51.
碳化La2O3—Mo阴极材料的高温XPS研究 总被引:6,自引:0,他引:6
采用高温X射线光电子能谱(XPS)对碳化La2O3-Mo阴极材料表面La的价成进行了研究。结果表明,材料中的La2O3可以被Mo2C还原成单质La。单质La的结合能高于La2O3的结合能。从实验上证实单质La3d5/2的结合能为835.96eV,并首次给出单质La3d3/2结合能实验数值为852.23eV。 相似文献
52.
53.
Chemical stability of La_2O_3 in La_2O_3-Mo cathode materials 总被引:1,自引:0,他引:1
1 INTRODUCTIONThO2 Wthermioniccathodesarestillwidelyusedinhigh powervacuumtubesforindustrialheat ing .ItiswellknownthattheradioactivityofThO2leadsproblemstoitsmanufactureandapplication .La2 O3 Mo ,oneoftheattractivealternatives,wasin ventedinthemidstof 1970s[1~ … 相似文献
54.
1 INTRODUCTIONAsoneofthealternativesofThO2 Wcathode ,La2 O3 Mothermioniccathode (La Mo)appearedinrecent 30 years[1~ 4 ] .Althoughthiscathodehasgoodemissivity ,ithasnotbeenusedcommerciallybecauseofitspooremissionstability[5~ 8] .Themicrostructurestudyonthiscathodesho… 相似文献
55.
56.
通过添加碳纳米管共沉淀的方法制备了Fe3O4-CNTs复合材料。研究发现,CNTs不仅可以降低复合材料作为锂离子电池负极的阻抗,而且对活性物质Fe3O4起到很好的支撑作用,极大地提高了Fe3O4在充放电过程中的电化学稳定性。在0.5 A/g的电流密度下Fe3O4-CNTs循环200圈后的放电比容量保持在1406 mAh/g。在10 A/g的大电流密度下循环,第100圈时Fe3O4-CNTs的放电比容量稳定在230 mAh/g左右。循环至第9999圈时,Fe3O4-CNTs的比容量下降至179 mAh/g,只损失了50 mAh/g,充放电效率高达99.98%。Fe3O4-CNTs复合材料在大电流密度超长循环的背景下表现出优异的性能,对负极材料的开发有重要的意义。 相似文献
57.
The substrate molybdenum doped with La2O3, Y2O3 cathode material was made by the powder metallurgy method. The secondary emission coefficients of the materials were tested. The experimental results show that Mo cathodes doped with La2O3, Y2O3 have good secondary emission properties. When the cathodes are activated, the maximal secondary emission coefficients of these cathodes are higher than 2.0 and can meet the practical requirement. The distribution of the rare earth in the interior and at surface of this kind of cathode material before and after emission was studied using Scanning Electronic Microscopic (SEM) and X-Ray Photoelectron Spectrum(XPS). The analysis results show that the rare earth is easy to gather at grain boundaries and the relevant concentration of rare earth on the surface after emission is obviously greater than that before emission. 相似文献
58.
Sm-Co基整体辐向永磁环的制备及性能 总被引:1,自引:0,他引:1
Sm-Co基整体辐向永磁环由于成型困难及烧结时易于变形和开裂等原因,限制了其应用和发展。为此,本文对Sm(Co,Fe,Cu,Zr):整体辐向永磁环的烧结制备工艺,以及烧结和时效处理对磁体性能、组织结构的影响进行了研究。结果表明:调整合适的烧结工艺,能有效地抑制永磁环缺陷的产生,改善磁体的性能:在1220℃下烧结70min时磁体的性能较好,Br≥1.08T,Hcj≥2200kA/m,(BH)max≥214kJ/m^3;烧结磁体的矫顽力主要与时效工艺有关,时效前磁体主要是2:17型相的过饱和固溶体,在时效过程中析出1:5型相,并逐步形成胞状的显微组织结构,磁体的内禀矫顽力Hcj明显增加,在850℃时效8h,磁体的Hcj可达到2200kA/m以上。如果在850℃时效时间过长,胞状组织会被破坏,磁性能开始恶化。 相似文献
59.
Mo-Y_2O_3阴极发射机理研究 总被引:2,自引:1,他引:2
采用热重分析、X射线衍射、扫描电镜及光电子能谱等方法对Mo Y2 O3阴极中钇的价态进行了研究 ,探讨了该阴极的发射机理。Y2 O3与Mo2 C在 1173K以上发生化学反应。Y2 O3与Mo2 C混合物经 1873K高温处理后 ,产物中含有两种价态的Y :Y0 和化合态的Y3 。Mo Y2 O3阴极的发射可用原子膜机理解释 ;在阴极工作过程中 ,Mo2 C将Y2 O3还原成单质钇 ,钇覆盖在钼基体表面 ,降低了基体钼的逸出功 ,促进了阴极的发射。 相似文献