Co掺杂对YBa_2Cu_3O_(7-δ)电阻率与塞贝克系数的影响

用固态反应法制备了YBa2Cu3-xCoxO7-δ(x=0.0,0.1,0.2,0.5)样品,研究了Co掺杂对YBa2Cu3O7-δ高温区的电阻率和塞贝克系数的影响。随着Co含量的增加,样品的电阻率和塞贝克系数逐渐增大,从金属性导电转变为p型半导体导电。x=0.2和0.5样品的电导活化能在500K处发生突变,高温区的活化能大于低温区的活化能。通过塞贝克系数与温度的关系,计算出x=0.2和0.5样品的费米能级分别为0.02和0.12 eV。当温度高于650-700K时,氧脱附显著影响样品的电输运性质,导致电阻率和塞贝克系数随温度增加而增大。     

Zn掺杂的YBa2(Cu1-xZnx)3O7-δ(x=0, 0.01, 0.02)体系的反常霍尔效应

利用脉冲激光沉积(PLD)方法制备了c轴取向的高质量YBa2(Cu1-xZn)3O7-δ(x=0, 0.01, 0.02)外延薄膜.超导临界温度随Zn掺杂量增加而较快地下降,与单晶样品的结果相符.在强磁场下的输运测量发现YBa2(Cu1-xZn)3O7-δ系列样品在Tc附近均出现反常的Hall电阻率符号反向,但其Hall电导率σxy随磁场的变化关系与氧欠掺杂的YBa2Cu3O6.66存在很大差异,说明Zn掺杂和氧掺杂对混合态中的磁通涡旋性质的影响有显著不同.     

Co掺杂对YBa2Cu3O7-δ微观结构及透氧性能的影响

利用XRD、TG和标准四电极法研究了YBa2Cu3-xCoxO7-δ(x=0~0.5)混合导体的结构和性能,稳态法考察了Co掺杂量对膜材料透氧性能的影响。实验表明当x<0.05时,Co掺杂可以提高透氧量,在x=0.05时达到最大值(940℃,厚1.4mm的膜材料透氧量为0.53ml/min.cm2)。当x>0.05透氧量开始减小,当x>0.01后,透氧量下降到比未掺杂的YBa2Cu3O7-δ还要小。从晶格结构与Co掺杂量的关系及Co-O键能与Cu-O键能的差别对透氧量随Co掺杂量的变化进行了讨论。     

Co掺杂的YBa2Cu2O6+δ的氧非计量和氧渗透性能研究

研究钴离子部分取代铜离子对YBa2 Cu3 O6+δ的氧非计量值δ和氧渗透率的影响 .对于钴替代的样品 ,氧非计量的绝对值变大 ,且其数值不再随温度和氧分压的变化发生显著变化 .YBa2 Cu2 CoO6+δ样品在中、高温具有可观的氧渗透率 .对于厚度为 1.2mm的致密YBa2 Cu2 CoO6+δ样品 ,在 85 0℃时 ,只要在样品两端施加较小的氧分压差(PO2 =2 1.2kPa、PO2 =10 1Pa) ,其氧渗透率即可达 5 7μmol/cm2 s,明显高于YBa2 Cu3 O6+δ的氧渗透率 (31μmol/cm2s) .YBa2 Cu2 CoO6+δ的高氧渗透率在结构上可被归结为位于晶胞基面上的氧离子和氧空位的均匀分布     

Y_(0.5)Gd_(0.5)Ba_2Cu_3O_(7-δ)体系中通氧时间对超导转变温度的影响

研究了高温氧化物超导体Y0.5Gd0.5Ba2Cu3O7-δ体系中通氧时间对超导转变温度及超导转变温区的影响。Y0.5Gd0.5Ba2Cu3O7-δ样品是按相等摩尔数的Gd与Y元素配比,采用传统的固相反应法烧结而成的多晶块材。实验结果显示:Y0.5Gd0.5Ba2Cu3O7-δ烧结样品与YBa2Cu3O7-δ烧结样品均具有很好的单相性,在一定的通氧条件下其超导临界转变温度TC与超导初始转变温度TCO值相对YBa2Cu3O7-δ烧结样品有提高。文中对此结果进行了讨论。     

赝能隙导致的YBa2(Cu1－xMx)3O7-δ(M=Co,Zn)薄膜的输运性质异常

报道了两类典型元素替代的超导Y123相体系-YBa2(Cu1-xCox)3O7-δ(x=001,002)和YBa2(Cu1-yZny)3O7-δ(y=0005,0010)薄膜的电阻率温度特性(ρ(T))和Hall效应(RH(T)).研究表明,Co掺杂的Y123相体系十分类似于氧欠掺杂的情况,对Co掺杂的薄膜样品,由电阻率温度特性定义的赝能隙打开的温度T分别为193和225K.而Zn掺杂的样品没有观察到赝能隙打开对电阻率温度特性的影响.由Hall效应的测量和Hall角(cotθH)定义了另一个特征温度T0, 关键词： 赝能隙 Y123相 Hall效应     

