NCT310型常温氧化锌脱硫剂的研究

介绍了NCT310型常温氧化锌脱硫剂实验室研究情况。结果表明，在常温（20～60℃）下，该脱硫剂对气体中的硫化氢有优越的脱除性能。在40℃、1000h-1、进口H2S～1．5g／m3条件下，可控制出口H2S＜7×10－4g／m3，穿透硫容（重量比）＞10％。     

基于环形微热板的ZnO微气体传感器设计

提出一种新型的设有环形结构微热板的硅基ZnO微气体传感器。利用ANSYS软件,将环形电极结构与传统的蛇形结构进行温度分布的模拟仿真,发现该结构能供给传感器更高的温度且中心温度分布均匀,进而解决了现有传感器功耗大的缺点。通过对RF磁控溅射ZnO薄膜的工艺摸索,得出了适宜作气敏薄膜的制备参数。该传感器在250℃下对（200-1000）×10-6CH4气体有很好的响应。     

不同纳米粒子改性PPR树脂的性能比较

以纳米碳酸钙、纳米二氧化钛和纳米氧化锌晶须为添加剂，对PPR树脂性能尤其在耐热性方面进行了改性。系统地比较了经改性处理后纳米粒子对PPR树脂耐热性、力学性能的影响。通过扫描电镜观察了粒子在基体中的分散状况。结果表明，在几种纳米粒子中，经0．5％的KH560处理后的氧化锌晶须的分散性最好，对PPR树脂的改性效果佳，与纯PPR相比，氧化锌晶须质量分数为4％时．改性PPR树脂的性能有较大提高，其热变形温度从72℃提高到102℃，断裂伸长率也由45％提高到112％。     

EXAFS and XPS Investigations of Cu/ZnO Catalysts and Their Interaction with CO and Methanol

Several investigations have been carried out on Cu/ZnO catalysts by employing extended Xray absorption fine structure (EXAFS) and Xray photoelectron spectroscopy (XPS). EXAFS investigations of Cu/ZnO catalysts subjected to hydrogen reduction show the presence of Cu¹⁺ species and Cu microclusters. The proportion of Cu¹⁺ depends on the rate of increase of the reduction temperature and on the amount of alumina added. An XPS study of the interaction of CO with model Cu/ZnO catalysts prepared in situ in the electron spectrometer shows the formation of CO₂ ^-, CO₃ ^2- and C₂O₄ ^2- species, their proportion relative to CO increasing with the Cu¹⁺/Cu⁰ ratio. A study of the interaction of CH₃OH with Cu clusters deposited on ZnO films reveals reversible molecular adsorption and the formation of CH₃O on clean Cu clusters. If the Cu clusters are pretreated with oxygen, however, both CH₃O and HCOO^- species are produced. Model Cu/ZnO catalyst surfaces containing both Cu¹⁺ and Cu⁰ species show interesting oxidation properties. On a Cu⁰-rich catalyst surface, only the CH₃O species is formed on interaction with CH₃OH. On a Cu¹⁺rich surface, the HCOO^- ion is the predominant species.     

An EXAFS study of Cu/ZnO and Cu/ZnO-Al2O3 methanol synthesis catalysts

Cu K-absorption edge and EXAFS measurements on binary Cu/ZnO and ternary Cu/ ZnO-Al₂O₃ catalysts of varying compositions on reduction with hydrogen at 523 K, show the presence of Cu microclusters and a species of Cu¹⁺ dissolved in ZnO apart from metallic Cu and Cu₂O. The proportions of different phases critically depend on the heating rate especially for catalysts of higher Cu content. Accordingly, hydrogen reduction with a heating rate of 10 K/min predominantly yields the metal species (>50%), while a slower heating rate of 0.8 K/min enhances the proportion of the Cu¹⁺ species ( 60%). Reduced Cu/ZnO-Al₂O₃ catalysts show the presence of metallic Cu (upto 20%) mostly in the form of microclusters and Cu¹⁺ in ZnO as the major phase ( 60%). The addition of alumina to the Cu/ZnO catalyst seems to favour the formation of Cu¹⁺/ZnO species.     

CDs/ZnO/g-C3N4三元组份协同作用促进光催化降解染料

采用浸渍-热聚合法制备CDs/ZnO/g-C3N4复合材料，考察其对罗丹明B的光降解效率。利用 XRD、TEM、XPS、UV-Vis DRS、FI-IR等手段对催化剂进行表征和评价。结果表明：CDs/ZnO/g-C3N4仍保持石墨相g-C3N4的晶型结构，三元组份相互协同作用使CDs/ZnO/g-C3N4表现出优异的光催化性能，其降解罗丹明B的效果优于单体g-C3N4、ZnO及ZnO/g-C3N4，脱色率可达到70%左右。     

稀土氧化物掺杂ZnO-Bi2O3系压敏陶瓷"软心"现象的研究

掺杂稀土氧化物的大尺寸ZnO压敏陶瓷具有明显的“软心”特征,即内部电位梯度远远低于表层。经过XPS关于Zn结合能的研究、SEM关于杂质分布状况的研究及XRD关于相态的研究表明:试样内部氧和添加剂的匮乏及晶态的不完善是影响内层电位梯度的三大主要因素。     

不同形貌ZnO气敏材料的制备及影响气敏性因素分析

以锌盐和碱为原料,采用水热和溶剂热法合成了三种形貌的氧化锌粉体,利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和X射线光电子能谱仪(XPS)对产物的结构和形貌及表面化学状态进行了表征,并将粉体制备成厚膜型气敏元件,测试了其对几种还原性气体的气敏性能,结果表明:在工作温度为395℃时,三种形貌氧化锌对相同浓度的同种测试气体的灵敏度大小顺序为:菜花状氧化锌﹥棒状氧化锌﹥六棱柱状氧化锌。并对影响氧化锌材料气敏性的各种因素进行了分析。     

ZnO压敏电阻器的性能及发展

简要回顾了ZnO压敏电阻器的历史，阐述了ZnO压敏电阻器的性能以及当前基础性研究的现状，并对其发展进行了展望。研究了Bi2O3和TiO2的掺杂对低压ZnO压敏电阻性能和微观结构的影响规律，从理论上分析了Bi2O3和TiO2添加剂的作用机理。为ZnO压敏电阻的低压化提供了理论依据和方法。     

室温固相合成掺杂ZnO纳米粉体制备ZnO压敏电阻

以金属离子盐和草酸为原料,采用室温固相化学反应合成掺杂ZnO前驱物,根据DSC-TG分析结果,将其在450℃热分解2 h,得到掺杂ZnO粉体,并用此粉体制备了片式ZnO压敏电阻。借助XRD、TEM、BET等检测手段对粉体产物的物相、形貌、粒度等进行了表征。研究了烧结温度对ZnO压敏电阻电性能的影响。结果表明,所制备的粉体为平均粒径24 nm左右、颗粒呈球状、分散性好的纤锌矿结构掺杂ZnO。在1 080℃烧结时,ZnO压敏电阻的综合电性能达到最佳,电位梯度为791.64 V/mm,非线性系数为24.36,漏电流为43μA。