Investigation of surface structure and composition of in situ annealed Fe–Mn binary alloy samples using RHEED and electron spectroscopy

The formation of oxides at the surface of Fe–1.5%Mn and Fe–0.6%Mn binary alloys was investigated as a function of the conditions of the heat treatments. Both the influence of temperature and the atmosphere under which the experiments were performed were studied. The range of annealing temperatures was adjusted to 800°C. The atmosphere consisted of a mixture of N₂–5%H₂ and traces of water vapour, with different fixed dew points ranging from −10°C to −30°C. The state of the annealed surfaces was determined using in situ analytical devices attached to the annealing reactor in order to avoid surface contamination or the formation of native oxides after the experiments due to contact with air. The structure and composition of the surfaces were determined by reflection high-energy electron diffraction (RHEED) and electron spectroscopy (XPS, AES). Copyright © 2002 John Wiley & Sons, Ltd.     

Sorption of spruce O-acetylated galactoglucomannans onto different pulp fibres

Sorption of spruce acetylated galactoglucomannans (GGM) onto different pulps, among which unbleached and peroxide-bleached mechanical pulps, and unbleached and bleached kraft (BK) pulps, was studied as a means of understanding the retention of acetylated GGMs in mechanical pulping and papermaking. The fibre surface coverage of lignin and carbohydrates was estimated by X-ray photoelectron spectroscopy (XPS) or electron spectroscopy for chemical analysis (ESCA). GGM sorption was clearly favoured on kraft pulps. Hardly any differences in sorption were, however, observed between unbleached and BK pulps, even if the surface coverage of lignin was lower on the bleached pulp. Neither thermomechanical pulp (TMP) nor chemithermomechanical pulp (CTMP) manufactured from spruce sorbed any acetylated GGMs. Peroxide bleaching of the pulp did not increase sorption. Only CTMP produced from aspen sorbed some GGMs. The anionic charge of neither chemical nor mechanical pulps influenced GGM sorption.     

Study of the first nucleation steps of thin films by XPS inelastic peak shape analysis

The initial steps in the formation of thin films have been investigated by analysis of the peak shape (both inelastic background and elastic contributions) of X‐ray photoelectron spectra. Surface coverage and averaged height of the deposited particles have been estimated for several overlayers (nanometre range) after successive deposition cycles. This study has permitted the assessment of the type of nucleation and growth mechanisms of the films. The experiments have been carried out in situ in the preparation chamber of an XPS spectrometer. To check the performance of the method, several materials (i.e. cerium oxide, vanadium oxide and cadmium sulfide) have been deposited on different substrates using a variety of preparation procedures (i.e. thermal evaporation, ion beam assisted deposition and plasma enhanced chemical vapour deposition). It is shown that the first deposited nuclei of the films are usually formed by three‐dimensional particles whose heights and degree of surface coverage depend on the chemical characteristics of the growing thin film and substrate materials, as well as the deposition procedure. It is concluded that XPS peak shape analysis can be satisfactorily used as a general method to characterize morphologically the first nanometric moieties that nucleate a thin film. Copyright © 2006 John Wiley & Sons, Ltd.     

含氟丙烯酸酯聚合物乳胶膜表面性质

采用XPS和界面张力仪分别测定了含氟丙烯酸酯聚合物乳胶膜表面的组成及水在其表面的动态接触角, 并用状态逼近方程模型计算了含氟聚合物乳胶膜的表面张力, 考察了温度对乳胶膜润湿性的影响. 结果表明, 含氟聚合物乳胶膜表层较深处的F 1s信号强度比近表面要弱, 乳胶膜表面张力随表面氟原子浓度增加在一定程度上呈现线性下降；含氟侧链(Rf)较长(碳原子数n＞6)的含氟聚合物, 其表面张力随Rf单元含量增加而下降的趋势显著高于Rf较短(n≤6)的含氟聚合物, 而水在含氟聚合物乳胶膜表面上的后退接触角θr随n增大出现急剧上升, n≥10 时, θr值几乎恒定不再随n增大而改变. 此外, 参与共聚的非氟丙烯酸酯酯基碳链较短时, 水在共聚物乳胶膜表面的θr随氟单元含量增加而增加的趋势更显著；温度超过40 ℃后, 水对聚合物乳胶膜的润湿性随温度上升略有改善.     

