石灰掺量、熟料C3S含量和细度对水泥性能的影响

本文就石灰石掺量（0%、5%）、熟料C3S含量和水泥细度（90μm筛筛余2%、5%）对水泥性能的影响进行了交叉试验。结果表明,90μm筛筛余相同的样品，掺加5%石灰石后，比表面积增加约45m^2/kg；标准稠度需水量下降约0.5%，与C3S含量低的熟料A结合，初凝时间缩短约50min。而与C3S含量高的熟料B结合，初凝时间只缩短约25min，对终凝时间的影响量大；掺5%石灰石后，早期抗压强度增加，28d抗压强度有所下降，但早期强度受熟料类型的影响更大，对水化热的影响，掺5%石灰石影响不明显，而与熟料B结合，水化热增大，细度筛余值越小，水化热越大，但14d后水化热随石灰石掺量的增加而有所下降。     

石灰石掺量、熟料C3S含量和细度对水泥性能的影响

本文就石灰石掺量(0％、5％)、熟料C3S含量和水泥细度(90μm筛筛余2％、5％)对水泥性能的影响进行了交叉试验。结果表明,90μm筛筛余相同的样品,掺加5％石灰石后,比表面积增加约45m2/kg;标准稠度需水量下降约0.5％;与C3S含量低的熟料A结合,初凝时间缩短约50min,而与C3S含量高的熟料B结合,初凝时间只缩短约25min,对终凝时间的影响更大;掺5％石灰石后,早期抗压强度增加,28d抗压强度有所下降,但早期强度受熟料类型的影响更大;对水化热的影响,掺5％石灰石影响不明显,而与熟料B结合,水化热增大,细度筛余值越小,水化热越大,但14d后水化热随石灰石掺量的增加而有所下降。     

不同C_3S含量阿利特-硫铝酸盐水泥熟料与粉煤灰混合材的适应性研究

研究了不同C3S含量的阿利特-硫铝酸盐水泥熟料与粉煤灰混合材的适应性。结果表明：C3S含量一定时,随粉煤灰掺量增加,水泥的凝结时间延长,抗压强度降低;粉煤灰掺量一定时,随C3S含量的增加,水泥的凝结时间延长,抗压强度增大;C3S含量增大时,随着粉煤灰掺量增多,水泥各龄期抗压强度降幅减小;掺加粉煤灰后水泥的早期抗压强度降低幅度较大,后期抗压强度降幅较小。熟料中C3S含量低时,对高粉煤灰掺量的适应性差;C3S含量高时,其适应性好。     

用石灰石作混合材生产硅酸盐水泥的试验

本文较系统地研究了石灰石掺量，熟料掺量，石膏掺量及熟料细度等因素对利用石灰石作混合材生产硅酸盐水泥强度的影响；找出了影响该品种水泥强度的主要因素和生产的最佳条件，并对石灰石硅酸盐水泥的性能进行了初步探讨。     

影响低需水量水泥性能的几个因素

采用立窑水泥熟料、矿渣和石膏，掺加适量助磨减水外加剂，研制了新型低需水量水泥。研究了粉磨工艺、细度及SO_3含量对低需水量水泥性能的影响。结果表明，当采用混磨工艺，比表面积大于500m～2／kg,SO_3含量3.0％～3.5％，矿渣掺量达40％时，仍可获得28d抗压强度高于50～60MPa的水泥，用这种水泥可直接配制C50～C60高流态混凝土。     

SO3掺杂对高镁熟料中方镁石含量,C3S晶粒尺寸及晶型的影响

随着水泥行业的快速发展,高品质石灰石成为日趋紧缺的资源,合理有效地利用高镁质石灰石原料煅烧水泥熟料又被赋予更加重要的资源综合利用的意义.本文借助化学分析、岩相分析、胶砂试验研究、XRD等检测方法等,探讨了不同掺量的SO3对高镁熟料中方镁石含量、C3S晶粒尺寸及晶型的影响.结果表明:适当的SO3掺加量能够有效减少高镁熟料中方镁石含量,有利于高镁熟料中氧化镁的固溶,促进C3S晶粒尺寸的增大,稳定熟料中M1型C3S,提高熟料的力学性能,在SO3掺量为1％时,得到的熟料力学性能最好,为高镁石灰石今后在水泥行业的利用提供一定理论和实验依据.     

