结晶轮用Cu-Cr-Zr合金的低周疲劳性能

研究了轮带式连铸机结晶轮用Cu-Cr-Zr合金的低周疲劳性能及微观组织演变。试验所用Cu-0.65Cr-0.15Zr(质量分数,%)合金在氩气保护氛围下于中频真空铸造炉中进行制备,并依次进行均匀化、热轧、固溶和时效处理,得到最终状态的合金。采用疲劳试验研究不同总应变幅下合金的低周疲劳性能,并结合扫描电子显微镜(SEM)以及电子背散射衍射(EBSD)分析疲劳试验过程中合金的显微组织演变和裂纹扩展规律。结果表明：总应变幅为0.4%,0.6%和0.8%时,Cu-Cr-Zr合金的疲劳寿命分别为5777次,1185次和661次。经过拟合后,Basquin公式和Coffin-Manson公式可以分别描述合金的疲劳寿命与弹性应变幅和塑性应变幅之间的关系。Cu-Cr-Zr合金的疲劳断裂以穿晶断裂的形式,沿着晶粒中某些特定的晶面进行,因此疲劳裂纹在扩展过程中会发生偏折。     

CMSX-4单晶高温合金在不同温度下的低周疲劳行为

研究了单晶高温合金CMSX-4在中温760 ℃和高温950 ℃下的低周疲劳行为。结果表明：在760 ℃下合金具有较长的疲劳寿命和较高的疲劳强度,断裂后断面高度差大并与应力轴方向呈45°角,裂纹沿着{111}面扩展;而在950 ℃下合金具有较短的疲劳寿命和较低的疲劳强度,断面与应力轴垂直,裂纹沿着{001}面扩展。低周疲劳断口的扫描电镜结果表明, 760 ℃试样表面的微孔是主要的疲劳源,而950 ℃试样表面的氧化层是主要的疲劳源且呈现多源开裂。低周疲劳断口的透射电镜结果表明,中温760 ℃下位错具有的平面滑移和波状滑移的变形机制,是由位错的平面滑移向波状滑移转变的过程;而高温950 ℃下位错主要通过交滑移和攀移进行运动。     

TC17合金低周疲劳性能与低周疲劳断口形貌

研究了不同温度下TC17合金低周疲劳性能和断口形貌,确定了不同温度下合金低周疲劳曲线的数学表达式,分析了合金棒材低周疲劳断口形貌特征.     

K40S钴基高温合金的高温低周疲劳行为——Ⅰ.疲劳性能

研究了K40S钴基高温合金在700℃和900℃温度条件下由应变控制的高温低周疲劳行为，对循环应力-应变数据和应变-疲劳寿命数据进行了分析，进而给出了K40S合金在此温度范围的疲劳参数，结果表明：与传统X-40合金相比，K40S合金具有优异的抗高温低周疲劳性能；合金的应力-应变响应行为在700℃时，呈现为循环强化，而在900℃时，为初期强化随后软化，且随着总应变幅的增加，强化效果均增强，上述行为归因于循环形变过程中位错-位错，位错-析出相及固溶原子间的相互作用。     

K40S钻基高温合金的高温低周疲劳行为Ⅰ.疲劳性能

研究了K40S钴基高温合金在700℃和900℃温度条件下由应变控制的高温低周疲劳行为.对循环应力-应变数据和应变-疲劳寿命数据进行了分析,进而给出了K40S合金在此温度范围的疲劳参数.结果表明:与传统X-40合金相比,K40S合金具有优异的抗高温低周疲劳性能;合金的应力-应变响应行为在700℃时,呈现为循环强化,而在900℃时,为初期强化随后软化,且随着总应变幅的增加,强化效果均增强.上述行为归因于循环形变过程中位错-位错,位错-析出相及固溶原子间的相互作用.     

应变波形对Inconel 625合金低周疲劳性能的影响

在650℃以及拉压对称三角波(TR)、慢拉快压锯齿波(ST)和快拉慢压锯齿波(FT)3种应变波形下对Inconel625合金进行了低周疲劳实验,研究了合金在不同应变波形下的低周疲劳变形与断裂行为。结果表明:3种应变波形加载条件下,合金在0.3%～0.7%的外加总应变幅下均呈现循环硬化,其中在ST下的循环应力幅最高;采用锯齿波形时,由于拉伸蠕变分量和压缩蠕变分量的引入造成合金的疲劳寿命缩短;此外,合金的循环应力和应变之间呈现单斜率线性关系,且其塑性应变幅与弹性应变幅和疲劳寿命之间亦呈线性关系。利用扫描电子显微镜对Inconel625合金在3种加载波形下的低周疲劳断口形貌进行观察,结果表明,Inconel 625合金的疲劳裂纹萌生和扩展均是以穿晶方式进行的。     