Synthesis and characterization of silver nanoparticle/kaolinite composites

Ag nanoparticles were synthetized in the interlamellar space of a layered kaolinite clay mineral. Disaggregation of the lamellae of non-swelling kaolinite was achieved by intercalation of dimethyl sulfoxide. The kaolinite was suspended in aqueous AgNO₃ solution and, after adsorption of Ag⁺, the ions were reduced with NaBH₄. The interlamellar space limits particle growth (d_ave=3.8–4.2 nm); however, larger silver particles may be formed on the exterior surface of kaolinite with d_ave=5.6–10.5 nm diameter. The diameter of the particles prepared in this way is depending on the initial AgNO₃ concentration. The silver nanoparticles prepared were characterized by UV–vis spectroscopy, X-ray diffraction (XRD), Small angle X-ray scattering (SAXS), X-ray photoelectron spectroscopy (XPS) and Transmission electron microscopy (TEM).     

共沉淀法合成稀土正磷酸盐(La,Gd)PO4:RE3+(RE=Eu,Tb)及其真空紫外光谱特性

采用共沉淀法制备了稀土正磷酸盐荧光粉(La,Gd)PO4:RE3+(RE=Eu,Tb).红外光谱分析发现GdPO4的红外光谱吸收峰与LaPO4一致,只是峰位向高波数方向移动.(La,Gd)PO4:RE3+的真空紫外光谱特性研究表明,Gd3+在能量传递过程中起中间体作用.XPS研究揭示,LaPO4的价带由O2-的2p能级构成,而GdPO4的价带则是由O2-的2p能级和Gd3+的4f能级共同构成.     

Cr,Fe,Cu/Al2O3界面化学结构的光电子能谱

应用Ｘ－射线光电子能谱，通过离子刻蚀，原位研究第四周期过渡金属与氧化铝所形成界面的化学状态，结果表明，Ｃｒ，Ｆｅ在界面处有不同程度的氧化，氧化程度Ｃｒ＞Ｆｅ，而Ｃｕ则无明显氧化。化学成份的定量分析表明，界面过渡层的厚度与界面化学反应强弱直接相关。     

Surface film formation on a graphite electrode in Li‐ion batteries: AFM and XPS study

The formation of a passivation film (solid electrolyte interphase, SEI) at the surface of the negative electrode of full LiCoO₂/graphite lithium‐ion cells using LiPF₆ (1M ) in carbonate solvents as electrolyte was investigated by means of x‐ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The analyses were carried out at different potentials of the first and the fifth cycles, showing the potential‐dependent character of the surface‐film species formation. These species were mainly identified as Li₂CO₃ up to 3.8 V and LiF up to 4.2 V. This study shows the formation of the SEI during charging and its partial dissolution during discharge. Copyright © 2005 John Wiley & Sons, Ltd.     

铈离子引发N-对甲苯基丙烯酰胺类聚合物膜上丙烯酰胺接枝共聚合的研究

合成了NTAAM,NTMAAM,NPMAAM功能单体,发现这类功能单体与铈离子组成的体系能引发丙烯酰胺聚合,带有这类功能单体的聚合物和共聚物铸成的膜,能用铈离子引发丙烯酰胺接枝共聚合。这可从反应后的膜比基膜有较大的吸水率、与水有较小的接触角,也可从扫描电子显微镜观察到表面上有凸起图象的高分子链,以及从膜表面的X射线光电子能谱所证实。同时研究了共聚物膜的组成、反应条件对接枝共聚合的影响。     

Evidence of lanthanum–chromium mixed oxides formed in CrOx/La2O3 model catalysts

CrO_x/La₂O₃ mixed oxides, prepared by impregnating La₂O₃ with appropriate aqueous solutions of (NH₄)₂CrO₄ and calcining at 600 °C for 4 h, have been investigated by means of XRD, TPR, XPS, DRIFTS, and Raman spectroscopy (RS). The formation of the compounds La₂CrO₆, La(OH)CrO₄ and LaCrO₄ under these conditions was evidenced. Strong peaks at 864, 884, 913, and 921 cm⁻¹, as well as weak peaks at 136, 180, 354, 370, and 388 cm⁻¹ in the RS spectrum of CrO_x/La₂O₃ have been assigned to La₂CrO₆.