Effects of structural parameters on water film properties of transpiring wall reactor

Corrosion and salt deposition problems severely restrict the industrialization of supercritical water oxidation. Transpiring wall reactor can effectively weaken these two problems by a protective water film. In this work, methanol was selected as organic matter, and the influences of vital structural parameters on water film properties and organic matter removal were studied via numerical simulation. The results indicate that higher than 99% of methanol conversion could be obtained and hardly affected by transpiration water layer, transpiring wall porosity and inner diameter. Increasing layer and porosity reduced reactor center temperature, but inner diameter's influence was lower relatively. Water film temperature reduced but coverage rate raised as layer, porosity, and inner diameter increased. Notably, the whole reactor was in supercritical state and coverage rate was only approximately 85% in the case of one layer. Increasing reactor length affected slightly the volume of the upper supercritical zone but enlarged the subcritical zone.     

切向结构永磁同步电机磁钢径向并联组合研究

针对低速大转矩切向结构永磁同步电机中磁钢尺寸对性能的影响进行研究.提出一种"工"字形排布的磁钢径向并联组合优化方案.在保证电机磁钢轴向长度和体积不变前提下,分析磁钢磁化方向长度变化对电机性能的影响.分析表明:磁钢的磁化方向长度在一定范围内增加可降低磁钢漏磁、增大反电动势和降低转矩波动;但磁钢的磁化方向长度过度增加会大大降低电机磁通面积,使得电机反电动势不增反降.在此基础上,提出一种降低磁钢漏磁、增大反电动势和降低转矩波动的三块磁钢径向并联组合的"工"字形排布方案:近气隙侧和近隔磁槽侧磁钢槽内分别插入磁化方向长度短、径向宽度窄的磁钢以降低近气隙侧和近隔磁套侧磁钢漏磁;近气隙侧磁钢和近隔磁槽侧磁钢之间采用磁化方向长度较短的磁钢以保证磁钢磁通面积降低得不多.通过仿真实验验证所提方案的可行性.     

Evaluation of bismuth doped La2-xBixNiO4+δ (x = 0, 0.02 and 0.04) as cathode materials for solid oxide fuel cells

Bismuth doped La_2-xBi_xNiO_4+δ (x = 0, 0.02 and 0.04) oxides are investigated as SOFC cathodes. The effects of Bi doping on the phase structure, thermal expansion, electrical conduction behavior as well as electrochemical performance are studied. All the samples exist as a tetragonal Ruddlesden-Popper structure. Bi-doped LBNO-0.02 and LBNO-0.04 have good chemical and thermal compatibility with LSGM electrolyte. The average TEC over 20–900°С was 13.4 × 10^?6 and 14.2 × 10^?6 K^?1 for LBNO-0.02 and LBNO-0.04, respectively. The electrical conductivity was decreasing with the rise of Bi doping content. EIS measurement indicates Bi doping can decrease the ASR values. At 750 °C, the obtained ASR for LBNO-0.04 is 0.18 Ωcm², which is 56% lower than that of the sample without Bi doping, suggesting Bi doping is beneficial to the electrochemical catalytic activity of LBNO cathodes.     

P-doped CoSe2 nanoparticles embedded in 3D honeycomb-like carbon network for long cycle-life Na-ion batteries

We report for the first time a Na-ion battery anode material composed of P-doped CoSe2 nanoparticles(P-CoSe2)with the size of 5-20 nm that are uniformly embed in a 3D porous honeycomb-like carbon network.High rate capability and cycling stability are achieved simultaneously.The honeycomb-like carbon network is rationally designed to support high electrical conductivity,rapid Na-ion diffusion as well as the accommodation of the volume expansion from the active P-CoSe2 nanoparticles.In particular,heteroatom P-doping within CoSe2 introduces stronger P-Co bonds and additional P-Se bonds that signif-icantly improve the structure stability of P-CoSe2 for highly stable sodiation/desodiation over long-term cycling.P-doping also improves the electrical conductivity of the CoSe2 nanoparticles,leading to highly elevated electrochemical kinetics to deliver high specific capacities at high current densities.Benefiting from the unique nanostructure and atomic-level P-doping,the P-CoSe2(2∶1)/C anode delivers an excel-lent cycle stability with a specific capacity of 206.9 mA h g-1 achieved at 2000 mA g-1 after 1000 cycles.In addition,this material can be synthesized using a facile pyrolysis and selenization/phosphorization approach.This study provides new opportunities of heteroatom doping as an effective method to improve the cycling stability of Na-ion anode materials.     

