Loss of precious metal from Pt-Rh alloy under refractory oxide environments

Loss of precious metals from a Pt-10 wt% Rh alloy was studied at 1300° C in refractory oxides and fused quartz environments. After 60 and 150 h annealings, samples exposed to gaseous environments showed significant weight loss. The surface was attacked and characterized by micron-sized pits, as well as river-like striations. The pits were found to be enriched with silicon and/or aluminium depending upon the heating environment. Laser Raman microprobe identified that the major compound formed in the pits is -cristobalite.Direct solid state contact of Pt-Rh with Al₂O₃ and SiO₂ showed interactions between materials. The interaction was more extensive between Pt-Rh with SiO₂ than with Al₂O₃. On the other hand, no evidence of interaction except pitting and striation was observed on Pt-Rh when exposed to a vapour environment.The presence of pits and striation patterns indicated that refractory oxides attacked Pt-Rh under atmospheric conditions, and gave rise to the weight loss. Calculation of weight loss by an oxidation mechanism shows one to two orders of magnitude lower value than the actual weight loss. A new loss mechanism is proposed and discussed in this article.     

Preparation of fluoroacrylate nanocopolymer by miniemulsion polymerization used in textile finishing

Latex based on fluoroacrylate (TAN) and other comonomers was prepared via miniemulsion polymerization in the presence of stearyl trimethyl ammonium chloride (STAC) and 2, 2′‐azobis (2‐amidinopropane) dihydrochloride (ABAP) as a water soluble initiator. Light transmittance studies demonstrated that the light transmittance of prepared emulsions increases with the amount of TAN, STAC, cosolvent DPM, and hydrophobe DM. Given suitable reaction temperature and quantities of TAN, STAC, DPM, and DM, a copolymer emulsion of fluoroacylate with a particle size of 50 nm was produced. The water repellency tested on polyester fabrics displayed greater effectiveness than that of commercial products with higher fluorine content. © 2004 Wiley Periodicals, Inc. J Appl Polym Sci 94: 1466–1472, 2004     

负载奈米银之二氧化钛光触媒及其光催化活性之研究

利用自制之奈米银粒子,或用化学还原法将银微粒直接沉淀在市售二氧化钛粉末上,并比较二者对亚甲基蓝光催化效果,由于银微粒可降低电子与电洞对再结合之效果,而使二氧化钛粒子光催化活性提高,其中并以直接沉淀法为佳.此外亦藉由高温氢气对二氧化钛粉末进行还原,形成部分的Ti3+,藉此亦达到提升光催化之效果.最后将奈米银负载于经还原过后之二氧化钛粒子,于紫外光与可见光下对酚作光催化分解,发现其亦得到一定程度的分解效果.     

Elastic Response and Effect of Transverse Cracking in Woven Fabric Brittle Matrix Composites

This paper examines the linear elastic tensile and fracture behavior of biaxial plain weave SiC/SiC ceramic woven fabric composites. Iso-phase mode and random-phase mode have been adopted to simulate multilayer stacking and to predict the initial linear elastic constants. It has been found that both modes predict very close results. Porosities in the composite affect the stiffness significantly, while fiber undulation shows only minimal effect. The nonlinear stress-strain relation of the composite is due to transverse cracks, which initiate mainly from interyarn pores. In the second part of this paper, two methods, classical fracture mechanics and energy balance approach, have been used to examine the crack initiation and growth. A finite element method and a modified shear-lag method have been developed to evaluate the stress distribution in the yarn with transverse cracks. The composite stiffness reduction due to transverse cracking has been obtained by both the finite element and shear-lag methods. Strain energy release rates of the growth of transverse cracks have been studied by the crack-closure procedure, using finite element methods. Effects of the yarn size and crack position on the strain energy release rate have been quantified. It is concluded that thinner yarns lead to higher critical strains for transverse cracking.     

Evaluation of two cooling systems under a firefighter coverall

Firemen often suffer from heat strain. This study investigated two chest cooling systems for use under a firefighting suit. In nine male subjects, a vest with water soaked cooling pads and a vest with water perfused tubes were compared to a control condition. Subjects performed 30 min walking and 10 min recovery in hot conditions, while physiological and perceptual parameters were measured. No differences were observed in heart rate and rectal temperature, but scapular skin temperature and fluid loss were lower using the perfused vest. Thermal sensation was cooler for the perfused vest than for the other conditions, while the cool pad vest felt initially cooler than control. However, comfort and RPE scores were similar. We conclude that the cooling effect of both tested systems, mainly providing a (temporally) cooler thermal sensation, was limited and did not meet the expectations.     