电化学氧化YBa2Cu3O6+x的晶体结构和超导电性研究

在较低温度下用电化学方法控制YBCO块材的氧含量对深入考察其氧含量、晶体结构和超导电性之间的关系有重要意义.我们用固态反应法合成并用惰性气体退火处理制备出非超导的四方相YBa2Cu3O6 x(x～0.1)块材样品,然后用熔融的KNO3-NaNO3作为电解质,用YBa2Cu3O6 x块材作为阳极对其进行电化学氧化.阳极氧化用恒流法在360℃进行.氧化产物的电阻、磁化率和结构特性分别用四引线法、SQUID磁强计和XRD进行测定.随着氧化时间和通过样品的电量(Q)的增加,样品中的超导相含量逐渐增加,依次可以获得超导相是60K相为主、60K和90K两相共存和90K单相的样品.XRD分析证明了电化学氧化后样品表面和内部的结构不同,表明了氧分布的不均匀性,样品表层的氧含量大于内部的氧含量.     

电泳共沉积含Ag的YBa2Cu3O7-δ厚膜

电泳共沉积了含Ag的YBa2Cu3O7-δ厚膜．共沉积膜中的Ag含量随着原料中Ag量的增加而增加．YBa2Cu3O7-δ与Ag两种粒子吸附质子所带电量之间的关系为QYBCO=-0．1638QAg 0．1519F．添加剂聚乙二醇消弱了固体粒子之间的静电斥力作用,使膜的表面光滑平整．在Ag基带表面有垂直于基带面的沿a—b面生长织构形成．     

NdBCO厚膜籽晶生长YBCO块体材料

本研究采用液相外延生长(Liquid phase epitaxy,简称LPE)的NdBa2Cu3O7-δ(NdBCO)高温超导厚膜作籽晶,通过冷籽晶熔融织构的方法生长YBa2Cu3O7-δ(YBCO)块体材料.与通常使用的籽晶相比,NdBCO厚膜籽晶具有如下优点:相对于非超导材料籽晶(MgO 等),NdBCO具有和YBCO相似的晶体结构和晶格常数,并对体系不会造成污染;与单晶体及熔融织构获得的籽晶相比,LPE获得的大尺寸NdBCO厚膜,有可能得到大单畴结构的YBCO块体材料;与NdBCO薄膜籽晶相比,NdBCO厚膜具有更高的结晶性能.本文讨论NdBCO厚膜籽晶生长YBCO块材过程中籽晶的影响及其热力学稳定性等问题.     

高温超导磁悬浮深冷测试系统设计

介绍一种使用 G- M制冷机实现深冷环境的高温超导磁悬浮测试系统。高温超导体块材YBa Cu O被固定在制冷机冷头上 ,其温度通过温度控制器可以控制在 1 0 0 K到 40 K范围内。永久磁体 Nd Fe B固定在位于 YBa Cu O上方高温超导磁悬浮测试系统的垂直运动部件上 ,并在计算机控制下作垂直运动以改变它与 YBa Cu O之间的距离。同时 ,计算机采集数据得到 YBa Cu O与 Nd Fe B之间悬浮力与距离的关系。通过温度设定 ,可得到 YBa Cu O在不同温度下的悬浮性能。     

单源进液金属有机化学气相沉积法工作气压对YBCO薄膜制备的影响研究

基于金属有机化学气相沉积法(MOCVD),在沉积有Y2O3/YSZ/ CeO2( YYC)多层过渡层的Ni - W_at.5％金属基带上沉积YBa2Cu3O7-x(YBCO)超导薄膜.通过对单源进液系统的优化,使金属有机源连续稳定地输送到蒸发皿进行闪蒸.优化总气压并通入N2O气氛,以获得高质量的YBCO薄膜.在优化的温...     

高温热处理气氛对低氟MOD法制备YBCO超导薄膜的影响研究

金属有机物沉积法(MOD)制备YBa2Cu3O7-x(YBCO)涂层导体是最具有商业前景的方法之一.本文使用环烷酸铜代替三氟乙酸铜,降低了前驱液中大约50%的氟含量.然后在带有缓冲层(Y2O3/YSZ/CeO2)的Ni-5at.%W基带上采用MOD法制备了YBCO薄膜并系统研究了高温热处理过程中气体流速和氧分压对YBC...     

Indications of an electronic phase transition in two-dimensional superconducting YBa2Cu3O(7-x) thin films induced by electrostatic doping

We successfully tuned an underdoped ultrathin YBa2Cu3O(7-x) film into the overdoped regime by means of electrostatic doping using an ionic liquid as a dielectric material. This process proved to be reversible. Transport measurements showed a series of anomalous features compared to chemically doped bulk samples and a different two-step doping mechanism for electrostatic doping was revealed. The normal resistance increased with carrier concentration on the overdoped side and the high temperature (180 K) Hall number peaked at a doping level of p～0.15. These anomalous behaviors suggest that there is an electronic phase transition in the Fermi surface around the optimal doping level.     

