Inhibition of char deposition using a particle bed in heating section of supercritical water gasification

Supercritical water gasification (SCWG) has attracted attention as a technology for utilizing wet biomass. We used a fluidized bed of alumina particles to prevent blockage of a SCWG reactor. A glucose solution was heated in the reactor with and without fluidized alumina particles. In the absence of alumina particles, char particles formed homogeneously in the reactor, but the use of a fluidized bed resulted in accumulation of char particles at the reactor’s exit rather than inside the reactor. Therefore, the fluidized bed was effective at preventing blockage of the reactor. However, the alumina particles did not remove deposits from the reactor’s walls. Instead, the fluidized bed caused larger char particles to form, preventing their adhesion to the reactor’s wall.     

Reactive processing of thermoset/thermoplastic blends: A potential for injection molding

Poly(2,6-dimethyl-1,4-phenylene ether) (PPE) is an engineering plastic with high heat distortion temperature. Melt processing of neat PPE is usually accompanied with thermal degradation. The degradation problem is solved by blending with polystyrene to reduce the processing temperature. We propose an alternative using triallylisocyanurate (TAIC). TAIC is a low viscosity liquid that can be cured by peroxide, e.g. α,α′-bis(t-butylperoxy-m-isopropyl)benzene (PBP), to provide a thermoset. The PPE/TAIC mixture was shown to have the upper critical solution temperature (UCST) type phase behavior. At the single-phase regime above UCST and below the cure temperature (∼180°C for PBP), the mixture had a low viscosity, less viscous than a conventional thermoplastic such as PC and PP. That is, a nice window for injection molding was available, e.g., at 100°C to 160°C for a 50/50 blend. After injecting into a hot mold set at cure temperature, the blend cured in a short time (∼80% conversion in 5 min). Then the molded and partly cured material kept its shape and dimensions during post-cure in a hot chamber at higher temperature (e.g. 250°C). Using transmission electron microscopy and dynamic mechanical analyses, it was shown that the cured blend had a bicontinuous two-phase structure with periodic spacings of ∼30 nm, suggesting a structure formation via a spinodal decomposition driven by the increase in molecular weight of TAIC during cure. The cured material showed excellent flexural strength and high chemical resistance.     

Steam Reforming of Methanol on Copper Catalysts Supported on Large-Surface-Area ZnAl2O3

Steam reforming of methanol on various supported Cu catalysts was examined. Supports strongly affected catalyst activity and, among the catalysts tested, Cu catalyst supported on large-surface-area ZnAl₂O₄ showed the highest activity, which, to the best of our knowledge, was higher than those for the supported catalysts reported so far. For supported Cu catalysts, two species were observed. One was a dispersed Cu species having strong interaction between Cu and support, and the other was an isolated Cu species. The activity of the former species strongly depended on supports.     

PMMA-SiO2杂化材料对天然橡胶的增强作用

提取了活性硅烷醇,用自由基共聚合法成了含硅高聚物,分析了SiO2含量对硫化天然橡胶力学性能的影响。     

Formation and thermal stability of new Zr–Cu-based bulk glassy alloys with unusual glass-forming ability

The simultaneous addition of Al and Ag to Zr–Cu binary alloys increased in the stabilization of supercooled liquid, the reduced glass transition temperature and γ value, leading to greatly enhance the glass-forming ability (GFA). The Zr–Cu–Ag–Al glassy alloy samples with diameters above 15 mm were obtained in the wide composition range of 42–50 at% Zr, 32–42 at% Cu, 5–10 at% Ag, and 5–12 at% Al. The best GFA was obtained for Zr₄₈Cu₃₆Ag₈Al₈ alloy, and the glassy samples with diameters up to 25 mm were fabricated by an injection copper mold casting. The Zr₄₈Cu₃₆Ag₈Al₈ glassy alloy exhibited high tensile and compressive fracture strength of over 1800 MPa.     

