铕掺杂TiO2的制备及其可见光光催化性能研究

采用溶胶-凝胶法制备了不同铕(Eu)掺杂量的TiO₂纳米颗粒(Eu-TiO₂),利用透射电镜(TEM),X射线光电子能谱(XPS),X射线衍射(XRD)及紫外可见漫反射(UV-Vis DRS)等方法对Eu-TiO₂进行了物理特性的初步表征.结果表明:与未掺杂纳米TiO₂比较,Eu-TiO₂禁带宽度变窄,具有可见光光催化活性.在可见光下(λ≥420 nm)照射下,以光催化降解染料罗丹明B(Rhodamine B,RhB)为目标反应,探讨了Eu-TiO₂不同制备条件对RhB降解光催化活性的影响,优化得到制备高活性Eu-TiO₂最佳pH为3、掺杂比例(n_Eu/n_Ti)为0.05%、煅烧温度为500 ℃.研究了可见光照射下Eu-TiO₂降解RhB和无色有机小分子水杨酸(SA)光催化反应条件及降解特性,RhB的12 h深度氧化矿化率为60.2%,SA的8 h降解率达到100%.通过跟踪测定可见光下Eu-TiO₂光催化反应过程中氧化物种的变化,研究了可见光激发Eu-TiO₂光催化反应机理,表明其光催化反应主要涉及羟基自由基(·OH)历程.     

TiO2-SiO2二维大孔薄膜的制备及其光催化活性研究

本文采用改进的溶胶-凝胶法制备了具有锐钛矿晶型结构和较小晶粒尺寸的TiO₂-SiO₂溶胶,并以聚苯乙烯(PS)小球为模板,采用旋涂法制备了新型大孔TiO₂-SiO₂复合薄膜,探究了煅烧温度、不同硅钛比以及溶胶添加量对所制备的大孔薄膜形貌及光催化活性的影响,并考察了该薄膜真空活化前后(Ti³⁺掺杂后)在紫外及模拟太阳光下光催化降解有机污染物罗丹明B的活性。通过Raman、DRS、SEM、EPR等方法对薄膜进行表征,发现制备的复合薄膜具有高透明度、良好附着力及优异的光催化活性。     

掺硼纳米TiO2的制备及光催化性能研究

采用改进的Sol-gel方法,制备了单分散椭球形微孔结构的掺B纳米TiO₂光催化剂,并用TG-DTA、XRD、XPS、UV-Vis、TEM、BET等手段进行表征.以难生化降解的染料罗丹明B为目标降解物,采用HPLC检测,通过不同光照时间下染料降解率考察了产物的光催化活性.结果表明,改进的Sol-gel法制得的光催化剂具有明显的孔结构,而且比表面积大、孔径分布窄、粒径小、分散性好;适量B的掺杂能够有效促进TiO₂纳米粒子的光催化活性.最佳催化剂制备条件:B掺杂的摩尔分数为20%、450℃煅烧2 h,此时所制得的B-TiO₂光催化剂活性比纯TiO₂有显著提高.     

水热法制备掺杂铁离子的TiO2纳米粒子及其光催化反应研究

以TiCl⁴为前驱体,采用水热法制备了掺杂铁离子的TiO₂纳米粒子,利用XRD对不同条件下制备的产物进行了表征,探讨了反应温度、胶体溶液pH值和反应时间对水热反应的影响.考察了所制备的Fe³⁺-TiO₂纳米粒子光催化降解罗丹明B的催化性能,实验发现,制备的掺杂0.1%Fe³⁺-TiO₂纳米粒子与纯TiO₂相比,具有更好的催化活性.     

胶体碳球制备新型Sn/Se共掺杂TiO2及其光催化性能

TiO₂的光催化性能改性是水污染治理和光催化领域研究的重点方向。为了增强TiO₂的光催化性能,以胶体碳球为模板,采用水热-煅烧法首次制备了TiO₂空心球、硒掺杂二氧化钛(Se-TiO₂)空心球和锡/硒共掺杂二氧化钛(Sn/Se-TiO₂)空心球。同时,对Sn/Se-TiO₂空心球的形貌、结构以及元素组成进行了表征,并以罗丹明B为模拟污染物,评价了样品的光催化性能。结果表明：TiO₂为单一的锐钛矿相,Sn和Se成功地掺杂进入了TiO₂晶格中;Sn/Se共掺杂形成了缺陷能级,降低了禁带宽度和电子-空穴对的复合几率,提高了可见光的响应范围。当Se掺杂2.0%(物质的量分数,下同),Sn掺杂0.5%时,样品光催化性能最好,去除率为76.92%。同等条件下空心球的光催化去除率：TiO₂22,说明Sn/Se共掺杂T...     

