低水分抗热震高铝可塑料在加热炉上的应用

用矾土作为主原料,选择适当结合剂和添加剂,引入微粉技术,采用真空炼泥等工艺手段,研制成低水分抗热震高铝可塑料。该制品用作热媒加热炉衬里,显示出良好的耐高温和耐热冲击性能。     

Catalytic aminolysis of epoxide by alumina prepared from amine-protected Al precursor

The catalytic activities of alumina prepared from an Al alkoxide-amine adduct monomer for the reaction of cyclopentene oxide with piperidine was determined after various pretreatments, including calcination and exposure to moisture. They were compared with the activity of alumina prepared by the conventional hydrolysis method. It was found that the as-prepared sample from the alkoxide-amine monomer preparation was five times more active than a conventional preparation, suggesting that it has a higher density of surface Lewis acid sites. However, its activity was much more severely suppressed by exposure to moisture.     

金属/Al2O3基纳米复合材料研究最新进展

金属／Al2O3纳米复合材料在保持原有金属的功能特性时，还可以获得 很好的力学性能，是有良好发展前景的一种纳米复合材料。本文回顾了近年来金属／Al2O3基纳米复合材料在制备工艺，微观结构和力学性能，增韧强化机理方面的最新进展，并指出了今后的研究方向。     

SiC（w）／TZP＋mullite陶瓷复合材料界面和组成设计与力学性能

本文从理论上分析了ＳｉＣ（ｗ）ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料界面残余热应力及其在基质内的分布规律。提出在ＳｉＣ（ｗ）表面涂复Ａｌ２Ｏ３和在ＰＺＴ中加入ｍｕｌｌｉｔｅ（ｐ）联合作用来降低晶须／基质界面残余热应力的界面设计方案，导出ＳｉＣ（ｗ）和ｍｕｌｌｉｔｅ（ｐ）协同补强ＰＺＴ的匹配条件。制备了ＳｉＣ（ｗ）／ＴＺＰ＋ｍｕｌｌｉｔｅ（ｐ）复合材料并了ＳｉＣ（ｗ）表面涂层Ａｌ２Ｏ３厚度和ＳｉＣ（ｗ     

Highly ordered anodic alumina nanotemplate with about 14 nm diameter

A novel method for the fabrication of highly ordered nanopore arrays with very small diameter of 14 nm was demonstrated by using low-temperature anodization. Two-step anodization was carried out at 25 V, sulfuric acid concentration of 0.3 M, and electrolyte temperature of −15 °C. After anodization, a regular pore array with mean diameter of 14 nm and interpore distance of 65 nm was formed. The pore diameter and regular arrangement were confirmed by scanning electron microscopy (SEM) and fast Fourier transformation (FFT), respectively. The present results strongly suggest that the diameter of pores in a highly ordered alumina template can be reduced by lowering the anodization temperature.     

反应结合氧化铝陶瓷制备新工艺

本文评述了反应结合氧化铝陶瓷的制备工艺原理，配料组成，研磨与原料细度，成形压力和升温速率等对陶瓷性能的影响。介绍了几种反应结合氧化铝陶瓷制造实例。     

Cobalt doped glass for the fabrication of percolated glass–alumina functionally graded materials

The present research was focused on the development of a new glass to produce glass–alumina FGMs. The glass formulation, belonging to the CaO–ZrO₂–SiO₂ system, was doped with cobalt, by adding a small molar percentage (about 0.1 mol%) of CoO, in order to obtain a blue glass, which could be useful to appreciate the final compositional gradient. The glass was accurately characterized, evaluating its thermal behaviour, its mechanical properties, and its attitude to crystallize during a thermal treatment. Subsequently, the glass was used to produce glass–alumina FGMs via percolation and the so obtained specimens were analysed in order to evaluate the effect of the glass infiltration. The possible development of new crystal phases, in particular, was tested via micro X-ray diffraction and the elastic properties gradient associated with the compositional gradient was measured via depth-sensing Vickers microindentation.     

搪瓷釉料新颖添加剂铝溶胶

搪瓷釉料新颖添加剂铝溶胶任岳荣（浙江省明矾石综合利用研究所３２５０２８）ＮｅｗＡｄｄｉｔｉｖｅＡｌｕｍｉｎａＳｏｌｆｏｒＧｌａｚｅｏｆＥｎａｍｅｌ￥ＲｅｎＹｕｅｒｏｎｇ（ＺｈｅｊｉａｎｇＩｎｓｔｉｔｕｔｅｏｆＣｏｍｐｒｅｈｅｎｓｉｖｅＵｔｉｌｉｚａｔ...     

Surface contact degradation of multilayer ceramics under cyclic subcritical loads and high number of cycles

Alumina/alumina–zirconia ceramic laminated composites produced by tape casting present a compressive residual stress at the alumina surface due to the thermal expansion mismatch between layers developed during processing. Because of this residual stress, the mechanical properties at the surface, such as wear or surface fracture, have proven to be better than the properties of a monolithic stress-free alumina. In a previous work, it was shown that this laminate composite has better resistance to the development of a ring crack when loaded with a spherical indenter, under both cyclic and static loads below the critical load for cone cracking. In this work, cyclic Hertzian indentations with subcritical loads are performed on the same laminate ceramic and a monolithic alumina, but with a higher number of cycles than the necessary to provoke the first damage (ring crack). Results show that for low and intermediate number of cycles, the laminated composite presents better resistance to damage than the monolithic alumina. However, for high number of cycles, spalling at the surface of the laminate material appears, whereas the monolithic alumina develops secondary cone cracking. This difference is attributed to the fact that laminate ceramics present an enhanced apparent fracture toughness of the material, which implies a higher quasi-plasticity due to shear driven microcracking. For a high number of cycles, these microcracks grow until coalescence at the surface, provoking exfoliation of the material at the contact area, enhanced by the fact that the indented and the indenter material have different elastic properties.