一种新型粉末高温合金的低周疲劳行为与寿命预测模型分析

对一种新型第3代粉末高温合金A3在700℃、应变范围0.6%～1.4%试验条件下的低周疲劳性能进行了研究,分析了材料的循环滞后回线、Massing特性、循环应力应变响应、应变-寿命关系等特性。采用Manson-Coffin模型、拉伸滞回能模型、三参数能量模型对疲劳寿命数据进行拟合预测,结果表明Manson-Coffin模型的寿命预测精度最高,在3倍分散带以内。用扫描电子显微镜对疲劳源区观察,结果表明:低应变时疲劳源数量上呈现单源,高应变时呈多源特征;随应变量增大,疲劳源位置趋向于试样表面,裂纹扩展区面积减小,瞬断区面积增大。疲劳断口典型的3个区域观察结果表明:疲劳源四周存在较多河流状线,其为裂纹扩展方向,裂纹扩展区存在较多二次裂纹,瞬断区出现韧窝与解理断裂特征。A3合金的断裂模式主要为穿晶断裂。     

粉末冶金高温合金FGH97的低周疲劳断裂特征

研究了粉末冶金镍基高温合金FGH97在650℃,30—980 MPa,1 Hz实验条件下的低周疲劳断口的宏观及微观特征,裂纹源的类型及其形貌特征,以及裂纹源的位置、缺陷类型、形状和尺寸对低周疲劳寿命的影响.结果表明,在本次实验条件下该合金的低周疲劳寿命均超过了5000 cyc;统计得出,低周疲劳断口裂纹源在表面的试样占23%,在亚表面的占47%,在试样内部的占30%;裂纹源分平台、粉末颗粒、夹杂物3种类型,其中平台类型约占5%,粉末颗粒间断裂占15%,夹杂物占80%.由统计分析和计算得出,不同类型裂纹源对疲劳寿命的影响程度不同:夹杂物最严重,其次为异常粉末颗粒,再次为局部塑性变形.     

DZ40M合金高温低周疲劳性能及其断口分析

测定了定向凝固钴基高温合金ＤＺ４０Ｍ９０℃低周疲劳性能并观察了疲劳断口,结果表明,ＤＺ４０Ｍ合金具有较高的抗高温低周疲劳性能;疲劳裂纹起源于试样表面优先氧化的碳化物。基体中骨架状分布的碳化物阻滞裂纹扩展;氧化不仅促进疲劳劳裂纹的形成,而且加速了裂纹扩展。ＤＺ４０Ｍ合金的高温疲劳破坏机械疲劳与环境氧化双重和所致。     

Al-7Si-0．3Mg合金低周疲劳行为及其机理

研究了Al-7Si-0.3Mg铸造铝合金在不同等效应变幅值下循环加载时的低周疲劳行为,并用透射电镜(TEM)观察了疲劳失效试样的位错结构.结果表明,位错结构对应变幅值有很强的依赖性,疲劳失效试样的位错密度随应变幅值的增大而增大;由于位错间的交互作用及颗粒的钉扎作用,铸造铝合金表现出明显的循环硬化现象,高应变幅值下,硬化区可贯穿整个疲劳过程;试样的疲劳寿命随应变幅值的提高而下降,并且符合Manson-Coffin关系式.     

TC4钛合金电子束焊接头低周疲劳性能与断裂行为

文中比较了30 mm厚TC4电子束焊接头和母材的低周疲劳性能。试验结果表明,母材的低周疲劳性能稍优于接头,母材和接头的应变疲劳极限分别为0.49%和0.44%。对接头的疲劳断裂位置进行了观察,接头的疲劳断裂位置在焊缝。对接头和母材的疲劳断口进行了观察,疲劳裂纹源均出现在试样表面,疲劳裂纹扩展区均发现典型的疲劳辉纹,但接头的辉纹间距要小于母材,最后拉伸断裂区均发现韧窝,为韧性断裂。最后运用高分辨SEM对接头的组织进行了研究,母材为典型的双态组织,主要是由等轴α相和晶间β相构成,热影响区等轴α相边缘逐渐溶解,转变成较多的层状α’相,焊缝主要是由针状α’相组成的网篮状组织构成。     

Low cycle fatigue properties and cyclic deformation behavior of as-extruded AZ31 magnesium alloy

The low cycle fatigue(LCF)properties of as-extruded AZ31 Mg alloy were investigated under total strain amplitudes in the range of 0.4%-1.2%with strain rate of 1×10- 2s -1.Due to the twinning effect in compression during loading and the detwinning effect during unloading,the alloy showed an asymmetric hysteresis loop.The cyclic stress response exhibited cyclic hardening at high total strain amplitudes.The cyclic deformation behaviors were discussed using the Coffin-Manson plot,which divided the plastic strain amplitudes into the tension side and the compression side.Through the LCF tests that were started from either tension or compression under a total strain amplitude of 1.0%,the interaction between the twinning effect and dislocation was analyzed.The twinning effect during the LCF test and the variation of the dislocation density were investigated using optical microscopy and transmission electron microscopy,respectively.     

