统计分析1307口探井实测压力系数和83l口探井使用的钻井液密度数据，发现东营凹陷古近系沙三段、沙四段普遍存在异常超压，超压(压力系数1．1-1．5)主要出现在2100-3500m深度，强超压(压力系数大于1．5)主要出现在2800-3500m深度。东营凹陷沙三段、沙四段主力烃源岩超压平面分布具有北高南低、东高西低的总体特点，超压主要分布在洼陷带、断裂构造带和中央背斜带上。烃源岩压力系数等值线北部陡坡带比较密集，南部缓坡带相对稀疏。生油洼陷中心附近异常高压带的分布与生油洼陷基本一致，洼陷深陷区压力系数很大，向周围斜坡和构造高部位呈辐射状逐渐减小至正常，压力分布带与洼陷、边缘斜坡和构造较高部位的欠压实与压实带发育、分布规律的一致性很好。图3表l参9     

Understanding chemical reactions between carbons and NaOH and KOH: An insight into the chemical activation mechanism

Direct mixing of an anthracite with hydroxides (KOH or NaOH) and heat treatment up to 730 °C has shown to be a very good activation procedure to obtain activated carbons with very high surface areas and high micropore volumes. The reactions involved during the heat treatment of these hydroxide/anthracite mixtures have been analysed to deep into the fundamental of the knowledge of this chemical activation process, that has not been studied before. For this purpose, the present paper analyses the drying process, the atmosphere during the carbonisation, the chemical state of the activating agents (NaOH, KOH and Na₂CO₃) and the chemical reactions occurring during the heat treatment which have been followed by FTIR and TPD. The analysis of our results allows us to conclude that steam is a good atmosphere for the carbonisation process, alone or joined with nitrogen, but not as good as pure nitrogen. On the other hand, during the activation process, the presence of CO₂ should be avoided because it does not develop porosity. The reactions, and chemical changes, involved during this chemical process are discussed both from a thermodynamical point of view as well as identifying the reaction products (H₂ by TPD and Na₂CO₃ by FTIR). As a result, this paper helps to cover the present lack of understanding of the fundamentals of the reactions of an anthracite with hydroxides which are necessary to understand the activation of the material.     

Biofiltration of toluene in the absence and the presence of ethyl acetate under continuous and intermittent loading

BACKGROUND: Two peat biofilters were used for the removal of toluene from air for one year. One biofilter was fed with pure toluene and the other received 1:1 (by weight) ethyl acetate:toluene mixture. RESULTS: The biofilters were operated under continuous loading: the toluene inlet load (IL) at which 80% removal occurred was 116 g m^?3 h^?1 at 57 s gas residence time. Maximum elimination capacity of 360 g m^?3 h^?1 was obtained at an IL of 745 g m^?3 h^?1. The elimination of toluene was inhibited by the presence of ethyl acetate. Intermittent loading, with pollutants supplied for 16 h/day, 5 days/week, did not significantly affect the removal efficiency (RE). Biomass was fully activated in 2 h after night closures, but 6 h were required to recover RE after weekend closures. Live cell density remained relatively constant over the operational period, while the dead cell fraction increased. Finally, a 15 day starvation period was applied and operation then re‐started. Performance was restored with similar re‐acclimatization period to that after weekend closures, and a reduction in dead cell fraction was observed. CONCLUSION: This study demonstrates the capacity of the system to handle intermittent loading conditions that are common in industrial practices, including long‐term starvation. Copyright © 2008 Society of Chemical Industry     

Batch cultures of Penicillium camembertii on glucose and amino acids—model for growth and ammonium production

BACKGROUND: Three groups of amino acids were previously characterized based on their ability to be assimilated as carbon source by Penicillium camembertii. To describe the diauxic growth recorded on glucose and amino acids from the second group, such as arginine, an unstructured model was previously developed, based on the sequential consumption of both carbon substrates, glucose, followed after its exhaustion, by arginine. The model was modified to describe also the behaviour recorded during growth on other amino acids. RESULTS: The growth model involved the carbon substrate consumption (Verlhust model) and the biomass on carbon substrate yield. Glucose was therefore considered during P. camembertii growth on nitrogen source amino acids (lysine—first group); and amino acid consumption was considered during growth on carbon source amino acids (glutamate—third group), with glucose being dissimilated only for energy supply. The excess nitrogen from amino acids was released as ammonium; the linking of this production to growth was found to increase with the ability of the amino acid to be assimilated as carbon source by P. camembertii. CONCLUSION: The various metabolic behaviours recorded during P. camembertii growth on amino acids, in the presence of a primary carbon source such as glucose, were proved to be satisfactorily described by the model, showing the robustness of the model. Copyright © 2007 Society of Chemical Industry     

