Processing,microstructure, and mechanical properties of hot-pressed ZrB2 ceramics with a complex Zr/Si/O-based additive

Densification behavior, microstructure, and mechanical properties of zirconium diboride (ZrB₂) ceramics modified with a complex Zr/Si/O-based additive were studied. ZrB₂ ceramics with 5–20 vol.% additions of Zr/Si/O-based additive were densified to >95% relative density at temperatures as low as 1400°C by hot-pressing. Improved densification behavior of ZrB₂ was observed with increasing additive content. The most effective additive amount for densification was 20 vol.%, hot-pressed at 1400°C (∼98% relative density). Microstructural analysis revealed up to 7 vol.% of residual second phases in the final ceramics. Improved densification behavior was attributed to ductility of the silicide phase, liquid phase formation at the hot-pressing temperatures, silicon wetting of ZrB₂ particles, and reactions of surface oxides. Room temperature strength ranged from 390 to 750 MPa and elastic modulus ranged from 440 to 490 GPa. Vickers hardness ranged from 15 to 16 GPa, and indentation fracture toughness was between 4.0 and 4.3 MPa·m^1/2. The most effective additive amount was 7.5 vol.%, which resulted in high relative density after hot-pressing at 1600°C and the best combination of mechanical properties.     

Ga2O3薄膜材料氧敏性能的研究

实验以三氯化镓为原料,柠檬酸为络合剂,通过NH3·H2O调节pH值,得到透明稳定的前躯体溶胶,红外光谱分析表明上述溶胶在向凝胶转变过程中,发生镓与柠檬酸的络合,并在干燥过程中依靠氢键形成大分子聚合物.采用提拉涂覆溶胶-凝胶法在多晶氧化铝基片表面形成凝胶膜后,经800℃下热处理,凝胶膜转化为单斜相β-氧化镓陶瓷薄膜.重复镀膜和热处理及超声清洗过程8个～10个周期,最后在800℃下烧结,保温1h,得到粒径为50nm～100nm左右的多孔纳米薄膜.采用自制系统检测β-Ga2O3薄膜的氧敏性能,结果表明Fe掺杂的氧化镓薄膜材料,在400℃～800℃范围内,在理论空燃比附近,电阻突变幅度大于2个数量级,具有较高的灵敏度.     

Pd／Ag纤维复合材料的制备工艺

用包套拉伸法和挤压法制备Ｐｄ／Ａｇ纤维复合材料，并通过金相和电子显微镜分别观察其微镜分别观察其微观结构，测试其性能，如电阻率，硬度，强度及接触电阻等。通过对比其工艺性及所得材料的微观结构和性能，认为挤压法优于包套拉伸法。此种Ｐｄ／Ａｇ纤维复合材料适合Ｐｄ／Ａｇ型复合铆钉和生产复铜铆钉。     

压入深度与膜厚对薄膜与基体复合硬度及弹性模量的影响

根据高华建的复合弹性模量模型，提出了用一个测点的载荷-位移曲线计算整个压入深度内薄膜和基体复合硬度分布的方法，探讨了压入深度与膜厚对硬度与弹性模量测量值的影响，指出可由膜-基复合性能反推膜本身的性能。     

Sn-9Zn-3Bi/Cu钎焊接头在170℃时效过程中的显微结构

采用ST50润湿实验仪完成了钎焊并研究分析了Sn-9Zn-3Bi/Cu接头在170℃下长期时效的显微结构变化.结果表明:Sn-9Zn-3Bi/Cn接头时效至200 h后在界面处形成单一连续的Cu5Zn8化合物层;时效至500 h和1000 h后,界面处形成了3层化合物层,从铜母材侧起,分别为Cu-Sn化合物层,Cu-Zn化合物层和Sn-Cu化合物层;随着时效时间的增加,整个金属化合物层变厚,而Cu-Zn化合物层减薄,表明Cu-Zn化合物层在时效过程中具有不稳定性.     

Conductivity enhancement in transparetn ZnO films via Al-dopping produced by CW-CO2 laser-induced evaporation

Highly conductive transparent aluminium-doped ZnO (ZnO:A1) films were successfully deposited by CW-CO₂ laser-induced evaporation. Optimisation of evaporation parameters was based on laser power, substrate temperature, O₂ partial pressure in the vacuum chamber and amount of Al in the ZnO source pellet. ZnO:A1 films with an electrical resistivity as low as 6.6 × 10⁻²Ω·cm and an optical transmission of 80% at 500nm were obtained at laser power of 15 W, substrate temperature of about 200°C, O₂ partial pressure of 6—7 × 10⁻⁴ Torr and 5wt.% Al. Conductivity of ZnO films can be increased one order via Al-doping in ZnO films. The films obtained by laser-induced evaporation have compared quite favorably with the high quality films obtained by sputtering.     

高性能纤维的弯曲疲劳断裂研究

在自制弯曲疲劳装置上 ,对 3种高强对位芳纶及超高相对分子质量聚乙烯纤维 (Dyneema SK65 )进行双面弯曲疲劳试验。结果表明 ,Twaron 2 0 0 0弯曲疲劳寿命的自然对数与预加应力、弯曲角度呈线性关系 ,Dyneema SK65弯曲疲劳寿命明显长于对位芳纶 ,Twaron 2 0 0 0 ,Kevlar 12 9相近 ,都比Kevlar 2 9略长 ;高强型对位芳纶的弯曲疲劳断裂断口芯层呈现出“毛笔头”或“拔丝形”原纤化分裂形态 ,超高相对分子质量聚乙烯纤维弯曲疲劳断裂断口有明显的脆性折断形态 ,无原纤出现。     

Plasma graft polymerization of acrylamide onto crosslinked HTPB based PU membrane for pervaporation

Pervaporation of water-ethanol mixtures through plasma graft polymerization of acrylamide onto crosslinked hydroxyl terminated poly-butadiene (HTPB) based PU membranes, plasma graft polymerization of acrylamide onto crosslinked PU membrane (AAm-p-CPU), were investigated. The grafting was dependent on the discharge power and pretreatment period. The effects of crosslinking, plasma treatment conditions, feed compositions, and feed temperature on the performance of these membranes were studied. The physical properties of crosslinked membrane were better than those of the uncrosslinked membrane. In addition, compared with crosslinked PU membranes (CPU), the plasma modified crosslinked PU membranes effectively improve the pervaporation separation performances.     

Synthesis and property of nanosized palladium catalysts protected by chitosan/silica

A chitosan (CTN)/silica‐supported nanosized palladium catalyst was obtained from a silica‐supported chitosan palladium complex through a complex transition method. An adsorption model was employed to simplify the structure of the di‐supporter. It was indicated that when the polymer coil adsorbed on the silica surface with even a monolayer the catalytic activity would reach an optimum value, and different situations of the, nanosized palladium particles would cause a different catalysis. The molar ratio of the chitosan structure unit to the palladium would affect the metal's size, which therefore influenced its catalytic activity. The experimental results corresponded with the inferences. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 85: 989–994, 2002     

浅谈如何提高化工原理的教学质量

化工原理是化工类及相近专业的一门主干课。要提高教学质量,必须加强教师自身建设,进一步强化课程内容和课程体系的改革,不断探索教学方法的改进,强化多媒体教学手段的运用。