基于SECM研究5083铝镁合金在不同pH NaCl溶液中的腐蚀行为

采用扫描电化学显微镜(SECM)中的极化曲线法和交流阻抗图谱法研究5083铝镁合金在不同pH NaCl溶液中的腐蚀行为,结果表明:在酸性体系(pH 3~7),随着pH的增加,其腐蚀电位正移,点蚀电位相差不大,维钝电流密度减小,电化学阻抗谱中仅有1个容抗弧且呈现收缩趋势.同时,阻抗和相位角减小,电荷传递电阻升高,耐腐蚀性能增大.在碱性体系(pH 9~12),随着pH的增加,腐蚀电流密度增加,而腐蚀电位减小,腐蚀速度由0.000 9mm/a增加到0.025 6?mm/a.电化学阻抗谱中有2个容抗弧,在pH=12处出现感抗弧.同时,阻抗和相位角减小,金属化合物颗粒溶解过程加快,合金耐腐蚀性能降低.      

5083铝合金在3.5%NaCl溶液中的电化学腐蚀行为研究

通过阳极化和交流阻抗法研究了不同Mg含量、不同的热处理状态下的5083铝合金在3．5％NaCl溶液中的电化学行为和腐蚀特征。研究结果表明：Mg含量越低,合金中B相（Mg5Al8）越少,耐蚀性越好;在轧制态以及150℃退火态,B相先沿晶界连续析出,耐蚀性较差;在200℃退火态,B相在晶界以及晶内同时呈不连续的球状析出,耐蚀性好;在280℃、330℃退火态,B相沿晶界呈连续网状析出,耐蚀性差。通过对比研究,进一步探讨了铝合金的腐蚀机理,为制定合理的热加工工艺,提高产品的耐蚀性能提供了依据。     

Ti-Ta合金在硝酸中电化学腐蚀研究

以8 mol/L硝酸溶液为腐蚀介质,对Ti-6Ta和Ti-32Ta合金进行极化曲线和交流阻抗谱测试,并与TA2纯钛进行对比,研究不同Ta含量钛合金的电化学性能差异。结果表明,加入6%的Ta元素后,合金的腐蚀电流密度比TA2纯钛降低了近一半;加入了32%的Ta元素后,合金的自腐蚀电位提高,腐蚀电流密度比TA2纯钛降低了66%;Ti-6Ta和Ti-32Ta合金腐蚀后表面氧化膜均为单层结构;添加Ta元素可以极大地提高钛合金的电荷转移电阻,使相位角升高、变宽,增强耐腐蚀性能。     

坡莫合金在pH=2.14的氯化钠溶液中的电化学腐蚀行为研究

针对金属薄膜复合板的金属膜选材问题,对坡莫合金进行成分、物相及显微硬度分析,同时研究了坡莫合金在pH=2.14氯化钠溶液中的电化学腐蚀行为,结果表明:镍成分(50%wt)的坡莫合金中的主物相为正方晶系的FeNi(97.7%wt)物相,多边形奥氏体组织;动电位极化曲线表明:镍成分(50%wt)的坡莫合金在pH=2.14的酸性氯化钠溶液中腐蚀以阳极的电化学反应为主,腐蚀速率控制在10~(-3)A/cm~2;交流阻抗表明:电化学腐蚀反应分两步,第一步为阳极的活化反应形成中间腐蚀产物并覆盖在电极表面,第二步为覆盖在电极上的中间腐蚀产物的活化溶解,腐蚀行为及腐蚀机理随着时间的延长未发生变化。     

Ti-3Ta-xNb合金在沸腾硝酸中的电化学腐蚀研究

采用非真空自耗电弧熔炼获得成分均匀的Ti-3Ta-xNb(x=0、1、3、5)合金。通过扫描电子显微镜(SEM)观察发现,随着Nb元素含量的增加,合金的等轴α相比例减少,晶粒细化。通过电化学测试研究了Ti-3Ta-xNb合金在6 mol/L沸腾硝酸溶液中的开路电位、动电位极化曲线及电化学阻抗谱。结果表明：随着Nb元素含量的增加,Ti-3Ta-xNb合金的腐蚀电流密度降低,极化电阻增加,即合金的耐蚀性增强。     

Al_(88)Ce_8Co_4非晶合金在NaCl溶液中的腐蚀行为研究

利用极化曲线测试方法、交流阻抗技术研究了Al88Ce8Co4非晶合金在NaCl溶液中的电化学腐蚀行为。研究结果表明,Al88Ce8Co4非晶合金在NaCl溶液中具有很好的耐腐蚀性能。NaCl溶液浓度严重影响Al88Ce8Co4非晶合金的抗腐蚀性能,在所研究的浓度范围内,极化曲线都表现出明显的钝化趋势,EIS图谱均由单一的容抗弧构成。在浓度为0.5mol/L~2mol/L范围内,随浓度的增加,自腐蚀电位有向负方向移动的趋势,腐蚀电流密度逐渐降低,电荷转移电阻逐渐增大,当浓度达到4mol/L时,自腐蚀电位向负方向移动较大,相较于2mol/L时,腐蚀电流密度又有所升高,电荷转移电阻有所降低。     