茨21-133井CO2吞吐技术初步试验

茨榆坨油田茨13块原油属于普通稠油，1993年开始蒸汽吞吐采油，从第二轮开始效果明显变差，注汽返排率低，有效周期短，产量下降快，套管变形井增多。针对这些问题，在该区块茨21—133井进行CO2吞吐采油工艺现场试验，获得成功，增油效果明显。     

Matrix mediated alignment of single wall carbon nanotubes in polymer composite films

Alignment of single wall carbon nanotubes (SWNT) in liquid crystalline (LC) polymer matrix imparting orientation to the nanotubes along the nematic director was studied by atomic force microscopy, measurements of electrical conductivity and Raman spectroscopy of the composite in the directions parallel and perpendicular to the nematic director. The composites were prepared through dispersion of SWNT with LC monomer in a common solvent, their alignment in nematic monomer and consequent UV polymerization of the monomer. The anisotropy of electrical and optical properties of the system depends strongly on the concentration of the nanotubes in the range of 1-10% SWNT being especially strong for smaller concentrations and negligible at higher loads. A simple semi-quantitative model is suggested to account for the orientational behavior of nanotubes in nematic matrices. It successfully describes the observed anisotropy of physical properties at microscale (up to 200 μm) in terms of anchoring of the polymer chains to the nanotubes surface and adjustment of the nanotubes orientation to the nematic direction due to such coupling. The increasing disorientation of the nematic domains at higher nanotubes loads is explained as a development of larger number of LC defects induced by the nanotubes in the nematic matrix due to their intrinsic nature of aggregation. The anisotropy of physical properties at macro scale (several millimeters) is much smaller and less dependable on SWNT concentration because differently oriented LC domains effectively wash out the anisotropy.     

用介孔材料制备定向碳纳米管的研究进展

综述了近年来采用介孔材料制备定向碳纳米管的研究进展,包括介孔材料的合成及介孔材料在制备定向碳纳米管方面的应用。重点介绍了采用合成介孔材料的模板剂石墨化及介孔材料作为载体制备定向碳纳米管的方法,探讨了模板剂种类、催化剂的制备方法及反应温度和时间对定向碳纳米管生长的影响和定向碳纳米管生长的介孔限制机理,并提出了这一领域的研究方向。     

低k氟化非晶碳层间介质对芯片性能的影响

讨论了通过合理设计的工艺流程将低k氟化非晶碳材料应用到制造工艺中作为互连介质对集成电路性能的影响。基于一个互连结构简化模型计算出采用低k氟化非晶碳材料作为互连介质后RC延迟、功率耗散和线间串扰的变化情况。采用低k氟化非晶碳介质后,RC延迟和功率耗散随着互连长度的增大而减小,线间串扰也得到显著抑制。     

Methane/natural gas storage and delivered capacity for activated carbons in dry and wet conditions

Methane/natural gas storage and delivered capacity for three different activated carbons in dry and wet conditions were measured. In all tests the temperature of the bed was maintained constant at 277.15 K and pressure was increased up to 10 MPa. Natural gas storage capacity was less than methane storage capacity in dry conditions for all the three activated carbons tested, while the gas delivery was almost the same. One of activated carbon tested (NC120) showed the possibility of hydrate forming for pressures higher than 4 MPa but the amount of gas stored still was less than the amount stored in dry conditions over the whole range of pressure. The analysis of the gas delivered at each pressure steps shows that considerable amount of heavy components do not come out from the bed even at very low pressures in both dry and wet condition tests. Repeatability of the sorption/desorption processes - vital for possible commercial/industrial use - has been examined over various cycles.     

A disposable sensor based on immobilization of acetylcholinesterase to multiwall carbon nanotube modified screen-printed electrode for determination of carbaryl

A simple method has been devised for immobilization of acetylcholinesterase (AChE) covalent bonding to a multiwall carbon nanotube (MWNT)-cross-linked cellulose acetate composite on a screen-printed carbon electrode (SPCE) and a sensitive and disposable amperometric sensor for rapid determination of carbaryl pesticide is proposed. The immobilized enzyme was preserved on this film because of the excellent biocompatibility and non-toxicity of cellulose acetate. Based on the inherent conductive properties of the MWNT, the immobilized AChE had greater affinity for ATCl and excellent catalytic effect in the hydrolysis of ATCl. MWNT improved the interface enzymatic hydrolysis reaction and increased the amperometric response of the sensor. Under optimum conditions, the inhibition of carbaryl on AChE increased linearly with the increasing concentration of carbaryl in two ranges, from 0.01 to 0.5 μg mL⁻¹ and from 2 to 20 μg mL⁻¹, with the correlation coefficients of 0.9985 and 0.9977, respectively. The detection limit was 0.004 μg mL⁻¹ taken as the concentration equivalent to 10% decrease in signal. The sensor showed acceptable stability, accuracy and could be fabricated in batches, thus it is economic and portable. This type of disposable enzyme-based amperometric sensor has extensive application potential in environmental monitoring of pesticides.