Preparation of fluoroacrylate nanocopolymer by miniemulsion polymerization used in textile finishing

Latex based on fluoroacrylate (TAN) and other comonomers was prepared via miniemulsion polymerization in the presence of stearyl trimethyl ammonium chloride (STAC) and 2, 2′‐azobis (2‐amidinopropane) dihydrochloride (ABAP) as a water soluble initiator. Light transmittance studies demonstrated that the light transmittance of prepared emulsions increases with the amount of TAN, STAC, cosolvent DPM, and hydrophobe DM. Given suitable reaction temperature and quantities of TAN, STAC, DPM, and DM, a copolymer emulsion of fluoroacylate with a particle size of 50 nm was produced. The water repellency tested on polyester fabrics displayed greater effectiveness than that of commercial products with higher fluorine content. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1466–1472, 2004     

熔体温度对气体辅助注射成型PC／PE共混物形态的影响

分别在低温（200℃）和高温（270℃）下制备了聚碳酸酯／聚乙烯（PC／PE）共混物的气体辅助注射成型制品，通过扫描电镜对PC相不同部位的形态观察，发现分散相PC的形变和分布受成型温度的影响比较大。在低温成型时，分散相PC从表层到气道都有变形，而在高温成型时，分散相PC在气道部位几乎没有变形。在形态分析的基础上，探讨了温度对气体辅助注射成型共混物形态的形成和分布的影响机理。     

Effect of ethylene-propylene copolymer with residual PE crystallinity on mechanical properties and morphology of PP/HDPE blends

Morphology and mechanical properties of polypropylene (PP)/high density polyethylene (HDPE) blends modified by ethylene-propylene copolymers (EPC) with residual PE crystallinity were investigated. The EPC showed different interfacial behavior in PP/HDPE blends of different compositions. A 25/75 blend of PP/HDPE (weight ratio) showed improved tensile strength and elongation at break at low EPC content (5 wt %). For the PP/HDPE = 50/50 blend, the presence of the EPC component tended to make the PP dispresed phase structure transform into a cocontinuous one, probably caused by improved viscosity matching of the two components. Both tensile strength and elongation at break were improved at EPC content of 5 wt %. For PP/HDPE 75/25 blends, the much smaller dispersed HDPE phase and significantly improved elongation at break resulted from compatibilization by EPC copolymers. © 1995 John Wiley & Sons, Inc.     

基于不同加载制度的轻骨料混凝土动态冲击性能

以SHPB冲击试验及落锤试验为依据,建立EPS混凝土有限元数值模型,运用连续损伤理论分析不同冲击加载制度对轻骨料混凝土动态缓冲性能的影响.对该类材料的动态响应进行时程分析,揭示峰值速度发生时间及加载周期对整体和局部材料动态冲击响应的影响.分析结果表明:在冲击势能相同的前提下,整体材料的动态耗能特性随着冲击峰值时间的推迟呈现先上升而后下降的趋势,随着加载时程的延长(冲击峰值速度降低)其对冲击势能的转化能力逐渐提高;而单位体积材料的动态耗能特性则随着峰值时间的延迟和加载周期的延长均呈现先上升而后下降的趋势.在材料的冲击损伤演化方面,冲击峰值时间的变化对材料的损伤度影响较小,且材料在峰值时间出现于中期阶段的冲击荷载下的损伤程度相对严重;同时,延长加载周期并降低冲击峰值对于材料冲击损伤的影响显著,并建立了基于加载周期预测材料损伤度的数学模型.     