激光熔化沉积TC18钛合金的低周疲劳行为

研究激光熔化沉积TC18钛合金的室温低周疲劳行为。通过双重退火热处理制度获得的TC18钛合金显微组织由细小的片层状初生α相和转变β基体组成,且晶界α相不均匀。采用光学显微镜和扫描电子显微镜分析了低周疲劳试样疲劳断口以及纵截面。结果表明,在低周疲劳断口可以观察到多个裂纹源。主裂纹源区与次裂纹源区具有不同的断裂形貌。当裂纹沿着晶界α相扩展时,连续的晶界α相导致平直的裂纹扩展模式,而不连续的晶界α相导致曲折的裂纹扩展路径。     

多轴载荷下ZL101铝合金的低周疲劳行为

研究不同等效应变幅下ZL101铝合金在多轴比例和非比例载荷下的低周疲劳行为,并用透射电镜观察合金的疲劳行为中的位错结构。结果表明：合金在两种加载方式下均表现为循环硬化;在非比例载荷下合金表现出附加强化,但程度不明显;合金的疲劳寿命随等效应变幅的增加而降低,合金在非比例加载下的疲劳寿命低于比例加载时的疲劳寿命。对位错结构的观察表明,随等效应变幅度的提高,合金的低周疲劳位错结构从交叉位错带转化为位错胞,合金在非比例加载下更易形成位错胞结构。     

铸造钛合金ZTC4不同应变比下的低周疲劳行为

采用岛津液压伺服疲劳试验机研究了铸造钛合金ZTC4在不同应变比下(R=-1、0.06和0.5)的低周疲劳行为。对比分析了不同应变比下应力-应变迟滞回线、循环应力响应曲线以及疲劳寿命的差异,并采用SWT模型和Walker等效应变模型对不同应变比下的试验结果进行表征。结果表明:在200℃时,应变比为-1时,迟滞回线基本以原点对称,且随着应变水平的增大,迟滞回线包围的面积呈上升趋势;应变比为0.06和0.5时,滞后环沿坐标轴发生了平移,且随着应变水平的降低,迟滞回线沿拉应力的方向移动;不同应变比下合金的循环疲劳寿命相差甚微,SWT模型和Walker等效应变模型能很好的表征材料不同应变比下的疲劳试验结果,精度在±2倍的分散带内。     

等通道转角挤压处理的镁合金AZ31的低周疲劳行为

研究了一道次等通道转角挤压(ECAP)处理的镁合金AZ31挤压棒材的低周疲劳行为,结果表明:在塑性应变幡为0.5％时,材料表现出显著地循环软化;而在应变幅不大于0.2％时,基本表现为循环稳定或微弱的循环软化.疲劳裂纹主要萌生于细晶区,并沿着细晶区扩展,并导致最终的断裂.     

Low cycle fatigue improvement of powder metallurgy titanium alloy through thermomechanical treatment

A low-cost β type Ti-1.5Fe-6.8Mo-4.8Al-1.2Nd （mass fraction, %）（T12LCC） alloy was produced by blended elemental powder metallurgy（P/M） method and subsequent thermomechanical treatment. Low cycle fatigue（LCF） behavior of P/M T12LCC alloy before and after thermomechanical treatment was studied. The results show that the LCF resistance of P/M titanium alloy is significantly enhanced through the thermomechanical treatment. The mechanisms for the improvement of LCF behavior are attributed to the elimination of residual pores, the microstructure refining and homogenization.     

分接开关主驱动轴低周疲劳行为及断裂特性

针对分接开关主驱动轴球墨铸铁部件,系统研究了其低周疲劳性能及断裂特性。结果表明,EN-GJS-700-2球墨铸铁的疲劳寿命强烈依赖于施加的循环应变幅。进一步研究发现,疲劳寿命主要取决于循环应变幅中的塑性分量,以至于疲劳寿命与循环总应变幅满足Coffin-Manson方程。SEM断口形貌显示,不论是低应变幅还是高应变幅下,球墨铸铁表面处的球状石墨/珠光体界面是疲劳裂纹的优先萌生位置,并呈现出多源特征。在随后的裂纹扩展过程中,高应变幅断口平坦,解理断裂特征明显,难于观察到疲劳条纹。但在低应变幅下,球形石墨和珠光体显著参与塑性变形,疲劳条纹变得明显。     

不同Cr含量Cu-Cr-Zr合金的热拉伸变形行为

采用Gleeble-3810热模拟试验机进行高温热拉伸试验,研究了不同Cr含量的Cu-Cr-Zr合金在变形温度350～500℃,应变速率0.01～1 s-1范围内的流变行为.发现随着应变速率和Cr含量的升高以及变形温度的降低,Cu-Cr-Zr合金的流变应力呈现上升规律.对断口组织的分析发现,应变速率、变形温度以及Cr含...