废旧锂电池中有价金属回收及三元正极材料的再制备

探讨了磷酸体系下不同因素对废旧锂电池正极材料中有价金属浸出效率的影响，结果表明：在浸出时间60min，反应温度60℃，磷酸浓度2mol/L，液固比20mL/g，还原剂(H₂O₂)体积分数为4%时，可得最佳浸出效果，Co、Li、Mn、Ni浸出效率分别可达96.3%、100%、98.8%和99.5%；浸出液添加相应比例金属离子，采用草酸共沉淀法制备前体材料(Ni_1/3Co_1/3Mn_1/3)C₂O₄，并得到相应再生磷酸溶液。再生磷酸进行循环浸出实验，实验研究结果表明：循环浸出5次之后Li的浸出率仍可保持在90.1%，而Co、Mn和Ni的浸出率在75.0%以上。前体添加锂源Li₂CO₃煅烧合成Li(Ni_1/3Co_1/3Mn_1/3)O₂材料，考察了不同温度对Li(Ni_1/3Co_1/3Mn_1/3)O₂材料合成的影响，结果显示，当合成温度为800℃时，得到的材料性能最优良，初次放电容量可达136.4mA·h/g。在0.2C下经过50圈循环后容量保持率为97.2%。     

Li3PO4掺杂的Li(Ni0.5Co0.2Mn0.3)O2锂离子电池正极材料的流变相法合成及电化学性能表征

采用氢氧化物共沉淀法制备了锂离子电池正极材料前驱体(Ni_0.5Co_0.2Mn_0.3)(OH)₂,并用流变相反应法合成了Li₃PO₄掺杂的Li(Ni_0.5Co_0.2Mn_0.3)O₂锂离子电池正极材料。运用X射线粉末衍射和恒电流充放电对产物进行了结构和电化学性能的表征,结果表明Li₃PO₄掺杂的Li(Ni_0.5Co_0.2Mn_0.3)O₂具有标准的层状α-NaFeO₂结构,样品为1 μm左右的片状一次颗粒聚集而成的类球形二次颗粒。掺杂1%(质量分数)Li₃PO₄的Li(Ni_0.5Co_0.2Mn_0.3)O₂锂离子电池在0.1C的倍率下首次放电比容量达到188.6 mA·h·g^-1(2.2～4.6 V vs Li⁺/Li),30次循环后容量保持率为 92.9%。循环伏安、交流阻抗测试表明Li₃PO₄的掺杂可减少充放电过程中电解液和电极之间的电荷传递电阻和锂离子扩散电阻,减小极化作用,从而提升了Li(Ni_0.5Co_0.2Mn_0.3)O₂材料的电化学性能。     

Ce1−xCuxO2−x/Al2O3/FeCrAl catalysts for catalytic combustion of methane

A series of the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts (x = 0–1) were prepared. The structure of the catalysts was characterized using XRD, SEM and H₂-TPR. The catalytic activity of the catalysts for the combustion of methane was evaluated. The results indicated that in the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts the surface phase structure were the Ce_1−xCu_xO_2−x solid solution, -Al₂O₃ and γ-Al₂O₃. The surface particle shape and size were different with the variety of the molar ratio of Ce to Cu in the Ce_1−xCu_xO_2−x solid solution. The Cu component of the Ce_1−xCu_xO_2−x/Al₂O₃/FeCrAl catalysts played an important role to the catalytic activity for the methane combustion. There were the stronger interaction among the Ce_1−xCu_xO_2−x solid solution and the Al₂O₃ washcoats and the FeCrAl support.     

Electrical resistivity and thermopower of (La1−xSrx)MnO3 and (La1−xSrx)CoO3 at elevated temperatures

Electrical resistivity and Seebeck (S) measurements were performed on (La_1−xSr_x)MnO₃ (0.02x0.50) and (La_1−xSr_x)CoO₃ (0x0.15) in air up to 1073 K. (La_1−xSr_x)MnO₃ (x0.35) showed a metal-to-semiconductor transition; the transition temperature almost linearly increased from 250 to 390 K with increasing Sr content. The semiconductor phase above the transition temperature showed negative values of S. (La_1−xSr_x)CoO₃ (0x0.10) showed a semiconductor-to-metal transition at 500 K. Dominant carriers were holes for the samples of x0.02 above room temperature. LaCoO₃ showed large negative values of S below ca. 400 K, indicative of the electron conduction in the semiconductor phase.     

