高碳马氏体不锈钢M390与奥氏体不锈钢304闪光对焊的微观组织及力学性能

通过闪光对焊方法连接M390高碳马氏体不锈钢与304奥氏体不锈钢.通过室温拉伸试验、显微硬度测试表征了焊接接头的力学性能.采用扫描电镜(SEM)、能谱分析(EDS)和X射线衍射(XRD)分析了焊接接头的微观组织形貌、元素扩散及各区域相组成.结果表明,利用合适的焊接工艺参数,M390与304之间可以形成焊缝形貌美观、抗拉...     

工艺参数对304不锈钢焊接接头组织性能的影响

采用光纤激光器对0.8 mm厚的304不锈钢薄板进行对接焊接试验,研究工艺参数对焊接接头的组织及力学性能的影响.基于两因素两水平的正交试验,以焊缝宽深比、显微硬度为指标,获得最佳焊接工艺参数,即焊接速度1300mm/min,激光功率1000 W.结果表明,焊接速度和激光功率对焊缝宽深比呈负相关性.焊缝中心为均匀、细小的...     

中低温热处理对SUS304不锈钢TIG焊接接头组织及力学性能的影响

轨道交通车辆在冲击振动试验后,部分设备SUS304不锈钢焊接件出现断裂失效现象.为了提升SUS304不锈钢焊后机械性能,采用金相显微镜、扫描电镜、硬度测试及拉伸试验等方法,研究了中低温热处理工艺对2 mm厚SUS304不锈钢板TIG焊接接头的组织及力学性能的影响.研究发现,经400℃热处理30 min及焊接后未处理态焊...     

T92/Super304H异种钢焊接接头的组织结构和力学性能

采用钨极氩弧焊(GTAW)技术,采用ERNiCr-3和ERNiCrMo-3两种镍基焊丝实施T92/Super304H异种钢焊接,并对接头的显微组织结构及力学性能进行测试分析。结果表明:T92侧热影响区(HAZ)中粗晶区析出大量的第二相颗粒,细晶区则为细小的索氏体组织;Super304H侧HAZ奥氏体晶粒长大,晶界析出明显;ERNiCr-3焊接的焊缝组织呈胞状结构,晶粒粗大;ERNiCrMo-3焊接的焊缝组织呈柱状晶组织特征。ERNiCrMo-3焊接的接头强度、塑性及硬度较大,拉伸断裂位于Super304H母材;而ERNiCr-3焊接的接头强度、硬度较低,但冲击韧性较高,拉伸断裂位于焊缝。     

A6N01铝合金焊接接头的微观组织与力学性能

对高速列车车体用新型A6N01铝合金进行MIG焊接,使用光学金相(OM)、扫描电镜(SEM)、透射电镜(TEM)、显微硬度计和拉伸试验机对焊接接头的显微组织与力学性能进行观察与分析。结果表明:焊缝金属为等轴晶状的铸态组织,焊缝边缘的熔合区形成柱状晶组织。在热影响区(HAZ),过时效区的晶粒比淬火区的更为粗大,形成HAZ软化区。A6N01铝合金母材析出短棒状β′(Mg2Si)过渡强化相。HAZ析出粗大的短棒状稳定强化相β(Mg2Si)。焊缝显微硬度最低,约为65 HV。焊接接头的抗拉强度为270 MPa,断后伸长率为6.0%。     

淬火工艺对M390刀具钢力学性能的影响

采用X射线衍射(XRD)和扫描电镜(SEM)等研究了经不同工艺淬火后M390刀具钢的物相、显微组织、硬度及拉伸性能。结果表明：随淬火温度从1100℃升高到1200℃,M390刀具钢的基体组织依次由铁素体为主转变为马氏体为主,再到马氏体与残留奥氏体的混合,而晶粒尺寸未发生明显变化,碳化物类型均为M₇C₃和M₂₃C₆;1150℃保温30 min水淬后基体组织以马氏体为主,含有少量的残留奥氏体,相连碳化物占比与圆度值均最小,硬度达到峰值62.38 HRC,抗拉强度与断裂应变总量分别为1121.88 MPa和3.25%,强韧性匹配最优。     

激光焊接过程中U-Nb合金的焊接接头微观组织与力学性能研究

以U-Nb合金为对象,研究了激光焊接过程中U-Nb合金焊接接头的微观组织和力学性能。结果表明,U-Nb合金母材的微观组织为片层状结构,主要物相为α-U+γ-U双相混合珠光体。U-Nb合金焊缝区的组织为致密的α-马氏体,相比于母材中的两相珠光体,屈服强度由820 MPa升高到1 200 MPa,塑性从25%下降到4%左右。     

