Sol-Gel Alumina Coating for Improved Cyclic Oxidation Resistance of Silicon Nitride

A 25 nm thick α-alumina layer was deposited on a turbine-grade silicon nitride by sol-gel dip coating and subsequent heat treatment in air at 1200°C. This layer had a nanometer grain structure. Silicon nitride protected by this thin layer showed a significant improvement in oxidation resistance over its uncoated counterpart after 200 cyclic exposures in air at 1250°C. The oxide layer grown on the coated silicon nitride also exhibited superior surface morphology, compared with the uncoated silicon nitride.     

Characterization and physical properties of polymethylphenylsilsesquioxane (PMPSQ) and hydroxyl‐functionalized polystyrene (PS–OH) hybrids

Polymethylphenylsilsesquioxane (PMPSQ–OH) and trimethylsilyl end‐blocked PMPSQ (PMPSQ–EC) were prepared. The thermal decomposition behavior of these polymers was studied by thermogravimetric analysis (TGA) and FT‐Raman spectroscopy. Hydroxyl‐functionalized polystyrene (PS–OH) was also prepared by anionic living polymerization. Thin hybrid films of PMPSQ/PS–OH with various blend ratios were obtained by spin‐coating on freshly cleaned glass. The surface morphology of the hybrid films was investigated by atomic force microscopy (AFM). In 80/20 PMPSQ/PS–OH hybrid film, the PS–OH component produced a very uniformly dispersed phase. This hybrid film contained small domains of PS–OH whose size ranged from 60 to 80 nm. As the content of PS–OH was increased, the domain morphology coarsened and phase inversion took place around 50 wt %. In the phase‐inversed system, the PMPSQ‐rich phase was uniformly distributed in the PS–OH‐rich continuous phase. In addition, temperature‐dependent dielectric properties of PMPSQ/PS–OH hybrids were investigated. Relaxation of the hybrids was observed with an increasing content of the PS–OH component due to the amorphous glass transition behavior of PS–OH. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 90: 2801–2812, 2003     

Honey bees mating optimization algorithm for process planning problem

Process planning is a very important function in the modern manufacturing system. It impacts the efficiency of the manufacturing system greatly. The process planning problem has been proved to be a NP-hard problem. The traditional algorithms cannot solve this problem very well. Therefore, due to the intractability and importance of process planning problem, it is very necessary to develop efficiency algorithms which can obtain a good process plan with minimal global machining cost in reasonable time. In this paper, a new method based on honey bees mating optimization (HBMO) algorithm is proposed to optimize the process planning problem. With respect to the characteristics of process planning problem, the solution encoding, crossover operator, local search strategies have been developed. To evaluate the performance of the proposed algorithm, three experiments have been carried out, and the comparisons among HBMO and some other existing algorithms are also presented. The results demonstrate that the HBMO algorithm has achieved satisfactory improvement.     

Thermal behavior and the determination of the polymer-polymer interaction parameter of polycarbonate and a thermotropic liquid crystalline polymer blends

Summary The surface modification of low-density polyethylene(PE) by liquid phase photograft polymerization with acrylic acid(AA), acrylamide(AM) and glycidyl methacrylate(GMA) was described. The grafting of AA and AM was proved and characterized by electron spectroscopy for chemical analysis(ESCA). It was found that fully hydrophilic surface can be obtained in very short irradiation time. With ESCA and attenuated total reflection infrared spectroscopy(ATR-IR), it can be confirmed that bifunctional monomer GMA was grafted onto the PE film surface. Through further reaction with GMA grafted film, heparin and protamine were immobilized onto the grafted film surface.     

Mechanical properties and morphology of polymer blends of poly(ethylene terephthalate) and semiflexible thermotropic liquid crystalline polyesters

Two thermotropic liquid crystalline polyesters (TLCPs) with long flexible spacer groups in the main chain were prepared by melt polymerization: one was a homopolymer with only decane groups (LCPHO) and the other was a copolymer with hexane or decane groups (LCPCO) between mesogen units. These polyesters were blended with a matrix polymer of poly(ethylene terephthalate) (PET). Scanning electron microscopy (SEM) revealed the excellent interfacial adhesion between polyester and PET, and the large aspect ratio of polyester microfibrils in the blend fiber made by extruding and drawing the blend through a die. The aspect ratio was estimated by using the modified Halpin-Tsai equation. The fiber with LCPHO showed more extensive fibril formation than that with LCPCO.     

