时效温度对7050铝合金屈服强度的影响与本构模型研究

目的 预测不同时效条件下7050铝合金力学性能的演化规律,为多级快速时效热处理工艺提供理论基础。方法 分别在120、160、180℃温度下对7050铝合金进行0～8 h时效热处理,并进行室温单拉试验,获得相应时效条件组合的应力-应变曲线及屈服强度演化曲线,建立统一时效本构模型,模拟微观组织（沉淀半径、溶质浓度）的演化规律,根据微观组织的演化规律,模拟由析出强度与固溶强度组成的屈服强度的演化规律。结果 在不同时效温度下,模拟的屈服强度演化规律与试验结果基本保持一致,模拟的微观组织演化规律与理论分析结果基本保持一致。在160℃时效热处理8 h和180℃时效热处理2 h条件下得到了试验峰值屈服强度,分别为578.6 MPa和555.8 MPa,在模拟结果中也得到了相应的演化结果。在120℃下,屈服强度的试验结果与模拟结果均呈上升趋势。结论 所建立的统一本构模型考虑了时效温度、时效时间的影响,成功预测了不同时效温度条件下析出相半径、溶质浓度等微观变量的演化规律,这些变量都有助于预测合金析出强度与固溶强度的演化规律,进而成功预测了由这2个强度分量组成的屈服强度的演化规律。     

升温速率对2219铝合金蠕变时效行为的影响

研究2219铝合金在蠕变时效成形过程中,升温速率对其蠕变行为及力学性能的影响规律。实验模拟构件在热压罐中的升温条件,降低材料的升温速率(0.75℃/min),延长其升温时间至4h(某典型构件真实蠕变时效升温时间),分别在0,150,210MPa 3种应力条件及不同的时效时间下进行蠕变实验,并对材料拉伸力学性能和微观组织(TEM)进行分析。结果表明:对比在材料尺度下0.5h的升温条件(5.5℃/min),升温速率的降低,在一定程度上提高了材料的力学性能,并且延长了材料强度达到峰值的时间;铝合金析出相的形状因子随着时效时间呈现先增长,到达峰值后下降的趋势;降低升温速率,材料在升温阶段即已发生了显著蠕变形变,在150MPa和210MPa应力条件下升温阶段的蠕变量分别占总蠕变量的29.28%和21.56%,且蠕变变形量和稳态蠕变速率会随着应力的升高而增加;由此,基于材料尺度(标准蠕变试样)的蠕变时效研究,用于表征构件尺度蠕变时效行为时,须进一步考虑升温速率对其成形及性能演变的影响。     

铝合金时效成形及时效成形铝合金

介绍了铝合金时效成形的方法、基本原理、工艺特点及应用情况,概括了国外研究铝合金时效成形工艺及相关可时效成形铝合金的现状,重点阐述了时效成形对铝合金微观组织结构的影响.     

时效成形对2324铝合金组织及性能的影响

研究了时效成形对2324铝合金力学性能的影响,利用透射电镜观察了时效成形过程中的微观组织.研究了时效成形产生的"应力位向效应"及其对力学性能的影响,对"应力位向效应"的特征和产生原因进行了分析.结果表明:由于外加应力造成了平行应力方向和垂直应力方向扩散系数的差异,导致析出相择优生长.无应力时效时析出相沿{201}晶面族均匀析出,时效成形过程中析出相沿平行(111)方向择优生长,择优生长方向主要取决于外加应力的方向.     

7050铝合金时效成形中应力松弛行为与回弹方程

通过自主设计的单向拉伸应力松弛装置研究7050铝合金时效成形过程中的应力松弛行为和回弹方程。结果表明:时效温度范围内7050铝合金的应力松弛曲线表现为典型的对数衰减曲线。该松弛过程可以分为应力快速下降,应力缓慢衰减和应力保持相对恒定3个阶段。随着温度的升高应力松弛极限逐渐降低。由于7050铝合金时效析出与应力松弛中位错蠕变的共同作用引起了松弛过程槛应力现象。通过解析7050铝合金应力松弛行为的特征和松弛曲线的泰勒方程得到该合金在时效温度范围内的应力松弛经验公式,以此获得该合金时效成形过程中的应力松弛方程,并利用该经验公式较好地预测时效成形后试样的回弹率。     

