CuO／γ—Al2O3上NO吸附及其歧化反应的低温红外光谱研究

应用原位低温红外光谱技术，研究了ＮＯ在氧化态和还原态ＣｕＯ／γ－Ａｌ２Ｏ３催化剂上，从１５０℃到室温的吸附及其在表面上发生的反应。重点研究了歧化反应与温度的关系和歧化产物之－Ｎ２Ｏ在表面的吸附。     

CuO／γ—Al2O3上CO和NO吸附的红外光谱研究：Ⅱ.还原态

应用红外光谱技术研究了CO和NO及其混合气体在还原态CuO/γ-Al_2O_3上的吸附.XRD分析样品物相仅有Cu~0,但是,XPS和IR都证明样品表面上除Cu~0外,还有Cu~(2+)和Cu~+。CO以分子态的形式吸附在Cu~+和Cu~0上(低于173K,无NO存在时,CO可以吸附在Cu~(2+)上);NO以分子态吸附在Cu~(2+)上,在Cu~0上为离解吸附(173K以下,无CO存在时,NO可以吸附在Cu~+上)。CO吸附时,表面还生成HCO_3~-、CO_3~(2-)、HCOO~-,NO吸附时,除被氧化为NO3~-外,表面上还出现N_2O物种;高于室温时,CO和NO共吸附,表面上除生成HCO_3~-、CO_3~(2-)和N_2O外,还有NCO~-物种生成,讨沦了CO和NO反应的基本步骤。     

低温红外光谱研究CuO/γ-Al2O3上CO和NO选择性吸附

The low temperature infrared spectroscopy was applied to investigate the adsorp-tion of NO and CO on CuO/γ-Al_2O_3. The measured infrared bands were asigned. The results of alternate adsorption and coadsorption of NO and CO exhibited that Cu~(2+) and Cu~+ sites coexist on the surface of oxidized CuO/γ-Al_2O_3 and the selective ad-sorption of CO/Cu~+ and NO/Cu~(2+) was observed.     

Ru—Co—Mo／Al2O3还原催化剂：CO和NO吸附的红外光谱研究

本文采用CO、NO作为探针分子,应用红外光谱法对其在还原态Mo/Al_2O_3,Co-Mo/Al_2O_3,Ru-Mo/Al_2O_3,Ru-Co-Mo/Al_2O_3系列催化剂上的吸附态进行了表征。CO和NO在Mo,Co,Ru中心上的吸附峰随着它们的担载量增加而增强。Co和Ru作为助剂对Mo中心的吸附能力产生显著不同的影响,增加Co担载量大大减少了Mo中心的吸附NO量,并且NO在Co中心上的吸附红外谱带1775,1860 cm~(-1)位移到1800,1879 cm~(-1);而增加Ru担载量则加强了CO和NO在Mo中心上的吸附量,并使得NO在Mo中心上的吸附红外谱带1706,1812 cm~(-1)红移至1679,1801 cm~(-1)。根据实验结果,本文分别对Co和Ru的助剂功能进行了讨论。     

原位红外光谱研究Ni/Al2O3催化剂上CO的吸附态:Ⅰ.CO的倒式吸附态

CO在过渡金属上的吸附方式一般认为可分成三类:线式吸附态,桥式吸附态和多重键吸附态.这些吸附态的C—O伸缩振动具有红外活性,共振动频率分别位于～2050,～1950和～1700cm~(-1).但也有人认为CO在过渡金属表面上可能会形成倒式吸附态,即C—O键向表面倾斜,甚至平行于表面.例如,Dijk等曾推测在Ni/SiO_2催化剂上CO可能形成倒式双点吸附态(即C,O原子同时与表面成键).Krasser等用喇曼光谱研究CO在Ni/SiO_2上的吸附态时发现在330cm~(-1)处有一喇曼峰,认为这个峰可能来自倒式     