轧制复合板及焊接接头组织与力学性能

为了能够更好的指导复合材料焊接工艺的制定,采用自熔等离子弧焊、埋弧焊和钨极气体保护焊3种焊接方法进行组合焊接。焊后通过金相显微镜、扫描电子显微镜、X射线能谱仪等分析方法,分析了轧制复合板及其接头的微观组织、界面元素分布、显微硬度及拉伸性能。结果表明,基材和覆材（复合材料的耐腐蚀层）界面元素扩散层厚度约10μm,由于增碳层和脱碳层的存在,显微硬度值随之升高和降低,抗拉强度达665 MPa,断口形貌呈韧脆混合断裂特征。焊接后,基材与过渡层焊缝界面扩散层厚度约5μm,基材与覆层焊缝界面扩散层厚度约3μm;第一道覆层焊缝由于受到多道焊缝焊接热的作用,铁素体体积分数含量达65%,平均显微硬度约380 HV0.2;接头抗拉强度与复合板相比降低约11%,断口韧窝大小、深度明显减小,断裂在焊缝处。     

焊接工艺对SUS444铁素体不锈钢焊接接头组织和力学性能的影响

设计了三种焊接工艺焊接SUS444铁素体不锈钢,通过金相、弯曲、拉伸和冲击等方法研究了其焊接接头的微观组织和力学性能.结果表明:三种焊接工艺都能得到抗弯性能和抗拉性能较好的焊接接头,采用线能量小于10k.J/cm两道次焊接的热影响区最窄,晶粒尺寸最小,常温冲击功最高,冲击断口为韧窝断口;填充奥氏体不锈钢焊丝可以保证焊缝具有足够的韧性,不填焊丝焊缝冲击功只有10J,呈现脆性断裂形貌.     

热处理对9Ni钢焊接接头组织与性能的影响

对9Ni钢焊接接头分别进行了QT处理和IHT处理,采用拉伸、硬度、冲击试验,断口电镜扫描等方法研究了两种热处理对焊接接头显微组织及性能的影响。结果表明,未经热处理时焊缝的组织为细晶铁素体+针状铁素体;QT处理后焊缝的组织为马氏体+奥氏体;IHT处理后焊缝组织为马氏体+奥氏体+铁素体。QT与IHT处理均能使9Ni钢焊接接头的强度、硬度下降,塑性上升;IHT处理后焊接接头的伸长率达到29.0%,塑性优于QT态。经QT和IHT处理后,焊缝的低温冲击吸收能量分别从48 J上升至78 J和100 J;IHT处理可明显提升焊缝的低温韧性,其冲击断口为典型的韧性断裂。     

热处理工艺对系泊链焊接接头组织与性能的影响

分析了不同热处理工艺对22MnCrNiMo钢系泊链的焊接接头的组织和力学性能的影响.结果表明,22MnCrNiiMo系泊链钢焊接接头经过930℃×30 min+620℃×30 min一次淬火回火后,强度和塑性明显改善;经过930℃×30min+930℃×30 min+620℃×30min二次循环淬火回火后,晶粒更加细小均匀,消除了大小晶粒不均匀的情况,力学性能尤其是塑性和冲击韧性得到进一步提高.     

Effect of post-weld heat treatment on microstructure and mechanical properties of welded joints of 6061-T6 aluminum alloy

6061 aluminum alloy T-joints were welded by double-pulsed MIG welding process. Then, the post-weld heat treatment was performed on the welded T-joints. The weld microstructure under different aging temperature and time was investigated by transmission electron microscopy and scanning electron microscopy. The mechanical properties were examined by hardness test and tensile test. The results showed that the micro-hardness was sensitive to heat treatment temperature and time. Increasing temperature was beneficial to the shortening of peak aging time. There were a large number of dislocations and few precipitates in the welded joints. With the increase of post-weld heat treatment temperature and time, the density of dislocation decreased. Meanwhile, the strengthening phase precipitated and grew up gradually. When the post-weld heat treatment temperature increased up to 200 °C, large Q' phases were observed. And they were responsible for the peak value of the micro-hardness in the welded joints.     

