烧结工艺对液相合成（SrPb）TiO3基陶瓷热敏特性影响的研究

本文在液相合成（ＳｒＰｂ）ＴｉＯ３粉的基础上，研究了升温速率、保温时间、烧结温度及降温方式对（ＳｒＰｂ）ＴｉＯ３基陶瓷的Ｖ型ＰＴＣ热敏特性的影响。实验表明：升温速率对其热敏特性影响不大，保温时间和烧结温度的作用是一致的，具有一最佳范围。而降浊方式对材料的热敏特性影响较大。综合各因素的影响，本配方中，样品的烧结制度定为：以２００℃／ｈ的速率升温，在１２５０℃保温１ｈ，炉冷至９５０℃，保温０．５ｈ，再     

大系统分散鲁棒容错控制的进展及主要成果

综述了近２０年来关联大系统分散鲁棒容错控制的研究动态及取得的主要成果。说明了统一地研究分散鲁棒容错控制的必要性。在分散控制、鲁棒控制和容错控制研究领域内，分析了各种设计方法的主导思想及实质；指出了这些研究成果的意义与存在的问题。文中着重论述了分散、鲁棒、容错控制研究方法的发展途径。     

Modeling and CW operation of a quasi-three-level 946 nm Nd: YAG laser

A model is developed for an end-pumped quasi-three-level laser with population in the lower laser level at equilibrium such as for transitions to the manifolds⁴I9/2in Nd³⁺,⁴I15/2in Er³⁺,⁵I8in Ho³⁺and³H6in Tm³⁺. It is shown that the effect of residual lower laser level population on laser operation can be treated as a saturable loss. Room temperature operation on the⁴F3/2-⁴I9/2transition in Nd:YAG under CW dye laser pumping has been demonstrated with a threshold as low as 11.5 mW incident power and a slope efficiency of 7 percent with 0.3 percent output coupling. Performance is limited by the low output coupling and diffraction loss.     

再谈石材幕墙干挂中存在的安全隐患

随着社会经济的发展，在建筑物装饰中，石材幕墙已占有相当大的比例，华丽的石材幕墙确实为装点城市增添了光彩。庞大的幕墙所用石材每块重达几十斤，并且是由一个个小小的、很不起眼的干挂件与结构体相连接，可见质量是何等的重要。　　但是，令人担忧的是，目前市场上的干挂件质量不容乐观。近几年，外交部大楼、首都机场候机楼等均发生过石板从天而降砸坏汽车和其他物品的事件。导致事件的原因是因挂件质量低劣、焊接头缝不饱满，且经过高温退火产生氧化而断裂所造成。去年中央电视台《焦点访谈》节目对江苏兴化生产的不锈钢产品质量…     

Effect of misalignment on electrical characteristics of ACF joints for flip chip on flex applications

The effect of misalignment on the electrical properties of anisotropic conductive film (ACF) joints is investigated in this work. It is found that along with the increase of misalignment, the connection resistance of ACF joints increases. When the misalignment in x-direction is less than 5 μm, the increase rate of connection resistance is quite large. Then, along with the severity of misalignment, the increase rate becomes smaller. Finally, when the misalignment is close to 20 μm, the increase rate rises again. The Holm's electric contact theory is used for understanding the connection resistance variation. On the other hand, with the increase of misalignment in x-direction, the insulation resistance between ACF joints decreases. If the misalignment exceeded 10 μm, the decrease is prominent for the Ni particle ACF joints. This phenomenon can be explained by the effect of dielectric damage of the epoxy.Computer programs are also developed to calculate the variation of the probability of open and shorting after misalignment and predicate the maximum misalignment tolerance. The results show that the open and shorting probability increase abruptly after misalignment. On the view of pad parameters, the open probability is mainly related to the pad area, while the pads gap is critical to the shorting probability. Large pads gap (small pad width) can reduce the shorting probability obviously. On the other hand, enlarging the pad area by increasing pad length decreases the open probability significantly. So comparing to square shape pad, rectangle shape pad can reduce the failure probability greatly.     

由制碱废渣制脱硫吸收剂配比优选的研究

文章探讨了由制碱废渣和电石渣混合制取脱硫吸收剂 ,不同混合比例对吸收剂的比表面积、脱硫能力的影响 ,从而确定最佳配比方案     

基于PⅢ工控机VI测控系统远程控制研究

虚拟仪器（VI）将计算机采集测试分析引入到电子测量领域，用数字化和软件技术极大地提高了测量的灵活性。而VI远程测控系统是网络技术、通信技术一计算机虚拟技术结合的产物。远程控制技术能够使操作突破地域的限制，已在网络环境下PⅢ工控机上实现。     

A dual-mode multiuser detector for DS-CDMA systems

We introduce a dual-mode multiuser detector that dynamically switches its detection mode between matched-filter and decorrelator operations based on the channel characteristics. This detector significantly reduces the overall computational requirement while maintaining similar performance as that of the decorrelator. The switching mechanism of our dual-mode detector is designed by exploiting the performance-complexity tradeoff between the decorrelator and the matched-filter. Extensions of this idea to other types of multiuser detectors are also proposed     

In-Situ observation on microfracture behavior ahead of the crack tip in 63Sn37Pb solder alloy

in-situ transmission electron microscopy (TEM) tensile tests on as-cast and aged 63Sn37Pb solder alloys were conducted, and the fracture behavior in nanometer scale ahead of the crack tip was inspected and discussed. Results show that the fracture was completed by connecting the discontinuous cracks or voids. Dislocation behavior was concentrated along the grain boundaries for as-cast samples, and displayed mainly as dislocation climb. The crack was intergranular dominated under the lower strain rate. While remarkable mutual dislocation emission was detected in the aged solder. Transgranular cracks were dominant in the fractured area, and they propagated by linking up with the nanometer scale cracks ahead of the crack tips under the effective promotion of the inverse dislocation emission. At the same time, the partial interphase or intergranular cracks in the thinned area were also found. Under this condition, a new critical stress intensity factor K _c ^′ to define the mutual dislocation emission was proposed.