ZrO2对CuO／γ—Al2O3催化剂CO氧化性能的影响

用流动反应法、TPR、TPO和TG等技术研究了ZrO2的改性和CuO负载量对Cuo／y－Al2O3催化剂的氧化性能及还原行为的影响．实验结果表明，在低负载量（wCuO=15%以下）时，ZrO2对γ-Al2O3的改性可明显提高CuO／γ-Al2O3催化剂的CO氧化活性．ZrO2的存在可增加活性铜物种在载体表面的富集和有效地促进CU2+物种的氧化还原循环，增加CuO催化剂表面上铜物种的可还原量，从而促进CuO催化剂的氧化活性．     

CuO/γ-Al_2O_3上CO和NO吸附的红外光谱研究——1.氧化态

应用红外光谱研究了CO,NO及其混合气在氧化态CuO/γ-Al_2O_3上的吸附。用XPS测量了表面铜的价态,用XRD分析了催化剂的物相。综合实验结果可知,催化剂体相为CuO,,CuAl_2O_4,,而Cu~+和Cu~(2+)则在样品表面上并存。红外光谱显示,CO在Cu~+上的吸附比在Cu~(2+)上的吸附强,而NO在Cu~(2+)上的吸附比在Cu~+上的吸附强。当CO和NO共存在体系中,CO选择吸附在Cu~+上,而NO选择吸附在Cu~(2+)上。高于室温时,除分子态吸附外,CO在催化剂表面上部分氧化为HCO_3~-,,CO_3~(2-)以及少量HCOO~-,NO吸附,被氧化为NO_3~-。CO和NO共吸附,CO抑制了NO的氧化。     

Effects of Carrier on CuO／TiO2 and CuO／Ti0.5Zr0.5O2 Catalysts in the NO＋CO Reaction

Using TiO2 and Ti0.5Zr0.5O2 as carriers, the CuO/TiO2 and CuO/Ti0.5Zr0.5O2 catalysts were prepared by the impregnation method with Cu(NO3)2 as active component. The catalytic activities in NO CO reaction were investigated using a microreactor-GC system, and structure and reducibility of catalysts were characterized by means of physical adsorption, TPR, XRD, NO-TPD technologies. It was found that the activity of CuO/Ti0.5Zr0.5O2 catalyst was higher than that of CuO/TiO2, probably due to the large specific surface area of Ti0.5Zr0.5O2 that played an important role in NO CO reaction.     

RhCo双金属催化剂的研究 Ⅱ. Rh+Co/Al2O3上CO吸附态的动态行为与CO歧化

利用CO与NO作为双探针分子和TP-IR动态方法研究了Rh+Co/Al2O3催化剂上的吸附中心类型, CO吸附态的动态行为以及CO歧化反应。结果表明在Rh+Co/Al2O3上存在大量的孪生CO吸附中心和少量的线式CO吸附中心以及Co上的NO吸附中心。在TPD(真空中)动态过程中, 孪生CO谱带强度逐渐减弱并在325℃完全脱除。明显低于Rh4/Al2O3上孪生CO谱带的脱附温度, 表明Co的加入减弱了孪生中心对CO的吸附强度。在TP(CO中)动态过程中, 吸附的CO谱带上250℃以上才发生强度减小直至消失的行为表明CO歧化在250℃以上才发生。并且孪生中心上的歧化速率高于线式中心。     

CO／H2合成甲醇CuO—ZnO—ZrO2催化剂的研究

通过活性测定，ＸＲＤ、ＴＧ－ＤＴＡ表征，考察了共沉淀法制备的铜锌锆合成甲醇催化剂中ＺｒＯ２对物相结构、催化活性及热稳定性的影响。结果表明，ＺｒＯ２能显著提高ＣＯ／Ｈ２合成甲醇的催化活性和热稳定性。催化剂母体、氧化态和还原态的物相并未发生变化，仍分别为：Ｃｕ２（ＯＨ）３ＮＯ３，（Ｃｕ，Ｚｎ）５（ＣＯ３）２（ＯＨ）６，（Ｃｕ，Ｚｎ）２ＣＯ３（ＯＨ）２，Ｚｎ５（ＣＯ３）２（ＯＨ）６；ＣｕＯ、ＺｎＯ；Ｃｕ     