热处理对新型铸造模具钢焊接接头组织和性能的影响

对新型铸造模具钢进行焊接修复,研究焊后热处理对焊接接头组织和性能的影响。结果表明,焊后回火处理使模具钢完全淬火区组织由淬火马氏体转变成回火马氏体,不完全淬火区和回火区组织变化不明显。回火处理后淬火区和焊缝硬度明显降低,焊接接头抗拉强度增加。焊后回火处理对焊缝磨损率和平均摩擦系数影响不大。     

热处理工艺对0Cr13Ni5Mo钢焊接接头组织和性能的影响

对马氏体不锈钢0Cr13Ni5Mo焊接接头经过1000℃油淬后,分别进行了600℃,620℃+600℃,400℃回火。通过显微组织分析、拉伸试验、冲击试验和硬度检测对3种焊接接头的组织和力学性能进行了研究。结果表明,3种焊接接头中焊缝组织粗大,硬度最高;焊接接头的韧性低于相应热处理状态下母材的韧性;随着回火温度的降低,韧性下降,强度提高。二次回火比一次回火组织更加细小,强度和韧性更好;620℃+600℃二次回火后焊接接头具有比较理想的综合力学性能。     

交流CMT焊接工艺对2198铝锂合金接头组织及性能的影响

铝锂合金是航空航天设备减重的理想轻质高强材料。采用交流CMT工艺并填充ER4043焊丝焊接厚2 mm的2198-T8铝锂合金薄板,并采用金相显微镜、维氏显微硬度计和拉伸试验机研究交流CMT对2198铝锂合金接头气孔、显微组织、力学性能的影响。结果表明,焊接电流90 A、电压10.7 V、焊接速度80 cm/min时,焊缝成形良好,焊接接头无宏观裂纹缺陷;利用显微镜可观察到焊接接头存在较多的气孔;熔合线显微硬度最低为68 HV;接头最大抗拉强度270 MPa,达到母材的64.3%,断裂方式为准解理断裂。     

热处理工艺对钢丝的组织及力学性能的影响

对直径ф3.2 mm的半成品钢丝采用重新奥氏体化后研究在不同风冷条件下力学性能的变化,探索了奥氏体化温度及风冷速度对70钢丝性能的影响关系.结果表明,随着保温温度增加钢丝的伸长率和断面收缩率随之下降;在相同奥氏体化温度下随冷却速度的加快,钢丝抗拉强度呈上升趋势,伸长率和断面收缩率没明显变化.钢丝在790℃奥氏体化,风冷时风机频率控制在50 Hz时可获得接近铅浴处理的力学性能.     

后热处理对激光焊接7075铝合金显微组织与力学性能影响

采用激光自熔焊接技术制备7075高强铝合金接头,研究了后热处理对接头显微组织与拉伸性能的影响. 采用SEM与EBSD系统表征了后热处理对7075Al接头显微组织演变与拉伸断裂行为的影响. 结果表明,焊缝中心到母材依次存在等轴晶区域、柱状晶区域、胞状晶区域与母材轧制态区域,并且胞状晶区域与等轴晶区域为接头薄弱区域. 与未后热处理接头相比,后热处理接头平均抗拉强度达到475 MPa,同比提升约59%. 后热处理构筑的纳米沉淀相触发了第二相强化机制,这是提升接头抗拉强度的主要因素.     

焊后热处理对P92钢焊接接头显微组织和力学性能的影响

采用光学金相显微镜和力学性能测试等方法,研究了电阻履带式和中频感应两种不同的焊后热处理方法对P92钢焊接接头显微组织和力学性能的影响。结果表明:中频感应处理下的焊缝组织较为细小,马氏体板条界面变得更加模糊;焊接接头各层母材、热影响区及焊缝硬度值分布均匀,内、中和外层的硬度差值较小;焊缝及热影响区冲击吸收能量沿壁厚方向分布较为均匀,且均高于P92母材标准要求值。因而,中频感应加热法不仅可以很好地改善焊缝组织,而且在壁厚方向上,可以使焊缝韧性等力学性能更加均匀。      

填充ER309焊丝的异种钢接头二型边界形成机理

提出对电弧施加横向磁场的方法,通过偏转电弧改变焊缝两侧电弧热分配,从而提升焊缝成形质量. 为了掌握外加横向磁场对电弧热输入分配的影响机制,开展了GTAW电弧热输入分配规律研究;建立了外加横向磁场下的异种钢角焊缝GTAW电弧-熔池耦合瞬态三维模型,对电弧温度场、电磁场、流场开展了耦合计算;对比分析了偏转焊枪与外加横向磁场偏转电弧两种电弧热量分配方式;在上述工作的基础上,研究了外加横向磁场偏转电弧方式磁感应强度对熔透形态和电弧热分配的影响规律. 结果表明,偏转焊枪方式在角焊中适应性较差,而外加横向磁场偏转电弧可获得更好的焊接质量. 相关研究可为此类异种钢角焊的焊接工艺参数优化提供技术支持.