低量La3+掺杂S-TiO2光催化剂的制备、表征及其光催化活性

采用溶胶-凝胶-浸渍法制备了La³⁺/S-TiO₂纳米光催化剂,通过XRD、BET、XPS、UV-Vis等手段进行了表征.以甲基橙溶液为光催化降解反应的模型化合物,考察了光催化剂的活性,探讨了低量La³⁺掺杂对TiO₂纳米粒子光催化活性的影响机制.实验结果表明:S改性TiO₂后明显提高了TiO₂纳米粒子的光催化活性,而La³⁺掺杂S-TiO₂后,进一步提高了TiO₂纳米粒子的光催化活性,La³⁺的最佳掺杂量(相对于TiO₂的质量分数)为0.369%;La³⁺/S-TiO₂(ω(La³⁺)=0.369%)为纳米光催化剂时,甲基橙的脱色率达到92.4%(光照120min);XRD和BET分析表明,低量La³⁺掺杂抑制了TiO₂由锐钛矿向金红石的转变,阻碍了TiO₂晶粒的生长,提高了TiO₂的比表面积;XPS分析表明,S、La³⁺掺杂可以导致粉体的表面羟基含量增加,掺杂S以S⁶⁺形式置换TiO₂晶格中的Ti⁴⁺;UV-Vis分析表明,光催化剂La³⁺/S-TiO₂比纯TiO₂具有较强的紫外光吸收性能.与纯TiO₂相比,La³⁺掺杂TiO₂纳米粒子光催化氧化活性的提高应归因于La³⁺掺杂增加了表面羟基含量,增大了比表面积,增强了样品表面的紫外光吸收能力.     

CeO2/TiO2复合纳米纤维的制备及光催化性能研究

采用静电纺丝技术和水热合成法制备了CeO₂/TiO₂复合纳米纤维. 利用X射线衍射(XRD)、拉曼光谱(Raman)、扫描电镜(SEM)、透射电镜(TEM)和比表面积测定(BET)等分析测试手段对样品的形貌及结构进行了表征, 并以罗丹明B的脱色降解为模式反应, 考察了样品的光催化性能. 结果表明: CeO₂纳米粒子均匀地生长在TiO₂纳米纤维表面, 形成了异质结构的CeO₂/TiO₂复合纳米纤维光催化材料. 通过改变碱源, 可以得到不同形貌的CeO₂. CeO₂的存在增加了TiO₂纳米纤维的比表面积, 有效地实现TiO₂光生电子和空穴的分离, 增强了体系的量子效率, 与纯TiO₂纳米纤维相比光催化活性明显提高. 初步探讨了异质结的形成机理.     

Li+掺杂纳米TiO2的制备及其光催化性能研究

采用溶胶-凝胶法和浸渍法制备了Li⁺掺杂纳米TiO₂光催化剂,并用XRD和TEM等技术进行了表征;用pH值漂移法测量了催化剂的零电位pH值(pHpzc).结果表明,500℃煅烧制得的催化剂均为锐钛矿相;Li⁺的掺杂抑制了TiO₂粒子的生长,提高了催化剂的分散性;催化剂的零电位pH值为6.6—8.1,其值取决于Li⁺的浓度和掺杂方式.分别以紫外光和太阳光为光源,孔雀石绿和甲基橙为降解物评价了催化剂的光催化活性;并用气相色谱测试了污染物降解产生的CO₂的含量.结果显示,对孔雀石绿的降解,浸渍法和溶胶-凝胶法掺Li⁺都能有效提高TiO₂的光催化活性,但浸渍法比溶胶-凝胶法效果更好,催化活性最高的为浸渍法制备的5%(摩尔分数)Li⁺掺杂TiO₂,其在紫外光和太阳光下的光催化活性分别比纯TiO₂提高了6—8倍和9—10倍;对甲基橙的降解,除溶胶-凝胶法制备的3%(摩尔分数)Li⁺掺杂TiO₂能稍提高光催化活性外,其它Li⁺的掺杂都不同程度降低了TiO₂的光催化活性;随污染物降解率的增加,最终降解产物CO₂的含量增加.实验结果表明,Li⁺掺杂改变了催化剂表面的电荷状态从而改变了催化剂的零电位pH值是造成催化剂降解不同污染物具有不同催化活性的主要原因.     