基于正交试验的小掺量超细石灰石粉对混凝土抗压强度的影响分析

采用正交试验的方法对小掺量超细石灰石粉混凝土抗压强度进行试验研究,讨论了超细石灰石粉取代率、细度和取代成分三因素三水平对混凝土各个龄期的抗压强度的影响规律。试验结果表明:通过极差分析可知,各因素对小掺量石灰石粉混凝土各个龄期的抗压强度影响程度的主次顺序为:超细石灰石粉取代率超细石灰石粉取代成分超细石灰石粉细度,有利于混凝土抗压强度发展的最优配合比为A3B1C1;通过方差分析可知,超细石灰石粉取代率对混凝土抗压强度有一定影响,超细石灰石粉细度及取代成分对混凝土抗压强度无显著影响;兼顾抗压强度和经济因素的最优配合比为A3B2C1,即超细石灰石粉取代率为10…%,超细石灰石粉细度为45…μm,超细石灰石粉取代成分为水泥。     

超细熟料活性效应及充填效应对石灰石硅酸盐水泥性能影响

为提高水泥熟料的有效利用率,降低水泥生产成本,改善石灰石硅酸盐水泥性能。用超细熟料、石灰石粉配制了石灰石硅酸盐水泥,在此基础上,研究了超细熟料充填效应对石灰石硅酸盐水泥堆积密实度、净浆流动性和胶砂强度的影响,以及超细熟料活性效应对胶砂强度和水化产物的影响。结果表明:超细熟料-石灰石粉复合水泥的颗粒充填堆积密实度与净浆流动性有一定的关联性,即堆积密实度越大越能改善净浆流动性;与普通细度水泥熟料对比,超细熟料具有更高的水化活性,提高了复合水泥的抗压、抗折强度,超细熟料掺量为30%时各龄期的活性效应最为理想;超细熟料的填充密实效应提高了复合水泥胶砂强度,当超细熟料掺量为30%时填充效应对强度影响最显著;与普通细度水泥熟料对比,超细熟料中的C_3A与石灰石粉中的CaCO_3反应生成了更多的水化碳铝酸钙。     

阿利特-硫铝酸盐自应力水泥的试验研究

根据阿利时－硫铝酸盐熟料具有快凝，早强，高强和微膨胀的特性，用其全部或部分代替强度组分和膨胀组分，试验研究了阿利特－硫铝酸盐自应力水泥。试验结果表明其技术可行；水泥强度，膨胀等性能主要取决于熟料中C3S和C4A3S含量及水泥中石膏掺量（可用石灰石部分代替石膏作缓凝剂）。     

C_3S含量变化对浆体强度及体积收缩的影响

为了研究硅酸三钙（C3S）含量对水泥浆体的抗压强度及线性收缩的影响,制备了不同C3S含量的水泥,并通过热质量损失法（TG）、扫描电镜（SEM）等方法分析了浆体中Ca（OH）2含量的变化规律和水化产物形貌,讨论了C3S含量对浆体基本性能的影响.结果表明：C3S质量分数为78.79%的水泥浆体水化过程中产生较多且晶粒尺寸较小的Ca（OH）2,其后期抗压强度出现倒缩.水化7 d时,C3S质量分数为67.33%的波特兰水泥抗压强度最大,28 d后C3S含量低的水泥的抗压强度可超过高C3S水泥浆体;加入质量分数为50%的粉煤灰后,熟料中C3S质量分数为67.33%的水泥浆体始终具有最高的强度.水泥浆体的线性收缩随着熟料中的C3S含量的增加而变大.从水泥硬化浆体的性能和节能方面考虑,熟料中C3S质量分数为67.33%较优.     

熟料中SO3对水泥性能的影响

新绛威顿水泥有限责任公司有拥1条1000t／d熟料的新型干法水泥生产线。因其所用燃煤w（SO3）较高，矿点杂，导致熟料中w（SO3）普遍较高且波动较大。文章以2002年～2004年生产数据为依据，对该厂熟料中SO3量高低对水泥性能的影响进行了归纳和分析，发现随着熟料中SO3量的增多，熟料凝结时间缩短，28d抗压强度有所增加，3d抗压强度基本无影响。所以，当熟料中SO3量变化较大时，要相应调整水泥中SO3的加入量，以保证水泥凝结时间的正常。     

Superplasticized portland cement: production and compressive strength of mortars and concrete

This paper deals with the effect of intergrinding different percentages of a naphthalene-based superplasticizer with Portland cement clinker and gypsum on the fineness of the product, and on the water requirement and the compressive strength of the mortars made with the superplasticized cement. The properties of the fresh and hardened concrete made with the superplasticized cements were also investigated. The results showed that the intergrinding of a given amount of a naphthalene-based superplasticizer with Portland clinker and gypsum reduced the grinding time required for obtaining the same Blaine fineness as that of the control Portland cement without the superplasticizer. The water requirement of the mortars made with the superplasticized cements was similar to that of the mortars made with the control Portland cements when the same amount of the superplasticizer was added at the mortar mixer; for a given grinding time and a Blaine fineness of 4500 cm²/g, the mortars made with the superplasticized cement had higher compressive strength than those made with the control Portland cement. For a given grinding time or Blaine fineness of cement ≥5000 cm²/g, the slump loss, air content stability, bleeding, autogenous temperature rise, setting times, and compressive strength of the concrete made with the superplasticized cements were generally comparable to those of the concrete made with the control Portland cements when the superplasticizer was added at the concrete mixer.     

