Hydrogenation and structural properties of Gd2Ni7 with superlattice structure

The crystal structure and hydrogenation properties of Ce₂Ni₇-type Gd₂Ni₇ were investigated by X-ray diffraction (XRD) and the hydrogen pressure–composition (P–C) isotherm. Ce₂Ni₇-type Gd₂Ni₇ was obtained by annealing at 1523 K for 12 h and quenching in ice water. Two superlattice reflections (002 and 004) of the Ce₂Ni₇-type were clearly observed at 2θ = 7.3° and 14.6° in the XRD profile. The refined lattice parameters were a = 0.49662(9) nm and c = 2.4255(3) nm, respectively. Two plateaus were clearly observed during the absorption–desorption process in the P–C isotherm. The first and second plateaus were at 0.015 and 0.13 MPa, respectively, in the first desorption. The maximum hydrogen capacity reached was 1.13 H/M. The enthalpy and entropy were calculated as −20 kJ/mol H₂ and −80 J/mol H₂ K, respectively, from the van’t Hoff plot. After the P–C isotherm, the GdNi₅ cell expanded by 2.15%, but the Gd₂Ni₄ cell shrank by 2.83%.     

Fabrication of fluorine-terminated diamond-like carbon thin film using a hyperthermal atomic fluorine beam

Surface modification of diamond-like carbon (DLC) film was performed using a hyperthermal atomic fluorine beam on the purpose of production of hydrophobic surface by maintaining the high hardness of DLC film. By the irradiation of atomic fluorine beam of a 1.0 × 10²⁰ atoms/cm², the contact angle of a water drop against the DLC surface increased from 73° to 111°. The formation of CF₃, CF₂ and CF bonding on the modified DLC surface was confirmed from the measurements of X-ray photoelectron spectra and near-edge X-ray absorption fine structure spectra. Irradiation of hyperthermal atomic fluorine beam was concluded to produce insulator fluorine-terminated DLC film, which has high F content on the surface, by the taking of the use of neutral atomic beam as a fluorine source.     

Feasible method,utilizing density changes,for estimating in situ dynamic strength and deformation properties of sand samples

Laboratory tests and design reliability are directly controlled by sample quality. The frozen sampling (FS) method is useful for dynamic strength and deformation tests of undisturbed clean sand. However, it is very expensive and requires considerable equipment. The sample quality of Toyoura sands obtained from 48 mm and 75 mm samplers are scrutinized based on void ratio, dynamic strength and deformation properties through model and cyclic undrained triaxial tests. A conventional method for estimating in-situ dynamic strength and deformation properties of sand samples utilizing density changes is examined and the applicability of the proposed method is discussed for the samples obtained from Niigata sand deposits.The main conclusions obtained from this study are summarized as follows:(1) A conventional method for estimating in-situ void ratio (e₀), D_r, stress ratio (R_L20) in a 20 cyclic time frame and the initial modulus of rigidity (G₀) of sand samples utilizing density changes is proposed.(2) The in-situ R_L20 and G₀ estimated from the proposed method for sand samples from tube samplers were similar to those of frozen sampling and the in-situ modulus of initial rigidity was calculated from the secondary wave velocity for Niigata sand deposits.Therefore, dynamic strength and deformation properties changes, caused by sampling, can be modified appropriately to an in-situ condition by this proposed method.     

Development of gap sensing system for narrow gap laser welding

Narrow gap welding with an oscillation laser beam is one of the effective processes for thick plate welding. To put this welding process into practical manufacturing, a groove-sensing system using image processing for narrow gap welding with an oscillation laser beam is used. This developed system uses still images of the weld zone taken by a coaxial CMOS camera. It can recognize the position of the groove wall by analysing the brightness distribution in the still image. It can then control the oscillation width and the laser-irradiated area by calculating the groove width and the groove centre position. Some narrow gap welding experiments were performed to evaluate the performance of the developed system. The results revealed that the developed system is effective for narrow gap welding with an oscillation laser beam. Using this system, the narrow gap groove can be welded even if the groove width has changed during the welding process.     

Effect of anisotropic yield functions on the accuracy of hole expansion simulations

The deformation behavior of 780 MPa grade dual-phase steel sheet subjected to hole expansion is investigated both experimentally and analytically to clarify the effect of the material model (anisotropic yield function) on the predictive accuracy of finite element analysis of hole expansion. Biaxial tensile tests of the material were conducted; contours of plastic work and the directions of plastic strain rates are precisely measured and are in good agreement with those predicted from the Yld2000-2d yield function with an exponent of 4 ( [Barlat et al., 2003] and [Yoon et al., 2004]). Finite element and experimental analyses on the hole expansion of the material were conducted. The Yld2000-2d yield function with an exponent of 4 provides closer agreement with the experimental results than other yield functions. Consequently, the anisotropic yield functions significantly affect the predictive accuracy of the deformation behavior of the steel sheet subjected to hole expansion, and the biaxial tensile test is effective for identification of the appropriate anisotropic yield function to be used for hole expansion simulation.     

Effect of trace Na additions on the hydriding kinetics of hypo-eutectic Mg–Ni alloys

Mg–Ni alloys are among the most promising candidates for solid-state hydrogen storage systems. This paper reveals the effect of Na doping in accelerating initial hydrogen uptake in Mg–Ni alloys using in-situ Synchrotron X-ray powder diffraction. A minimum concentration of approximately 0.2 wt.% Na must be achieved for the alloys to show reasonably fast hydriding kinetics. Surface analysis shows that a Na-modified Mg–Ni surface facilitates the chemisorption and dissociation of hydrogen molecules in the early stage of hydriding as evidenced by a rapid formation of the saturated hydrogen solid solution Mg₂NiH_0.3 from the original Mg₂Ni. The subsequent hydrogen absorption is based on a mechanism of nucleation and growth of MgH₂ where a high density of dislocations develops ahead of the growing hydride-metal interface.