氮铋共掺杂TiO2的合成及其可见光催化性能研究

以纳米管钛酸为钛的前驱体,Bi(NO₃)₃·5H₂O为N源和Bi源,采用水热法制备了N、Bi共掺杂的TiO₂;并以甲基橙为目标降解物考察了所制备样品的可见光催化性能(λ≥420 nm).利用XRD、XPS、UV-Vis DRS、TEM等技术对不同条件下制备的产物进行了表征.结果表明,所得样品主要为锐钛矿型,粒径20 nm左右,掺杂的Bi主要以Bi₂O₃和BiONO₃两种形式存在.N元素除了以NO₃^-的形式存在于BiONO₃中,还有少量N以间隙氮掺杂于TiO₂中形成Ti-O-N键.N、Bi共掺杂的TiO₂在可见光下表现出了优越的光催化性能,其中水热温度为130 ℃,Bi/Ti摩尔比为1%时,催化活性最高.催化活性的提高源于N和Bi的掺杂增加了样品对可见光的利用效率,降低了光生电子空穴的复合速率.     

Nd2O3/TiO2光催化剂的光生羟基自由基和光活性

以硝酸钕和钛酸四正丁酯作为前驱体,采用溶胶-凝胶法制备了Nd₂O₃/TiO₂纳米光催化剂,并通过XRD和BET等手段进行了表征.以对苯二甲酸作为探针分子,结合化学荧光技术研究了光催化剂表面羟基自由基的生成;并以甲基橙为光催化降解反应模型化合物,考察了光催化剂的活性.测定了甲基橙在TiO₂和Nd₂O₃/TiO₂(1.0%)光催化剂上的吸附常数.结果表明:Nd₂O₃掺杂使TiO₂的粒径减小,比表面积增大;羟基自由基的生成速率越大,催化剂的催化活性越高.Nd₂O₃掺杂有利于反应底物在催化剂表面的吸附,Nd₂O₃的最佳掺入量为Nd/Ti(摩尔比)=1.0%.     

Preparation and Photocatalysis of Mesoporous TiO2 Nanofibers via an Electrospinning Technique

Mesoporous TiO₂ nanofibers have been synthesized by a new method that combines sol-gel chemistry and electrospinning technique. The obtained mesoporous TiO₂ nanofibers were characterized with scanning electron microscopy(SEM), X-ray diffraction(XRD), transmission electron microscopy(TEM) and nitrogen adsorption-desorption isotherms. The photocatalytic performance was evaluated by the photocatalytic degradation of Rhodamine B under UV light irradiation. The results show that mesoporous TiO₂ nanofibers exhibit higher photocatalytic activity compared with nonporous TiO₂ nanofibers.     

Characterization and photocatalytic properties of silver and silver chloride doped TiO2 hollow nanoparticles

Using polystyrene（PSt） particles as template,PSt/TiO₂ composite particles with AgCl incorporation were prepared through hydrolysis of tetrabutyl titanate in the presence of AgNO₃ and NaCl.AgCl doped TiO₂ hollow particles were successfully prepared with the PSt/TiO₂ composite microspheres pretreated at 180℃followed by calcination.The morphology of PSt/TiO₂ particles and the crystal structures of the AgCl doped TiO₂ hollow particles were characterized.The photocatalytic activity of the doped TiO₂ hollow particles in degradation of Rhodamine B was tested under UV and visible lights and compared to that with Ag doped TiO₂ particles.The results showed that TiO₂ hollow particles,either doped with Ag or AgCl,demonstrated higher photocatalytic activity than the pure TiO₂ particles.This enhancement in photocatalytic activity was more significant with AgCl doped TiO₂ than that with Ag doped,and more distinct when the degradation was done under visible light than that under LTV light.     

