Influence of buried structure on polarization sensitivity instrained bulk semiconductor optical amplifiers

In order to achieve an accurate design of polarization-insensitive semiconductor optical amplifiers based on tensile strained bulk InGaAsP, the reduction of strain in the active layer of the buried heterostructure and its influence on polarization sensitivity are analyzed numerically for the first time. The gain calculation, including the strain distribution in the active layer, is examined based on the k · p method for the different active layers. It is found that the strain introduced during the epitaxial growth is strongly reduced after regrowth of the burying layer. In an active layer having the aspect ratio of 1 : 4, the strain reduction causes more than a 0.5-dB deviation in the polarization sensitivity of the gain. From a comparison with the experimental results, it is shown that including the effect of the burying layer in the calculation gives an accurate determination of the amount of strain for the polarization independence     

High performance 35 nm gate length CMOS with NO oxynitride gate dielectric and Ni salicide

The 35 nm gate length CMOS devices with oxynitride gate dielectric and Ni salicide have been fabricated to study the feasibility of higher performance operation. Nitrogen concentration in gate oxynitride was optimized to reduce gate current I/sub g/ and to prevent boron penetration in the pFET. The thermal budget in the middle of the line (MOL) process was reduced enough to realize shallower junction depth in the S/D extension regions and to suppress gate poly-Si depletion. Finally, the current drives of 676 /spl mu/A//spl mu/m in nFET and 272 /spl mu/A//spl mu/m in pFET at V/sub dd/=0.85 V (at I/sub off/=100 nA//spl mu/m) were achieved and they are the best values for 35 nm gate length CMOS reported to date.     

Simulation study of eutrophication in Hiroshima Bay: Simulation of particulate and dissolved organic matter using cyclic transformation of carbon

A phytoplankton model, which includes a carbon cycle combined with a constant current obtained by the computation of tidal currents, was applied to the coastal region (Hiroshima Bay, Japan). The transformation rate constants for the carbon cycle were experimentally evaluated.The seasonal variations of particulate and dissolved organic matter by the simulation model were reasonably consistent with the field data. Carbon concentration increased by primary production in the upper layer was approx. 10 times that augmented by loading of carbon from land at the shore in summer. Sinking plays an important role in the elimination of particulate organic matter. On the other hand, horizontal advection and turbulent diffusion are important factors for the diminution of dissolved organic matter.     

Murine coronavirus-induced subacute fatal peritonitis in C57BL/6 mice deficient in gamma interferon

Gamma interferon-deficient (IFN-gamma-/-) mice with a C57BL/6 background were infected intraperitoneally with mouse hepatitis virus strain JHM (JHMV). In contrast to IFN-gamma-+/- and IFN-gamma+/+ mice, JHMV persisted in IFN-gamma-/- mice and induced death during the subacute phase of the infection. Unexpectedly, infected IFN-gamma-/- mice showed severe peritonitis accompanying the accumulation of a viscous fluid in the abdominal and thoracic cavities in the subacute phase. Destructive changes of hepatocytes were not observed. Administration of recombinant IFN-gamma protracted the survival time of IFN-gamma-/- mice after JHMV infection. These results demonstrate that IFN-gamma plays a critical role in viral clearance in JHMV infection. They also show that a resultant persistent JHMV infection induces another form of disease in IFN-gamma-/- mice, which bears a resemblance to feline infectious peritonitis in cats.     

Humidity Sensor Characteristics of Woodceramics

The humidity sensor characteristics of Woodceramics were investigated. The Woodceramics used in this experiment were prepared at 650–900°C. The size of specimens selected was 1 × 1 × 10 mm . One was used as-cut and the other was polished. Above 700°C, the resistance of the specimen was below 50 and the decrease of resistance with increasing relative humidity was small. The specimen prepared at 650°C had a resistance of about 1 k. The resistance of as-cut specimens decreased with increase in relative humidity, but that of the polished specimen did not change significantly. The difference between as-cut and polished samples was explained by the differences in surface micro-structure.     