预处理对2124铝合金板材蠕变时效微结构与力学性能的影响

研究了预处理(15%预变形+100℃×5h预时效)对2124铝合金板材蠕变时效成形微结构与力学性能的影响。结果表明,富Fe(Si)杂质相粒子在蠕变成形过程中会因应力集中效应而破碎,从而改善材料性能,固溶-淬火后直接进行蠕变时效处理,θ′相在{100}面上的析出行为呈现出明显的应力位向效应,但基体中存在的弥散第二相粒子周围存在着很大的晶格畸变能,能促进析出第二相的形核、长大,局部降低应力位向效应。在本研究条件下,预处理使得{111}面上析出了Ω强化相,显著提高了2124铝合金蠕变时效后的强度,但不会显著降低延伸率。     

Al-Zn合金热成形本构模型

目的 表征Al-Zn合金在预时效强化温热成形工艺下的流动行为。方法 利用MMS200热模拟机对Al-Zn合金进行热拉伸试验,变形参数分别为变形温度180~220 ℃、应变速率0.01~1 s^?1。通过对试验值进行修正,可得到不同变形条件下的真应力-应变曲线,并建立应变补偿的含Z参数本构模型和PSO-BP人工神经网络本构模型。结果 Al-Zn合金热变形过程中呈现正的应变速率敏感性和热软化效应;应变补偿的含Z参数本构模型的R值和EAARE值分别为0.961和8.761%;而PSO-BP人工神经网络本构模型的R值和EAARE值分别为0.993 5和2.51%。结论 PSO-BP人工神经网络本构模型的预测值和试验值高度吻合,拥有更准确、更快速的数据采集和分析能力,对铝合金及其他合金材料的热变形行为预测有着重要意义。     

封面图片说明

封面图片出自论文“工艺参数对7075铝合金板材时效成形性的影响”。为了从微观上探索工艺参数对7075铝合金时效成形后室温拉伸性能的影响情况,对不同时效制度下成形后试件的拉伸断口进行断裂刃口形貌观察。这幅图片为7075铝合金板材在时效制度为180℃／12 h下时效成形后试样的拉伸断口微观扫描形貌,可以看出,断口形貌主要由韧窝组成,并存在高低不一的剪切台阶,韧窝是等轴的,大小不均匀,在高倍扫描下可观察到尺寸较大的韧窝底部残存一些破碎的第二相颗粒,这些说明粗大第二相引发的韧窝断裂是过时效后期的主要断裂方式。该图片反映了过时效后期粗大第二相颗粒析出诱发的韧窝断裂。     

2A12铝合金筋板件T型搅拌摩擦焊工艺及焊后热处理

为评价2A12铝合金筋板件搅拌摩擦焊工艺并探寻提高接头强度的途径,进行了2A12铝合金筋板件的T型搅拌摩擦焊焊接工艺试验,并对不同人工时效热处理下焊接接头的微观组织及性能进行了研究.研究表明:采用T型搅拌摩擦焊即可实现2A12铝合金筋板件的成形,当搅拌头旋转速度为750 r/min、焊接速度60mm/min时,接头的抗...     

3003铝合金蠕变行为与本构方程

研究了3003铝合金冷轧变形后再结晶组织控制和175~250℃、外加应力25~50 MPa条件下3003铝合金的蠕变行为。采用弹性模量归一化应力幂律蠕变本构方程,对实验数据进行线性拟合,建立了能够较好描述稳态蠕变速率与应力、温度三者之间关系的本构方程。结果表明:采用350℃和600℃的两步再结晶退火,可获得有利于提高合金蠕变性能的长条状再结晶组织;温度越高,应力增加对稳态蠕变速率增加的贡献越大;不同温度下3003铝合金的蠕变机制不同,175℃时,应力指数n=3.5,蠕变主要由位错滑移控制;在200~250℃范围内,n处于5.1~8.6之间,蠕变主要由位错攀移控制。     

SiCw／7475Al复合材料时效硬化研究

通过硬度测试，结合ＤＳＣ曲线，对ＳｉＣｗ／７４７５Ａｌ复合材料的时效析出过程进行了研究。结果表明，与基体合金相比，复合材料的时效硬化效果较代，最佳人工时效温度提高，析出过程稍有延缓，分析认为，该复合材料时效特征与增中相引入的高密度位错，析出相与基体位错的相互作用有密切关系。     

促进剂对浅色硫化橡胶抗老化及耐黄变性能的影响

以红外光谱(FT-IR),扫描电镜(SEM),紫外线照射和热老化方法研究了促进剂对硫化胶的力学性能、抗紫外线、耐热老化以及耐黄变性能的影响,其结果表明,促进剂对浅色硫化胶的抗紫外线和耐热老化能力有决定性的功能作用,紫外线照射和受热使橡胶表面发生氧化而黄变和开裂,并使力学性能劣化。253.7 nm紫外线照射可作为快速测试、评判和预示白色或浅色硫化胶的抗紫外线、耐热老化以及耐黄变能力的方法。     

