装配式中空凸轮轴凸轮材料及装配技术研究

研究了装配式中空凸轮轴的两个关键技术:凸轮材料和连接技术.本试验凸轮材料采用铁基粉末冶金材料,并对其工作表面进行宽带激光表面淬火处理.研究结果表明,经激光处理后,材料的耐磨性得到了明显的提高.凸轮与芯轴的连接采用滚花连接技术,对不同齿距的滚花式凸轮轴静连接强度及疲劳强度进行了实验研究.研究结果表明,制成的凸轮轴在静扭时的破坏扭矩约是凸轮轴实际工作扭矩的20～30倍,疲劳破坏方面亦符合工作要求.     

Effect of graphite particle size on wear property of graphite and Al_2O_3 reinforced AZ91D-0.8%Ce composites

The graphite particles and Al_2O_3 short fibers reinforced AZ91D-0.8%Ce composites were fabricated by squeeze-infiltration technique.The researches about the effects of different graphite particle sizes on the microstructure and wear property of the composites were performed under the condition of constant contents of graphite particles and Al_2O_3 short fibers.The results reveal that the grain size of the composites changes less when the graphite particle size descends.Moreover,Ce enriches around the gr...     

Morphological evolutions of cast and melt-spun Mg_(97)Zn_1Y_2 alloys during deformation and heat-treating

Mg_(97)Zn_1Y_2 alloy has been studied as an elevated temperature creep resistant Mg-based alloy for nearly ten years.While, the strength of the cast Mg_(97)Zn_1Y_2 alloy with long-period stacking(LPS) structure is lower than that of the commercial AZ91 alloy at room temperature.The microstructure evolutions in Mg_(97)Zn_1Y_2(molar fraction,%) alloys with LPS phase,processed by rolling and annealing the as-cast alloy and rapidly solidifying/melt-spinning and age treating at different temperatures respecti...     

粉末冶金高温金属基固体自润滑材料

对粉末冶金高温金属基固体自润滑材料的研制开发与应用情况进行了综合论述,系统介绍了固体润滑剂特征以及粉末冶金高温金属基自润滑材料的高温摩擦学特性。     

Microstructure and mechanical properties of Mg-6Al-0.3Mn-xY alloys prepared by casting and hot rolling

Mg-6Al-0.3Mn-xY(x=0,0.3,0.6 and 0.9,mass fraction,%) magnesium alloys were prepared by casting and hot rolling process.The influence of yttrium on microstructure and tensile mechanical properties of the AM60 magnesium alloy was investigated.The results reveal that with increasing the yttrium content,Al2Y precipitates form and the grain size is reduced.The ultimate strength,yield strength and elongation at room temperature are 192 MPa,62 MPa and 12.6%,respectively,for the as-cast Mg-6Al-0.3Mn-0.9Y alloy.All ...     

激光快速重熔对铸造共晶铝合金组织及性能的影响

本文对含稀土铸造共晶铝合金(ZL108)激光重熔组织进行了变时及变温时效处理,与固溶加时效样品相比,激光重熔组织的显微硬度峰值,在HV—H曲线上后移两小时,在HV—T曲线上后移20℃。激光重熔组织比固溶加时效组织具有较好的耐磨性。该两种工艺样品的磨损量随时效时间及时效温度的变化规律与显微硬度随时效时间及时效温度的变化规律完全一致。激光重熔组织细且耐时效,铝枝晶沿 <100> 晶向生长,θ′相沿{100}晶面析出,该θ′相可使显微硬度和耐磨性得到提高。     

合金元素Cr对粉末冶金凸轮材料摩擦学特性的影响

研究了不同Cr含量对3种状态下(烧结态、高频淬火和激光表面淬火)的粉末冶金凸轮材料的密度、硬度以及摩擦磨损特性的影响.研究结果表明,不同Cr含量的铁基粉末冶金凸轮材料经高频淬火和激光表面淬火后,材料的表面硬度和耐磨性得到了明显的提高,激光表面淬火比高频淬火提高得更多;随着Cr含量的增加,硬化层的硬度和深度都有所增加;随着Cr含量的增加,凸轮材料的磨损率和摩擦系数曲线均表现为先降后升,含Cr量1.0%(质量分数)处为最低点;随着Cr含量的增加,材料由马氏体 下贝氏体的复相组织逐渐变为单相马氏体组织,具有强韧性搭配的复相组织在较高载荷下表现出更好的耐磨性.     

低碳钢在铝合金熔体中冲蚀磨损的研究

重点研究了在搅拌铸造过程中低碳钢搅拌桨在铝合金 熔体中的冲蚀磨损随时间和转速的变化规律和机理.结果表明：搅拌桨的冲蚀磨损速度随搅拌时间和搅拌速度的增加而增加，但随搅拌时间的增加有一孕育期，低于孕育期，冲蚀磨损速度很小.该孕育期随搅拌速度的增加而减小，并且在转速超过1000 r/min以上，加速减小.搅拌桨在铝合金熔体的冲蚀磨损过程是一个表面净化，铝原子扩散，化合物的形成和剥离过程，冲蚀磨损速度主要与氧化物的生成速度和氧化物的剥离速度有关.旋转速度的变化主要影响化合物的剥离速度.     

电厂飞灰颗粒增强铝基复合材料的摩擦磨损行为

对挤压铸造制成的飞灰颗粒增强ZL109复合材料在不同条件下的的摩擦磨损行为进行了研究。结果表明：飞灰颗粒的加入可提高铝合金材料的耐磨性,复合材料同基体合金相比,摩擦因数也较低。在摩擦磨损过程中,在较低载荷下复合材料的摩擦表面形成一稳定的摩擦转移层,该转移层的存在可以起到降低摩擦因数的作用。在较高载荷下由于该摩擦转移层遭到破坏,从而影响了其减摩作用的发挥。镶嵌在基体中的飞灰颗粒在摩擦过程中主要起到承受载荷、限制对磨材料与铝基体直接接触的作用。脱落的飞灰颗粒可以起到“滚珠”的作用,在摩擦表面形成“三体”摩擦,从而起到减摩的作用。