Structure and Parameters of Boundary Vortices in a Superconducting Josephson Medium

JETP Letters - The dynamics of the formation of different-scale vortices and antivortices in bulk and film YBa2Cu3O7–x samples in the process of their “decomposition” into twins...     

利用微带谐振技术研究MgB_2/Al_2O_3和YBa_2Cu_3O_(7-x)/LaAlO_3超导薄膜的微波性质(英文)

利用微带谐振技术研究了MgB2/A12O3和YBa2Cu3o7-X/LaAlO3(YBCO/LAO)超导薄膜的微波性质.一个颗粒尺寸模型被用来分析超导薄膜的穿透深度和表面电阻.结果表明,对于高质的YBCO/LAO,微波性质主要由颗粒决定.对于低质的MgB2/Al2O3,该薄膜的微波性质主要由颗粒边界决定.     

金属有机物化学气相法制备YBCO超导薄膜研究

运用金属有机物化学气相沉积法(MOCVD),在LaAlO3(LAO)单晶上沉积YBa2Cu3O7-x(YBCO)超导薄膜。通过使用优化的进液装置,使金属有机源连续、稳定地输送至蒸发皿进行闪蒸。通过优化总气压、氧分压等生长条件,获得高质量的YBCO薄膜。在固定的温度条件下,调节反应总气压和氧分压,在总压为380Pa,氧分压为180Pa获得YBCO薄膜临界电流密度Jc=0.6MA/cm2。随着氧分压增大,YBCO薄膜产生a轴取向,(005)峰向左偏移,且薄膜中的Cu/Ba由1.0变化至1.63。在Cu/Ba=1.48时,YBCO薄膜结构与性能较优。     

显微拉曼研究外延生长的BaTiO_(3-x)薄膜的结构相变与结构动力学(英文)

我们用显微拉曼、卢瑟福背散射谱、X射线散射和非对称摇摆等实验手段研究了在1 0 - 2 到1 0 - 5帕氧气压下用激光分子束外延技术生长的BaTiO3-x薄膜的结构动力学特性。测量结果表明生长氧压越低,晶格常数c和c/a越大,晶格常数a稍微减小,晶胞体积变大。随着生长氧压的减小,薄膜中氧含量减小。在3 0×1 0 - 5帕氧气压下生长的薄膜中氧缺陷可达0 48,但是样品的四方相结构可以很好的维持。显微拉曼研究进一步确定了样品都是四方相结构。另外,在BaTiO2 52 薄膜的拉曼光谱中发现高频段有两个新峰,其可能是由于氧缺陷导致的二级拉曼散射引起的。随着生长氧压的减小,拉曼峰向低频移动,表明薄膜中的应力减小。同时,拉曼峰变宽,这可能是由于氧缺陷导致的结构畸变引起的。由于在薄膜中存在二维张应力,BaTiO3单晶样品中的结构相变特征在我们的样品中从78到5 5 0K的温度范围内不存在。     

氧分压对Cu-NiFe_2O_4金属陶瓷相成份的影响

用高温固相法合成的NiFe2O4陶瓷粉末,选取Cu为金属陶瓷的金属相成分,研究了氧分压对Cu-NiFe2O4金属陶瓷的相成份的影响,结果表明:当烧结温度为1150℃,氧分压大于2.23Pa时,Cu被大量氧化;氧分压小于4.2×10-3Pa时,Cu和离解的Ni反应生产Cu3.8Ni合金,试样的导电性或抗氧化性都会降低,1150℃下烧结制备Cu-NiFe2O4金属陶瓷的最佳氧分压是(0.3-42.0)×10-2Pa。     

Precursor evolution and growth mechanism of BTO/YBCO films by TFA–MOD process

In this study, BaTiO3 （BTO）-doped YBCO films are prepared on LaA103 （100） single-crystal substrates by metal- organic decomposition （MOD） using trifluoroacetate （TFA） precursor solutions. The critical current density （Jc） of BTO/YBCO film is as high as 10 MA/cm2 （77 K, 0 T）. The BTO peak is found in the X-ray diffraction （XRD） pattern of a final YBCO superconductivity film. Moreover, a comprehensive study of the precursor evolution is conducted mainly by X-ray analysis and μ-Raman spectroscopy. It is found that the TFA begins to decompose at the beginning of the thermal process, and then further decomposes as temperature increases, and at 700 ℃ BTO nanoparticles begin to appear. It sug- gests that the YBCO film embedded with BTO nanoparticles, whose critical current density （Jc） is enhanced, is successfully prepared by an easily scalable chemical solution deposition technique.