脉冲激光沉积BNT和KNN系陶瓷薄膜的比较研究

利用脉冲激光沉积技术(PLD),在不同的制备工艺条件下,分别在Pt/Ti/SiO2/Si基片上制备了Bi0.5Na0.5TiO3(BNT)系列的Bi0.5(Na0.7K0.2Li0.1)0.5TiO3(BNKLT)和K0.5Na0.5NbO3(KNN)系列的Li0.04(Na0.5K0.5)0.96(Nb0.775Ta0.225)O3(KNNLT)无铅压电陶瓷薄膜,并利用X射线衍射仪(XRD)、扫描电镜(SEM)和原子力显微镜(AFM)对薄膜的晶体结构及表面形貌进行了比较研究.研究结果表明:薄膜的衬底温度、沉积室的氧气压力和薄膜的热处理温度对BNT和KNN薄膜结构和形貌都有较大影响,且影响程度不同;在最佳制备工艺参数下,利用PLD制备的BNT和KNN无铅压电陶瓷薄膜都具有精细的表面结构.     

激发态极化效应的修正模型

本文考虑到极性晶体中不同的热释电过程以及辐射跃迁中平均发射频率ν₂与电子跃迁频率ν₃的差异(斯托克斯位移),提出了激发态极化效应的修正模型。根据该模型及不同作者利用不同激发光源在不同实验条件下对厚度不同的LiNbO₃:Cr³⁺晶体样品所得的实验结果,计算了该晶体中Cr³⁺离子激发态的偶极矩改变△μ。在实验误差范围内,由不同的实验数据算得的△μ完全一致:△μ约为3Debye;在整个实验温度区间(50—300K)内,△μ几乎与温度无关。 关键词：     

草酸镁空心纳米结构的一步低热固相化学合成(英)

Nanostructuredmaterialsareafocusedresearchfieldduetotheirunusualpropertiesandpotentialap-plicationsrangingfrommesoscopicresearchtothede-velopmentofnanodevices[1,2].Especially,allsortsofnanoscalematerialswithspecificstructureorinter-estingmorphologyhavepro…     

电化学沉积技术制备LiNiO2薄膜及表征

Well-crystallized LiNiO₂ thin films were prepared directly on nickel substrates in LiOH solution by constant current electrochemical deposition technique at 95 ℃. The as-prepared LiNiO₂ thin films were characterized by using XRD, SEM and XPS, and the results reveal that the as-prepared LiNiO₂ thin films are dense and uniform in surface and show hexagonal structure. The influence of processing parameters such as reaction temperature, duration, electrical current density as well as the concentration of LiOH solution on the structure and morphologies of as-prepared LiNiO₂ thin films were studied，and the preferable electrochemical processing conditions for preparing LiNiO₂ thin films were suggested.     

室温电化学沉积Ba1-xCaxMoO4多晶固溶体薄膜

近年发展起来的制备功能薄膜的电化学沉积技术,是软溶液工艺路线(Soft Solution Processing简记为SSP)中的重要技术[1]。与传统的薄膜制备技术相比,电化学沉积技术在反应控制、形貌控制、沉积速度、能量消耗、环境影响、薄膜晶化以及沉积设备等方面都有较明显的优势,同时避免了     

氢氧化钴纳米棒的室温固相化学合成及其表征

一维或准一维纳米结构体系或纳米材料的研究,既是研究其他低维材料的基础,又与纳米电子器件及微型传感器密切相关,是近年来国内外研究的前沿.尽管有许多合成一维纳米材料的方法[1～4],但是这些方法往往各有其局限性且大多需要多个步骤,操作复杂,条件苛刻.因此,寻找反应条件温和,易于操作,适用范围广,一步就能制备一维纳米材料的新方法尤为重要.     

SOL-GEL法制备钛酸锶钡(BST)粉体

Ba1-x SrxTiO3 (BST) powders were fabricated by sol-gel process by using strontium carbonate for the substitution of strontium acetate. Barium acetate, strontium carbonate and titanium-tetrabutoxide were used as raw materials. The BST gel was studied by thermal analysis techniques, the physical structure of the BST powders was measured by XRD and the grain size was measured. The results showed that the powders possess a single perovskite phase after 700℃ and the ideal powder size even after 800℃ calcining. This indicated that the powder can be used for BST ceramics and the fabrication of the sol-gel derived BST can be carried out well by using carbonate as the starting materials.     

(K_(0.485)Na_(0.485)Li_(0.03))NbO_3-Pb(Zr_(0.53)Ti_(0.47))O_3陶瓷的介电铁电性能

采用传统电子陶瓷工艺制备新型钙钛矿体系(1-x)(K_(0.485)Na_(0.485)Li_(0.03))NbO_3-Pb(Zr_(0.53)Ti_(0.47))O_3陶瓷,研究了该体系陶瓷的介电铁电性能.X射线衍射分析表明:所有陶瓷样品都具有单一的钙钛矿结构,在0.65≤x≤0.75时,出现明显的正交相和四方相的准同型相界区.测试结果表明:陶瓷具有高介电常数.低介质损耗,良好的温度稳定性;获得了饱和的电滞回线,显示了优良的铁电性能.尤其在x=0.75时各项性能达到最佳,其中介电常数ε_r=1590,介电损耗tan δ=0.017,居里温度T_c=295℃,剩余极化强度P,=28.6 μC·cm~(-1),矫顽场强E_c=0.89 kV·mm~(-1).     

钼酸锶基二元固溶体粉末的化学溶液沉积法制备及其发光特性研究

采用化学溶液沉积(CSD)技术,用廉价的无机盐(SrCO3、(NH4)6Mo7O24 · 4H2O)为主要初始原料、常见的有机试剂(丙三醇、冰乙酸和乙二醇甲醚)为溶剂,成功地制备了Ca0.7Sr0.3MoO4和Ba0.3Sr0.7MoO4两类具有白钨矿结构的二元固溶体粉末,并对两种粉体的结构、形貌、颗粒分布以及室温光致发光性能进行了测试.研究表明,两类钼酸锶基固溶体粉末都具有单一的四方相结构,且固溶特性良好,没有检测到明显的杂质峰;固溶体粉末的形貌和尺寸与粉体的成分密切相关,Ca0.7Sr0.3MoO4粉体的晶粒较小,为纳米量级,而Ba0.3Sr0.7MoO4粉体呈现明显的四棱锥外观,晶粒尺寸较大,为微米量级;两类粉末均呈现宽带发光特性,最大发光波长位于蓝绿光波段;Ca0.7Sr0.3MoO4粉体在室温下的发光强度较高,而Ba0.3Sr0.7MoO4粉体在同样条件下的发光强度极其微弱.     

光热(释)电光谱及其应用

光热（释）电光谐（ＰＰＦＳ）是近二、三年来发展起来的用以研究凝聚态物质特性的新的光谐技术．本文概述了 ＰＰＥＳ的基本原理及其在热波扫描显微术、研究固体相变、测定固体热扩散率等方面的应用，指出了潜在的应用前景，并比较了这种新的光热光谱技术的优点和缺点．