Synthesis, characterization and catalytic activity for NO–CO reaction of Pd–(La, Sr)2MnO4 system

La_xSr_2−xMnO₄ (0 ≤ x ≤ 0.8) oxides were synthesized and single-phase K₂NiF₄-type oxides were obtained in the range of 0.1 ≤ x < 0.5. The catalytic activity of La_xSr_2−xMnO₄ for NO–CO reaction increased with increasing x in the range of solubility limit of La. La_0.5Sr_1.5MnO₄ showed the highest activity among La_xSr_2−xMnO₄ prepared in this study, but its activity was inferior to perovskite-type La_0.5Sr_0.5MnO₃. Among the Pd-loaded catalysts, however, Pd/La_0.8Sr_1.2MnO₄ showed the higher activity and the selectivity to N₂ than Pd/La_0.5Sr_0.5MnO₃ and Pd/γ-Al₂O₃. The excellent catalytic performance of Pd/La_0.2Sr_1.2MnO₄ could be ascribable to the formation of SrPd₃O₄ which was detected by XRD in the catalyst but not in the other two catalysts.     

The homogeneity range and the microwave dielectric properties of the BaZn2Ti4O11 ceramics

Ceramics with a composition close to BaZn₂Ti₄O₁₁ were synthesized according to various substitutional mechanisms in order to verify an existence of a homogeneity range in the vicinity of this composition. Structural and microstructural investigations showed that the crystal structure of BaZn₂Ti₄O₁₁ was formed in the homogeneity range corresponding to the formula BaZn_2 − xTi₄O_11 − x (0 < x < 0.1). Densely sintered BaZn_2 − xTi₄O_11 − x (0 < x < 0.1) ceramics exhibited a dielectric constant around 30, τ_f = −30 ppm/K and high Q × f values, which increased from 68,000 GHz at x = 0 to 83,000 GHz at x = 0.05. Structurally, the deficiency of Zn in BaZn_2 − xTi₄O_11 − x (0 < x < 0.1) resulted in a slight decrease in the unit-cell volume. The influence of secondary phases in the BaZn₂Ti₄O₁₁-based materials on the microwave dielectric properties was also investigated. A presence of small amounts of ZnO, BaTiO₃, hollandite-type solid solutions (Ba_xZn_xTi_8 − xO₁₆) and BaTi₄O₉ caused a decrease in Q × f values.     

AMnO3 (A=La, Nd, Sm) and Sm1−xSrxMnO3 perovskites as combustion catalysts: structural, redox and catalytic properties

Catalytic combustion of methane has been investigated over AMnO₃ (A = La, Nd, Sm) and Sm_1−xSr_xMnO₃ (x = 0.1, 0.3, 0.5) perovskites prepared by citrate method. The catalysts were characterized by chemical analysis, XRD and TPR techniques. Catalytic activity measurements were carried out with a fixed bed reactor at T = 623–1023 K, space velocity = 40 000 N cm³ g⁻¹ h⁻¹, CH₄ concentration = 0.4% v/v, O₂ concentration = 10% v/v.

Specific surface areas of perovskites were in the range 13–20 m² g⁻¹. XRD analysis showed that LaMnO₃, NdMnO₃, SmMnO₃ and Sm_1−xSr_xMnO₃ (x = 0.1) are single phase perovskite type oxides. Traces of Sm₂O₃ besides the perovskite phase were detected in the Sm_1−xSr_xMnO₃ catalysts for x = 0.3, 0.5. Chemical analysis gave evidence of the presence of a significant fraction of Mn(IV) in AMnO₃. The fraction of Mn(IV) in the Sm_1−xSr_xMnO₃ samples increased with x. TPR measurements on AMnO₃ showed that the perovskites were reduced in two steps at low and high temperature, related to Mn(IV) → Mn(III) and Mn(III) → Mn(II) reductions, respectively. The onset temperatures were in the order LaMnO₃ > NdMnO₃ > SmMnO₃. In Sm_1−xSr_xMnO₃ the Sr substitution for Sm caused the formation of Mn(IV) easily reducible to Mn(II) even at low temperature. Catalytic activity tests showed that all samples gave methane complete conversion with 100% selectivity to CO₂ below 1023 K. The activation energies of the AMnO₃ perovskites varied in the same order as the onset temperatures in TPR experiments suggesting that the catalytic activity is affected by the reducibility of manganese. Sr substitution for Sm in SmMnO₃ perovskites resulted in a reduction of activity with respect to the unsubstituted perovskite. This behaviour was related to the reduction of Mn(IV) to Mn(II), occurring under reaction conditions, hindering the redox mechanism.     