浅谈预拌砂浆对水泥的评价与选择

通过两种不同水泥配制成干混砂浆的性能对比,研究了水泥对砂浆保水性、稠度、2 h稠度损失、分层度、含气量、凝结时间、黏聚性、流动度、强度等性能的影响。结果表明:水泥细度对砂浆稠度、分层度、含气量有明显影响;水泥混合材种类与掺加量影响砂浆的保水性、黏聚性;水泥熟料矿物组成影响砂浆保水性;水泥凝结时间影响砂浆凝结时间、2h稠度损失等。而且这些影响不是孤立的,每个水泥参数可能对砂浆多种性能产生作用,故建议水泥生产应根据砂浆需求提供个性化的产品;砂浆企业应根据砂浆品种和施工条件选择合适的水泥品种。     

用矿渣微粉配制高掺量早强矿渣水泥的研究

通过正交试验研究不同细度、掺量的矿渣微粉和熟料对渣水泥性能的影响。试验发现,影响矿渣水泥3d、28d强度的主次因素不同,3d强度主要受矿渣细度的影响,28d强度则主要受矿渣掺量影响。采用分别粉磨后混合的生产工艺,用一定细度的矿渣微粉可以生产出掺量较高、早强性能好的矿渣水泥。     

影响预拌混凝土专用水泥性能的因素及改善途径

影响预拌混凝土专用水泥性能的因素有:水泥矿物组成与化学成分;熟料的碱含量及煅烧气氛;水泥调凝剂;掺用混合材的种类及细度;水泥的细度、温度及存放时间等。改善途径包括:对水泥生产原料进行超前控制;优化熟料矿物组成、烧成温度、烧成速度及冷却速度;优化水泥颗粒级配;合理控制出厂水泥的强度值,确保水泥均匀性。     

Investigation of the effects of fatty acids on the compressive strength of the concrete and the grindability of the cement

In cement industry, a great energy consumption has been observed during grinding of clinker. To reduce this consumption, some waste products have been used as grinding aids.In this investigation, the effects of sunflower oil (SO), oleic acid (OA), stearic acid (SA), myristic acid (MA) and lauric acid (LA) on the fineness and strength of the cement have been examined. These aids were added into clinker in certain ratios based on the cement clinker weight and the grinding has been done for a definite time at the same condition.All of the fatty acids used increased the fineness as compared with the cement without the grinding additives. SO and OA decreased the strength significantly, LA decreased it to a lesser extent and SA increased it definitely according to the common cement. But MA did not alter the strength of the cement as much as SA. In addition, the covering of the balls influences the grinding of cement clinker unfavourably.     

熟料及矿物掺合料对复合水泥最早期强度的影响

研究了不同品种熟料及细度,粉煤灰、矿渣粉及钢渣粉对复合水泥最早期强度的影响.研究表明:随熟料细度提高,水泥24h内最早期强度有明显提高.在化学组成及含量接近的情况下,熟料品种对水泥最早期强度影响不明 显.掺加粉煤灰、矿渣粉和钢渣粉等矿物掺合料后,复合水泥浆体最早期强度均有明显降低,但12h后复合水泥与纯硅酸盐水泥...     

高性能粒度调配水泥及其在混凝土中的应用研究

通过设计和调配水泥组分的细度和颗粒分布,制备了一种高性能粒度调配水泥,并测试了该水泥及其配制的混凝土的物理力学性能。试验结果表明:粒度调配水泥的标准稠度用水量与普通球磨水泥相当;在相同熟料含量条件下,粒度调配水泥比对比水泥的抗压强度提高3～4MPa;在混凝土应用中,粒度调配水泥和普通球磨水泥相比具有更为明显的性能优势,利用粒度调配水泥配制的C60高强混凝土不但工作性能良好,而且力学性能优异,28d抗压强度达到了96.1MPa。     

少熟料磷渣水泥的研究

试验研究了少熟料磷渣水泥强度的影响因素,结果表明,复合外加剂四组分Ｎ、Ｇ,Ｓ,Ｆ的配比为３：４：５：４时,对少熟料磷渣水泥的抗压强度最有利,生产该水泥的适宜工艺参数为：外加剂掺量１２％￣１４％,水泥细度４００ｍ＾２／ｋｇ。混合粉磨有利于外加剂的均匀分散,从而有利于水泥强度的提高。测试了少熟料磷渣水泥的物理力学性能,孔结构性能,干缩性能和抗侵蚀性能,并与硅酸盐水泥进行了相应的对比。     

利用工业废渣制备复合水泥的研究

采用分别粉磨再混合的方式,利用正交试验方法,研究了熟料、矿渣及粉煤灰的不同细度组合对复合硅酸盐水泥物理性能的影响。结果表明,熟料细度是影响复合水泥3d强度的决定因素;影响水泥28d强度的主次因素依次为:矿渣细度、熟料细度、粉煤灰细度。得到了复合水泥3种主要组分的细度最佳控制参数为:熟料420m2/kg,矿渣500m2/kg,粉煤灰400m2/kg。并对复合水泥水化各龄期的试样进行了SEM分析。