7075铝合金在不同pH值NaCl溶液中的腐蚀行为

用Tafel曲线和电化学阻抗谱(EIS)研究7075铝合金在不同pH值(pH=3、5、7、9、11) 的0.6 mol/L NaCl溶液中的腐蚀行为.结果表明,溶液pH值在3~7时,腐蚀电位正移,pH值在7~11时,腐蚀电位负移,pH值为11时腐蚀电位最负. pH值在3~11时,腐蚀速度呈现先降低后增大的过程,pH值为11时腐蚀速度最大,达到2.122 2 mm/a.在强酸溶液中,电化学阻抗谱中出现明显的感抗弧,表明存在不均匀点蚀现象. pH值为7和9时,电化学阻抗谱中只出现1个容抗弧,表明铝合金腐蚀属于金属基体溶解过程. pH值为11时,阻抗谱中出现2个容抗弧,表明铝合金腐蚀伴随铝合金的自溶解行为.      

咪唑啉缓蚀剂在NaCl溶液中对2099Al-Li合金的缓蚀行为

采用极化曲线、交流电化学阻抗谱（EIS）和扫描电化学显微镜（SECM）技术研究了咪唑啉在3 %（指质量分数,下同）NaCl溶液中对2099 Al-Li合金的缓蚀行为.结果表明:咪唑啉有很好的缓蚀效果.极化曲线测试和交流阻抗测试都验证了咪唑啉浓度达到0.01 mmol/L时,缓蚀效率达77 %以上的准确性.采用扫描电化学显微镜技术（SECM）研究0.01 mmol/L咪唑啉缓蚀剂在3 % NaCl+5 mmol/LKI溶液中对2099铝锂合金的缓蚀行为.结果表明:在缓蚀剂条件下,合金表面电流峰数量减少,强度减弱.      

电化学方法在不锈钢腐蚀研究中的应用现状及发展趋势

电化学手段可以实现对不锈钢材料的快速评价和腐蚀机理研究,因而受到广泛应用。在不锈钢耐蚀性评价方面,最常采用的电化学手段主要有腐蚀电位测试、交流阻抗测试、恒电位极化测试以及循环动电位极化测试。本文分别针对上述四种电化学方法在不锈钢耐蚀性评价上的应用情况进行了介绍,明确了各种检测方法的特点。腐蚀电位及交流阻抗测试是无损检测手段,可以满足长周期腐蚀监测需求;恒电位极化和循环动电位极化测试可以获得材料的极化特征参数,有利于对材料的腐蚀机理及耐蚀性进行评价。结合当前的不锈钢腐蚀研究现状,展望了电化学方法在腐蚀研究领域的发展趋势:未来电化学方法将更多作为腐蚀调控手段,需要结合其他检测技术实现对不锈钢腐蚀过程的精细分析。      

Ce含量对Al在3.5％NaCl溶液中腐蚀行为影响的研究

稀土元素及其含量对铝合金耐腐蚀性能的影响及其机制是铝合金开发利用的重要研究课题,采用高频熔炼方法制备Al1-xCex(x=0,0.2％,2.0％(原子分数))合金,通过X射线衍射、金相分析、电化学测试、扫描电镜和能谱等分别对制备的Al1-xCex合金的结构、动电位线性扫描极化曲线、浸泡与电化学腐蚀前后表面形貌的变化进行了研究;对Al1-xCex在3.5％ NaCl溶液中耐腐蚀性能与铈含量的关系进行了系统的分析.结果表明:由于Cl-离子的存在,铝在3.5％ NaCl溶液中发生点蚀破坏;稀土Ce的加入能够细化晶粒,改善合金微观结构,减弱Cl-离子对点蚀的影响;Ce元素在腐蚀表面层富集,有利于形成连续钝化膜,提高合金在NaCl溶液中的耐蚀能力;微量稀土Ce(0.2％)的加入使合金的自腐蚀电位升高,腐蚀电流密度降低,耐腐蚀性能改善明显;但随着Ce含量的增加,即含量高于铈在铝中的溶解度后,铝与铈将形成金属间化合物,基底与金属间化合物相界面的存在使合金的耐腐蚀性能有所降低,Ce含量为0.2％合金的耐腐蚀性能比Ce含量为2.0％的合金要好.所有合金腐蚀后的主要产物为Al2O3.     