Performance of fluorine-added CoMoS/Al2O3 prepared by sonochemical and chemical vapor deposition methods in the hydrodesulfurization of dibenzothiophene and 4,6-dimethyldibenzothiophene

The performance of a new type of CoMoS/Al₂O₃ catalyst, with added fluorine and prepared by sonochemical and chemical vapor deposition (CVD) methods, was investigated in the hydrodesulfurization (HDS) of dibenzothiophene (DBT) and 4,6-dimethyldibenzothiophene (4,6-DMDBT). The catalyst, which was designed to contain optimum amounts of fluorine and cobalt, exhibited a higher activity, ca. 4.6 times higher activity particularly in the HDS of 4,6-DMDBT, than a fluorine-free catalyst prepared by a conventional impregnation method. The enhanced activity of the new catalyst can be attributed to the cumulative effects of individual factors involved in the catalyst preparation. That is, the use of a sonochemical synthesis led to a high dispersion of small MoS₂ crystallites on the alumina, and the addition of the Co species to the catalyst by CVD caused a close interaction between the Co species and the MoS₂ crystallites to produce numerous CoMoS species, which are the catalytically active species for HDS. The addition of fluorine increased the amounts of acidic sites in the catalyst, which promoted hydrogenation (HYD) route to a greater extent than the direct desulfurization (DDS) route in DBT HDS and both HYD and DDS routes to similar extents in the case of 4,6-DMDBT HDS. Accordingly, the addition of fluorine led to a greater increase in catalytic activity for 4,6-DMDBT HDS than for DBT HDS.     

Geometric origin of pair production by electric field in de sitter space

Particle production in de Sitter space provides an interesting model for understanding the curvature effect on Schwinger pair production by a constant electric field or the Schwinger mechanism on de Sitter radiation. For that purpose, we employ the recently introduced complex analysis method in which the quantum evolution in complex time explains pair production via the geometric transition amplitude and gives the pair-production rate as a contour integral. We compare the result from the contour integral with that of the phase-integral method.     

Effects of poly(acrylic acid) and poly(ethylene oxide) adsorption on the stability of alumina suspension

The effect of adsorbed polymer on the stability of alumina suspension was investigated. Poly(ethylene oxide) (PEO), poly(acrylic acid) (PAA) and similar kinds of polymer salts were used as a dispersant. The amount of polymer adsorbed on alumina surface and the suspension stability was measured. The pH, molecular weight, and concentration were considered as experimental parameters. PEO shows low affinity on the alumina surface while PAA has high affinity. In the case of PAA adsorption, the surface charge change by polymer adsorption influences suspension stability strongly, but not in the case of PEO adsorption. In simultaneous adsorption of PEO and PAA, the PAA concentration was fixed and PEO concentration was varied. The stability of suspension increased with increasing PEO concentration, and this is partly due to the steric stabilization by adsorption of PAA-PEO complex or adsorption of PEO through pre-adsorbed PAA and the depletion effect of non-adsorbed polymer. Suspension adsorbing sodium salts of PAA and poly(methacrylic acid) (PMA) each showed similar stability. But, when the PEO and these kinds of salts were added together to the suspension, the one with PAA sodium salt could keep a higher stability even with lower molecular weights of PEO compared with suspension with PMA sodium salt.     

Fault identification for process monitoring using kernel principal component analysis

In this research, we develop a new fault identification method for kernel principal component analysis (kernel PCA). Although it has been proved that kernel PCA is superior to linear PCA for fault detection, the fault identification method theoretically derived from the kernel PCA has not been found anywhere. Using the gradient of kernel function, we define two new statistics which represent the contribution of each variable to the monitoring statistics, Hotelling's T²and squared prediction error (SPE) of kernel PCA, respectively. The proposed statistics which have similar concept to contributions in linear PCA are directly derived from the mathematical formulation of kernel PCA and thus they are straightforward to understand. The main contribution of this work is that we firstly suggest a fault identification method especially applicable to process monitoring using kernel PCA. To demonstrate the performance, the proposed method is applied to two simulated processes, one is a simple nonlinear process and the other is a non-isothermal CSTR process. The simulation results show that the proposed method effectively identifies the source of various types of faults.     

增强聚氨酯硬泡塑料的冲击性能研究

本文研究了SiO2和纤维增强剂对于聚氨酯硬泡塑料冲击性能的增强效应.试验结果表明,加入SiO2并不能增强聚氨酯硬泡塑料冲击性能.然而以2.5% KH550偶联剂四氢呋喃溶液处理的玻璃纤维作为增强剂,能使聚氨酯硬泡塑料的冲击性能有显著的提高.