氧化铈对Cu—Mn—O催化剂吸附NO,CO性能的影响

运用微反和程序升温脱附（ＴＰＤ）技术研究了ＣＯ＋ＮＯ在Ｃｕ－Ｍｎ－Ｃｅ－Ｏ（Ⅱ）催化剂上的动力学特性和ＮＯ，ＣＯ，ＣＯ２和Ｎ２Ｏ在催化剂表面的吸附行为。对于ＣＯ＋ＮＯ反应，催化剂（Ⅱ）比（Ⅰ）具有较高的活性、在高转化率范围，差别更明显，对于（Ⅰ），ＮＯ的消除速率ｒＮＯ对ｃＮＯ，ｘＣＯ和ｃＣＯ２的级数分别为０．７５、０．９５和－０．２８。氧化铈加入（Ⅰ）后，使ｒＮＯ对ｃＮＯ，ｃＣＯ的级数下降（分别为     

红外光谱研究CO在NiY沸石上的吸附

1.前言 关于负载过渡金属的沸石体系,其CO吸附态的研究较少。就已报导的几篇论文看,载镍沸石上CO的行为与载镍氧化物上大不相同。如在NiY沸石上,吸附CO时不仅在2170和2120cm~(-1)附近有吸收带,而且在更高的频率约2200cm~(-1)也呈现吸收峰;但在载镍氧化物体系上就观察不到。对上述3个峰的归属目前仍无定论。已经报导的也互相矛盾。为此,本文藉原位红外光谱探讨了CO在NiY沸石上的吸附,并通过与不载镍沸石和非晶形SiO_2 -A1_2O_3体系比较,对上述3个峰的归属提出初步看法。     

硫化态NiW/Al2O3催化剂加氢脱硫活性相的研究Ⅲ.低温CO吸附-原位红外光谱表征

 采用低温CO吸附-原位红外光谱法对硫化态和经过氢还原处理的W/Al2O3,Ni/Al2O3以及不同Ni含量的NiW/Al2O3催化剂进行了表征. 结果表明,在WS2相上的两个CO特征吸收峰分别位于2117和2066 cm-1处; 硫化镍上吸附CO的特征峰位于2098 cm-1处; NiW/Al2O3催化剂中引入的助剂Ni与WS2相之间相互作用,并分别在2128,2096和2078 cm-1处出现三个新的谱峰,标志着NiWS活性相的形成,并且NiWS相的量随着助剂Ni含量的增加而增大. 在不同温度下对NiW/Al2O3催化剂进行氢还原处理时发现,NiWS活性相在高温下逐步分解,并发生烧结. 以上结果有力地支持了前文中通过XPS,HREM和TPR等方法所获得的有关催化剂活性相的形成及其还原分解过程的表征结果.     

CuO／活性炭和Fe2O3／活性炭催化还原NO

ＣｕＯ／活性炭和Ｆｅ_２Ｏ_３／活性炭催化还原ＮＯ高志明，赵震，杨向光，吴越（中国科学院长春应用化学研究所长春１３００２２）关键词活性炭，还原，ＮＯ，氧化铜，氧化铁目前，对固定源的ＮＯ处理是采用Ｖ２Ｏ５／ＴｉＯ２作催化剂，ＮＨ３作还原剂的选择催化还原方...     

硫化MoO3／Al2O3甲烷化催化剂上不同吸附物种的作用

运用加压动态分析装置研究了硫化MoO_3/A1_2O_3,甲烷化催化剂上CO和H_2的吸附及反应。结果表明,在给定反应条件下催化剂上吸附的CO和H_2可分为可逆与不可逆两类,且对甲烷化反应有着不同的贡献。甲烷的生成是可逆吸附氢和不可逆吸附CO共同作用的结果。不可逆吸附氢与CO不生成甲烷,可逆吸附的CO加氢则与副产物乙烷等的生成密切相关。结合前人的动力学考察结果,解释了Mo系甲烷化催化剂与Ni系甲烷化催化剂要求不同反应压力的实质性原因。