Microwave dielectric properties and co-firing with copper of (Bi1−xCux)(Nb1−xWx)O4 ceramics

Effect of substitution of CuO and WO₃ on the microwave dielectric properties of BiNbO₄ ceramics and the co-firing between ceramics and copper electrode were investigated. The (Bi_1−xCu_x)(Nb_1−xW_x)O₄ (x = 0.005, 0.01, 0.015, 0.02) composition can be densified between 900 and 990 °C. The microwave dielectric constants lie between 36 and 45 and the pores in ceramics were found to be the main influence. The Q values changes between 1400 and 2900 with different x values and sintering temperatures while Q_f values lie between 6000 and 16,000 GHz. The microwave dielectric losses, mainly affected by the grain size, pores, and the secondary phase, are discussed. The (Bi_1−xCu_x)(Nb_1−xW_x)O₄ ceramics and copper electrode was co-fired under N₂ atmosphere at 850 °C and the EDS analysis showed no reaction between the dielectrics and copper electrodes. This result presented the (Bi_1−xCu_x)(Nb_1−xW_x)O₄ dielectric materials to be good candidates for LTCC applications with copper electrode.     

Catalytic oxidation of nitrogen monoxide over La1−xCexCoO3 perovskites

This paper presents an investigation on the NO oxidation properties of perovskite oxides. La_1−xCe_xCoO₃ (x = 0, 0.05, 0.1, 0.2, 0.3, 0.4) perovskite-type oxides were synthesized through a citrate method and characterized by XRD, BET and XPS. The catalytic activities were enhanced significantly with Ce substitution, and achieved the best when x was 0.2, but decreased at higher x values. The performed characterizations reveal that the adsorbed oxygen on the surface plays an important role in the oxidation of NO into NO₂. The surface compounds after the co-adsorption of NO and O₂ at room temperature, were investigated by DRIFTS and TPD experiments. Three species: the bridging nitrate, the hyponitrites and the monodentate nitrate, were formed on the surface. The order of thermal stabilities was as follows: monodentate > hyponitrite > bridging. Among them, only the monodentate nitrate which decomposed at above 300 °C, would desorb NO₂ into the gas phase. When Ce was added, the temperature of monodentate nitrate desorption became low and the adsorption of the other two species decreased. This might be related to the oxidation state of Co on the surface. Analysis by synthesizing the characterization results and catalytic activity data shows that large amounts of adsorbed oxygen, small amount of inactive compounds on the surface and low NO₂ desorption temperature are favorable for the oxidation of NO.     

A stabilization mechanism for the perovskite La2/3TiO3 compound with Fe2O3: A structural and electrical investigation

We have stabilized the perovskite La_2/3TiO₃ by adding LaFeO₃ and shown that in general the stabilization mechanism for the (1 − x)La_2/3TiO_3–xLaFeO₃ mixture involves the formation of a solid solution for compositions with x ≥ 0.04. The crystal structure of the solid solution transforms from orthorhombic to tetragonal at x = 0.2, becomes cubic in the range 0.3 < x < 0.8, and transforms again into orthorhombic (typical for pure LaFeO₃) for values greater than 0.8. Detailed impedance-spectroscopy measurements for various compositions and conditions showed that the limiting step in the conduction mechanism was conduction across the grain boundaries. In the concentration range 0.04 < x < 0.25 the room temperature conductivity increases up to 0.0017 S cm⁻¹, after which it decreases again. Part of the initial increase is probably due to the formation of free electrons in accordance with (Fe_Ti)′ → (Fe_Ti)^x + n′. Other defect-formation mechanisms are also discussed, but are ruled out for a variety of reasons. Another interesting phenomenon that also affected the average conductivity was identified, i.e., the variation of the average particle size with composition.     