Studies on sublimation of disperse dye out of dyed polymers. I. Rate of sublimation and amorphous transition points of poly(ethylene terephthalate)

Four samples of poly(ethylene terephthalate) film of various crystallinities and orientation were dyed with p-nitroaniline and disperse dyes. When these films were heated under a 2–3 × 10^?3 mm Hg vacuum at a specified temperature T, the dye sublimed out of the dyed specimen. The amount (M_t/M_∞) of sublimed dye is in linear proportion to the square root of the sublimation time, t^½, where M_t and M_∞ are the amounts of dye sublimed for times t and t = ∞. The diffusion coefficient D, calculated from the slope of the above plot, is independent of the dye concentration of the film. When log D is plotted against 1/T°K over the temperature range 320–520°K, the relation is composed of two to four intersecting lines with the slope decreasing with elevation of temperature and with the breaks at about 89°–98°, 122°–135°, 155° and 175°–176°C. These breaks are the amorphous transitions: the first is the glass transition temperature T_g, the second and the fourth are the amorphous transitions corresponding to the crystalline transition points, i.e., the cold crystallization temperature and the smectic–triclinic transition temperature. With some exceptions, these amorphous transitions are found also by dilatometry and electrical conductivity measurements. The apparent activation energy for diffusion decreases from about 100 kcal/mole for the glass state to 22–24 kcal/mole for the region above 180°C. The activation energy for each region changes slightly with the size of dye molecule and the crystallinity and orientation of the film.     

Biocomposites Made from Short Abaca Fiber and Biodegradable Polyesters

Natural fiber‐reinforced biodegradable polyester composites were prepared from biodegradable polyesters and surface‐untreated or ‐treated abaca fibers (length ca. 5 mm) by melt mixing and subsequent injection molding. Poly(butylene succinate)(PBS), polyestercarbonate (PEC)/poly(lactic acid)(PLA) blend, and PLA were used as biodegradable polyesters. Esterifications using acetic anhydride and butyric anhydride, alkali treatment, and cyanoethylation were performed as surface treatments on the fiber. The flexural moduli of all the fiber‐reinforced composites increased with fiber content. The effect of the surface treatment on the flexural modulus of the fiber‐reinforced composites was not so pronounced. The flexural strength of PBS composites increased with fiber content, and esterification of the fiber by butyric anhydride gave the best result. For the PEC/PLA composites, flexural strength increased slightly with increased fiber content (0–20 wt.‐%) in the case of using untreated fiber, while it increased considerably in the case of using the fiber esterified by butyric anhydride. For the PLA composite, flexural strength did not increase with the fiber reinforcement. The result of soil‐burial tests showed that the composites using untreated fiber have a higher weight loss than both the neat resin and the composites made using acetylated fiber.

Flexural modulus of PBS composites as a function of fiber content.     

Morphology,thermal, and mechanical properties of vinylester resin nanocomposites with various organo‐modified montmorillonites

New nanocomposites based on a vinylester resin (VER) and the organo‐montmorillonites (ODA‐M, BHL‐M, DEM‐M, BHLV‐M) modified with octadecylammonium, bis(2‐hydroxyethyl)lauryl ammonium, diethyl[2‐(methacryloyloxyl)ethyl]ammonium, and bis(2‐hydroxyethyl)lauryl(vinylbenzyl)‐ammonium chlorides, respectively, were prepared by dispersing the organoclays in VER, and subsequent crosslinking at finally 120°C. X‐ray diffraction studies and morphological studies using transmission electron microscopy revealed that exfoliation occurs for the VER/ODA‐M and BHL‐M composites, intercalation occurs for the VER/BHLV‐M composite, and neither intercalation nor exfoliation occur for the VER/DEM‐M and unmodified montmorillonite composites. On the whole, although the enhancement in flexural modulus was observed for the exfoliated ODA‐M and BHL‐M composites, the flexural strength was rather lowered. Dynamic viscoelastic measurement revealed that the ODA‐M, BHL‐M, and BHLV‐M nanocomposites have significantly higher storage modulus at the rubbery state than the other composites. Polym. Eng. Sci. 44:2041–2046, 2004. © 2004 Society of Plastics Engineers.     

Nonlinear effects on spin waves in3He-4He dilute solutions

Spin dynamics of³He-⁴He dilute solution have been studied in the collisionless regime by NMR methods. In cw NMR experiments, we observed spin waves in a magnetic field gradient. The frequency difference between the first mode and the others obeyed a two-thirds power law in the strength of the field gradient. By using a pulsed NMR method, nonlinear spin dynamics were studied. We observed the large amplitude spin waves after an rf pulse. The frequency of each spin-wave mode depended on the tipping angle. By using the parameter determined in the present experiment, the numerical calculated results based on Leggett-Rice theory are in good agreement with the results of the pulsed NMR experiments.