Grinding Characteristics Of Directionally Aligned SiC Whisker Wheel-Comparison With Al2O3 Fiber Wheel

A unique SiC whisker wheel was invented,in which the whiskers were aligned normally to the grinding wheel surface.In this paper,grindabilities of the SiC whisker wheel are investigated and compared with those of other wheels of SiC grains,Al2O3 grains,as well as Al2O3 long and short fibres which were also aligned normally to the grinding wheel surface,respectively.The main research contents concern grinding characteristics of a directionally aligned SiC whisker wheel such as material-removal volume,wheel-wear rates,integrity of the ground surfaces,grinding ratios and grinding efficiency.Furthermore,grinding wheels of whiskers and fibres have a common disadvantage:they tend to load easily.The authors have proposed a simple method of loading-free grinding to overcome this propensity and investigate some related grinding characteristics under loading-free grinding conditions.     

Al_2O_3/SiC纳米陶瓷复合材料的制备及力学性能

采用一次粒径分别为10nm和15nm的αAl2O3和SiC粉体为原料,制备了Al2O3/SiC纳米陶瓷复合材料·纳米SiC颗粒明显抑制Al2O3基体晶粒的长大,SiC体积分数超过4%时,材料的断裂方式由沿晶断裂变为穿晶断裂·随SiC含量的增加,Al2O3/SiC纳米复合材料的硬度增大·材料的弯曲强度和断裂韧性在SiC体积分数为5%时达到最大值·最大三点弯曲强度和断裂韧性分别为641MPa和47MPam1/2,明显高于热压单相Al2O3陶瓷(344MPa和31MPam1/2)·复合材料的强化主要来源于内晶颗粒残余应力强化和晶粒细化...     

高温SiC/Al2O3复合抗氧化涂层性能的研究

本文通过SiC及SiC/Al2O3复合涂层抗氧化性能的研究，认为采用高温浸渗工艺，在石墨制品表面形成的SiC涂层与基体有合理的界面结构，该涂层能对石墨制品起到良好的抗氧化防护作用。而SiC/Al2O3复合涂层使石墨制品具有更佳的抗氧化能力。     

纳米SiC颗粒对Al2O3—ZrO2复合材料断裂模式的影响

本文观察了Al2O3-ZrO2和纳米SiC复合Al2O3-ZrO2陶瓷材料的断口形貌。在Al2O3-ZrO2样品中表现为典型的沿晶断裂。复合纲米SiC颗粒后,出现相当一部分的穿晶断裂形貌。并且讨论论了残余热应力对断裂模式的影响。     

Al_2O_3-SiC-C砖基质组成对抗渣性影响

分析了Ａｌ２Ｏ３ＳｉＣＣ砖基质组成对抗渣性影响。实验结果表明,以莫来石为基质的Ａｌ２Ｏ３－ＳｉＣ－Ｃ砖,其抗渣性优于以刚玉为基质的制品,并用ＣａＯ－Ａｌ２Ｏ３－ＳｉＯ２三元系统相图给予了解释。     

SiC_p/Al_2O_(3f) 混杂增强 2024Al 复合材料摩擦磨损性能的研究

研究了２０２４铝合金、ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料与汽车刹车材料对磨时的摩擦磨损性能．借助扫描电镜对磨损形貌的观察,分析了材料的磨损机理．在本研究的试验条件下,２０２４铝合金的磨损极为严重,ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的耐磨性能良好．由于ＳｉＣｐ／Ａｌ２Ｏ３ｆ混杂增强２０２４Ａｌ复合材料的密度较低,因而该材料在汽车工业中有广泛的应用前景．