并焊后热处理 ;12CrMo和 15CrMo耐应力腐蚀性能好 ;设备停运后马上进行清洗并用碱液中和     

Trypsin Inhibitor Activity In Vitro Digestibility and Sensory Quality of Meat-Like Yuba Products as Affected by Processing

ABSTRACT: :
Soybeans ( Glycine max ) were soaked and ground to obtain soymilk. The soymilk was cooked in an open tank and held at 85 to 90 deg;C. Yuba films were picked up in 20 min intervals and dried for 20 min. Yuba films were soaked in chicken-flavor solutions (25% and 35%), and baking soda (BS) solutions (0%, 1%, 2%, and 3% BS), and cooked at 100 °C for 30 min, 60 min, and 90 min. TIA decreased (p < 0.05) with the increase of heating time and BS concentration. In vitro protein digestibility (IVPD) decreased with heating time and BS concentration (p < 0.05). Sensory characteristics were affected by flavor concentration. By using 0% BS, 25% of the chicken flavor concentration, and a short heating time method, meat-like products with low TIA, high IVPD, and good sensory characteristics were obtained.     

合成氨中置锅炉的修复

本文在分析中置锅炉失效原因的基础上，提出了详细的修复措施，为类似情况的设备修复提供了借鉴。     

The corrosion behavior of sputter-deposited aluminum-tungsten alloys

Thin films on aluminum-tungsten alloys were prepared by co-deposition of pure aluminum and pure tungsten, each sputtered by an independently controlled magnetron source, on glass and sapphire substrates. Completely amorphous films were obtained in the Al₈₀W₂₀-Al₆₇W₃₃ composition range. Passivity and corrosion behavior of amorphous Al-W alloys were investigated in 1 M deaerated hydrochloric acid solution using polarization and impedance spectroscopy measurements and have been correlated with the properties of pure alloy components. Tungsten and sputter-deposited Al-W thin films are inherently passive materials while aluminum undergoes pitting corrosion in hydrochloric acid solution. The passive film formed at the OCP on each alloy possesses excellent electric and dielectric properties comparable to those of the isolating film on tungsten. The absolute impedance increases with increasing tungsten content in the alloy. According to electrochemical polarization measurements, alloying Al with W in solid solution significantly enhances the material's resistance to pitting corrosion by shifting the breakdown potential above 2000 mV (Al₆₇W₃₃) and lowering the corrosion rate at the OCP by more than two orders of magnitude. The most likely mechanism explaining the passivity of amorphous Al-W alloys, the Solute Vacancy Interaction Model (SVIM), involves the formation of complexes between highly oxidized solute atoms (W⁺⁶) and mobile cation vacancies, which restrict the transport of Cl⁻ through the oxide film and inhibit its breakdown in hydrochloric acid solution. The role that film stress relaxation effects and microscopic defects in amorphous Al-W films, of the some composition, and deposited on various substrates play in their corrosion resistance is discussed.     

φ1m氨合成塔20钢异径管失效分析

分析了氨合成塔底部副线20钢异径管爆破的原因。结果表明：异径管长期处于200℃以上工作，管内H2与管材中的碳或Fe3发生化学反应，生成CH4致使管内脱碳并产生裂纹，异径管强度降低脆性增加，导致爆破。     

换热站容积式加热器管束失效原因及防护

对换热站容积式加热器管束失效原因进行了分析 ,指出主要是由于汽蚀和电化学腐蚀所致。从操作工艺和采用 12Cr2AlMoV材质两方面进行改进 ,可使管束的使用寿命由 4个月延长到 2年     

Inhibition of atmospheric corrosion of mild steel by sodium benzoate treatment

The objective of this study was to evaluate the effectiveness of sodium benzoate as an inhibitor to slow down or prevent atmospheric corrosion/discoloration of the local mild steel during storage in the Arabian Gulf region. Test specimens were prepared from locally produced reinforcing steel products. The inhibitor solution was applied on steel specimens at a concentration of 100 mM for 1 day at room temperature. Wooden exposure racks were used to hold as-received and inhibitor-treated specimens during atmospheric exposure for different periods. Corrosion was evaluated through weight loss determination and electrochemical technique. As expected, the Arabian Gulf atmosphere was corrosive on the as-received local mild steel. On the other hand, treatment of steel with sodium benzoate lowered its corrosion rate during initial days of its exposure to atmosphere. However, atmospheric corrosion inhibition performance of sodium benzoate deteriorated with exposure time after 30 or more days of atmospheric exposure, and the corrosion rates of sodium benzoate-treated specimens reached that of the unprotected specimens at the end of 90 days of atmospheric exposure.     

浅析6063铝型材表面“铝丝印”的成因与对策

在介绍“铝丝印”概念的基础上，从金属腐蚀学的观点出发，分析了“铝丝印”形成的电化学腐蚀机理，并提出了具体的解决措施。     

长距离油、气、水混输管道内壁流动腐蚀的研究进展

就近几十年来，多相流管线的流动腐蚀（CO2腐蚀，H2S腐蚀，腐蚀/冲蚀协同作用），腐蚀/冲蚀数学模型和设计准则，腐蚀检测，腐蚀防护与控制技术等方面的研究进展进行了综述。指出了当前研究中所存在的一些问题，就多相流的研究方向提出了相应的建议。