Regeneration of thermally aged Pt-Rh/CexZr1−xO2-Al2O3 model three-way catalysts by oxychlorination treatments

Pt-Rh/Ce_xZr_1−xO₂-Al₂O₃ with 0.6 and 1.0 wt.% noble metal loadings were prepared and characterized for their metal dispersion with respect to Ce_xZr_1−xO₂-free Pt-Rh/Al₂O₃ in fresh, thermally aged and oxychlorinated states. Thermal ageing at 973 K led to loss of metal dispersion in all cases but to negligible effect on the dispersion of the Ce_xZr_1−xO₂ component where present. Oxychlorination was able to fully recover metal dispersion in all cases but led to different effects on the redox properties of Ce_xZr_1−xO₂ which appeared to be related to the metal loadings. Despite showing improved dispersion following regeneration, higher loaded catalyst showed no improvement in light-off performance for either NO reduction or CO oxidation and showed poorer oxygen storage (OSC) ability, particularly at higher temperatures. Lower loaded catalyst showed improved dispersion, improved OSC and reduced light-off temperatures for NO reduction and CO oxidation after oxychlorination compared to that in the thermally aged state.     

Preparation of CexZr1−xO2 (x = 0.75, 0.62) solid solution and its application in Pd-only three-way catalysts

Nanoparticles of Ce_xZr_1−xO₂ (x = 0.75, 0.62) were prepared by the oxidation-coprecipitation method using H₂O₂ as an oxidant, and characterized by N₂ adsorption, XRD and H₂-TPR. Ce_xZr_1−xO₂ prepared had single fluorite cubic structure, good thermal stability and reduction property. With the increasing of Ce/Zr ratio, the surface area of Ce_xZr_1−xO₂ increased, but thermal stability of Ce_xZr_1−xO₂ decreased. The surface area of Ce_0.62Zr_0.38O₂ was 41.2 m²/g after calcination in air at 900 °C for 6 h. TPR results showed the formation of solid solution promoted the reduction of CeO₂, and the reduction properties of Ce_xZr_1−xO₂ were enhanced by the cycle of TPR-reoxidation. The Pd-only three-way catalysts (TWC) were prepared by the impregnation method, in which Ce_0.75Zr_0.25O₂ was used as the active washcoat and Pd loading was 0.7 g/L. In the test of Air/Fuel, the conversion of C₃H₈ was close to 100% and NO was completely converted at λ < 1.025. The high conversion of C₃H₈ was induced by the steam reform and dissociation adsorption reaction of C₃H₈. Pd-only catalyst using Ce_0.75Zr_0.25O₂ as active washcoat showed high light off activity, the reaction temperatures (T₅₀) of 50% conversion of CO, C₃H₈ and NO were 180, 200 and 205 °C, respectively. However, the conversions of C₃H₈ and NO showed oscillation with continuously increasing the reaction temperature. The presence of La₂O₃ in washcoat decreased the light off activity and suppressed the oscillation of C₃H₈ and NO conversion. After being aged at 900 °C for 4 h, the operation windows of catalysts shifted slightly to rich burn. The presence of La₂O₃ in active washcoat can enhance the thermal stability of catalyst significantly.     

Thermoelectric characterization of NaxMx/2Ti1−x/2O2 (M=Co, Ni and Fe) polycrystalline materials

Layered -titanate materials, Na_xM_x/2Ti_1−x/2O₂ (M=Co, Ni and Fe, x=0.2–0.4), were synthesized by flux reactions, and electrical properties of polycrystalline products were measured at 300–800 °C. After sintering at 1250 °C in Ar, all products show n-type thermoelectric behavior. The values of both d.c. conductivity and Seebeck coefficient of polycrystalline Na_0.4Ni_0.2Ti_0.8O₂ were ca. 7×10³ S/m and ca. −193 μV/K around 700 °C, respectively. The measured thermal conductivity of layered -titanate materials has lower value than conductive oxide materials. It was ca. 1.5 Wm⁻¹ K⁻¹ at 800 °C. The estimated thermoelectric figure-of-merit, Z, of Na_0.4Ni_0.2Ti_0.8O₂ and Na_0.4Co_0.2Ti_0.8O₂ was about 1.9×10⁻⁴ and 1.2×10⁻⁴ K⁻¹ around 700 °C, respectively.     

