扫描速度对硼铸铁气缸套表面钨极氩弧硬化效果的影响

研究了钨极氩弧扫描速度对硼铸铁表面硬化效果的影响规律。结果表明：扫描速度增加,硬化层宽度、深度减小,而硬度提高,裂纹率增大；硬化层硬度沿层深的分布是从表及里由高而低,在过渡区下降缓慢；沿层宽的分布是层中心最高,向两侧逐渐降低,直至硼铸铁基体达到最低值；在保证不出现裂纹的条件下,硬化层表面的最高硬度值可达61．4HRC,硬化层最高显微硬度值可达1156．4HV0．1；硼铸铁材料采用氩弧热源淬火时,淬硬层与基体之间过渡区明显,硬化区组织为莱氏体,过渡区为马氏体、残余奥氏体和少量石墨。     

Ni3Al中B和Mg的非平衡晶界共偏聚

在1023－1373K的初始温度和0.05-268.91K/s的冷速范围内，用Auger剖层分析确定含B和Mg的Ni3Al合金中B和Mg的非平衡晶界共偏聚行为，按照溶质－空位复合体迁移机制所导出的描述非平衡晶界偏聚的扩散速率方程解析表达式，很好地模拟了本实验结果，并确定了Ni3Al-B-Mg合金中B及B－空位复合体，Mg及Mg-空位复合体的扩散系数及复合体激活能。     

Process Requirements for Cost-Effective Precision Grinding

Costs in precision cylindrical grinding are compared for different abrasives, machines and grinding conditions. The analysis is for repeated batch production. Account is taken of machine cost and abrasive cost. Cost comparisons were based on extensive trials to assess re-dress life against workpiece quality requirements. Experiments show that different workpiece materials require different strategies to reduce costs. Easy-to-grind AISI 52100 and difficult-to-grind Inconel 718 materials were ground at conventional speeds and at high speeds. It is shown that wheel speed affects production rate through acceptable values of re-dress life, removal rate and dwell time. Advantages were gained using vitrified CBN at conventional speed and at high speed. For both materials, vitrified CBN wheels used at high speed, gave better quality at lower cost than conventional abrasives. Wheel costs became negligible and labour costs greatly reduced. Re-dress life trials, usually neglected, are shown to be essential to reduce costs and maintain quality [1].     

PREFERENTIAL SITE SATURATION FOR NUCLEATION AND GROWTH OF α-PHASE AT EARLY STAGE OF AUSTENITE DECOMPOSITION IN LOW CARBON STEEL BEARING BORON

借助经典体视学方法和“扩展组织”概念,定量研究了低碳硼钢620℃过冷奥氏体等温分解早期显微组织的演变路径。结果表明,母相晶界网络仍是低碳硼钢中α相形核长大的择优位置集合,择优顺序为晶粒棱(含隅)、晶界界面.棱集和隅集的位置饱和总是早于面集。钢中有效硼量对趋于饱和的路径和晶界面集的饱和迟早有显著影响。     

含B4C中性盐浴渗硼工艺问题的研究

在含Ｂ４Ｃ中性盐浴渗硼的高温反应研究的基础上，对该盐浴存在的工艺问题进行了分析研究。指出了渗硼能力均匀性，工件表面腐蚀斑与玻璃体的关系，分析了老化盐致使工件清洗困难的成因。     

Influence of the stress,strain, and temperature on the surface roughness of an AlSl 52100 steel due to an orthogonal cut

In recent years, the finite element method (FEM) has become the main tool for simulating the metal cutting process because research based on trial and error is time consuming and requires high investment. Early studies were done by different investigators. In this research AISI 52100, hardened steel (62 HRC) was selected for an orthogonal machining process as well as metal cutting simulation using the software DEFORM-2D. This software is based on a forging process and has been adapted to an orthogonal machining process. The results of simulated cutting forces were compared with experimental cutting force data to validate the orthogonal cut simulation. Also, the surface roughness was measured, and the influence of the stress, strain, and temperature on the surface roughness was studied.     

Electrosyntheses and characterization of poly(5‐bromoindole) in boron trifluoride diethyl etherate

Poly(5‐bromoindole) (PBrI) films were synthesized electrochemically by direct oxidation of 5‐bromoindole in pure boron trifluoride diethyl etherate. The oxidation potential of 5‐bromoindole in this medium was measured to be only 0.97 V vs. saturated calomel electrode, which was lower than that determined in acetonitrile + 0.1 mol L^?1 Bu₄NBF₄ (1.08 V). PBrI films obtained from this medium showed good electrochemical behavior and good thermal stability. Structural studies showed that the polymerization of 5‐bromoindole ring occurred at 2,3 position. As‐formed PBrI films were thoroughly soluble in strong polar solvent dimethylsulfoxide and partly soluble in tetrahydrofuran. Fluorescent spectral studies indicated that PBrI was a good blue‐light emitter. The excitation and emission spectra of PBrI showed a significant shift to longer wavelength compared with that of the monomer, consistent with the greater extent of electron delocalization. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 539–547, 2006     

Lewis酸存在下的自由基共聚合——Ⅰ.GeCl_4与BCl_3存在下的乙酸乙烯酯与丙烯酸交替共聚

乙酸乙烯酯(VAc)与丙烯酸(AA)在GeCl_4及BCl_3存在下通过自由基聚合可得到交替共聚物。对GeCl_4体系,聚合反应速率正比于[引发剂]~(0.5)。当VAc/AA=1:1(mol比)时有最大反应速率。CCl_4对本聚合反应无链转移作用。通过紫外光谱分析可证实VAc及AA均与GeC\(?)生成络合物;ESR分析表明,络合AA自由基较未络合AA有较强的阳离子特性,交替共聚的原因可能与络合AA自由基及活化单体络合物二者有关。     

硼酚醛树脂在涂料中的应用

通过将硼酚醛树脂和环氧树脂进行混用,利用硼酚醛树脂优异的耐酸、碱腐蚀性能以及耐高温性能和环氧树脂可以常温固化成膜的特点,制备常温固化的耐高温防腐蚀涂料。     

氢氧化镁中微量元素硼硅铝的测定

以盐湖高镁卤水为原料生产的氢氧化镁产品纯度不高,含有部分无机杂质离子,为提高产品质量,改进产品性能,通过实验确定了氢氧化镁中微量元素硼、硅、铝的分光光度测定方法。此方法准确度与精密度较高,测定样品中的硼、硅、铝加标回收率分别为98.3%-101.5%,96.0%-99.3%,96.5%-97.3%,相对标准偏差（n=6）分别为2.06%,2.27%,2.39%,快速、简便、成本低,可作为企业生产的常规检测方法使用。