Deposition of Al-doped ZnO films on polyethylene naphthalate substrate with radio frequency magnetron sputtering

100 nm Al-doped ZnO (AZO) thin films were deposited on polyethylene naphthalate (PEN) substrates with radio frequency magnetron sputtering using 2 wt.% Al-doped ZnO target at various deposition conditions including sputtering power, target to substrate distance, working pressure and substrate temperature. When the sputtering power, target to substrate distance and working pressure were decreased, the resistivity was decreased due to the improvement of crystallinity with larger grain size. As the substrate temperature was increased from 25 to 120 °C, AZO films showed lower electrical resistivity and better optical transmittance due to the significant improvement of the crystallinity. 2 wt.% Al-doped ZnO films deposited on glass and PEN substrates at sputtering power of 25 W, target to substrate distance of 6.8 cm, working pressure of 0.4 Pa and substrate temperature of 120 °C showed the lowest resistivity (5.12 × 10^− 3 Ω cm on PEN substrate, 3.85 × 10^− 3 Ω cm on glass substrate) and high average transmittance (> 90% in both substrates). AZO films deposited on PEN substrate showed similar electrical and optical properties like AZO films deposited on glass substrates.     

一种新型的相变储能功能高分子材料

介绍了本实验室制备的一种新型的固态相变材料,叙述了它的合成方法,讨论了该类材料的相变机理及其特点等,结果表明,该类新型固态相变材料不仅相变焓大,而且热稳定性有明显改善,各项综合性能优异,具有很大的使用价值和发展前途。     

丙烯酸聚乙二醇单酯的合成研究

以聚乙二醇-200与丙烯酸直接缩合反应,在不加有毒带水剂的条件下合成了丙烯酸聚乙二醇单酯。探讨影响缩合反应酯化率的因素,确定酯化反应的最佳条件：丙烯酸与PEG200的摩尔比为1.2∶1.0,反应温度是110-140℃,阻聚剂对苯二酚为0.6%（以醇酸总质量计）,反应时间为6 h,催化剂对甲苯磺酸为1.0%（以醇酸总质量计）,产率达89.4%。     

我国医用聚氯乙烯增塑剂的发展现状

我国医用聚氯乙烯(PVC)以可致癌的邻苯二甲酸二辛酯(DOP)为主增塑剂,这严重影响了国内人民的健康和医用PVC行业的发展。通过对国内外各新型环保增塑剂的比较可知:无毒环保的乙酰柠檬酸三丁酯(ATBC)适合作为我国医用PVC制品的主增塑剂。这为改善医用PVC制品使用者的健康状态,加快医用环保PVC行业的发展提出了可行性。     

环氧乙烷催化水合制乙二醇催化剂研究进展

介绍了从催化水合法、碳酸乙烯酯法、乙二醇与碳酸二甲酯联产法制备乙二醇的均相催化剂和非均相催化剂,分析了催化剂的应用状况,提出了采用新技术合成乙二醇的建议。     

新型有机-无机杂化物(TB0.5Zr0.5H0.5PW)催化合成苯甲醛乙二醇缩醛反应

通过离子交换法制备了系列季铵盐锆盐共掺杂磷钨酸催化剂,利用SEM、FT-IR、XRD、XPS、TGA-DTG以及正丁胺电位法等技术手段对催化剂结构、酸度进行表征,并对其催化缩醛反应性能进行研究。考察了催化剂用量、醇醛摩尔比、带水剂量和反应时间对苯甲醛乙二醇缩醛产率的影响。研究表明,TB_0.5Zr_0.5H_0.5PW(TB为四丁基溴化铵)固体酸催化剂具有优异的催化性能,催化剂强的Bronsted酸性、Bronsted与Lewis酸中心间的协同效应及“假液相”特性是该催化剂具有高活性的原因。以TB_0.5Zr_0.5H_0.5PW为催化剂,经响应面优化所得苯甲醛乙二醇缩醛最佳制备工艺条件为：乙二醇与苯甲醛摩尔比1.5:1,TB_0.5Zr_0.5H_0.5PW用量为苯甲醛质量的1.9%,反应时间3 h,带水剂环己烷量12.6 mL,该条件下苯甲醛乙二醇缩醛产率为94.6%。TB_0.5Zr_0.5H_0.5PW固体酸催化剂在重复使用6次后仍然表现出优异的催化性能,表明该催化剂具有较好的工业应用前景。关键词：磷钨酸;季铵盐;缩醛反应;苯甲醛乙二醇缩醛;催化技术 中图分类号：TQ655 文献标识码： A 文章编号：1003-5214 (2020) 01-0000-00     

乙二醇在氧化物增强Pd/C催化剂上的电化学氧化

研究了乙二醇在氧化物CeO2、NiO和Co3O4增强Pd/C催化剂上的碱性溶液中电化学氧化活性,结果显示虽然纯Pd/C催化剂对乙二醇的电化学氧化活性非常低以及抗催化剂毒化作用非常弱,其电化学性能远远比不上Pt/C催化剂。但添加氧化物CeO2、NiO和Co3O4后,Pd/C对乙二醇电化学氧化催化活性和抗毒化能力都得到大幅度提高,甚至超过商业催化剂E-TEKPt/C。三种氧化物增强Pd/C催化剂的电化学活性顺序为Pd-Co3O4(质量比为2︰1,以下同)/C>Pd-NiO(4︰1)/C>Pd-CeO2(1.3︰1)/C。     

多组分共聚酯纤维在碳酸钠/乙二醇中的碱减量处理

研究了多组分共聚酯在碳酸钠(Na2CO3)的有机溶剂乙二醇溶液中的碱处理条件,如温度、碱浓度和碱处理时间与纤维减量率的关系,考察了处理后纤维表面形态和纤维的强度变化,利用红外光谱分析了碱处理残留物的结构。研究结果表明,在乙二醇中,以低浓度弱碱Na2CO3代替强碱NaOH同样可以获得较为理想的碱处理效果。在温度为100～120℃、时间为60～120 min下进行碱处理,碱减率保持在20%左右,纤维强度保持在80%以上;红外光谱表明,共聚酯在乙二醇/Na2CO3中的碱解产物与其在水/NaOH中的一致。     

新型聚羧酸混凝土减水剂中间大分子单体合成研究

用正交实验法研究了聚乙二醇(PEG)和丙烯酸(AA)醇化合成聚乙二酵丙烯酸酯的酯化工艺,以该酯化物合成聚羧酸减水剂,并分析酯化率对水泥净浆流动度的影响.得到最佳酯化工艺条件:原料最佳摩尔比为:n(AA):n(PEG)=3:1,反应的最佳温度为100℃,反应的最佳催化剂加入量为总质量10%,最佳反应时间为5 h.酯化率为50%时,水泥的净浆流动度最大.     

一种用于三维打印系统的光敏预聚物的合成

用聚丙二醇二缩水甘油醚作为原料与丙烯酸反应,合成聚丙二醇二缩水甘油醚二丙烯酸酯,较好的合成条件是反应温度宜控制在100℃~110℃,催化剂N,N-二甲基苄胺的质量分数为0.80%,阻聚剂选用对羟基苯甲醚,其质量分数为0.20%~0.40%。通过实验测试,用这种光敏预聚物制备的光敏树脂,可以作为三维打印快速成形系统使用的实体材料。