Ti-IF冷轧搪瓷钢的贮氢机理和氢渗透试验研究

分析了Ti-IF冷轧搪瓷钢的贮氢机理,通过3种不同成分钢板的氢渗透试验,研究化学成分、冷轧压下率、第二相粒子等对钢板贮氢性能的影响。结果表明,Ti、S含量较高的钢中第二相的体积分数也高,贮氢性能越好;冷轧压下率越高,钢板贮氢性能越好,相应的抗鳞爆性能越好。     

DC01EK冷轧搪瓷用钢开发及其抗鳞爆性能

在保证成形性能和抗鳞爆性能的前提下,以传统冷轧板DC01的成分为基础,适当的提高碳、锰和硫的含量,通过热轧、冷轧和退火工艺控制,获得了一种低成本高贮氢性能的搪瓷用钢。钢板的屈服强度不大于270 MPa,抗拉强度不大于400 MPa,伸长率不小于30%。钢板中的Fe3C和MnS均为有效的贮氢陷阱。随着退火温度的升高,Fe...     

抗鳞爆性优良的搪瓷用钢板的研制

鳞爆是搪瓷制品常见的重大缺陷。根据钢板搪烧后产生鳞爆的机理，作者采用热轧高温卷取和增大冷轧变形量的新工艺，试制成抗鳞爆性优良的搪瓷用钢板，且制坯成形性良好。     

冷轧搪瓷钢板的抗鳞爆性能的研究

研究了冷轧超低碳搪瓷钢板的抗鳞爆性能,该钢板具有优良的抗鳞爆性能,氢在钢板（厚度为１ｎｍ）中的穿透时间为１１．４ｍｉｎ,钢板中不可逆陷阱的贮氢容量为１２．６ｍｏｌ／ｍ＾３。     

搪玻璃用热轧中厚钢板氢穿透时间及贮氢性能

搪玻璃用中厚钢板是制作搪玻璃设备的关键材料,要求钢板在搪玻璃过程中具有良好的贮氢性能和抗鳞爆性能,但长期以来主要使用普通压力容器用中厚钢板Q245R,极易产生鳞爆。因此,对比常用的含0.16%C+0.013%Ti(质量分数)的热轧正火态中厚钢板Q245R,设计并工业化生产了w(C)=0.10%、w(Ti)=0.10%的搪玻璃用热轧中厚钢板B245GT,通过光学显微镜、渗氢试验和透射电镜等研究和对比分析了厚度为20 mm的2种钢板在表层、厚度1/4处和1/2处的显微组织、氢穿透时间和贮氢性能,观察并分析了B245GT中的析出相。结果表明,Q245R钢板的显微组织由带状珠光体和铁素体组成,而B245GT钢板由铁素体和极少量珠光体组成,珠光体组分远低于Q245R。对测定氢穿透时间的试样厚度归一化后,Q245R沿不同厚度处的氢穿透时间TH₂介于2.7～4.4 min/mm²,均远低于阈值6.7 min/mm²,B245GT钢板沿不同厚度处的TH₂为11.6～13.6 min/mm²,显...     

深冲搪瓷钢DC03EK析出物及其抗鳞爆性能分析

对DC03EK深冲用冷轧搪瓷钢铸坯、热轧基料进行析出物检测,对其冷轧成品卷进行析出物、抗鳞爆敏感性TH值、成形极限FLD测试。结果表明,DC03EK深冲用冷轧搪瓷钢材料中存在弥散分布的Ti(C,N)、TiN、TiC、TiS、Ti4C2S2和极少量的MnS等析出物,铸坯中析出物颗粒较大,经热轧轧制较大颗粒析出物变小,经冷轧轧制及罩式退火后,析出物变得细小并弥散分布,使得DC03EK具有高的抗鳞爆敏感性TH值,同时又具有良好的成形性。     

含钛超低碳搪瓷钢板的退火工艺

 研究了两种不同退火工艺——罩式退火和连续退火工艺对含钛超低碳搪瓷钢板成型性能和贮氢性能的影响。试验结果表明,材料经连续退火后其成型性能略优于罩式退火,而其贮氢性能是经罩式退火后的明显好于连续退火。因此综合考虑,采用罩式退火工艺可实现成型性能和贮氢性能的良好匹配。     

