Finite element analysis on electron beam brazing temperature and stresses of stainless steel radiator

Based on thermal-elasto-plastic finite element theory, a two-dimensional finite element model for calculating electron beam brazing temperature and residual stress fields of stainless steel radiator are presented. The distributions of temperature and residual stress are studied. The resuhs showed that temperature distribution on brazing surface is rather uniform, ranging from 1 026 ℃ to 1 090 ℃. The residual stresses are varied from initial compressive to tensile , and the variation of residual stress is very little in total zone of brazing surface.     

7A52铝合金电子束焊接头的组织与性能

采用ЭЛY-K型中压电子束焊机对7A52铝合金进行焊接,并对焊接接头的显微组织和力学性能进行了研究.结果表明,其焊缝组织均匀致密、晶粒细小,由α(Al)+T(Mg<,3>Zn<,3>Al<,2>)相组成,与母材的组成相相同;焊缝中Mg、Zn元素均有不同程度的烧损,其中Zn元素的烧掼情况较Mg元素严重,焊缝中心Mg、Zn元素烧损情况较焊缝边缘严重:焊缝中心硬度最低;焊接接头平均拉伸断裂强度为431.7MPa,平均冲击韧度为27.67J/cm<'2>,为母材冲击韧度的82.4%.     

液压支架结构用Q550低合金高强度钢常温下的焊接

对液压支架用Q550低合金高强度钢常温下焊接工艺进行了研究.进行了焊接接头的拉伸、弯曲、低温冲击试验,并对其冲击断口及显微组织进行了观察.结果表明,采用低氢型渣系的低合金高强钢药芯焊丝PK-YJ707A焊接后,焊接接头的屈服强度于母材等强度;冲击吸收功Akv值在-20℃时达到107J,在-40℃时达到80J;焊接接头弯曲后无裂纹或裂纹小于3mm.力学性能均符合Q550低合金高强度钢的要求.表明合理的焊接工艺、合适的焊接材料可以取消焊前预热.     

微弧氧化膜对7A52铝合金搅拌摩擦焊接头腐蚀不均匀性的影响

7A52铝合金搅拌摩擦焊接头焊核区由于发生动态再结晶，晶粒比较细小，组织呈现“洋葱环”分布，热力影响区的组织沿塑性流动方向分布，热影响区晶粒尺寸发生了明显的长大.接头组织不均匀导致不同区域的腐蚀行为不同. 结果表明，没有微弧氧化膜时，母材的致钝电流远小于焊核区及热(力)影响区，更容易钝化；当微弧氧化膜的厚度为50 μm，母材的致钝电流小于焊核区及热(力)影响区，较薄的微弧氧化膜对接头腐蚀不均匀性的改善作用不明显；当微弧氧化膜的厚度为70 μm时，接头不同区域钝化特征接近，微弧氧化膜有助于减小接头组织不均匀对接头不同区域的腐蚀不均匀的影响.     

7A52铝合金激光焊接头单级时效行为

通过力学性能、电导率测试、EDS分析和TEM分析,对7A52铝合金激光焊接头单级时效行为特征进行了研究,并确定了较为合理的单级时效工艺。结果表明,7A52铝合金激光焊焊缝和母材在不同温度下达到峰值硬度所需要的时间基本是一致的,当时效温度由120上升到160℃时,接头时效硬化速度明显加快,达到峰时效时间明显缩短。与120℃时的峰时效状态相比,经140℃,16h时效处理后的接头抗拉强度为351 MPa,失重量为0.0070g/min,电导率为21.2mS/m,接头抗拉强度下降了1.13%,失重量增加了2.94%,电导率却提升了12.2%,综合考虑以140℃保温16h单级时效工艺为宜。焊缝和母材的析出相均是相,随时效时间的延长析出相逐渐增多粗化,且峰时效状态下的起主要强化作用的是η′相和GP区。     

超声冲击处理冷轧钢板缝焊接头的疲劳性能

用窄搭接电阻缝焊机对汽车用SPCC（冷轧低碳普通钢板）进行焊接,采用超声冲击仪对缝焊接头进行处理;通过拉压疲劳试验、X射线应力分析仪、OM、SEM对处理和未处理的缝焊接头疲劳性能和组织进行测试和观察分析对比.结果表明,未经超声冲击处理的缝焊接头经5×104次交变载荷作用即在焊趾区萌生裂纹,裂纹与载荷方向呈45°;经超声冲击处理过的缝焊接头经1.88×106次交变载荷作用未发生断裂;超声冲击处理使缝焊接头表层晶粒细化并形成塑性变形层,降低了其表面的微裂纹缺陷造成的应力集中,使表面残余拉应力变为了压应力,有利于改善缝焊接头的疲劳性能.     

Microstructure and mechanical properties of dissimilar steel plate resistance plug welding joints

A new type of hybrid welding method called resistance plug welding (RPW) was firstly adopted to achieve the connecting of dissimilar steel,mainly as for the poor welding characteristics of high strength steel produced by increasing carbon,manganese,silicon,etc.Microstructures and mechanical properties of RPW joint were analyzed by optical microscope,micro-hardness test and shear tensile measurement.Experimental results indicate that the RPW joint has a rounded rectangle nugget,and the size is larger than elliptical nugget of resistance spot welding (RSW) joint;the hardness value of RPW joint is evenly distributed,accordingly there is no hard brittle phases;the shear tensile strength of RPW joint increases by 20％ in comparison with RSW joint under the same welding conditions.     

7A52铝合金双丝MIG焊接温度场数值模拟

采用ANSYS的"生死"单元技术,对7A52铝合金双丝MIG焊接的热过程进行数值模拟。实现多层焊中焊缝填充的动态过程,与真实试验过程完全吻合。结果表明,7A52铝合金双丝MIG焊接过程中,焊点处的峰值温度可达到837℃。     

中间层铜对铝/钢电阻点焊接头性能的影响

研究中间加厚度为50μm的铜箔对6061-T6铝合金与TRIP980高强钢异种金属电阻点焊组织与性能的影响。结果表明:采用厚度为50μm铜中间层,点焊接头主要由两部分组成,分别为熔核区与界面区,实质为熔-钎焊特征。当预热电流为8kA、预热时间为20cycle、焊接电流为16kA、焊接时间为15cycle、电极压力2.7kN时,接头拉伸力达到最大值为4.32kN,为纽扣断裂,较之未加铜片拉伸力提高约14%,且塑韧性提高。     

7075铝合金的研究现状

7075铝合金具有强度高、韧性好的特点,是应用前景较佳的轻质高强结构材料。在查阅大量文献的基础上,结合近年来开展的研究工作,介绍了国内外7075铝合金的发展应用概况,重点讨论了该合金的焊接工艺,还介绍了合金的3种主要时效处理工艺和析出方式,并针对7075铝合金目前存在的问题,提出了今后研究开发的方向。