Structural,morphological, dielectric and magnetic properties of Zn-Zr co-doping yttrium iron garnet

In this study, yttrium iron garnet co-doped with Zn and Zr atoms with a chemical formula Y₃Zn_xZr_xFe_(5−2x)O₁₂ (x = 0.0-0.3) has been successfully prepared by the solid-state reaction method. The effects of doping concentration on the microstructure, crystal structure, magnetic properties, and dielectric properties of Y₃Zn_xZr_xFe_(5−2x)O₁₂ were investigated. The microstructure analysis indicates that co-doping of YIG with Zn and Zr can effectively reduce the grain size of the ceramic. The crystal structure results reveal that the doping concentration of Zn–Zr has substantial influence on the lattice parameters of YIG, such as, increases the lattice constant, crystal cell size, and interplanar spacing. However, the second phase of ZrO₂ appears once x ≥ 0.15. Additionally, the dielectric properties of YIG ferrite can be regulated using this Zn–Zr co-doping method. Zn–Zr co-doping can improve the dielectric stability and reduce the dielectric loss at high temperature. The magnetization measurement shows that the saturation magnetization is stabilized at x < 0.15, and the magnetic loss is decreased with the increase in the doping concentration. Overall, the findings show that the ceramic with x = 0.1 exhibits better properties included high saturation magnetization (24.607 emu/g), low magnetic loss (0.0025 @ 1 MHz), and relatively low dielectric loss (496 @ 400°C).     

Personality expression and recognition in Chinese language usage

User Modeling and User-Adapted Interaction - Personality plays a pivotal role at work. Many scholars have investigated the association between personality and language usage habits in the English...     

Unsteady free convection of second‐grade nanofluid with a new time‐space fractional heat conduction

The Caputo and Caputo–Fabrizio derivative are applied to study a second‐grade nanofluid over a vertical plate. A comparative analysis is presented to study the unsteady free convection of a second‐grade nanofluid with a new time–space fractional heat conduction. The governing equations with mixed time–space fractional derivatives are non‐dimensionalized and solved numerically, and a comparison between the Caputo and the Caputo–Fabrizio models is made. It is found that the temperature is higher for the Caputo–Fabrizio fractional model than the Caputo model, but the higher velocity only exists near the vertical plate for the Caputo–Fabrizio model than the Caputo model. Moreover, the velocity for the Caputo model will exceed the Caputo–Fabrizio model as y evolves.     

Transformation of the reabsorption characteristics of lignite treated by low and high temperature drying process

Abstract

The reabsorption characteristics of the lignite treated by low and high temperature drying process were addressed in the paper. The information about the moisture form, functional groups, effective water-filled porosities and equilibrium moisture content of the lignite before and after the drying process was investigated using Differential scanning calorimetry (DSC), Fourier transform infrared (FTIR) spectroscopy, nuclear magnetic resonance (NMR) spectroscopy and a self-made reabsorption device, respectively. The results show that the low drying temperature (140, 190, 230?°C, 10?min, N₂) has little impact on the effective water-filled porosities of the resulted samples, whereas it has a great influence on the main oxygen-containing functional groups, which amount firstly decreases and then increases with the drying temperature increasing. In the case of the lignite samples dried under high-temperature (600, 700, 800?°C, 30?s, N₂), the amount of the effective water-filled porosity of the sample decreases and the amount of oxygen-containing functional groups increases as the temperature increasing. The reabsorption capability of the high temperature dried sample is much lower than that of the sample treated under low drying temperature. The reabsorption characteristics of the low-temperature dried samples are affected by the amount of the oxygen-containing functional groups, while the effective water-filled porosity is main factor for the lignite samples derived from high temperature drying process. Moreover, the work gives a good evidence that the high-temperature drying process is an effective choose for lignite upgrading.