Ti／Mn基Laves相贮氢合金贮氢性能的影响因素

介绍了影响Ti/Mn基Laves相贮氢合金贮氢性能的一些因素,这些因素包括锆部分取代钛,Cr、V、Fe、Cu、Ni、Co、Mo等元素部分取代锰,非化学计量,非金属杂质元素与杂质气体。同时也介绍了热处理、熔炼方式、氟化处理对Ti/Mn基Laves相贮氢合金贮氢性能的影响。     

鞍钢搪瓷用热轧带钢的开发与应用

制取了9种不同Ti含量的试样,通过实验室正火处理等方法调整析出相的析出状态,通过测试氢渗透时间、搪瓷试验等研究了Ti含量和析出状态对抗鳞爆性能的影响。结果表明,氢渗透时间随Ti含量及Ti／C比值的升高而延长。当Ti以析出粒子存在时,钢板具有更好的抗鳞爆效果。介绍了基于研究结果开发的双面搪瓷用热轧钢板的技术特点、实际性能水平和应用情况。     

冷轧超深冲搪瓷用钢DC06EK产品开发

为提升产品的档次和效益,通过科学的、经济的成分设计以及合理的冶炼、热轧、酸轧、连续退火全流程工艺控制,成功开发出了屈服强度小于140 MPa、平均塑性应变比大于2.30、抗鳞爆敏感系数TH大于6.7 min/mm2的冷轧超深冲搪瓷用钢DC06EK产品。微观组织分析表明,DC06EK中含有均匀、等轴的铁素体组织,以及大量细小的、弥散分布的TiS、TiN等第二相析出粒子,由此保证了钢板兼有优良的成形性能和抗鳞爆性能。工业试用的结果进一步证实了该产品具有大批量推广入市的广阔前景。     

MnS夹杂对钢中氢扩散行为的影响

通过实验和有限元计算研究了MnS夹杂对钢中氢扩散行为的影响.结果表明:当MnS夹杂长度取向与氢渗透方向平行时,氢在钢中的表观扩散系数随MnS含量的增加而增加;当MnS夹杂长度取向与氢渗透方向垂直时,氢在钢中的表观扩散系数随MnS含量的增加而降低.对于具有扩散通道效应和陷阱效应的第二相,它对氢扩散的影响取决于扩散通道效应和陷阱效应的强弱以及第二相的形状、数量和取向.     

晶粒尺寸对高锰奥氏体TWIP钢氢脆行为的影响

主要研究了晶粒尺寸对Fe- 17Mn- 1Al- 0.6C TWIP钢的氢脆行为的影响。原始材料经过不同的热处理制度,得到晶粒尺寸为17和45μm的材料。通过慢拉伸试验研究氢质量分数在0～0.001%材料的氢脆敏感性。试验结果表明,充氢后的试验材料比未充氢试验材料易发生氢脆,充氢后的试验材料断裂强度和断裂应变均降低。随着晶粒尺寸的增大,试验材料的氢脆敏感性增强。在氢质量分数为0.001%,晶粒尺寸增加到45μm时,应变损失率为17%,随着晶粒尺寸的增大,氢脆敏感性增加的原因是晶粒尺寸较大的材料孪晶较早出现,孪晶密度较大,同时单位晶界氢质量分数增加。     

注氢诱发ODS铁素体钢中第二相分解

采用室温离子注入和低压电镜原位观察的方法,研究了注氢对国产ODS铁素体钢微观结构的影响.结果表明:原始未注氢ODS铁素体钢中存在有一定数量的(Fe,Cr)₂O₃,室温注氢后,(Fe,Cr)₂O₃无明显改变;但将其加热至450℃,(Fe,Cr)₂O₃即开始分解;到550℃时,部分(Fe,Cr)₂O₃消失,残余(Fe,Cr)₂O₃的成分也发生了改变.与此相反,原始未注氢ODS铁索体钢的微观结构在加热过程中却没有明显改变,(Fe,Cr)₂O₃并不分解.     