Crystallographic characteristics and microwave dielectric properties of Ni-modified MgTa2O6 ceramics

Ni²⁺ modified MgTa₂O₆ ceramics with a trirutile phase and space group P4₂/mnm were obtained. The correlations between crystallographic characteristics and microwave dielectric performance of MgTa₂O₆ ceramics were systematically studied based on the chemistry bond theory (PVL theory) for the first time. The results indicate that the introduction of Ni²⁺ causes a change in polarizability and the Mg–O bond ionicity, which contributes to the variation of dielectric constant. Moreover, the lattice energy, and packing fraction, full width at half maximum of the Raman peak of Ta–O bond, as the quantitative characterization of crystallographic parameters, regulate the dielectric loss of MgTa₂O₆ ceramics in GHz frequency band. In addition, the study of sintering behavior shows that the densification and micromorphology are the crucial factors affecting the microwave dielectric performance. Typically, Ni²⁺ doping on the A-site of MgTa₂O₆ can effectively promote the Q × f values to 173,000 GHz (at 7.43 GHz), which ensures its applicability in 5G communication technology.     

Investigation of crystal characteristics,Raman spectra,and microwave dielectric properties of Mg1-xZnxTa2O6 ceramics

Mg_(1-x)Zn_xTa₂O₆ (x = 0.00?0.08) dielectric ceramics were synthesized via the traditional solid-state reaction method. We used XRD and Rietveld refinement to demonstrate that a pure Mg_(1-x)Zn_xTa₂O₆ phase with trirutile structure was formed. Zn²⁺ substitution helped to decrease the Raman full width at half width of the A_1g mode at 703 cm^?1, which resulted in an increase in the order and rigidity of the TaO₆ octahedron, this in turn contributed to improving the Q×f values. Additionally, the introduction of Zn²⁺ significantly promoted grain growth and increased the dense, and the molecular polarizability, these factors lead to a higher permittivity. Moreover, enhanced Ta-O bond energy resulted in a more stable TaO₆ octahedron in the Mg_(1?x)Zn_xTa₂O₆ system, which contributed to enhanced τ_f values via substitution of Zn²⁺ doped on the A-site. Correspondingly, the microwave dielectric properties were significantly improved for 0.04-doped samples, obtaining: ε_r = 27, Q × f = 185,000 GHz (at 7.47 GHz), τ_f =32 ppm/°C.     

Structural,optical and electrical properties of indium doped Cu2ZnSn(S,Se)4 thin films synthesized by the DC and RF reactive magnetron cosputtering

Element doping into the Cu₂ZnSn(S,Se)₄ (CZTSSe) absorber is an effective method to optimize the performance of thin film solar cells. In this study, the Cu₂In_xZn_1-xSn(S,Se)₄ (CIZTSSe) precursor film was deposited by magnetron cosputtering technique using indium (In) and quaternary Cu₂ZnSnS₄ (CZTS) as targets. Meanwhile, the In content was controlled using the direct current (DC) power on In target (P_In). A single kesterite CIZTSSe alloy was formed by successfully doping a small number of In³⁺ into the main lattice of CZTSSe. The partial Zn²⁺ cations were substituted by In³⁺ ions, resulting in improving properties of CZTSSe films. Morphological analysis showed that large grain CIZTSSe films could be obtained by doping In. The well-distributed, smooth, and dense film was obtained when the P_In was 30 W. The band gap of CIZTSSe could be continuously adjusted from 1.27 to 1.05 eV as P_In increased from 0 to 40 W. In addition, the CIZTSSe alloy thin film at P_In = 30 W exhibited the best p-type conductivity with Hall mobility of 6.87 cm²V^?1s^?1, which is a potential material as the absorption layer of high-performance solar cells.     

Toughness enhancement and equivalent initial fracture toughness of cementitious composite reinforced with aligned steel fibres

Based on theoretical analysis and numerical simulation, the impact of steel fibres on the stress intensity factor (SIF) at the crack tip for cementitious composite was studied. The enhanced toughness of steel fibre reinforced cementitious composite (SFRC) in resisting cracks was explained by the decrement of SIF caused by steel fibre inclusions at the crack tip of the composite. The equivalent initial fracture toughness was used to characterize the crack initiation of SFRC. A simplified method for determining the of SFRC was proposed based on a linear regression method. Fracture tests were conducted on three‐point bending notched beams with different steel fibre volume fractions and specimen sizes to study the crack initiation behaviour of aligned steel fibre reinforced cementitious composite (ASFRC). of ASFRC was calculated, and the size effect of was analysed. The results showed that slightly increased with the steel fibre volume fraction and gradually became stable. For the tested specimens, whose heights varied between 40 and 100 mm, the specimen size had little impact on the .