 为了获得优质镁质球团矿,在添加0.7%新型复合黏结剂的条件下进行了MgO添加方式(菱镁石粉、轻烧镁粉)对造球过程、氧化焙烧及冶金性能影响的试验研究。结果表明,复合黏结剂改善了生球指标、提高了球团矿铁品位,球团矿中w(TFe+MgO)质量分数提高0.65%;当w(MgO)/w(SiO₂)为0.14～0.24时,球团矿添加菱镁石粉改善了生球落下强度、提高了球团矿还原性,MgO添加方式对抗压强度的影响很小,球团矿添加菱镁石粉、轻烧镁粉都降低了还原膨胀率,改善了低温还原粉化指标、熔滴性能。     

竖炉球团提镁试验研究与实践

基于龙钢现有条件及实验数据,开展了竖炉生产镁质球团的工业试验,重点分析了竖炉使用轻烧镁粉后球团矿质量及冶金性能的变化规律.实践表明,配加轻烧镁粉后,随MgO含量的提高,生球落下强度和抗压强度均呈增大趋势,成品球团抗压强度1500～2000 N合格率逐渐升高,还原度指标和RDI+3.15提升,高炉料的软化区间降低13℃,...     

w(MgO)对熔剂性球团矿冶金性能的影响

 为了研究添加高镁粉时w(MgO)对熔剂性球团矿冶金性能的影响。考察了w(MgO)为1.6%～2.4%时,其对球团矿抗压强度、RI(还原性指数)、RDI(低温还原粉化指数)和RSI(还原膨胀指数)的影响。采用光学显微镜和X射线衍射仪对球团矿微观结构和矿物组成进行了分析。结果表明,随着MgO质量分数的增加,抗压强度呈先升高后降低的趋势,w(MgO)为2.0%时,抗压强度最大,为3 533 N;随着w(MgO)由1.6%增加到2.4%,球团矿RI、RDI和RSI得到改善;w(MgO)为1.8%～2.0%时,球团矿微观形貌和矿物组成较好,赤铁矿成片结晶,球团矿强度良好。在用高镁粉和研山精粉造球时,w(MgO)控制为1.8%～2.0%,以期得到较低的还原膨胀指数和较好的冶金性能。     

复合镁质添加剂对球团生产影响的试验分析

球团矿作为一种优质的高炉炼铁原料,其配比不断增加。试验采用复合镁质添加剂代替膨润土,提高球团矿中的MgO含量,考察其对生球质量和球团冶金性能的影响规律和作用机理。试验结果表明,采用复合镁质添加剂代替膨润土后,生球抗压强度略有降低,落下次数变化不大,爆裂温度均高于600 ℃;球团矿的低温还原粉化指数(RDI_+3.15)变化不大,均高于92%,完全能够满足高炉冶炼要求;还原度和还原膨胀性能显著提高,MgO质量分数由0.2%增加到2.0%,球团矿还原度RI由67.58%增加至91.47%,还原膨胀指数RSI由23.51%降低至19.25%。为高炉优化炉料结构、进一步增加球团矿的配比提供支撑。     

马钢生产镁质球团的工业试验

竖炉配加1.4%轻烧氧化铁粉生产镁质球团矿,生球质量较好.竖炉炉况稳定;成品镁质球团矿MgO含量为1.96%,达到了顶期指标;其转鼓强度为92.08%,抗压强度为2945 N/个,基本与酸性球团矿持平;冶金性能较酸性球团有所改善,其中RDI+3.15提高了3.13%,膨胀率下降了0.96%.将镁质球团矿用于高炉生产后....     

不同含镁添加剂对球团矿工艺参数及质量的影响

 MgO对高铁低硅烧结中烧结矿的质量有不利影响,但其可以改善球团矿的冶金性能。因此,不在烧结矿而在球团矿中添加MgO,可在改善烧结矿质量的同时提高球团矿的冶金性能。不同的含镁熔剂对球团工艺参数和性能影响不同。通过试验研究了在高铁低硅条件下,白云石、蛇纹石、硼泥和镁质添加剂等4种含镁添加剂对球团造球,焙烧工艺及对球团矿物化性能和冶金性能的影响。试验结果显示,镁质添加剂对提高球团矿MgO含量、控制低硅球团矿还原膨胀率、改善球团矿还原度和熔滴性效果最好。     

