Low-pressure CO2 sorption in ammonium-based poly(ionic liquid)s

Ammonium-based ionic liquid monomers and their corresponding polymers [poly(ionic liquid)s] are synthesized and characterized for CO₂ sorption. The polymers have much higher CO₂ sorption capacities than the room-temperature ionic liquids and imidazolium-based poly(ionic liquid)s. For example, P[VBTMA][PF₆] with polystyrene backbone has a CO₂ sorption capacity of 10.67 mol%. The CO₂ sorption is selective over N₂ and O₂. The effects of cation, backbone, substituent, anion and crosslinking on CO₂ sorption are discussed. The sorption mechanism study indicates that CO₂ sorption by the poly(ionic liquid)s is a bulk and surface phenomenon.     

Phase Evolution and Dielectric Properties of MgTiO3–CaTiO3-Based Ceramic Sintered with Lithium Borosilicate Glass for Application to Low Temperature Co-Fired Ceramics

Effects on phase evolution caused by the addition of a new sintering agent, lithium borosilicate, Li₂O·B₂O₃·SiO₂ (LBS) glass to 0.9MgTiO₃–0.1CaTiO₃ ceramic and resultant dielectric properties were investigated. The added LBS glass, a liquid phase sintering agent, significantly lowered the densification temperature from 1300° to about 950°C, while yielding decomposition of MgTiO₃ into MgTi₂O₅ and Mg₂TiO₄. At the same time, the by-products of the decomposition reaction, MgO and TiO₂, were dissolved into the glass network. Such phase evolution partly compensated the influence of deleterious glass addition so that the specimen demonstrated fairly good apparent dielectric properties.     

弹性条缝筛网用聚氨酯弹性体的研制

采用预聚法常压浇注制备煤矿用聚氨酯筛网，考察了聚醚多元醇、甲苯二异氰酸酯异构体种类、预聚体的NCO质量分数、扩链反应温度、后熟化温度及时间等条件对制筛网用的浇注型聚氨酯弹性体体系操作性能及物理性能的影响。实验表明，采用聚四氢呋喃二醇与聚氧化丙烯二醇的混合二醇(质量比为80：20)，制得的预聚体NCO质量分数控制在4．5％左右；再以MOCA和一种三官能度扩链剂的混合扩链剂进行扩链，制得的浇注型聚氨酯弹性体满足洗煤用筛网的性能要求。     

Grafting polymerization of l-lactide on the surface of hydroxyapatite nano-crystals

A novel method of grafting ring-opening polymerization of l-lactide (LLA) onto the surface of hydroxyapatite nano-particles (n-HAP) was developed. PLLA was directly connected onto the HAP surface through a chemical linkage. The PLLA-g-HAP particles could be stably dispersed in organic solvent such as chloroform for several weeks. The n-HAP particles still retained the original dimension and shape after the grafting of PLLA. Compared with the ³¹P MAS-NMR spectrum of pure HAP powders, there appeared a downfield displacement of 1.2 ppm in the spectrum of PLLA-g-HAP. Fourier transformation infrared (FT-IR) spectra further confirmed the existence of PLLA on the surface of PLLA-g-HAP. The amount of grafted polymer determined by thermal gravimetric analysis (TGA) was about 6% in weight. The tensile strength and elongation at break of the PLLA/PLLA-g-HAP composite containing 8 wt% of PLLA-g-HAP were 55 MPa and about 10-13%, respectively, while those of the PLLA/n-HAP composites were 40 MPa and 3-5%, respectively.     

Morphology and characterization of conductive films based on polyaniline‐coated polystyrene latexes

The polyaniline (PANI)‐coated polystyrene (PS) latexes were synthesized, and the electrically conductive films were prepared thereafter. The weight ratio of PANI was 5%. Thermal analysis of the latices was performed using DSC and TGA. In this study, the electrically conductive films were prepared above the PS glass transition temperature (T_g). During the film formation, the effects of the annealing temperature and atmosphere (air or N₂) on the film resistance were investigated. In addition, the film morphology was observed utilizing scanning electron microscopy. The film resistance decreased in the initial heating stage due to the increasing temperature and the compaction of film. Then the film resistance increased with further annealing due to the aging of PANI. Typically, the film resistance was about 6000 Ω/sq, and the conductivity was 0.3 S/cm. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 5406–5413, 2006     

汽车尾气用催化剂载体研究现状及展望

汽车尾气催化净化器中，催化剂载体是实现高效尾气净化的一个关键因素。本文综述了对尾气净化催化剂载体的要求和研究现状。并提出导电型复合陶瓷是今后尾气净化载体材料研究和发展的一个新型方向。     

Mechanical properties of poly(lactic acid) and wheat starch blends with methylenediphenyl diisocyanate

Poly(lactic acid) (PLA) and wheat starch are biodegradable polymers derived from renewable sources. A previous study showed that thermally blending starch and PLA in the presence of methylenediphenyl diisocyanate (MDI) enhanced the mechanical properties of the blends. In this work, blends of PLA with various levels of wheat starch and MDI were hot mixed at 180°C then hot‐pressure molded at 175°C to form test specimens. The blends were characterized for mechanical properties, fracture microstructure, and water absorption. Pure PLA had a tensile strength of 62.7 MPa and elongation of 6.5%. The blend with 45% wheat starch and 0.5 wt % MDI gave the highest tensile strength of about 68 MPa with about 5.1% elongation. The blend with 20% starch and 0.5 wt % MDI had the lowest tensile strength of about 58 MPa with about 5.6% elongation. Dynamic mechanical analysis showed that storage modulus increased and tan δ decreased as starch level increased, but almost leveled off when starch level reached 45% or higher. Water absorption of the blends increased significantly with starch content. Yet the blend, if water proofed on its surface, has potential for short‐term disposable applications. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 84: 1257–1262, 2002; DOI 10.1002/app.10457     

在方箱炉、圆筒炉中区域法计算辐射传热的数学模型及其应用

本文叙述了以区域法计算辐射传热的数学模型。在区域法中,系统被分为表面区和气体区,区域数取决于所要求的结果精度和计算时间。炉子的温度分布可通过解每区的能量平衡而得。作为Hottel和Cohen的原始开发,直接交换面积限于立方体和正方形;本文给出了在方箱炉、圆筒炉中任何两区之间直接交换面积方程式的推导。这些方程式可适用于任何大小的矩形、共轴圆筒壁、炉底环形区和其他形状。 本文提供了一个关于烃类一段蒸汽转化炉和圆筒炉的设计方法。计及反应动力学、对流传热、管内压降,采用区域法计算这些炉子的温度分布,从而预言工艺气、烟气、管表面和耐火墙表面的温度分布。计算结果与工厂实测数据相吻合。     

Cortex—MO＋的RFID读卡器模块设计

本文设计一种基于NXP公司的LPC812微控制器和SLRC610射频芯片的RFID模块方法。该模块采用内置天线,预留串口与外部通信。该模块性能优良、易于集成到RFID系统中,使用户更专注于系统功能方面的设计。