Plastic deformation of ZnO thin films through edge and screw dislocation movements

Columnar wurtzite grains were formed in sputtered ZnO thin films deposited on a plastic polyethylene terephthalate substrate. Selected-area diffraction patterns reveal that the columnar grains in the sputtered films present two preferred growth planes, namely, the basal (0002) and prismatic (100) growth planes. The diffraction patterns obtained also confirm that the microstructure of sputtered indium tin oxide thin films is amorphous in nature. Tensile tests indicate that the fracture strain of the ZnO thin film occurs between 1.73% and 2.14%, while the fracture strain of the indium tin oxide thin film occurs between 0.24% and 0.67%. Thus, the fracture toughness of the sputtered ZnO thin film is greater than that of the sputtered indium tin oxide thin film. High-resolution transmission electron microscopic images demonstrate that edge and screw dislocations could be identified in the sputtered ZnO thin films. Moreover, edge and screw dislocation movements may, respectively, be observed in the basal- and prismatic-oriented ZnO columnar grains of the sputtered ZnO thin films. Our results indicate that movements of the edge and screw dislocations in the basal- and prismatic-oriented ZnO columnar grains account for the plastic deformation of the investigated ZnO thin films under tensile stress.     

A new model for evaluating the electrical conductivity of nonferrous slag

Electrical conductivity of molten slag is an important physicochemical property for designing the refining process in electric smelting furnaces.Though conductivities of many slag systems have been measured,the quantitative relationships of conductivity with slag composition and temperature are still very limited.In this article,the Arrhenius law was used to describe the experimental data of conductivities for CaO-MgO-Al2O3-SiO2,CaO-Al2O3-SiO2,CaO-MnO-Al2O3-SiO2,as well as CaO-MgO-MnO-Al2O3-SiO2 systems,and...     

Cation interdiffusion between thick film of YBa2Cu3O7-δ and ceramic substrate

Thick films of superconducting oxides, YBa₂Cu₃O_7-, were successfully made by conventional screen-printing technology on Al₂O₃, MgO, and ZrO₂ substrates. Interdiffusion between the superconductive film and substrate was investigated using analytical electron microscopy. The results indicate that MgO and ZrO₂ are superior to Al₂O₃ for substrate materials.     

A STUDY OF THE STRESS CORROSION CRACKING OF SENSITIZED 1Cr18Ni9Ti STAINLESS STEEL IN HIGH TEMPERATURE HIGH PRESSURE WATER

从环境角度研究了敏化1Cr18Ni9Ti不锈钢在高温水中的腐蚀行为.研究指出,在一定浓度Cl~-和(或)O_2存在情况下,在酸性和中性高温高压水中都会出现应力腐蚀破裂.断口电子金相表明,在氯离子为主的环境中,破裂系晶间型;在氧为主的环境中,破裂系以解理为主的混合型.给出了1Cr18Ni9Ti在高温水中腐蚀的表观和真实动力学曲线,表明腐蚀包含溶解和湿氧化两部分,而以湿氧化为主.借Mossbauer内转换电子谱研究了氧化膜结构与腐蚀的关系,指出在一般腐蚀条件下,膜的主要组分为Fe_3O_4,而在应力腐蚀条件下,膜的主要组分为Fe_2O_3,并且系Fe_2O_3和Fe_3O_4多层重叠结构.当水中添加了一定量的硼,在氧化膜中会局部出现FeBO_3相,既不会引起也不会抑制应力腐蚀.硼的这种“惰性”作用和膜结构中Fe_3O_4相的非化学计量比,膜具有阴离子选择性有关.根据腐蚀电化学,认为应力腐蚀系发生在钝化/过钝化区域,增高Cl~-或O_2含量,从不同角度都会使合金的电位接近过钝化区.Cl~-的作用在于改变阳极极化曲线,O_2的作用在于改变阴极极化曲线.在含Cl~-水中,晶界TiC的迅速溶解是应力腐蚀的主要原因,而在含氧水中,晶粒Fe-Cr-Ni中Cr的选择性溶解是应力腐蚀的主要原因.在分析应力腐蚀的特征后,指出应力既是某些严重腐蚀点形     

Application of Graham scan algorithm in binary phase diagram calculation

Graham scan, a computational geometric algorithm for finding a two-dimensional convex hull, is introduced to calculate binary phase diagrams. This algorithm is modified and applied to find the convex hull of discrete points in the space of Gibbs energy vs mol fraction. The modified Graham scan algorithm has a very low computational cost, which improves efficiency in binary phase diagram calculation.