Effect of ceria–zirconia ratio on the interaction of CO with PdO/Al2O3–(Cex–Zr1−x)O2 catalysts prepared by sol–gel method

The current work is devoted to study of CO interaction with PdO/Al₂O₃–(Ce_x–Zr_1−x)O₂ catalysts. Ceria–zirconia–alumina supports with different Ce/Zr ratio were prepared by sol–gel technique. The FT-IR characterization of CO adsorbed at −120 and 25 °C on oxidized and reduced samples revealed that Ce/Zr ratio modifies the surface properties of support and oxidation state of palladium. The catalyst with Ce/Zr molar ratio 0.5/0.5 was characterized with the highest ability to stabilize palladium in oxide state and the highest activity to oxidize CO. Redox treatment of catalysts improves their catalytic activity.     

K+掺杂LiNi1/3Co1/3Mn1/3O2材料的制备及电化学性能研究

锂离子电池正极材料LiNi_1/3Co_1/3Mn_1/3O₂具有放电比容量大、热稳定性好、成本低、安全性能好等优点,但其倍率性能有待进一步提升。本文采用水热法制备了K⁺掺杂LiNi_1/3Co_1/3Mn_1/3O₂材料LNCM-xK。通过X射线衍射谱、场发射扫描电镜和X射线光电子能谱表征LNCM-xK的形貌和结构,通过电化学工作站和蓝电测试系统测试其电化学性能。结果表明:K⁺掺杂能有效降低阳离子混排程度,改善LiNi_1/3Co_1/3Mn_1/3O₂材料的电化学性能,其中当x=0.125时K⁺掺杂LiNi_1/3Co_1/3Mn_1/3O₂样品(LNCM-0.125K)阳离子混排程度最低;LNCM-0.125K样品电化学性能最佳,0.2 C下50次循环后容量保持率为96.15%;在不同电流密度(0.2 C,0.5 C,1 C,2 C,5 C)下进行倍率性能测试,连续充放电30次后LNCM-0.125K样品容量保持率为97.00%。     

Effect of glass additions on the sintering and microwave properties of composite dielectric ceramics based on BaO–Ln2O3–TiO2 (Ln = Nd, La)

Ten weight percent BBZS (Bi₂O₃, B₂O₃, ZnO and SiO₂) glass was added to x(Ba₄Nd_9.333Ti₁₈O₅₄) − (1 − x)(BaLa₄Ti₄O₁₅) (BNLT, 0 ≤ x ≤ 1) composite dielectric ceramics to lower their sintering temperature whilst retaining microwave properties useful for low temperature co-fired ceramic and antenna core technology. With the addition of 10 wt% BBZS glass, dense BNLT composite ceramics were produced at temperatures between 950 and 1140 °C, depending on composition (x), an average reduction of sintering temperature by 350 °C. X-ray diffraction, scanning and transmission electron microscopy and Raman spectroscopy studies revealed that there was limited inter-reaction between BLT/BNT and the BBZS glass. Microwave property measurement showed that the addition of BBZS glass to BNLT ceramics had a negligible effect on _r and τ_f, although deterioration in the measured quality factor (Qf) was observed. The optimised composition (xBNT − (1 − x)BLT)/0.1BBZS (x = 0.75) had _r  61, τ_f  38 ppm/°C and Qf  2305 GHz.     

Structure and microwave dielectric properties of Nd(2−x)/3LixTiO3

The structure evolution, and microwave dielectric properties of Nd_(2−x)/3Li_xTiO₃ ceramics (0 ≤ x ≤ 0.5) were investigated in this paper. X-ray diffraction (XRD) and scanning electron microscopy (SEM) results show that samples with x = 0.2–0.4 exhibit single phase. Multi-phases of Nd₂Ti₂O₇, Nd_2/3TiO₃ and Nd₂Ti₄O₁₁ were observed when x = 0 and 0.1. The concentration and ordering degree of A-site decrease with the increase of x value. The dielectric constant increases up to x = 0.2 and then decreases with the further increase of x value. The Qf value decreases with the increase of x value. The temperature coefficient of resonant frequency exhibits negative value and the absolute value decreases greatly with the decrease of x value.     