Stress-corrosion cracking susceptibility of the superplastically formed 5083 aluminum alloy in 3.5 pct NaCl solution

The slow strain rate test (SSRT) method was employed to study the stress corrosion cracking (SCC) susceptibility of the superplastic 5083 Al alloy in a 3.5 pct NaCl solution after superplastic forming and various heat treatments. Experimental results showed that both superplastically formed specimens and specimens subject to the same thermal processes as that used in superplastic forming suffered severe SCC susceptibility, and obvious intergranular fracture surfaces were also observed. Furthermore, scanning transmission electron microscopy (STEM) and energy-dispersive X-ray spectroscopy (EDS) analyses demonstrated that the thermal processes of superplastic forming led to continuously distributed precipitation layers of β phase (Mg₂Al₃) at grain boundaries, i.e., sensitization had occurred. However, postforming annealing treatment at 345 °C for 1 hour eliminated the sensitization effect of both specimens. In this case, the SCC susceptibility was alleviated, and the fracture surfaces changed to a transgranular dimpled structure, characteristic of that found in the as-received specimen. From the metallographic observations, it was also seen that a number of cavities appeared at the grain boundaries of the superplastically formed specimen. However, the cavitation effect on SCC susceptibility is minor in comparison with the sensitization effect.     

填充金属对5083铝合金焊接性能的影响

采用手工MIG焊接方法,ER5087焊丝与ER5356焊丝分别对3mm5083铝合金板材进行焊接,对焊接接头的表面成形、显微组织及力学性能进行检测,研究结果表明:采用ER5087焊丝的力学性能优于ER5356焊丝;两种焊丝的焊接接头抗拉强度分别达到母材94%和84%.     

Corrosion behavior on the different zones of AA2014 welded aluminum alloy by AA5554 filler aluminum alloy with TIG process: Before and after solution heat treatments followed by ageing

In this work, we have studied the effects of solution heat treatment followed by ageing on the corrosion behavior of AA2014 aluminum alloy welded by AA5554 aluminum alloy. Two samples are then analyzed, in the first case the solution heat treatment is followed by quenching and natural ageing of 90 days (sample 1), and in the second one, the solution heat treatment is followed by quenching and artificial ageing of twelve hours at 190°C (sample 2). The principal observations can be summarized as: evaporation of magnesium in fusion zone, and diffusion of magnesium and copper from the heat affected zone to the fusion zone were identified. Solution heat treatment, quenching and 90 days of natural ageing leads to a uniform corrosion in the heat affected zone and in the fusion one, when the material is immersed for ten seconds in Keller reagent solution. After immersion in 0.3% NaCl chloride solution, and after solution treatment and quenching, we observed that applied artificial ageing at 190°C causes localized corrosion surrounding precipitates and then develops uniform corrosion in all zones, particularly in the fusion one. Finally, it is noted that the surface of different zones became nobler after applying solution heat treatment followed by natural ageing.     

5083铝合金焊接管表面裂纹产生原因分析

5083铝合金具有优良的焊接性能和良好的抗蚀性能,在能源、化工等领域被广泛应用。针对5083铝合金焊接管表面产生裂纹,使用理化检测、扫描电镜、能谱检测、金相显微等技术手段对试样的化学成分、力学性能以及金相组织进行综合分析,发现在试样母材组织和裂纹处存在大量C、Cl、Si、S、O等非金属夹杂。铝合金焊接过程中存在焊接热影响,会导致铝合金焊缝附近存在较大的内应力。结果表明,焊接过程中焊接应力的存在和材料组织中存在大量的非金属夹杂是裂纹产生的根本原因。     

5083铝合金焊接管表面裂纹产生原因分析

5083铝合金具有优良的焊接性能和良好的抗蚀性能,在能源、化工等领域被广泛应用。针对5083铝合金焊接管表面产生裂纹,使用理化检测、扫描电镜、能谱检测、金相显微等技术手段对试样的化学成分、力学性能以及金相组织进行综合分析,发现在试样母材组织和裂纹处存在大量C、Cl、Si、S、O等非金属夹杂。铝合金焊接过程中存在焊接热影响,会导致铝合金焊缝附近存在较大的内应力。结果表明,焊接过程中焊接应力的存在和材料组织中存在大量的非金属夹杂是裂纹产生的根本原因。     

铝合金5083镁元素质量分数光谱分析法不确定度的研究

本文对铝合金5083镁元素质量分数进行分析,并对测量过程中系统效应和随机效应所导致的测量结果不确定度进行评定.试验表明,不确定度的主要来源,由建立工作曲线、标准化样品及数字修约等引入.