Effect of precipitated phase on resistance to hydrogen embrittlement of high Co- Cr- Mo- Ni bearing gear steel

High Co- Cr- Mo- Ni bearing gear steel was used as the test material, and hydrogen induced fracture process of the test steel was studied by TDS test, slow strain rate drawing and micro analysis. The results show that the high plasticity of the test steel is obviously decreased. Most of the hydrogen in the test steel is diffusible hydrogen, which is controlled by the weaker hydrogen trap. By comparing the grain size, the size of the strip, the number of residues, the dislocation density and the precipitation of the two kinds of test steels, the main influencing factors of the anti- hydrogen brittleness of test steel are the carbon density and distribution, and dispersed fine carbides are more conducive to improve hydrogen embrittlement resistance. The critical hydrogen concentration is obtained and the critical hydrogen concentration is deduced, which provides a reference for the high reliability and safe service of the components.     

超纯铁素体不锈钢脆性及形成特点对性能的影响

超纯铁素体不锈钢是一种具有良好耐蚀性能、加工性能和焊接性能的材料,主要应用于汽车行业、厨房用具和家用电器以及大型建筑的屋面设计等领域.主要研究超纯铁素体不锈钢脆性形成原因以及对性能的影响,总结了超纯铁素体不锈钢σ相脆性、475℃脆性和高温脆性等主要特征,并对其脆性形成的原因进行了详细分析,认为σ相,x相,α相,Lave...     

表面处理对海洋工程用316L不锈钢耐点蚀性能的影响

316L不锈钢为常用的耐蚀合金材料,然而其在海洋大气环境服役时易遭受点腐蚀而发生失效。通过点腐蚀速率、临界点蚀温度、点蚀电位、极化曲线测试等评价方法,对经过不同表面处理(光亮退火、抛光、酸洗钝化)后的316L不锈钢的耐点蚀性能进行测试分析。结果表明,不同表面处理对316L不锈钢的临界点蚀温度影响不大,但会使点腐蚀速率、点蚀电位有所差异;在测试条件下,抛光及酸洗钝化均可有效提高316L不锈钢的耐点蚀性能,其中酸洗钝化态的耐点蚀性能最好,因此建议对海洋工程用316L不锈钢产品在使用前进行酸洗钝化处理。     

溶解氧变化对阴极极化下10Ni5CrMo钢氢脆敏感性的影响

摘要：为研究溶解氧质量浓度对10Ni5CrMo钢在阴极极化条件下氢脆敏感性影响规律，对10Ni5CrMo钢进行了阴极极化下的电化学交流阻抗谱测试﹑并采用慢应变速率拉伸实验和断口分析方法研究了海水中溶解氧质量浓度变化和不同阴极极化下10Ni5CrMo钢的氢脆敏感性。结果表明：溶解氧质量浓度变化对10Ni5CrMo钢强度几乎没有影响；同一溶解氧质量浓度下，随极化电位负移，断裂时间、伸长率、断面收缩率明显降低，氢脆系数增加，氢脆敏感性显著提高，极化电位达到-1000mV时，氢脆系数已超过安全区允许的最高值25%，进入危险区；同一极化电位下，随着海水中溶解氧质量浓度减少，材料塑性变差，断裂时间、伸长率和断面收缩率不断降低，氢脆系数增加，氢脆敏感性提高。     

Effect of Ti（C,N）Precipitation on Texture Evolution and Fish-Scale Resistance of Ultra-Low Carbon Ti-Bearing Enamel Steel

 The Ti(C,N) precipitation and texture evolution in ultra-low carbon Ti-bearing enamel steel were studied to discover their correlation. Two different cooling paths of simulative coiling were adopted to gain different morphologies of Ti(C,N) precipitate in hot strips. It is found that the Ti(C,N) precipitate in hot strip using Path 2 (put into asbestos box and air cooled) are finer and much more in quantity than that in hot strip using Path 1 (held at 730 ℃ for 30 min and furnace cooled). The morphology of Ti(C,N) precipitate in hot strip has great effect on recrystallization texture in the subsequent cold-rolled annealed sheet. γ-fiber texture of strong recrystallization is gained in cold-rolled and annealed sheet came from Path 1. On the contrary, in the one came from Path 2, the γ-fiber texture is weak. This may be due to the pinning force of numerous fine Ti(C,N) precipitate which retard the growth of preferential nucleated {111} orientated grains. Annealed steel sheets in the test came from both paths have excellent fish-scale resistance.