Synthesis and characterization of Li ion conducting La2/3−xLi3xTiO3 by a polymerizable complex method

Ultrafine lithium ion conducting La_2/3−xLi_3xTiO₃ (x = 0.11, LLT) powder was synthesized by a simple polymerizable complex method based on the Pechini-type process. The formation mechanism, homogeneity and microstructure of the samples were investigated by thermal analysis (TG/DTA), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). XRD analysis indicated the formation of pure perovskite-type phase. The powder synthesized at a temperature as low as 900 °C in a much shorter time than solid-state reaction method was well crystallized. The lithium ion conductivity of the LLT ceramics sintered at 1200 °C was found to be 9 × 10⁻⁴ S/cm at room temperature.     

Effect of Ca on the microstructural and electrochemical properties of La2.3−xCaxMg0.7Ni9 hydrogen storage alloys

The microstructural and electrochemical properties of La_2.3−xCa_xMg_0.7Ni₉ hydrogen storage alloys have been studied systematically. The microstructure examined by XRD, SEM and EDX shows that the alloys consist of multi-phases, which are (La, Mg)₂Ni₇ phase, LaMgNi₄ phase, (La, Mg)Ni₃ phase and LaNi₅ phase. It is can be found that Ca does not appear to segregate. This phenomenon is different from Mg. With increasing Ca content, the main phase varies from (La, Mg)₂Ni₇ phase (x = 0) to (La, Mg)Ni₃ phase (x = 0.3), LaNi₅ phase (x = 0.6, 0.8) and (La, Mg)Ni₃ phase (x = 1.0, 1.3). The maximum discharge capacities of the alloy electrodes increase from 244.6 mAh/g (x = 0) to 380 mAh/g (x = 1.0), and then decrease to 353.6 mAh/g (x = 1.3). The discharge capacities of the alloys are related to phase content. Cell volumes of LaNi₅ phase, (La, Mg)₂Ni₇ phase and (La, Mg)Ni₃ phase all decrease and the high rate dischargeability (HRD) is improved by adding Ca. The alloy electrodes also show relative good cycling stability up to 100 cycles.     

AFeO3 (A=La, Nd, Sm) and LaFe1−xMgxO3 perovskites as methane combustion and CO oxidation catalysts: structural, redox and catalytic properties

Catalytic methane combustion and CO oxidation were investigated over AFeO₃ (A=La, Nd, Sm) and LaFe_1−xMg_xO₃ (x=0.1, 0.2, 0.3, 0.4, 0.5) perovskites prepared by citrate method and calcined at 1073 K. The catalysts were characterized by X-ray diffraction (XRD). Redox properties and the content of Fe⁴⁺ were derived from temperature programmed reduction (TPR). Specific surface areas (SA) of perovskites were in 2.3–9.7 m² g⁻¹ range. XRD analysis showed that LaFeO₃, NdFeO₃, SmFeO₃ and LaFe_1−xMg_xO₃ (x·0.3) are single phase perovskite-type oxides. Traces of La₂O₃, in addition to the perovskite phase, were detected in the LaFe_1−xMg_xO₃ catalysts with x=0.4 and 0.5. TPR gave evidence of the presence in AFeO₃ of a very small fraction of Fe⁴⁺ which reduces to Fe³⁺. The fraction of Fe⁴⁺ in the LaFe_1−xMg_xO₃ samples increased with increasing magnesium content up to x=0.2, then it remained nearly constant. Catalytic activity tests showed that all samples gave methane and CO complete conversion with 100% selectivity to CO₂ below 973 and 773 K, respectively. For the AFeO₃ materials the order of activity towards methane combustion is La>Nd>Sm, whereas the activity, per unit SA, of the LaFe_1−xMg_xO₃ catalysts decreases with the amount of Mg at least for the catalysts showing a single perovskite phase (x=0.3). Concerning the CO oxidation, the order of activity for the AFeO₃ materials is Nd>La>Sm, while the activity (per unit SA) of the LaFe_1−xMg_xO₃ catalysts decreases at high magnesium content.