Effect of graphite content on wear property of graphite/Al_2O_3/Mg-9Al-1Zn-0.8Ce composites

Using squeeze-infiltration technique, Mg-9Al-1Zn-0.8Ce composite reinforced by graphite particles and Al2O3 short fibers was fabricated. The reinforcing phases combined closely with the matrix and no agglomeration was observed. The microstructure, hardness and wear property of the composites with the graphite content of 5%, 10%, 15% and 20% were investigated, respectively. The results reveal that Ce tends to enrich around the boundaries of graphite particles and Al2O3 short fibers, and forms Al3Ce phase. Wh...     

铸造及半固态成型镁-铝-锌合金在盐水中的腐蚀行为

通过光学显微镜、SEM和EDS等研究了不同成分铸造及半固态成型镁-铝-锌合金在盐水浸泡试验中的腐蚀行为。结果表明:当合金的锌含量(质量分数,下同)低于1%时,铸造试样的腐蚀速率高于其相应半固态成型试样的;当锌含量高于3%时,铸造试样的腐蚀只发生在表面,腐蚀速率低于其相应半固态成型试样的;腐蚀速率受合金锌含量及固相颗粒尺寸和数量的共同影响,合金锌元素含量越高,铸造试样的腐蚀速率越低;半固态成型试样的固相颗粒数量越多、尺寸越小,则腐蚀速率越高。     

钢/锌层状复合材料的力学性能与耗能行为

对复合铸造法制成的钢/锌层状复合材料在不同条件下的单向拉伸和低周疲劳实验进行了研究.结果表明:锌的加入使钢/锌复合材料的塑性得到提高,同时其强度与钢相比有所降低.在单向拉伸条件下,拉伸速度对钢/锌复合材料试样的应力-应变曲线影响不大.在±0.5%,±1.0%,±1.5%应变范围内,所对应的拉压应力随着循环次数的增多而增大,表明材料出现循环硬化行为,并且循环应变的提高使材料的循环硬化行为逐渐明显,进一步循环使拉压应力趋于稳定.     

16Mn/Zn抗震复合材料的单向拉伸与循环变形行为

采用复合铸造工艺将16Mn钢和工业纯锌制备出双金属层状抗震复合材料,并对其在不同条件下的单向拉伸性能和循环变形行为进行了研究.研究表明:在单向拉伸条件下,应变速率对复合材料试样的应力-应变曲线影响不大;在0.5%、1%、1.5%应变下所对应的拉压应力随循环次数的增多而增大,材料出现循环硬化行为,并且循环应变的提高使材料的循环硬化行为逐渐明显,进一步循环使拉压应力趋于稳定;16Mn钢/锌抗震复合材料试件具有滞回特性,使结构适应反复载荷作用下的内力和变形,起到减震的作用.     

半固态触变注射成形镁合金显微组织的评定

针对不同注射速度的半固态触变注射成形镁合金显微组织,并结合不同工艺条件下的固相率和抗拉强度,采用分形方法对其固相颗粒二维形态进行了评定。分析结果表明,采用分形描述可以为镁合金半固态组织中固相颗粒的分析提供一个定量方法,为研究半固态成型镁合金的工艺-组织-性能之间的关系提供了一个理想的定量分析参数。     

金属基抗震复合材料的研究现状与展望

研制开发具有抗震性能的金属基复合材料具有广阔的发展前景，对近几年来金属基抗震复合材料的最新进展进行了系统论述，提出了金属基抗震复合材料研究中存在的问题，并对金属基抗震复合材料的应用与发展前景进行了展望。     

Filling analysis for thixomolded process of AZ91D magnesium alloy

Mold filling in lately-developed Thixomolding process is a complex process, of which numerical simulation is necessary for development. Governing equations and numerical models are first given, and then the experiment and its filling simulation are carried out. The results demonstrate that the modeling temperature changes from 864 to 873 K when the barrel temperature is 873 K. The difference is primarily in the runner system, but nearly invariable in the part. Consequently, the slurry fills the cavity smoothly with low solid fraction, and the filling process finishes in 5 ms, the filling process completes successfully before solidification of the slurry, which has good agreement with the experiment. Through a snapshot of the filling process and defects tracking, drawbacks are displayed and confirmed in the experiment.     

触变注射成形Mg-9%Al-1%Zn合金组织特性和凝固行为

为了研究触变注射成形AZ91D合金中固相颗粒的形貌演变和液相的凝固行为,对该合金的组织和凝固行为进行了试验观察和理论分析。典型触变注射成形AZ91D合金由α-Mg和β-Mg17Al12两相构成,α-Mg相又可分为未熔固相和初生固相。未熔固相主要有形貌较为接近球状的固相、形貌不规则的固相、内部含有小液池的固相以及包裹液相的固相4种形貌。形貌不规则的固相被认为是球状固相和包裹液相的固相的中间发展形貌,内部含有小液池的固相可能是包裹液相的固相的初级形貌,包裹液相的固相则可能发生破裂形成不规则固相,最终发展成球状固相。球状固相被认为是最理想的也是最终的固相形貌。初生固相在液相合金中形核并长大,直至有不稳定长大行为发生为止,较为细小、圆整,主要受冷却速率的影响。Mg-Al合金二元相图的分析结果与试验观察到的组织相吻合。     

触变注射成形AZ91D的固溶和时效热处理

对触变注射成形AZ91D固溶和时效处理后的组织和硬度变化进行了研究.结果表明,固溶处理过程中,溶质扩散、溶解和固溶体熟化相继发生.而固溶体的硬度受固溶强化的影响,随固溶温度的升高而升高.时效处理过程中,β-Mg17Al12首先在α-Mg的晶界处非连续析出,随后在α-Mg晶内连续析出.受沉淀强化影响,α-Mg的硬度值随着时效时间的延长和时效温度的提高逐渐增大.     

TiB_2颗粒增强钛基复合材料抗氧化性能

采用粉末冶金法制备了TiB2/Ti颗粒增强钛基复合材料,研究了不同烧结温度(800、900、1000和1100℃)TiB2/Ti复合材料在600、700、800和900℃空气中的恒温氧化行为,分析了TiB2对钛基复合材料氧化动力学行为的影响,并对氧化层表面的相组成、形貌以及氧化层剖面的显微结构进行了分析。结果表明:该复合材料的氧化层表面的氧化产物主要为金红石型TiO2,此外还有Fe2O3、Al2O3和B2O3,未发现其它类型钛的氧化物;TiB2/Ti复合材料800℃恒温空气中氧化的氧化动力学曲线初始阶段氧化速度较快,随着氧化时间的延长,形成的氧化膜减慢了氧化的速度;随着增强体TiB2体积分数的增加和烧结温度的提高,复合材料的抗氧化性能提高,这主要是由于提高烧结温度和提高增强体TiB2的体积分数均有利于氧化层的致密度提高,从而提高了材料的抗氧化性能。