鞍钢球团配加白云石熔剂的研究

以鞍钢生产用原料条件为基础,针对不同碱度配比白云石熔剂性球团矿、白云石不同添加量的生球性能进行研究,采用数学优化方法确定添加白云石球团的焙烧制度;同时对球团矿低温粉化性能、还原性能、膨胀性能和荷重软化性能进行了研究;试验得出配加白云石的熔剂性球团质量良好。     

济钢烧结配加复合轻烧镁粉的试验研究与应用

为了优化烧结熔剂结构,寻求最优的烧结镁质熔剂,济钢开展了配加复合轻烧镁粉的烧结试验研究与生产应用,即用复合轻烧镁粉完全取代轻烧白云石粉,增加石灰石粉用量以维持烧结矿碱度稳定。结果表明,配加复合轻烧镁粉比配加轻烧白云石粉能提高烧结矿化学成分的稳定性（尤其是碱度及MgO的稳定性）,改善烧结矿粒级组成及冶金性能,降低烧结矿成本;同时,烧结过程参数得到了优化稳定,烧结机产能水平得到了提高。     

不同MgO熔剂添加剂的烧结试验及生产

介绍了白云石、轻烧白云石、高镁粉等分别作烧结矿MgO熔剂添加剂的实验室试验情况和工业生产情况.试验和工业生产结果表明,在安钢原料工艺条件下,和白云石和轻烧白云石相比,高镁粉是一种比较理想的烧结矿MgO熔剂添加剂.     

球团配加镁质熔剂及新型皂土试验

为生产含MgO的镁质球团用来替代烧结矿中MgO,确保高炉造渣所需的适宜的MgO质量分数,考察了在球团生产中添加一种新型球团黏结剂(新型皂土)和一种氧化镁质熔剂(镁石粉)时,对造球焙烧及球团矿冶金性能的影响。试验结果表明,镁质球团生球落下强度有所提高,350℃时未发生爆裂。配加新型皂土可提高球团品位,降低Si O2质量分数。镁质球团的低温还原粉化指标和体积膨胀率指标均有所改善。而且,软化温度升高,软化温度区间变窄,有利于软熔带由高炉上部往下部移动,改善高炉透气性。在保证综合入炉铁料MgO质量分数不变的条件下,当烧结矿自然带入的MgO质量分数为1.2%时,球团矿中的MgO质量分数大于1.90%,可满足高炉要求。     

不同质量分数MgO对球团质量的影响

通过某球团厂现有生产所用的矿粉配矿得到不同MgO质量分数的球团矿,运用一系列的试验方案和检测手段找出球团矿最优的抗压强度和冶金性能下的MgO质量分数,并探究了不同MgO质量分数对其球团矿的抗压强度和冶金性能影响的规律。结果表明,MgO质量分数为0.5%时,所生产的球团矿抗压强度最强,随着MgO质量分数的增加,球团矿的抗压强度下降。MgO质量分数为0.5%时,还原度最高,达到了75.59%,随着MgO质量分数的增加,球团矿的还原度下降。MgO质量分数为1%时,低温还原粉化率最大,随着MgO质量分数的增加,球团矿的低温还原粉化率先升高后降低;MgO质量分数为1%时,软化开始温度最高,熔滴温度区间最窄,熔滴性最好,随着MgO质量分数的增加,球团矿的软化开始温度先上升后下降,熔滴温度区间先变窄后变宽。     

Effects of MgO Containing Additive on Low-Temperature Metallurgical Properties of Oxidized Pellet

 As a main charging form of BF (blast furnace), pellets play an important role in blast furnace process. However, comparing with sinters, pellets have many disadvantages, such as reduction swelling, low softening and melting temperature and so on. Therefore, the flux pellets have been applied in blast furnace widely, especially MgO containing pellets. The light burned magnesite is applied as MgO containing additive in pellet production. The characters of light burned magnesite are explored. Meanwhile, the effects of it on low-temperature metallurgical properties are investigated such as low-temperature reduction degradation index (RDI), compressive strength (CS) and the reduction swelling index (RSI). The light burned magnesite calcined at 850 ℃ manifests better grindability, larger specific surface area, and higher hydration activity. It is found that the addition of light burned magnesite can improve low-temperature metallurgical properties (RDI, RSI) of the pellets. With the increase of light burned magnesite in pellets, the RSI and RDI decrease gradually; when the proportion of light burned magnesite does not exceed 2. 0% in pellets, the CS decreases slightly, but it still surpasses 2689 N, which can still meet the demand of BF.     