Synthesis of CeO2-ZrO2 solid solution by glycothermal method and its oxygen release capacity

The glycothermal (GT) reaction of Ce acetate and Zr alkoxide directly yielded CeO₂-ZrO₂ solid solutions in a region of low Ce content ≤40 mol%. Of the CeO₂-ZrO₂ solid solutions obtained by the GT method and subsequent calcination at 500 or 800 °C, the sample with 20 mol% Ce content had the largest BET surface area. This sample exhibited the highest Ce-based oxygen release capacity in the whole Ce/Zr composition range. The oxygen release capacities of CeO₂-ZrO₂ solid solutions synthesized by the GT method were much larger than those of the samples prepared by a coprecipitation (CP) method. The Reitveld analysis and the repetitive reduction-oxidation experiment indicated that the CeO₂-ZrO₂ solid solution synthesized by the GT method has a homogeneous structure as compared with that prepared by the CP method.     

Surface and pore structure of alumina derived from xerogel/aerogel

The alkyl derivatives of boehmite were prepared by solvothermal reaction of aluminum isopropoxide in n-alcohols (ethanol, 1-butanol, 1-hexanol, 1-octanol and 1-dodecanol) and the products were recovered as aerogel/xerogel by the removal of the solvent at the end of reaction. Aerogel or xerogel can be obtained simply by using only a reaction vessel (autoclave) and the obtained products were composed of plate-like particles having a well-developed boehmite structure. The alumina powders obtained by calcination of these products had relatively large pore-volumes ranging from 1.35 to 2.56 cm³/g. Transformation into α-Al₂O₃ was retarded even after calcination at 1200 °C. The effect of n-alcohols used in the solvothermal reaction on the phase, morphology and pore-texture of the alumina samples are discussed.     

Waveguide polarization-independent optical circulator

We fabricated a new type of waveguide polarization-independent optical circulator which does not need a polarization-beam splitter. The circulator is based on a non-reciprocal Mach-Zehnder interferometer which consists of two waveguide Faraday rotators, two thin-film half-waveplates and two planar lightwave circuit-type 3-dB couplers. The fabricated circulator provides a 14.0-23.7-dB isolation and a 3.0-3.3 dB insertion loss at λ=1.55 μm. This circulator presents a new possibility for developing non-reciprocal devices in the field of integrated optics     

Removal of fluoride from aqueous solution onto Zr-loaded garlic peel （Zr-GP） particles

Garlic peel, as the raw material, was modified by loading with zirconium(IV), exhibiting quite good uptaking behaviour for fluoride anion. The adsorption experiments were carried out in batch shaking vessels, and the process was strongly dependent on the pH value. The adsorption fits Langmuir model well, and the maximum adsorption capacities at equilibrium pH 2 and 6 are evaluated to be 1.10 and 0.89 mol(fluoride)/kg of Zr-loaded garlic peel gel, respectively. The evaluation of effects of coexisting anions such as nitrate, sulfate and phosphate shows that nitrate and sulfate have no negative effect on the adsorption of fluoride, while phosphate has a little effect. Adsorption kinetics of fluoride is well described by pseudo-second-order rate equation, and the corresponding adsorption rate constant is calculated to be 3.25×10⁻³ g/(mg·min).     

Synthesis, structure and mechanical properties of Zr-Cu-based bulk metallic glass composites

The unusual glass-forming ability(GFA) of the Zr_(48)Cu_(36)Ag_8Al_8 alloy and the high ductility of the Zr_(48)Cu_(36)Ag_8Al_8 metallic glass-matrix composites containing Ta powder were reported.The bulk metallic glass rod with a diameter of 25 mm was successfully synthesized using copper mold casting for the Zr_(48)Cu_(36)Ag_8Al_8 alloy.High GFA of this alloy was found to be related to a large supercooled liquid region and a quaternary eutectic point with low melting temperature.The bulk metallic glass...