Design of High-Quality Pt–CeO2 Composite Anodes Supported by Carbon Black for Direct Methanol Fuel Cell Application

A Pt on nano-sized CeO₂ particles that in turn are supported on carbon black (CB) was synthesized using the co-impregnation method. This potential anode material for fuel cell applications was synthesized in a stepwise process. The pure CeO₂ was synthesized using an ammonium carbonate precipitation method, and the Pt particles dispersed on the CeO₂ in such a way that a uniform dispersion with the CB was obtained (Pt–CeO₂/CB). The electrochemical activity of the methanol (CH₃OH) oxidation reaction on the Pt–CeO₂/CB was investigated using cyclic voltammetry and chronoamperometry experimentation. The onset potential of CH₃OH oxidation reaction on the Pt–CeO₂/CB anode was shifted to a lower potential as compared with that on commercially available Pt–Ru/carbon (C) alloy anode. In addition, the activation energy of the Pt–CeO₂/CB anode was much lower than that of the Pt–Ru/C alloy anode. Moreover, the current density of the Pt–CeO₂/CB anode was much higher than that of the Pt–Ru/C alloy anode at temperatures between 28° and 60°C. These results suggest that the anode performance of the Pt–CeO₂/CB anode at the operating temperature of typical fuel cells (80°C) is superior to that of the more usual Pt–Ru/C alloy anode. Importantly, the rare metal, Ru, is not required in the present anode material and the amount of Pt required is also significantly reduced. As a consequence, we report a promising candidate Pt–CeO₂/CB composite anode for application in the development of direct methanol fuel cells.     

The role of pressure on thin amorphous carbon films deposited using microwave surface wave plasma CVD

We report the effects of gas composition pressure (GCP) on the optical, structural and electrical properties of thin amorphous carbon (a-C) films grown on p-type silicon and quartz substrates by microwave surface wave plasma chemical vapor deposition (MW SWP CVD). The films, deposited at various GCPs ranging from 50 to 110 Pa, were studied by UV/VIS/NIR spectroscopy, atomic force microscopy, Raman spectroscopy, X-ray photoelectron spectroscopy and current–voltage characteristics. The optical band gap of the a-C film was tailored to a relatively high range, 2.3–2.6 eV by manipulating GCPs from 50 to 110 Pa. Also, spin density strongly depended on the band gap of the a-C films. Raman spectra showed qualitative structured changes due to sp³/sp² carbon bonding network. The surfaces of the films are found to be very smooth and uniform (RMS roughness < 0.5 nm). The photovoltaic measurements under light illumination (AM 1.5, 100 mW/cm²) show that short-circuit current density, open-circuit voltage, fill factor and photo-conversion efficiency of the film deposited at 50 Pa were 6.4 μA/cm², 126 mV, 0.164 and 1.4 × 10^− 4% respectively.     

Influence of dry operating conditions: observation of oscillations and low temperature CO oxidation over Co3O4 and Au/Co3O4 catalysts

A Sm(III) exchanged NaY zeolite prepared from aqueous SmCl₃ was modified with various amounts of fluorine using NH₄F. These fluorinated zeolites exhibit enhanced catalytic activity for the dealkylation of cumene. The evaluation of acid sites by infrared spectroscopy and pyridine adsorption was correlated with fluorine content.     

The effects of oxygen diffusion on the surface photooxidation of polystyrene

This paper further illustrates the applicability of multiple internal reflectance infrared spectroscopy to the analysis of near-surface photooxidation. The results are compared with transmission infrared spectra to evaluate compositional gradients resulting from photooxidation and the influence of oxygen diffusion. The sample was a solvent-cast film of atactic, narrow distribution polystyrene, M_w of 100,000, that had been drawn to a ratio of 3.0 at 110°C by solid state coextrusion. Irradiation of these thin films, ～25μm thickness, was performed on exposure to air at 35°C for periods of up to 6 h using a mercury source emitting at 254 nm. On photooxidation, a board peak appears at 3200–3500 cm^?1, attributable to hydroperoxide formation. The most dramatic increase in the infrared spectra is found for a carbonyl band at 1730 cm^?1. It appears to result from an aromatic acid group since it is shifted to 1660 cm^?1 on immersion of the oxidized polystyrene films in aqueous ammonium hydroxide. It is confirmed that the photooxidation of polystyrene occurs preferentially at the surface and that this reaction rate is greatly reduced in the drawn polystyrene film.     

