Effect of B2O3 on the structural and in vitro biological assessment of mesoporous bioactive glass nanospheres

In this paper, the boron-containing mesoporous bioactive glass (MBG) nanospheres have been successfully synthesized by modified sol-gel method assisted by surfactant, and the effect of boron substitution on structure and bioactivity was evaluated by combining experiments and ab initio molecular dynamics (AIMD) simulations. All of the samples exhibit regularly uniform mesoporous spherical microstructure with an average size of about 60 nm, and the boron-containing MBGs show higher specific surface area with the value up to 416.20 m²/g. The simulated body fluid (SBF) immersion test confirms that the deposited hydroxyapatite (HA) evidently increases with the increasing of boron content, indicating that the biological behavior has been significantly improved resulting from incorporation of boron. Additionally, our results also reveal that B₂O₃ substitution has positive impact on cell proliferation of human periodontal ligament cells (hPDLCs) at lower extracted concentration. Furthermore, AIMD simulation is employed to understand the relationship between structural changes and in vitro bioactivity in terms of structural information, especially the boron coordination number. The results illustrate that the boron-containing MBG nanospheres with excellent bioactivity are great potential for biomedical applications.     

载体包裹填料提高PE/PP/EPDM/BN材料导热性

以三元乙丙橡胶(EPDM)/氮化硼(BN)复合材料为母料,通过熔融共混EPDM/BN复合材料与聚乙烯(PE)、聚丙烯(PP),制备PE/PP/EPDM/BN复合材料。采用PE∶PP的比例为5∶5,以使复合材料形成共连续结构;通过EPDM包裹BN的方法,实现BN在PE/PP/EPDM/BN复合材料共连续结构的相界面处分布,以形成导热通路,从而提高PE/PP/EPDM/BN复合材料的导热性能。通过接触角测试和扩散系数公式计算预测了EPDM会选择性分布在PE/PP/EPDM复合材料共连续结构的相界面处。通过连续度计算结果得出,EPDM为PE和PP总质量的15%时,EPDM的连续度为85.3%。由扫描电子显微镜分析表明EPDM在PE/PP/EPDM/BN复合材料中连续贯通。由导热测试分析知,随着BN含量的增加,PE/PP/EPDM/BN复合材料的热导率逐渐增加。这项研究提高了PE/PP复合材料的热导率,此材料在电子工业中可能具有潜在应用。     

Wet-chemical coating of silicon carbide fibers with hexagonal boron nitride layers

Hexagonal BN fiber coatings and BN powders were prepared by pyrolysis of the raw materials boric acid and urea in an atmosphere consisting of hydrogen and nitrogen. The powders were used to determine the appropriate mixing ratio of the raw materials to produce BN with the desired composition and crystal structure. The pyrolysis of boric acid and urea in a molar mixing ratio of 1:2 resulted in a BN that was hexagonal and had a near-stoichiometric composition.To prepare a solution for the coating of fibers, boric acid and urea were dissolved in an ethanol-water mixture. The coating was then applied to SiC filaments using a continuous roll-to-roll dip-coating process. It could be shown by SEM/EDS that BN layers were applied to the fibers. No significant bridging in the fiber bundle was found. Furthermore, it could be demonstrated by grazing incidence x-ray diffraction that the layers were crystalline.     

EFFECTS OF NUCLEATION AGENTS ON EFFICIENCY OF BORON EXTRACTION FROM MgO－B_2O_3－SiO_2 SLAGS

ＥＦＦＥＣＴＳＯＦＮＵＣＬＥＡＴＩＯＮＡＧＥＮＴＳＯＮＥＦＦＩＣＩＥＮＣＹＯＦＢＯＲＯＮＥＸＴＲＡＣＴＩＯＮＦＲＯＭＭｇＯ－Ｂ_２Ｏ_３－ＳｉＯ_２ＳＬＡＧＳ￥Ｚｈａｎｇ，Ｐｅｉｘｉｎ；Ｌｏｕ，Ｈａｉｌｉｎｇ；Ｓｕｉ，Ｚｈｉｔｏｎｇ（Ｄｅｐａｒｔｍｅｎ?..     

烧结型钕铁硼电镀锌工艺研究

研究了不同前处理工艺对烧结型钕铁硼电镀锌层性能的影响，通过对镀层孔隙率、结合力、耐蚀性等性能的测试，确定了封孔、除油、除锈、活化、浸锌、电镀锌工艺，得到了光亮、孔隙率低、结合力和耐蚀性强的镀层。     

稀土镁对高硼铁基合金的影响

高硼铁基合金是一种新型的耐磨材料,其特点是以组织中硬脆的共晶硼化物作为材料的耐磨相。但是,由于共晶硼化物在晶界处呈网状分布,破坏了基体的连续性,导致材料韧性偏低。提高该种材料韧性的有效途径便是改善硼化物的形态,文中采用稀土镁对高硼铁基合金进行变质,在热处理条件下,改善了硼化物的形态,将材料的冲击韧度提高了34.6%。     

铸造金属耐磨材料研究的进展

详细介绍了耐磨材料奥氏体锰钢、低合金钢和白口铸铁的成分、组织、性能及其应用进展,还对耐磨钢结材料和耐磨铸造复合材料以及新开发的高硼铸造耐磨合金进行了评述,期待为科学选择耐磨材料提供参考。     

活性元素Ti在CBN与钎料结合界面的特征

通过扫描电镜、能谱仪、X射线衍射仪研究了Ag-Cu-Ti钎料中的活性元素Ti在钎料与立方氮化硼（CBN）磨粒高温钎焊结合界面的扩散现象，并运用动力学分析对界面反应层的生长过程及反应激活能进行了探讨。结果表明：钎焊过程中，钎料中的活性元素Ti明显向磨粒侧扩散偏聚并发生化学反应，实现了磨粒与基体材料的牢固结合；钎焊CBN磨粒表面生成的TiB2和TiN化合物形貌接近平衡状态下生长的理想形貌；界面反应层在钎焊温度1153K～1193K，保温时间5min～20min之间依据抛物线生长法则所得扩散激活能值表明其生长过程主要受新生TiN影响。     

高硼铸钢的制备与应用

针对常用磨球材质脆性大、耐磨性低、磨耗高,以硼为主要合金元素,研制了高硼铸钢磨球。为了净化钢液,研究了高硼钢液吹氩净化工艺,选择氩气流量1 5~2 5 L/min,氩气压力1 0~1 5 MPa,吹氩时间5~8 min,吹氩后钢液的静置时间5~8 min的吹氩净化处理工艺,钢液净化效果好。高硼铸钢磨球经9 5 0~1 0 5 0℃加热后快速淬火和1 8 0~2 5 0℃回火处理后,具有硬度高、硬度均匀性好和韧性高等特点,用于研磨矿粉和煤粉,磨耗与高铬铸铁球相当,成本降低3 0%以上,综合效益显著。     

添加剂对Al2O3／BN可加工陶瓷性能的影响

采用Si3N4和SiC作为Al2O3／BN可加工陶瓷的添加剂，考察了添加剂种类和含量对材料力学性能及可加工性能的影响。研究表明，2种添加剂均对调节体系中由于热膨胀失配所引起的人的内应力起到积极的作用。材料的抗弯曲强度随添加剂含量的增加而提高，同时可加工性能略有降低。尤其是Si3N4的加入使体系在热压烧结过程中原位反应生成液相x-Sialon，显著降低了烧结温度，促进材料的致密化。