Ti-MOF Derived N-Doped TiO2 Nanostructure as Visible-light-driven Photocatalyst

Nanostructured N-doped TiO₂ photocatalyst has been prepared via a new approach from Ti-based MOF[NH₂-MIL-125(Ti)] precursor. The success of N doping enhances light absorption and narrows the bandgap. Moreover, the as-prepared nanostructure is constructed with tiny nanoparticles and resembles a pie-like morphology inherited from the MOF, which accelerates electron transfer. Hence, as a photocatalyst for the degradation of methylene blue(MB) under visible light irradiation, the N-doped TiO₂(N-TiO₂) nanostructure shows higher photocatalytic activity with a reaction rate constant of 0.018 min^-1 than that of the TiO₂-P25 and TiO₂ under the visible light.     

Heterostructured Nitrogen and Sulfur co-Doped Black TiO2/g-C3N4 Photocatalyst with Enhanced Photocatalytic Activity

Conventional titanium dioxide(TiO₂) photocatalyst could absorb only ultraviolet light due to its wide bandgap. In this paper, black TiO₂ with narrow bandgap was prepared by introducing oxygen vacancies. Meanwhile, nitrogen(N) and sulfur(S) elements were doped to further broaden the visible light response range of TiO₂(NS-BT), and then heterostructured N,S-doped black TiO₂/g-C₃N₄(CN/NS-BT) was successfully constructed by easily accessible route. The formation of CN/NS-BT heterojunction structure increased the generation and separation efficiency of photogenerated electron-hole pairs, as well as accelerated the transfer rate of the carriers. The as-prepared CN/NS-BT exhibited excellent photocatalytic performance towards the degradation of Rhodamine B(RhB) under visible light irradiation with satisfactory stability. The apparent reaction rate constant of CN/NS-BT(0.0079) was 15.8-fold higher than that of commercial P25(0.0005). The structure, morphology, chemical composition and optical properties of the as-prepared CN/NS-BT were characterized by various analytical methods, and possible photocatalytic enhancement mechanism was proposed. Overall, CN/NS-BT composites look promising as photocatalytic material for future environmental treatment.     

掺杂WO3的SiO2/TiO2的溶胶热液合成及光催化性能

采用溶胶-热液合成法制备了掺杂WO₃的SiO₂/TiO₂复合光催化剂,用X射线衍射、红外光谱、Zeta电位分析、BET和透射电镜对样品进行了表征,并以甲基橙降解评价了其光催化性能.结果表明:改性后的光催化剂表现出较高的光催化性能,WO₃和SiO₂不仅增加了锐钛矿TiO₂的稳定性,并阻止了TiO₂晶粒的聚集生长.     

High-performance titanium dioxide photocatalyst on ordered mesoporous carbon support

Anatase TiO₂ photocatalysts supported with the ordered mesoporous carbon, CMK-3, were synthesized by the incorporation of TiO₂ into CMK-3 followed by heating at 700 °C. The structural properties of the TiO₂ on CMK-3 were investigated by X-ray diffraction, nitrogen physisorption and electron microscopy techniques. In particular, TiO₂ was observed both inside and the external surface of CMK-3. The photocatalytic activity of TiO₂ on CMK-3 under UV-light exhibited higher efficiency in removing the Rhodamine 6G dye solution than the commercial photocatalyst P25 and TiO₂ on activated carbon. It was attributed to the synergistic effect of large surface area adsorption provided by mesoporous CMK-3 and the distinctive location of TiO₂ on the external surface of CMK-3.     

LaNiO3/TiO2纳米管阵列的电化学制备及其光催化性能

利用脉冲电沉积与高温退火相结合的方法制备了镍酸镧(LaNiO₃)纳米颗粒负载的二氧化钛(TiO₂)纳米管阵列. 修饰于TiO₂纳米管阵列上的LaNiO₃纳米颗粒粒径小（< 10 nm）、分布均匀、负载量可控,一些LaNiO₃纳米颗粒沉积于TiO₂纳米管内. 紫外可见吸收光谱显示,LaNiO₃/TiO₂纳米管阵列的吸收带边较TiO₂纳米管阵列明显红移,可见光吸收明显增强. 可见光下光催化降解罗丹明B（RhB）的结果表明,脉冲循环沉积500次制得的LaNiO₃/TiO₂纳米管阵列的光催化活性最佳,其对RhB光催化降解速率是TiO₂纳米管阵列的3.5倍,并且表现出极好的光催化稳定性.     