含镁添加剂用于铁矿球团的试验研究

应用含镁添加剂,并配以膨润土,对铁矿球团进行了实验室试验。试验研究表明:添加轻烧白云石和镁砂对提高生球质量能起到一定的促进作用,而镁橄榄石的影响较小;随着添加剂用量的增加,三种球团矿的抗压强度均显著降低,其下降幅度由大到小依次为镁砂球团、轻烧白云石球团和镁橄榄石球团;适当提高焙烧温度,延长焙烧时间,有利于提高球团的抗压强度。另外,冶金性能研究也表明:随着添加剂用量的增加,球团还原度和软熔性能有一定提高,低温还原粉化和还原膨胀性能显著改善。     

高硅镁质熔剂性球团成球过程及冷态性能实验

生球质量的好坏是直接关系到企业是否顺利生产高质量熔剂性球团的前提。为探明SiO2、碱度及MgO含量对生球性能的影响规律,以唐钢生产所用3种磁铁矿为原料,通过添加生石灰调节碱度,添加白云石调节MgO含量,配比3种铁矿粉调节SiO2含量,进行了造球及生球冷态性能的试验。研究发现,无论是改变SiO2、碱度还是MgO含量,其生球适宜水分基本都保持在8%~9%(质量分数)之间。生球的成球率维持在90%以上,成球率良好。生球的抗压强度、落下强度的大小以及爆裂温度的高低,主要受铁矿粉及熔剂的粒度组成、物理性能以及生球适宜水分大小的影响。     

MgO含量和来源对球团焙烧特性及冶金性能的影响

分别以5种不同的含镁添加剂（高镁磁铁矿、镁橄榄石、白云石、菱镁石和氧化镁粉）制备镁质球团,阐述MgO含量和来源对磁铁矿球团焙烧特性及冶金性能的影响。研究结果表明:不同的含镁添加剂对于生球的落下强度有着一定影响,其中氧化镁粉与高镁磁铁矿均能够提高球团的落下强度。相同的预热焙烧制度下,提高MgO含量会增加球团孔隙率,降低预热和焙烧球团的抗压强度,其中白云石对焙烧球团强度的不利影响最小。增加预热球团的氧化度有利于促进镁质焙烧球团固结,提高其抗压强度。在MgO来源相同的情况下,MgO含量的增加会导致球团孔隙的增减,降低了球团强度,而配加不同种类的含镁添加剂,均能不同程度改善球团的还原膨胀性、低温还原粉化性和还原性,其中配加高镁磁铁矿的球团的还原膨胀性和低温还原粉化性均优于于其他含镁球团。      

基于矿相结构与冶金性能的酸性球团质量综合评价

针对中国高炉冶炼沿用的"高碱度烧结矿+酸性球团+块矿"的炉料结构,立足于化学成分、微观矿相结构、物理性能及冶金性能,从多角度对5种进口酸性球团矿的质量进行综合评价.结果表明,北美酸球物理性能相对较好,转鼓指数分别为95.67％、95.55％;巴西酸球还原后的抗压强度普遍偏低,分别为282.8、347.6 N.巴西酸球主...     

添加赤铁矿对碱性球团性能的影响

通过向碱度为1的球团矿中配加不同比例赤铁矿,探究赤铁矿的加入对碱性球团性能的影响。试验结果表明,随着赤铁矿的配比由0%提高到40%,生球落下强度提高、抗压强度变化不明显;焙烧球团矿的抗压强度下降,由未加赤铁矿的2 460 N/P降低到含40%赤铁矿的1 890 N/P;成品球内部孔隙率由25.84%下降到21.45%,平均孔径由2 184.7提高到3 937.9 nm;通过显微观察,发现赤铁矿再结晶比磁铁矿固相固结方式形成的晶体结构松散,晶体间的联结较弱;配加赤铁矿对碱性球团矿还原膨胀率起到明显改善作用,由30.45%降低到13.23%。综合来看,向碱度为1的球团矿中配加适量赤铁矿的技术是可行的。