Initial age of unlicensed motorcycling experience for a cohort of high school students

The aim of this study is to use retrospective data to examine the initial age of unlicensed motorcycling experience for a cohort of senior high school students in Taiwan. The life-table method was applied to estimate the probability of unlicensed motorcycling at different age intervals below the minimum licensing age. The results indicated that an increase in the prevalence of unlicensed teenage motorcycling began at 10 years of age and peaked in the ages between 16 and 17 years. Only 38% of students had no motorcycle riding experience when they reached the minimum licensing age of 18 years. Gender and parental attitude were the factors that had a significant influence on the initial motorcycling age. In addition, we observed a significant difference between licensed and unlicensed students in the following areas: parental attitude, proportion of students using borrowed motorcycles, and riding and accident frequency. The results reveal a number of important implications, such as the promotion of alternative modes of transport, increased parental monitoring, and penalty enhancement, that may help to suppress the tendency of teenagers' unlicensed motorcycling.     

具有吸毒年龄和治疗年龄的海洛因模型的全局稳定性（英）

本文建立了一个吸毒人群具有吸毒年龄,治疗人群具有治疗年龄的海洛因传播模型．得到了基本再生数．通过波动引理和李雅普诺夫泛函,证明了当基本再生数小于1时无海洛因吸食平衡点是全局渐近稳定的,当基本再生数大于1时,海洛因传播平衡点是全局渐近稳定的．     

Age of drinking onset, driving after drinking, and involvement in alcohol related motor-vehicle crashes.

This study assessed whether persons who begin drinking at younger ages are more likely to report drunk driving and alcohol-related crash involvement over the life course, even after controlling analytically for diagnosis of alcohol dependence, years of drinking alcohol, and other personal characteristics associated with the age respondents started drinking. A national survey asked 42,862 respondents the age that they started drinking, whether they drove after drinking too much, and whether they were in motor-vehicle crashes because of their drinking. This analysis focused on 27,081 (65%), who reported ever drinking in their lifetime. The earlier the age respondents started drinking, the more likely they were to report driving after drinking too much and being in a motor-vehicle crash because of their drinking even after adjusting for current/ever diagnosis of alcohol dependence, number of years respondents had been drinking, and other characteristics and behaviors associated with the age respondents started drinking. Particularly, among persons who were never alcohol-dependent, those who began drinking in each age group under 21, relative to those starting at age 21 or older, were more likely to report "ever" and "in the past year" being in a crash after drinking too much. The traffic safety benefits of delaying drinking may extend well beyond the legal drinking age of 21.     

数字时代背景下标志设计的动态化发展

分析了数字时代背景下标志设计已进入动态化发展,论述了标志设计动态化的具体表达,进而分析了动态化的标志视觉表达、二维表现、网站表现、新媒介表现,并结合动态化、多元化的终端进行展示。在此基础上,提出了数字时代背景下标志设计动态化发展的意义,以及运用多种媒体的交互表达已成为人们一种极其强烈的心理及审美需求,从而推动标志设计的动态化发展。     

信息时代汽车展示的交互设计研究

目的实现汽车展示设计由传统的以汽车为主体的静态展示向以人的体验为主体的转变,体现信息时代汽车展示设计的特征和设计方式。方法通过分析信息时代汽车展示设计特点,归纳出交互设计在信息时代汽车展示设计的重要性和作用。结论动作交互、数据交互、声音交互、图像交互等交互设计方式可以运用到汽车展示设计中,并能够取得很好的展示效果,吸引观众的注意力,有效传递汽车信息。     

室温强塑性变形下回溶和再析出的机理研究

为了研究室温强塑性变形下回溶和再析出的机理,利用透射电镜、硬度测量等手段,采用压缩变形方法对Al-Zn-Mg-Cu铝合金在强塑性变形下第二相的回溶和再时效过程进行了观察.研究结果表明:强塑性变形过程中存在第二相回溶和再析出的交替过程;由强变形产生的过饱和固溶体再时效时,在高密度的缠结位错区或者等轴超细晶粒的边界上直接析出平衡相η.     

Age Hardening in Rapidly Solidified Al-V-Zr Alloy

Rapidly solidified Al-3.9V-0.1 Zr alloy is a single sol-id solution.The metastable limited solid solubility ofsolute V in Al reaches 3.9 wt-% under about 10~6 K/scooling rate.A strong age hardening response have beenobserved in this alloy.A large amount of dislocation linesand loops were observed in the alloy aged at 100-150℃:and an age peak occurs at 450℃,the hardness value in-creases by a factor of 2.The precipitate which is responsi-ble for age hardening is identified to be Al_V(Al).