黄原酸钾含量的示波滴定

报道了用示波滴定法测定黄原酸钾含量 ,在 p H5～ 6的 HAc- Na Ac缓冲底液中 ,加入四苯硼钠 ( Na- TPB)沉淀 K+ ,过量的 Na- TPB用氯化四乙基铵标准溶液滴定 ,滴至 Na- TPB示波图切口消失为终点 ,终点直观敏锐 ,方法快速简便 ,准确度、精密度均高。标准加入回收率在 99.8%～1 0 0 .2 % ,RSD<0 .2 %     

In vivo aging of gutta‐percha dental cone

Gutta‐percha cone is the most widely used material for root canal filling. The in vivo aging of this cone focus on the degradation of its main organic component, trans‐1,4‐polyisoprene, was studied. Aged cones (25 samples) from 2 to 30 years of root canal filling were extracted from different patients in the occasion of retreatment by mechanical way. The information about the aging time was given by the patients. Gel‐permeation chromatography (GPC) and infrared spectroscopy (FTIR) were the analytical techniques used. Polyisoprene degrades with time of aging, but in a slow process. Decrease in polymer molar mass from 5.7 × 10⁵ to 1.7 × 10⁵ g/mol was observed in polyisoprene from cone after 30 years of root canal filling and inside a noninfected tooth. In tooth with caries and periodontal infection, the decrease in molar mass is higher (4.6 × 10⁴ g/mol in cone with 10 years of aging). The production of carbonyl and hydroxyl groups in the aged material indicates that the process is oxidative, even in closed teeth. In these cases, the oxygen could be provided from tissue fluid. The degradation mechanism is complex and depends on many factors, besides time of root canal filling. The dental problem caused by the aging could be the production and migration of cytotoxic substances to periodontal ligament and the reduction on the canal sealing property due to the polymer weight loss. Both of them could contribute to the root canal treatment failure. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100:4082–4088, 2006     

Effects of substituted aromatic heterocyclic phosphate salts on properties,crystallization, and melting behaviors of isotactic polypropylene

Nucleation effects of 2,2′‐methylene‐bis (4,6‐di‐tert‐butylphenyl) phosphate metal salts as a nucleating agent for isotactic polypropylene (iPP) were investigated with differential scanning calorimeter and polarized optical microscope, and their effects on mechanical, optical, and heat resistance properties of iPP were also studied. The results showed that monovalent metal salts of substituted aromatic heterocyclic phosphate such as sodium salt, lithium salt, and potassium salt had a good performance. With 0.2 wt % of sodium salt, lithium salt, or potassium salt incorporated into iPP, the crystallization peak temperature of iPP could be increased by 13.5, 13.6, and 15.0°C, respectively; the mass fraction of crystallinity of iPP could be increased by about 5%; and crystallization rate was enhanced increasingly. Meanwhile the tensile strength and flexural modulus of iPP could be increased by about 10 and 30%, respectively, and the clarity and heat distortion temperature of iPP could also be improved significantly. But bivalent and trivalent metal salts of substituted aromatic heterocyclic phosphate had little effect on properties of iPP. Meanwhile the morphology study showed that the addition of monovalent sodium salt could decrease the spherulite size of iPP significantly. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 100: 4868–4874, 2006     

热固型甲基丙烯酸酯真空浸渗剂发展概况

本文简述了真空浸渗剂的发展概况，着重介绍了其中的热固化浸渗剂及其组成和浸渗工艺。     

Supported Molybdenum Carbides Lie Between Metallic and Sulfided Catalysts for Deep HDS

Hydrodesulfurization (HDS) of 4,6-dimethyldibenzothiophene on alumina-supported Mo₂C has been studied. These catalysts are stable and active under deep HDS conditions (0-250 wt ppm S). However, although they are well known to have hydrogenation properties, they lead preferentially to a non-hydrogenated product of the HDS reaction: dimethylbiphenyl. For the same reaction, supported platinum and sulfided molybdenum oxide lead to the hydrogenated products dimethyldicyclohexyl and methylcyclohexyltoluene, respectively. The ranking of HDS activity is as follows: MoS₂/Al₂O₃ < Mo₂C/Al₂O₃ < Pt/SiO₂.     

Preparation of carbon nanotubes/hydrogenated nitrile rubber composite by ultrasonic technique

将低相对分子质量的液体氢化丁腈橡胶(HNBR)溶于丙酮溶剂中,加入碳纳米管,用超声波技术制备了液体HNBR与碳纳米管的复合母料,然后再与HNBR混炼、硫化,获得碳纳米管/HNBR复合材料.结果表明,碳纳米管在HNBR中分散性好,对HNBR有较好的增强性,但在后期机械加工中产生了断裂.