风电叶片大梁用碳纤维拉挤板材组合式加载压缩(CLC)测试浅析

依据ASTM D6641/D6641M-16《采用组合加载方式(CLC)测定聚合物基复合材料层压板压缩性能试验方法》标准,对风电叶片大梁用碳纤维拉挤板材进行压缩性能测试,通过采用不同类型的加强片制备压缩试样,对所测得的压缩强度、压缩模量和压缩应变的试验结果与失效模式进行分析.结果 表明,采用文中C型加强片制备的压缩试样,测得的压缩强度、压缩模量、压缩应变以及失效模式均较为理想,试验结果重复性较好.     

隔焰辊道窑碳化硅板的研究

本文主要对隔焰辊道窑碳化硅板的配方选择、热震损伤、抗氧化性能和结构形状进行探讨.     

Mercury transformation across particulate control devices in six power plants of China: The co-effect of chlorine and ash composition

This paper presents the results of field measurements on mercury speciation in six power plants of China by applying the Ontario hydro method. During the tests, flue gas was sampled simultaneously before and after particulate control devices (electrostatic precipitator and fabric filter baghouse) along with the pulverized coal, bottom ash and fly ash sampling. The amount of oxidized mercury in gas phase before and after ESP/FF suggests that mercury oxidation after combustion is a kinetically controlled process. The comparison of mercury speciation in different power plant indicates a clear relationship with coal type, especially the chlorine concentration and the basic ash compositions in coal. Both of the factors are analyzed quantitatively in this study. A new parameter C (ratio of chlorine in coal to base/acid ratio) has been introduced to evaluate the co-effect of the two factors above on mercury speciation.     

结晶性高聚物作为相变材料的应用

本文研究了结晶性高聚物聚乙烯及其共混物作为相变材料对模拟发热体铜片热量的吸收作用，由于相变的吸热，铜片的温度在一定时间范围内保持在一个定值。选择不同的相变材料，可使这种温度平台出现在不同的温度范围，不共晶的共混物可有两个以上的温度平台，提高了降温效果。     

Effect of miscibility and forced compatibility on damping properties of CIIR/PAc blend

In this study, a kind of novel damping materials was prepared based on the blend of chlorinated butyl rubber (CIIR) and polyacrylate (PAc) synthesized by different molar ratio of butyl methacrylate and ethyl acrylate. Research results from experiments and analyses by employing DMA, TEM, and FTIR show that whether at a cocured system or noncocured system, it can be achieved to shift a loss peak of CIIR towards a higher temperature region and to keep the damping value from markedlly decreasing, which broadens the effective damping function area of CIIR to the vicinity of ambient temperature. In the former system, the thermodynamical miscibility of CIIR and PAc, to some extent, is predominated by the molecular design of PAc, while in the latter system, covulcanized networks play a more significant role in improving compatibility and abating the peak split, though the suppression effect of thermal stress on the transition of CIIR T_ll transition still can not be neglected. Furthermore, transition state derived from the cocuring CIIR and PAc cannot make the phase separation completely take place, and consequently results in the deformation of phase morphology of the cocured CIIR/PAc blend. It is the influence of thermodynamics miscibility and forced compatibility in different size that makes the suppression effect of foreign PAc on CIIR T_ll transition be controllable. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3127–3133, 2006     

2,6-二乙酰基吡啶合成方法的改进

优化了2，6—二乙酰基吡啶的合成工艺。以2，6—吡啶二羧酸为原料，经过醇化及克莱森酯缩合反应，合成了2，6—二乙酰基吡啶，2，6—吡啶二羧酸二乙醇和2，6—二乙酰基吡啶的分离收率分别为94．1％和88．9％，2，6—二乙酰基毗啶的质量分数大于99％。     

An Attractive Synthetic Approach to Methyl Formate from Methanol via Methyl Nitrite

Catalytic synthesis of methyl formate has been investigated by a novel route starting from methyl nitrite in vapor phase. The acidic sites of the catalysts play a crucial role for the catalytic activity and the selectivity of formation of methyl formate. The H-Y zeolite catalyst gave higher yield and selectivity of the target product. This study provides a new approach for the synthesis of methyl formate from methanol via methyl nitrite.     

水溶性富勒烯衍生物的设计合成及在生物医药中的应用

介绍了水溶性富勒烯衍生物在抗艾滋病、DNA的裂解、消除自由基和抗菌等方面的应用,及一些水溶性富勒烯衍生物的设计合成。     

利用氯碱厂废弃盐泥制备NO3-吸附剂

将氯碱厂废弃盐泥与丙烯酸、钛酸四正丁酯等共聚，过硫酸钾作引发剂，制得TNO3^-吸附剂，同时还得到了有利用价值的二氧化硅和碳酸钙。用正交试验法与单纯形优化法相结合，确定了废弃盐泥制备NO3^-吸附剂的优良配方及合适的工艺。增添了水净化剂的新品种，探索了氯碱工业废弃盐泥利用的新途径。     

铁电晶体TGS的快速生长

报道了TGS晶体的溶液状态及其快速生长的实验结果。发现了pH为2.52的溶液是实现快速生长的最佳溶液,利用快速旋转叶片来加速溶液对流,对于截面积为40mm×40 mm的(010)面,其生长速度达到了5mm/d,对快速生长的TGS晶体的性能研究表明:其热电和介电性能也发生了一些变化。