Chemospecific ring-opening polymerization of α-methylenemacrolides

α-Methylenemacrolides having various groups, such as aromatic, ether, and amine, were enzymatically, anionically, and radically polymerized. The polymerization with the lipase catalyst successfully afforded polymers only through the ring-opening process, whereas the vinyl polymerizations selectively proceeded by using anionic and radical initiators. The polyesters obtained by the enzymatic polymerization have a polymerizable methacrylic methylene group in the main-chain, in addition to the aromatic and polar groups, and were further radically polymerized to quantitatively produce a cross-linked polymer gel.     

Decomposition of chlorofluorocarbons on TiO2ZrO2

The decomposition of chlorofluorocarbons (CFCs) in the presence of water was examined over a variety of solid acid catalysts. The TiO₂ZrO₂ catalyst was found to have the highest activity and longest life among the catalysts examined. The activity of the TiO₂ZrO₂ catalysts depended upon the content of TiO₂. At the contents of TiO₂ from 58 to 90 mole%, the TiO₂ZrO₂ catalysts exhibited high activity, and these catalysts were proven to contain TiZrO₄ crystal. From the study of the XRD peak intensity of the TiZrO₄ crystal, it was highest on the TZ-58 which contained 58 mole% of TiO₂, and decreased with increasing the content of TiO₂. Furthermore, the conversion of CFC113 measured at 673 K was highest at TZ-58, and decreased gradually with increasing TiO₂ content. Therefore, the TiZrO₄ crystal influences the activity of decomposition of CFC113. However, the TiO₂ZrO₂ catalyst was gradually deactivated during the reaction due to the elimination of titanium atoms. A good relationship was found between the activity on TiO₂ZrO₂ catalyst and bond energy of CCl in the compounds of chlorofluorocarbons and hydrochlorocarbons, suggesting that the rate controlling step was the cleavage of CCl bond.     

Characterization of styrene–methyl methacrylate–n-butyl acrylate terpolymers. II. Effects of sequence distribution on glass transition temperature

The effects of sequence distribution on the glass transition temperature (T_g) of the title terpolymers prepared by radical polymerization were studied. T_g was examined by thermomechanical analysis. The average diad concentrations, as estimation of sequence distributions were calculated from monomer reactivity ratios. A modified Gibbs–Dimarzio equation for binary copolymers was extended to terpolymers to explain the relation between observed T_g and average diad concentrations. The observed T_g showed good agreement with the calculated values determined by the extended equation.     

Gelation of poly(vinyl alcohol)/phenol/water solutions and gel spinning

The light transmittance of the gels of poly(vinyl alcohol) (PVA)/phenol/water solutions was examined for the entire range of phenol/water content. Excellent transparency was found for the gels with phenol contents of 70–95 vol %. In full consideration of the results for the transparency and melting temperature of the gels and the viscosity and gelation ability of solutions, the PVA solutions of 75 vol % phenol content were selected for the gel spinning. The maximum dynamic moduli of drawn filaments at 25°C (room temperature) were 42 GPa (15x) for atactic PVA and 45 GPa (14x) for syndiotacticity-rich PVA. © 1995 John Wiley & Sons, Inc.     

Deposition of dense isotropic carbon from acetylene in fluidized bed

Pyrolytic carbon was deposited from acetylene in a fluidized bed at 1100°C on alumina microspheres. In case when only argon was used as the diluent gas, density and BAF of the deposit decreased and deposition yield increased with increasing acetylene concentration. Hydrogen sypply suppressed carbon formation and, consequently, caused an increase in density and Lc. BAF was relatively independent of hydrogen concentration. It was found that high density, isotropic carbon can be deposited from acetylene at 1100°C, if an appropriate proportion of hydrogen is added.