Keggin型铬取代的磷钨杂多阴离子/二氧化钛纳米膜光催化剂的制备及可见光催化性能

以钛酸四丁酯Ti(OC₄H₉)₄为TiO₂前驱体,Keggin型铬取代的杂多阴离子PW₁₁Cr为可见光活性组分,采用溶胶-凝胶提拉法在玻片表面制备了PW₁₁Cr/TiO₂纳米膜光催化剂,并用UV-Vis DRS、IR、XRD、SEM和TEM等技术手段对催化剂的光吸收性质、化学组成、晶相和表面结构形貌等进行了表征;讨论了膜中PW₁₁Cr和TiO₂相互作用的方式;以染料模型污染物RhB的可见光催化降解为探针,评估了PW₁₁Cr/TiO₂光催化剂的可见光催化活性,讨论了光催化反应机理,并与TiO₂的光催化反应机理进行了比较;考察了焙烧温度、PW₁₁Cr剂量和溶液pH值对光催化活性的影响;最后用RhB的循环降解实验评估了催化剂的光催化稳定性。 实验结果表明,PW₁₁Cr/TiO₂光催化剂对可见光有明显吸收,较低焙烧温度(100 ℃)下得到的膜为无定形结构,而较高焙烧温度(500 ℃)为纳晶结构;前者的光催化活性较高,在200 W金卤灯照射下降解10 μmol/L RhB,120 min的降解率为95%,4 h的COD去除率为72%;羟基自由基是导致RhB降解的主要氧活性物质;低的膜处理温度,高的PW₁₁Cr负载量和溶液酸性有利于提高PW₁₁Cr/TiO₂膜的光催化活性;经循环重复使用10次,PW₁₁Cr/TiO₂膜的光催化活性仅有较少损失。     

C/Cr2O3/TiO2复合材料的制备及其光催化性能研究

本文以制革含铬革屑为原材料,基于矿物鞣剂复鞣的原理,将Ti(IV)均匀、稳定地负载到含铬革屑上,在氮气氛围下,经高温热解制备得到C/Cr₂O₃/TiO₂光催化剂,并研究了其对四环素(TC)的光催化降解效果及机理。结果表明,C/Cr₂O₃/TiO₂光催化剂具有明显的介孔结构,比表面积较大,为277.47 m²·g^-1,Cr₂O₃和TiO₂已实现复合并负载在生物炭(C)上。通过光催化降解发现,在模拟自然光照下,当催化剂用量为0.04 g,TC初始浓度为50 mg·L^-1,溶液pH为2时,TC的去除率可高达99.99%。结合自由基捕获实验发现,C/Cr₂O₃/TiO₂光催化剂对TC的降解作用主要依靠反应体系中产生的大量·O₂^-,·OH和h⁺。     

太阳光照射浮石负载二氧化钛降解氨氮废水

采用溶胶-凝胶法制备了Ti O_2,并使Ti O_2负载在浮石上制备Ti O_2/浮石光催化剂。用X射线荧光光谱(XRF)、电镜扫子显微描(SEM)和傅里叶红外光谱(FT-IR)表征浮石、Ti O_2及Ti O_2/浮石。在太阳光照射下,用Ti O_2/浮石处理模拟氨氮废水,以废水中氨氮降解率为标准,考察影响氨氮降解因素。结果表明,Ti O_2成功固定在浮石表面,负载率为3.71%;废水中氨氮降解率随太阳光照射时间、废水p H值、催化剂Ti O_2/浮石含量增加而增大。当初始氨氮浓度为500 mg/L、太阳照射180 min、废水p H=11、催化剂Ti O_2/浮石剂量为20 g/L时,氨氮降解率达82.0%,氨氮除去率86.8%,降解产物中未发现污染成分NO_2~-和NO_3~-产生。催化剂再生/催化3次,每次再生后氨氮降解率约下降10.0%。该方法快速、简单、低消耗和产生二次污染少,能有效地降解废水中的氨氮。